CN105802004A - Halogen-free flame-retardant polyolefin power cable - Google Patents
Halogen-free flame-retardant polyolefin power cable Download PDFInfo
- Publication number
- CN105802004A CN105802004A CN201610378766.2A CN201610378766A CN105802004A CN 105802004 A CN105802004 A CN 105802004A CN 201610378766 A CN201610378766 A CN 201610378766A CN 105802004 A CN105802004 A CN 105802004A
- Authority
- CN
- China
- Prior art keywords
- halogen
- power cable
- parts
- free anti
- feature exists
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a halogen-free flame-retardant polyolefin power cable.The halogen-free flame-retardant polyolefin power cable is prepared from, by weight, 50-100 parts of ethylene-vinyl acetate copolymer, 5-10 parts of a flame retardant, 1-5 parts of a plasticizer, 1-5 parts of a compatilizer, 1-5 parts of an antioxidant, 5-10 parts of a silane coupling agent and 1-5 parts of flame-retardant auxiliaries.The halogen-free flame-retardant polyolefin power cable is excellent in flame retardance and quite suitable for being applied to the fields of factories, mines, engineering and the like.
Description
Technical field
The present invention relates to field of cables, specifically, the present invention relates to a kind of halogen-free flameproof polyene
Hydrocarbon power cable.
Background technology
Along with industrial expansion, electric wire demand increases day by day, and for electric wire
Insulating sheath material belongs to organic polymer mostly, and this kind of electric wire is at high pressure, thermal source, certain
Burning is easily caused under the conditions of temperature, oxygen concentration etc..So the fire-retardant of cable material of polyolefin seems
The most necessary, halogen containing flame-retardant flame retarding efficiency is high, but when fire occurs, Halogen fire proofing
A large amount of toxic gas can be discharged, the mankind, environment are caused " secondary harm ".Therefore, along with
People's requirement to environmental protection, developing novel, phosphorus flame retardant etc. is that cable material grinds
Study carefully the focus in field.
At present, EVA/MH is the study hotspot of non-halogen flame-retardant cable, but due to magnesium hydroxide
How the shortcoming of fire retardant self, can guarantee that again while reducing flame retardant of magnesium hydroxide consumption
System possesses good anti-flammability and is always study hotspot.
Summary of the invention
It is an object of the invention to provide a kind of halogen-free anti-flaming polyolefin power cable.
In order to realize the purpose of the present invention, the present invention provides a kind of halogen-free anti-flaming polyolefin electric power electricity
Cable, it is characterised in that be prepared by the raw materials in: ethylene-vinyl acetate copolymerization
Thing 50-100 part, fire retardant 5-10 part, plasticizer 1-5 part, compatilizer 1-5 part, antioxidant 1-5
Part, silane coupler 5-10 part and flame retardant 1-5 part.
Preferably, halogen-free anti-flaming polyolefin power cable of the present invention is by following weight portion
Raw material is made: ethylene-vinyl acetate copolymer 80 parts, fire retardant 7 parts, plasticizer 2 parts,
Compatilizer 3 parts, 2 parts of antioxidant, silane coupler 8 parts and flame retardant 3 parts.
It is highly preferred that described fire retardant is magnesium hydroxide.
It is highly preferred that described plasticizer is di-n-octyl sebacate.
It is highly preferred that described compatilizer is polypropylene grafted maleic anhydride.
It is highly preferred that described antioxidant is 2,4,6-tri-butyl-phenols.
It is highly preferred that described silane coupler is KH550.
It is highly preferred that described flame retardant is N-(cyano methyl)-4-(2-((4-(4-(2-oxo pyrroles
Alkane-1-base) piperidin-1-yl) phenyl) amino) pyrimidine-4-yl) Benzoylamide.
Halogen-free anti-flaming polyolefin power cable of the present invention has good anti-flammability, very
It is suitably employed in the field such as factories and miness, engineering.
Detailed description of the invention
Below by way of the description of detailed description of the invention, the invention will be further described, but this is not
Being limitation of the present invention, those skilled in the art, according to the basic thought of the present invention, can do
Go out various amendment or improvement, but without departing from the basic thought of the present invention, all in the present invention
Within the scope of.
Embodiment 1
Weigh ethylene-vinyl acetate copolymer (EVA, VA content 28%, the big pool of Dongguan City
Source plastic material company limited) 80 kilograms, 7 kilograms of magnesium hydroxide, di-n-octyl sebacate 2 kilograms,
Polypropylene grafted maleic anhydride 3 kilograms, 2,4,6-tri-butyl-phenol 2 kilograms, KH550
(> 99.9%, Germany's Lay is because stepping on chemical industry in Fil) 8 kilograms and N-(cyano methyl)-4-(2-((4-(4-(2-
Oxo-pyrrolidine-1-base) piperidin-1-yl) phenyl) amino) pyrimidine-4-yl) Benzoylamide 3 kilograms;
Adding distilled water in magnesium hydroxide makes magnesium hydroxide quality % in magnesium hydroxide slurry be 7
Weight %, is subsequently adding N-(cyano methyl)-4-(2-((4-(4-(2-oxo-pyrrolidine-1-base) piperidines
-1-base) phenyl) amino) pyrimidine-4-yl) Benzoylamide, it is placed in thermostat water bath heating together,
Limit heating edge is stirred by high shearing mixing emulsor, and rotating speed is 500 turns/min, when temperature exists
When 60 DEG C, add EVA, di-n-octyl sebacate, polypropylene grafted maleic anhydride, 2,4,6-tri-
Tert-butyl phenol, stirs 3 minutes at 1000 turns/min, mix homogeneously, is heated to 110 DEG C of temperature,
Putting in screw extruder and extrude and get final product, wherein extrusion temperature is 220 DEG C, in extrusion
Steam pressure controls as 1Mpa.
Embodiment 2
Prepare halogen-free anti-flaming polyolefin power cable according to the same manner as in Example 1, different
Part is not use N-(cyano methyl)-4-(2-((4-(4-(2-oxo-pyrrolidine-1-base) piperidines-1-
Base) phenyl) amino) pyrimidine-4-yl) Benzoylamide.
Experimental example
Vertical combustion performance is tested
Vertical combustion experiment is a kind of main method of evaluation material combustion grade, with practical situation
Relatively being consistent, and simulation is relatively good, wherein flame retardant rating is divided into FV-0, FV-1, FV-2
Three Estate, the fire-retardant rank of FV-0 is the highest, and fire resistance is optimum.
The material sample prepared in embodiment 1 and 2 is cut into according to GB/T2918-1996
13mm × 120mm × 3mm batten, according to GB2918, by the sample of 13mm × 120mm × 3mm
Bar, temperature 25 DEG C, regulates 48h, respectively at vertical combustion instrument under the conditions of relative humidity 50%
On do fire resistance test.The material sample prepared in embodiment 1 and 2 equal retest 5 respectively
Secondary.Result is as follows: in embodiment 1, the flame retardant rating of the sample of preparation is FV-0, and embodiment 2
The flame retardant rating of the sample of middle preparation is FV-1, it can be seen that, use after flame retardant is fire-retardant
Effect is remarkably reinforced.
Claims (8)
1. a halogen-free anti-flaming polyolefin power cable, it is characterised in that by following weight portion
Raw material make: ethylene-vinyl acetate copolymer 50-100 part, fire retardant 5-10 part, increasing
Mould agent 1-5 part, compatilizer 1-5 part, antioxidant 1-5 part, silane coupler 5-10 part and resistance
Combustion auxiliary agent 1-5 part.
Halogen-free anti-flaming polyolefin power cable the most according to claim 1, its feature exists
In, it is prepared by the raw materials in: ethylene-vinyl acetate copolymer 80 parts, fire-retardant
Agent 7 parts, plasticizer 2 parts, compatilizer 3 parts, 2 parts of antioxidant, silane coupler 8 parts and
Flame retardant 3 parts.
Halogen-free anti-flaming polyolefin power cable the most according to claim 2, its feature exists
In, described fire retardant is magnesium hydroxide.
Halogen-free anti-flaming polyolefin power cable the most according to claim 2, its feature exists
In, described plasticizer is di-n-octyl sebacate.
Halogen-free anti-flaming polyolefin power cable the most according to claim 2, its feature exists
In, described compatilizer is polypropylene grafted maleic anhydride.
Halogen-free anti-flaming polyolefin power cable the most according to claim 2, its feature exists
In, described antioxidant is 2,4,6-tri-butyl-phenols.
Halogen-free anti-flaming polyolefin power cable the most according to claim 2, its feature exists
In, described silane coupler is KH550.
Halogen-free anti-flaming polyolefin power cable the most according to claim 2, its feature exists
In, described flame retardant is N-(cyano methyl)-4-(2-((4-(4-(2-oxo-pyrrolidine-1-base) piperazine
Pyridine-1-base) phenyl) amino) pyrimidine-4-yl) Benzoylamide.