CN105566757A - Environmentally-friendly flexible polyvinyl chloride cable sheath composition - Google Patents

Environmentally-friendly flexible polyvinyl chloride cable sheath composition Download PDF

Info

Publication number
CN105566757A
CN105566757A CN201610073786.9A CN201610073786A CN105566757A CN 105566757 A CN105566757 A CN 105566757A CN 201610073786 A CN201610073786 A CN 201610073786A CN 105566757 A CN105566757 A CN 105566757A
Authority
CN
China
Prior art keywords
parts
polyvinyl chloride
calcium carbonate
powder
environmentally
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610073786.9A
Other languages
Chinese (zh)
Inventor
沈学忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Hua Tian Cable Co Ltd
Original Assignee
Anhui Hua Tian Cable Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Hua Tian Cable Co Ltd filed Critical Anhui Hua Tian Cable Co Ltd
Priority to CN201610073786.9A priority Critical patent/CN105566757A/en
Publication of CN105566757A publication Critical patent/CN105566757A/en
Pending legal-status Critical Current

Abstract

The invention discloses an environmentally-friendly flexible polyvinyl chloride cable sheath composition. The environmentally-friendly flexible polyvinyl chloride cable sheath composition is prepared from, by weight, 20-30 parts of bisphenol, 12-30 parts of stearic acid, 22-30 parts of ABS resin, 28-36 parts of polyvinyl chloride resin, 9-20 parts of ABS high-glue powder, 8.9-12.6 parts of an antioxidant 1035, 25-36 parts of maleic anhydride grafted ethylene, 5-9 parts of a vinyl acetate copolymer, 6-16 parts of mullite powder, 13-22 parts of asbestos powder, 31-39 parts of calcium carbonate, 10-15 parts of perlite, 9.3-15.2 parts of poly acid ammonium, 35-38 parts of pentaerythritol, 25-39 parts of antimony trioxide slightly crosslinked resin, 19-39 parts of a flame retardant, 10-20 parts of a flame retardant synergist, 20-26 parts of chlorinated rubber, 8.2-18.6 parts of an ultraviolet light absorber, 15-22 parts of a stabilizer, 30-35 parts of a lubricant, 42-49 parts of a calcium carbonate material and 55-59 parts of a polypropylene material. The environmentally-friendly flexible polyvinyl chloride cable sheath composition is simple in technological process and reasonable in raw material proportion, has good thermal insulation and fire proofing property, ensures the normal use of a cable, prolongs the service life of the cable, is good in use effect and guarantees the quality of a cable product.

Description

A kind of environmental protection flexible polyvinyl chloride cable overcoat formula
Technical field
The present invention relates to a kind of environmental protection flexible polyvinyl chloride cable overcoat formula.
Background technology
Along with the develop rapidly of China's expanding economy and communications industry, the usage quantity of powerful device gets more and more, and this just has higher requirement to the use properties of cable.The tolerance power of cable and the difference of inner wire top temperature and envrionment temperature linear, and the maximum operating temperature of inner wire is limited by cable insulation material, the Long-term service temperature of cable insulation material is exactly the highest permission working temperature of inner wire, but most CABLE MATERIALS does not have outstanding resistance to elevated temperatures in the market, the demand of present powerful device cannot be met.Therefore the present inventor is by the new cable material formula of design and technique, creates the novel cable material being suitable for large-power flexible environmental protection and using.
In view of the defect existed in above prior art, be necessary it to improve further, make it have more standby practicality, could realistic service condition.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, the object of this invention is to provide a kind of environmental protection flexible polyvinyl chloride cable overcoat formula.
Invention is taked following technical scheme to realize: a kind of environmental protection flexible polyvinyl chloride cable overcoat formula, it is made up of following raw material: get by a point gauge, bis-phenol 20-30 part, stearic acid 12-30 part, ABS resin 22-30 part, polyvinyl chloride (PVC) RESINS 28-36 part, ABS high glue powder 9-20 part, oxidation inhibitor 10358.9-12.6 part, maleic anhydride grafted ethene 25-36 part-acetate ethylene copolymer 5-9 part, mullite powder 6-16 part, asbestos powder 13-22 part, calcium carbonate 31-39 part, perlite 10-15 part, poly-sour ammonium 9.3-15.2 part, tetramethylolmethane 35-38 part, antimonous oxide micro-cross-linked resin 25-39 part, fire retardant 19-39 part, fire retarding synergist 10-20 part, chlorinated rubber 20-26 part, UV light absorber 8.2-18.6 part, stablizer 15-22 part, lubricant 30-35 part, calcium carbonate material 42-49 part, polypropylene material 55-59.
Particularly, the present invention it be made up of following raw material: get by a point gauge, bis-phenol 21 parts, stearic acid 16 parts, ABS resin 23 parts, polyvinyl chloride (PVC) RESINS 29 parts, ABS high glue powder 10 parts, 1035812 parts, oxidation inhibitor, maleic anhydride grafted ethene 28 parts-acetate ethylene copolymer 6 parts, mullite powder 13 parts, asbestos powder 16 parts, 35 parts, calcium carbonate, perlite 13 parts, poly-sour ammonium 14 parts, tetramethylolmethane 37 parts, the micro-cross-linked resin of antimonous oxide 29 parts, fire retardant 20 parts, fire retarding synergist 10-20 part, chlorinated rubber 20-26 part, UV light absorber 8.2-18.6 part, stablizer 15-22 part, lubricant 30-35 part, calcium carbonate material 42-49 part, polypropylene material 55-59.
Beneficial effect of the present invention: present invention process flow process is succinct, reasonable raw material proportioning, preparation method is simple, for cable provides high-quality weighting agent, raw material is easy to get, and has high thermal resistance, there is certain flame retardant resistance simultaneously, avoid core temperature too high and cause security incident, result of use is obvious, ensure that the reasonable employment of feature cable.
Embodiment
For make the present invention existing technique means, creation characteristic, reach object and effect is easy to understand, below in conjunction with embodiment, set forth the present invention further.
The present invention takes following technical scheme to realize: a kind of environmental protection flexible polyvinyl chloride cable overcoat formula, it is made up of following raw material: get by a point gauge, bis-phenol 20-30 part, stearic acid 12-30 part, ABS resin 22-30 part, polyvinyl chloride (PVC) RESINS 28-36 part, ABS high glue powder 9-20 part, oxidation inhibitor 10358.9-12.6 part, maleic anhydride grafted ethene 25-36 part-acetate ethylene copolymer 5-9 part, mullite powder 6-16 part, asbestos powder 13-22 part, calcium carbonate 31-39 part, perlite 10-15 part, poly-sour ammonium 9.3-15.2 part, tetramethylolmethane 35-38 part, antimonous oxide micro-cross-linked resin 25-39 part, fire retardant 19-39 part, fire retarding synergist 10-20 part, chlorinated rubber 20-26 part, UV light absorber 8.2-18.6 part, stablizer 15-22 part, lubricant 30-35 part, calcium carbonate material 42-49 part, polypropylene material 55-59.
Particularly, the present invention it be made up of following raw material: get by a point gauge, bis-phenol 21 parts, stearic acid 16 parts, ABS resin 23 parts, polyvinyl chloride (PVC) RESINS 29 parts, ABS high glue powder 10 parts, 1035812 parts, oxidation inhibitor, maleic anhydride grafted ethene 28 parts-acetate ethylene copolymer 6 parts, mullite powder 13 parts, asbestos powder 16 parts, 35 parts, calcium carbonate, perlite 13 parts, poly-sour ammonium 14 parts, tetramethylolmethane 37 parts, the micro-cross-linked resin of antimonous oxide 29 parts, fire retardant 20 parts, fire retarding synergist 10-20 part, chlorinated rubber 20-26 part, UV light absorber 8.2-18.6 part, stablizer 15-22 part, lubricant 30-35 part, calcium carbonate material 42-49 part, polypropylene material 55-59.
Although give detailed description and explanation to the specific embodiment of the present invention above; but what should indicate is; we can carry out various equivalence according to conception of the present invention to above-mentioned embodiment and change and amendment; its function produced do not exceed that specification sheets contains yet spiritual time, all should within protection scope of the present invention.

Claims (2)

1. an environmental protection flexible polyvinyl chloride cable overcoat formula, it is characterized in that, it is made up of following raw material: get by a point gauge, bis-phenol 20-30 part, stearic acid 12-30 part, ABS resin 22-30 part, polyvinyl chloride (PVC) RESINS 28-36 part, ABS high glue powder 9-20 part, oxidation inhibitor 10358.9-12.6 part, maleic anhydride grafted ethene 25-36 part-acetate ethylene copolymer 5-9 part, mullite powder 6-16 part, asbestos powder 13-22 part, calcium carbonate 31-39 part, perlite 10-15 part, poly-sour ammonium 9.3-15.2 part, tetramethylolmethane 35-38 part, antimonous oxide micro-cross-linked resin 25-39 part, fire retardant 19-39 part, fire retarding synergist 10-20 part, chlorinated rubber 20-26 part, UV light absorber 8.2-18.6 part, stablizer 15-22 part, lubricant 30-35 part, calcium carbonate material 42-49 part, polypropylene material 55-59.
2. a kind of environmental protection flexible polyvinyl chloride cable overcoat formula according to claim 1, it is characterized in that, it is made up of following raw material: get by a point gauge, bis-phenol 21 parts, stearic acid 16 parts, ABS resin 23 parts, polyvinyl chloride (PVC) RESINS 29 parts, ABS high glue powder 10 parts, 1035812 parts, oxidation inhibitor, maleic anhydride grafted ethene 28 parts-acetate ethylene copolymer 6 parts, mullite powder 13 parts, asbestos powder 16 parts, 35 parts, calcium carbonate, perlite 13 parts, poly-sour ammonium 14 parts, tetramethylolmethane 37 parts, the micro-cross-linked resin of antimonous oxide 29 parts, fire retardant 20 parts, fire retarding synergist 10-20 part, chlorinated rubber 20-26 part, UV light absorber 8.2-18.6 part, stablizer 15-22 part, lubricant 30-35 part, calcium carbonate material 42-49 part, polypropylene material 55-59.
CN201610073786.9A 2016-02-03 2016-02-03 Environmentally-friendly flexible polyvinyl chloride cable sheath composition Pending CN105566757A (en)