CN105754310A - Graphene nanoplatelet master batch for enhancing bioplastics and preparation method - Google Patents
Graphene nanoplatelet master batch for enhancing bioplastics and preparation method Download PDFInfo
- Publication number
- CN105754310A CN105754310A CN201610189912.7A CN201610189912A CN105754310A CN 105754310 A CN105754310 A CN 105754310A CN 201610189912 A CN201610189912 A CN 201610189912A CN 105754310 A CN105754310 A CN 105754310A
- Authority
- CN
- China
- Prior art keywords
- graphite
- graphene microchip
- polylactic acid
- masterbatch
- graphene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a graphene nanoplatelet master batch for enhancing bioplastics and a preparation method.A lactic acid monomer is conveyed between graphitic layers through solvents to obtain modified graphite, a polycondensation initiator is added, the lactic acid monomer is subjected to a polymerization reaction to obtain polylactic acid macromolecules between the graphitic layers in situ, the distance between the graphitic layers is increased, the acting force between the graphitic layers is lowered, and alternate stacking composite materials of the obtained graphene nanoplatelet/polylactic acid macromolecules are sheared, stripped, extruded and pelletized to obtain the graphene nanoplatelet/polylactic acid composite master batch.Cheap graphite is adopted as a raw material, the production cost can be effectively lowered, the obtained master batch is of a graphene nanoplatelet and polylactic acid alternate stacking wrapping structure, the master batch has the flexibility of graphene and the excellent mechanical performance, and then the defects that bioplastics is low in strength, poor in high temperature resistance and poor in hot workability can be overcome.
Description
Technical field
The present invention relates to technical field of nanometer material preparation, particularly to a kind of graphene microchip masterbatch for strengthening biological plastics and preparation method.
Background technology
Biodegradable plastic be a kind of can promptly by the polymer substance of enzyme or microbial decomposition.Biodegradable plastic, since the eighties is come out, has become the hot issue of new material research always.The leading biodegradable plastic of current China utilizes starch to develop, be desirable Green Polymer Material alternative be raw material with oil plastics, cost is only the 1/5 of oil plastic raw materials.Along with the development of biological plastics technology, in biodegradable plastic, the consumption of starch is also improving constantly, and degradation rate is more and more higher.But, owing to pure polylactic resin material is crisp, processing heat stability is poor, limits its application as engineering plastics.How polylactic resin is strengthened, become the new problem of the industry.
The Two-dimensional Carbon nano material that Graphene is made up of one layer of carbon atom, is be currently known the thinnest two-dimensional material, and its thickness is only 0.335nm, and it is made up of hexagonal lattice, it is possible to regard one layer of graphite flake layer being stripped as.Graphene has the structural rigidity of excellence, makes Graphene have very vast potential for future development.And use Graphene doping macromolecular material to increasingly become study hotspot in functional high polymer material field.
China Patent Publication No. 103467943A provides a kind of glass fiber reinforced polylactic acid biological plastics, is made up of by weight following component: polylactic resin 50-70 part, glass fibre 30-50 part, coupling agent 0.6-1.0 part.The glass fiber reinforced polylactic acid biological plastics of the present invention, improves the mechanical property of polylactic resin.But the shortcoming of this method is in that fiberglass surfacing is smooth, it is necessary to formation potentiation could be bonded with polylactic resin by modified, and glass fibre compliance is poor, it does not have improve the processing characteristics of polylactic resin.
China Patent Publication No. 102030830A discloses nanocrystalline enhancing Biocomposite material of bamboo fibre and preparation method thereof.Starch or protein matrices material are added in glycerin/water, stirs under 30-80 DEG C of condition, add above-mentioned bamboo fibre nanocrystal suspension, after continuing stirring 0.5-3 hour, put in mould flow casting molding under 30-80 DEG C of condition.Nanocrystalline addition substantially increases the mechanical strength of biomaterial.This method utilizes Renewable resource to prepare degradation material, with low cost, and synthesis technique is simple, building-up process green non-pollution, the Product Green environmental protection of gained, and has good biocompatibility.But, the method bamboo fibre complicated process of preparation, manufacturing cycle is long, uses apparatus expensive, and the nanocrystalline also difficulty of dispersion in biomaterial of bamboo fibre accomplishes to be uniformly distributed, it is possible to cause that yield rate is low.
China Patent Publication No. 101484628 discloses a kind of method of strength and stiffness improving fiber.The method graphene film is adhered among carbon filament bundle or yarn or on to form modified fibre, wherein nanoreinforcement material adheres to or is trapped in carbon filament bundle.Modified resin fibre improves notable relative to the fiber stiffness of unmodified resin and strength character, but Graphene is relatively costly, is unfavorable for that large-scale production is promoted.
In sum, with low cost but without a kind of raw materials for production in prior art, and biological plastics low-intensity can be effectively improved, the technological means of heat-resisting quantity is poor, hot-workability is poor defect.
Summary of the invention
In order to solve deficiency and the defect of said method, the present invention develops a kind of graphene microchip masterbatch for strengthening biological plastics and preparation method.Lactic acid monomer is transported to graphite between layers by solvent by the present invention, stand a Preset Time, obtain modified graphite, add polycondensation reaction initiator, lactic acid monomer is obtained polylactic acid macromolecule by polyreaction in graphite layers original position, increase graphite layers distance, reduce graphite layers active force, obtain the high molecular alternative stacked composite of graphene microchip/polylactic acid, then by applying shear action in the high molecular alternative stacked composite of graphene microchip/polylactic acid, natural cooling obtains primary Graphene polylactic acid composite master batch, then sheared by screw extruder and peel off, extruding pelletization obtains Graphene polylactic acid composite master batch.
On the one hand, the present invention provides a kind of graphene microchip masterbatch for strengthening biological plastics, and described masterbatch is prepared from by the raw material including following parts by weight:
Graphite 32-46 part,
Lactic acid monomer 50-66 part,
Plasticizer 1-2 part,
Bulking agent 1-2 part,
Wherein, described graphite is compact crystal shape graphite, one or more in crystalline flake graphite, expanded graphite or expansible graphite, described bulking agent is at least one in ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, and described plasticizer is aklylene glycol.
Optionally, the structure of described masterbatch is graphene microchip and polylactic acid alternative stacked package structure.
On the other hand, the present invention provides a kind of method peeling off preparing graphite alkene, said method comprising the steps of:
The preparation method of a kind of graphene microchip masterbatch for strengthening biological plastics, said method comprising the steps of:
A. 50-66 part lactic acid monomer and proper amount of surfactant are dissolved in solvent, then 32-46 part graphite is immersed in described solvent, by described solvent, described lactic acid monomer is transported to graphite between layers, after standing a Preset Time, it is thus achieved that modified graphite;
B. 0-1 weight portion polycondensation reaction initiator, 1-2 parts by weight of plasticizer and 1-2 weight portion solubilizing agent are added in solvent, cause lactic acid monomer generation polycondensation reaction, increase graphite gap between layers, reduce graphite layers active force, obtain the high molecular alternative stacked composite of graphene microchip/polylactic acid;
C. described graphene microchip/polylactic acid polymer composite is taken out from described solvent drying and carries out slicing treatment, graphene microchip/polylactic acid polymer composite the microplate obtained is added banburying formula three-screw extruder, extrusion temperature is set and is 100-120 DEG C, shear stripping, extruding pelletization graphene microchip/polylactic acid composite master batch.
Optionally, described surfactant is one or more in vinyltrimethoxy silane, vinyl triethoxyl silicon, sodium lauryl sulphate, dodecyl sodium sulfate and polyvinylpyrrolidone, described solvent is one or more in methanol, ethanol, acetone, described bulking agent is at least one in ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, and described plasticizer is aklylene glycol.
Optionally, the percentage by weight of described surfactant, described lactic acid monomer and described solvent is 0.05-0.2:34.95-44.8:55-65.
Optionally, in stepb, add polycondensation reaction initiator when described initiation lactic acid monomer generation polycondensation reaction, described polycondensation reaction initiator is the soap of at least one metal in stannum, lead, zinc, titanium, germanium, manganese, magnesium and rare earth element, carbonate, sulfate, phosphate, oxide, hydroxide, alkoxide.
Optionally, the temperature controlling described polycondensation reaction is 100-220 DEG C.
Optionally, in step c, described graphene microchip/polylactic acid polymer composite is taken out from described solvent after drying carries out slicing treatment, it is thus achieved that graphene microchip/polylactic acid polymer composite microplate lamellar spacing is 5-10mm.
Said one in the embodiment of the present application or multiple technical scheme, at least have one or more technique effects following:
1, the present invention adopts lactic acid monomer to serve not only as the remover of graphite material as raw materials for production, and graphene microchip alternative stacked parcel high molecular with polylactic acid, the graphene microchip in masterbatch pellet of preparation can be uniformly distributed at polylactic acid macromolecule, and then the compliance of Graphene and excellent mechanical performance can be utilized, improve the intensity of biomaterial, high temperature resistant and processing characteristics.
2, the present invention adopts lactic acid monomer generation polycondensation reaction at graphite layers fabricated in situ polylactic acid and to obtain graphene microchip, employs conventional biological plastics and graphite as raw material, reduces masterbatch production cost.
3, present invention process is simple, and manufacturing cycle is short, and the equipment cost of use is cheap, is suitable for large-scale production.
Detailed description of the invention
By detailed description of the invention, the present invention is described in further detail, but this should not being interpreted as, the scope of the present invention is only limitted to Examples below.When without departing from said method thought of the present invention, the various replacements made according to ordinary skill knowledge and customary means or change, should be included in the scope of the present invention.
Embodiment one
The present embodiment comprises the steps:
The lactic acid monomer of 66 weight portions and surfactant vinyltrimethoxy silane are dissolved in methanol solvate, again the expanded graphite of 32 weight portions is immersed in methanol, wherein, the percentage by weight of vinyl trimethoxy silicon and lactic acid monomer and methanol is 0.05:34.95:65, after standing 12 hours, by methanol, lactic acid monomer is transported to graphite between layers, obtain modified graphite, by 0.5 weight portion polycondensation reaction initiator stearic acid stannum, the aklylene glycol of 1 weight portion and the ethylene-vinyl acetate copolymer of 1 weight portion add in solvent, the temperature controlling polycondensation reaction is 100 DEG C, cause lactic acid monomer generation polycondensation reaction, increase graphite gap between layers, reduce graphite layers active force, obtain the high molecular alternative stacked composite of graphene microchip/polylactic acid.Graphene microchip/polylactic acid polymer composite is taken out drying from methanol and carries out slicing treatment, it is thus achieved that graphene microchip/polylactic acid polymer composite microplate lamellar spacing is 5-6mm.Graphene microchip/polylactic acid polymer composite the microplate obtained is added banburying formula three-screw extruder, and arranging extrusion temperature is 100 DEG C, extruding pelletization, and natural cooling obtains primary Graphene polylactic acid composite master batch.
Embodiment two
The present embodiment comprises the steps:
The lactic acid monomer of 66 weight portions and surfactant vinyl triethoxyl silicon are dissolved in acetone solvent, again by the expanded graphite submergence of 32 weight portions in acetone, wherein, the percentage by weight of vinyl triethoxyl silicon and lactic acid monomer and acetone is 0.05:34.95:65, after standing 12 hours, by acetone, lactic acid monomer is transported to graphite between layers, obtain modified graphite, by 0.5 weight portion polycondensation reaction initiator stearic acid stannum, the aklylene glycol of 1 weight portion and the ethylene-acrylic acid copolymer of 1 weight portion add in solvent, the temperature controlling polycondensation reaction is 100 DEG C, cause lactic acid monomer generation polycondensation reaction, increase graphite gap between layers, reduce graphite layers active force, obtain the high molecular alternative stacked composite of graphene microchip/polylactic acid.Graphene microchip/polylactic acid polymer composite is taken out drying from acetone and carries out slicing treatment, it is thus achieved that graphene microchip/polylactic acid polymer composite microplate lamellar spacing is 5-6mm.Graphene microchip/polylactic acid polymer composite the microplate obtained is added banburying formula three-screw extruder, and arranging extrusion temperature is 100 DEG C, extruding pelletization, and natural cooling obtains primary Graphene polylactic acid composite master batch.
Embodiment three
The present embodiment comprises the steps:
The lactic acid monomer of 66 weight portions and surfactant vinyl triethoxyl silicon are dissolved in acetone solvent, again by the expanded graphite submergence of 32 weight portions in acetone, wherein, the percentage by weight of vinyl triethoxyl silicon and lactic acid monomer and acetone is 0.05:34.95:65, after standing 12 hours, by acetone, lactic acid monomer is transported to graphite between layers, obtain modified graphite, by 0.5 weight portion polycondensation reaction initiator stearic acid stannum, the aklylene glycol of 1 weight portion and the ethylene-vinyl acetate copolymer of 1 weight portion add in solvent, the temperature controlling polycondensation reaction is 220 DEG C, cause lactic acid monomer generation polycondensation reaction, increase graphite gap between layers, reduce graphite layers active force, obtain the high molecular alternative stacked composite of graphene microchip/polylactic acid.Graphene microchip/polylactic acid polymer composite is taken out drying from acetone and carries out slicing treatment, it is thus achieved that graphene microchip/polylactic acid polymer composite microplate lamellar spacing is 9-10mm.Graphene microchip/polylactic acid polymer composite the microplate obtained is added banburying formula three-screw extruder, and arranging extrusion temperature is 100 DEG C, extruding pelletization, and natural cooling obtains primary Graphene polylactic acid composite master batch.
Embodiment four
The present embodiment comprises the steps:
The lactic acid monomer of 50 weight portions and Surfactant SDS are dissolved in acetone solvent, again by the crystalline flake graphite submergence of 46 weight portions in acetone, wherein, the percentage by weight of vinyl triethoxyl silicon and lactic acid monomer and acetone is 0.05:34.95:65, after standing 12 hours, by acetone, lactic acid monomer is transported to graphite between layers, obtain modified graphite, by 0.5 weight portion polycondensation reaction initiator stannous octoate, the aklylene glycol of 2 weight portions and the ethylene-acrylic acid copolymer of 2 weight portions add in solvent, the temperature controlling polycondensation reaction is 220 DEG C, cause lactic acid monomer generation polycondensation reaction, increase graphite gap between layers, reduce graphite layers active force, obtain the high molecular alternative stacked composite of graphene microchip/polylactic acid.Graphene microchip/polylactic acid polymer composite is taken out drying from acetone and carries out slicing treatment, it is thus achieved that graphene microchip/polylactic acid polymer composite microplate lamellar spacing is 9-10mm.Graphene microchip/polylactic acid polymer composite the microplate obtained is added banburying formula three-screw extruder, and arranging extrusion temperature is 120 DEG C, extruding pelletization, and natural cooling obtains primary Graphene polylactic acid composite master batch.
Embodiment five
The present embodiment comprises the steps:
The lactic acid monomer of 50 weight portions and Surfactant SDS are dissolved in acetone solvent, again by the crystalline flake graphite submergence of 46 weight portions in acetone, wherein, the percentage by weight of vinyl triethoxyl silicon and lactic acid monomer and acetone is 0.1:40:59.9, after standing 12 hours, by acetone, lactic acid monomer is transported to graphite between layers, obtain modified graphite, by 0.5 weight portion polycondensation reaction initiator stannous chloride, the aklylene glycol of 1 weight portion and the ethylene-vinyl acetate copolymer of 2 weight portions add in solvent, the temperature controlling polycondensation reaction is 220 DEG C, cause lactic acid monomer generation polycondensation reaction, increase graphite gap between layers, reduce graphite layers active force, obtain the high molecular alternative stacked composite of graphene microchip/polylactic acid.Graphene microchip/polylactic acid polymer composite is taken out drying from acetone and carries out slicing treatment, it is thus achieved that graphene microchip/polylactic acid polymer composite microplate lamellar spacing is 9-10mm.Graphene microchip/polylactic acid polymer composite the microplate obtained is added banburying formula three-screw extruder, and arranging extrusion temperature is 120 DEG C, shears and peels off extruding pelletization, and natural cooling obtains primary Graphene polylactic acid composite master batch.
Although preferred embodiments of the present invention have been described, but those skilled in the art are once know basic creative concept, then these embodiments can be made other change and amendment.So, claims are intended to be construed to include preferred embodiment and fall into all changes and the amendment of the scope of the invention.
Obviously, the present invention can be carried out various change and modification without deviating from the spirit and scope of the present invention by those skilled in the art.So, if these amendments of the present invention and modification belong within the scope of the claims in the present invention and equivalent technologies thereof, then the present invention is also intended to comprise these change and modification.
Claims (8)
1., for strengthening a graphene microchip masterbatch for biological plastics, described masterbatch is prepared from by the raw material including following parts by weight:
Graphite 32-46 part,
Lactic acid monomer 50-66 part,
Plasticizer 1-2 part,
Bulking agent 1-2 part,
Wherein, described graphite is compact crystal shape graphite, one or more in crystalline flake graphite, expanded graphite or expansible graphite, described bulking agent is at least one in ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, and described plasticizer is aklylene glycol.
2. the graphene microchip masterbatch being used for strengthening biological plastics, it is characterised in that the structure of described masterbatch is graphene microchip and polylactic acid alternative stacked package structure.
3. the preparation method for strengthening the graphene microchip masterbatch of biological plastics, it is characterised in that said method comprising the steps of:
A. 50-66 part lactic acid monomer and proper amount of surfactant are dissolved in solvent, then 32-46 part graphite is immersed in described solvent, by described solvent, described lactic acid monomer is transported to graphite between layers, after standing a Preset Time, it is thus achieved that modified graphite;
B. 0-1 weight portion polycondensation reaction initiator, 1-2 parts by weight of plasticizer and 1-2 weight portion solubilizing agent are added in solvent, cause lactic acid monomer generation polycondensation reaction, increase graphite gap between layers, reduce graphite layers active force, obtain the high molecular alternative stacked composite of graphene microchip/polylactic acid;
C. described graphene microchip/polylactic acid polymer composite is taken out from described solvent drying and carries out slicing treatment, graphene microchip/polylactic acid polymer composite the microplate obtained is added banburying formula three-screw extruder, extrusion temperature is set and is 100-120 DEG C, shear stripping, extruding pelletization graphene microchip/polylactic acid composite master batch.
4. the preparation method of a kind of graphene microchip masterbatch for strengthening biological plastics according to claim 3, it is characterized in that, described surfactant is one or more in vinyltrimethoxy silane, vinyl triethoxyl silicon, sodium lauryl sulphate, dodecyl sodium sulfate and polyvinylpyrrolidone, described solvent is one or more in methanol, ethanol, acetone, described bulking agent is at least one in ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, and described plasticizer is aklylene glycol.
5. the preparation method of a kind of graphene microchip masterbatch for strengthening biological plastics according to claim 3, it is characterised in that the percentage by weight of described surfactant, described lactic acid monomer and described solvent is 0.05-0.2:34.95-44.8:55-65.
6. the preparation method of a kind of graphene microchip masterbatch for strengthening biological plastics according to claim 3, it is characterized in that, in stepb, add polycondensation reaction initiator when described initiation lactic acid monomer generation polycondensation reaction, described polycondensation reaction initiator is the soap of at least one metal in stannum, lead, zinc, titanium, germanium, manganese, magnesium and rare earth element, carbonate, sulfate, phosphate, oxide, hydroxide, alkoxide.
7. the preparation method of a kind of graphene microchip masterbatch for strengthening biological plastics according to claim 3, it is characterised in that the temperature controlling described polycondensation reaction is 100-220 DEG C.
8. the preparation method of a kind of graphene microchip masterbatch for strengthening biological plastics according to claim 3, it is characterized in that, in step c, described graphene microchip/polylactic acid polymer composite is taken out from described solvent after drying carries out slicing treatment, it is thus achieved that graphene microchip/polylactic acid polymer composite microplate lamellar spacing is 5-10mm.