CN105734768B - A kind of anti-slippage sportswear fabric of woven nylon and its method for weaving - Google Patents
A kind of anti-slippage sportswear fabric of woven nylon and its method for weaving Download PDFInfo
- Publication number
- CN105734768B CN105734768B CN201610230049.5A CN201610230049A CN105734768B CN 105734768 B CN105734768 B CN 105734768B CN 201610230049 A CN201610230049 A CN 201610230049A CN 105734768 B CN105734768 B CN 105734768B
- Authority
- CN
- China
- Prior art keywords
- fabric
- slippage
- warp
- nylon
- dyeing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of anti-slippage sportswear fabric of woven nylon, the raw materials used fabric is nylon fully drawn yarn, it is process through woven, dyeing, final finishing, the warp thread of the nylon fully drawn yarn is 70D/24F, the weft yarn of the nylon fully drawn yarn is 200D/48F, the anti-slippage fabric through it is close be 180 pieces/inch, the filling density of the anti-slippage fabric is 92 pieces/inch, the fabric structure is 2 times twills on 2, and the fabric weight weaved is 120 ~ 130g/m2.The present invention is designed by fabric structure and thread count, the processing of dyeing final finishing, significantly increases fabric slippage intensity, and the face weave technique is simple, is not had coating in final finishing processing, is not increased production cost additionally.
Description
Technical field
The invention belongs to textile material field, more particularly to a kind of anti-slippage sportswear fabric of woven nylon and its weaving
Method.
Background technology
Slippage refer to sutured fabric by vertical sealing pulling force effect when, the yarn in a direction is in another side
To yarn on produce sliding, the de- seam or breach presented.Garment material has to pass through quilting process and will could cut
The garment piece of different parts is connected as real clothes, and wearing in sportswear particularly autumn and winter series close-fitting sports garment
During, bear to produce in suture site due to stress compared with the position (such as ancon, shoulder, oxter) of big load individually
The sliding of yarn, cloth cover produce slippage, not only directly affect the attractive in appearance of clothes, reduce the quality of clothes;Serious meeting causes to take
Dress garment piece is mutually disengaged, and inevitable embarrassment, therefore the especially high-grade sportswear fabric of garment material are caused to wearer
Strict requirements are suffered to the splitting parameter of fabric.
It is CN201610011782.8 that the patent for the anti-slippage fabric announced at present, which only has Chinese invention patent application number,
Patent name is《A kind of frivolous fancy crepe georgette fabric of anti-slippage and its method for weaving》Propose a kind of true with anti-slippage performance
The method for weaving of silk twill-weave, solves the problems, such as the slippage of silk woven fabric by the design of institutional framework.But current fortune
Dynamic clothes are most to use chemical fibre, such as nylon, terylene etc..The performance and silk of chemical fibre have larger difference, together
When fancy crepe georgette fabric can not also meet the requirement of sportswear.
Woven nylon fabric in the market can meet high-end sportswear face in fabric weight, color fastness etc.
The requirement of material, but slippage intensity always can not be up to standard.Through third party testing agency (Tongbiao Standard Technology Service Co., Ltd,
SGS) test, method of testing uses and " Adidas Method 4.13 ", as a result shows that the slippage intensity of warp-wise and broadwise only has 80N
Left and right.There is larger gap from the minimum value 200N of customer requirement.
Therefore, for above-mentioned technical problem, it is necessary to provide a kind of anti-slippage sportswear fabric of high-grade woven nylon and
Its method for weaving, to overcome drawbacks described above.
The content of the invention
In view of this, it is an object of the invention to provide a kind of anti-slippage sportswear fabric of high-grade woven nylon and its knit
Method is made, the fabric is the market demand for current high-grade sportswear fabric, from nylon fiber, is selected by institutional framework
Select and designed with thread count, a series of production processes such as dyeing final finishing processing, is process.
To achieve the above object, the present invention provides following technical scheme:
A kind of anti-slippage sportswear fabric of woven nylon, it is characterised in that:The fabric is raw materials used to be drawn entirely for nylon
Silk is stretched, the warp thread of the nylon fully drawn yarn is 70D/24F, and the weft yarn of the nylon fully drawn yarn is 200D/48F, described anti-
Slippage fabric through it is close be 180 pieces/inch, the filling density of the anti-slippage fabric is 92 pieces/inch.
Preferably, in the anti-slippage sportswear fabric of above-mentioned woven nylon, the fabric structure is 2 oblique on 2
Line, the fabric weight weaved are 120~130g/m2。
A kind of anti-slippage sportswear face weave method of woven nylon, it is characterised in that:Including step:
Select raw material:It is the raw material of fabric to select nylon fully drawn yarn, and wherein warp thread is 70D/24F, weft yarn 200D/
48F;
Warping:Warp thread carries out warping by warp warping machine, and yarn is parallel to each other and is closely wound on warp beam, elongation
Control is 0.5%~0.8%;
Starching:Warp sizing, slurry are mainly 3% polyacrylate and 2.5% PVA-205, add 0.2%
Antistatic additive, 0.5% oil emulsion, the rate of sizing are 3~5%;
Weaving:Warp thread sizing well after gaited denting according to pegging plan and warp count design requirement, loom uses jet
Loom, fabric structure are 2 times twills on 2, and the fabric weight weaved is 120~130g/m2;
Drying and fabric are examined:Length and door width have retraction after drying, and it is 15m/min that fabric, which examines locomotive speed,;
Cold pad--batch:First by fabric alkali immerging at room temperature, the then clot on the cloth beam of draw off mechanism, yardage roll plastics
Film is wrapped up, and prevents cloth cover from air-drying, and last yardage roll is banked up 72 hours at room temperature, during which keeps yardage roll with 6-8r/min speed
Revolution;
Washing:The good yardage roll of cold pad--batch is washed 0.5~1 hour in 60 DEG C of hot water;
Dyeing:Middle acid dyeing, Value in Dyeing Process first is adjusted to 4~6 with acetic acid, and add 1~2% levelling agent,
Dye bath temperature heats up to starting to dye after 40 DEG C and rises to 80~85 degree with the speed of 1 degree/2 minutes, insulation rises again after 15 minutes
Temperature, after dye bath temperature is increased to 95 DEG C, boiling dye 70~90 minutes, then gradually cooling drops to 40 DEG C with 1 degree/min of speed,
Add 1~2% color fixing agent simultaneously;
Drying:Dry and carried out in the cylinder group that surface temperature is 80~90 DEG C, the time 10 that cloth cover is bonded with cylinder~
25 seconds;
Thermal finalization:In tank before forming machine, anti-agent 1~3% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent are added by proportioning
1~2%, often shape 800~1000 meters, quantitatively supplement waterproofing agent, setting temperature is 130~140 DEG C, and machine rotational speed is 50 yards;
Examine clot, packaging.
Preferably, in the anti-slippage sportswear face weave method of above-mentioned woven nylon, the warp of the anti-slippage fabric
Close is 180 pieces/inch.
Preferably, in the anti-slippage sportswear face weave method of above-mentioned woven nylon, the latitude of the anti-slippage fabric
Close is 92 pieces/inch.
Compared with prior art, the beneficial effects of the invention are as follows:
(1) present invention is designed, dyed the processing of final finishing by fabric structure and thread count, makes fabric slippage strong
Degree significantly increases, and is tested through third party testing agency (Tongbiao Standard Technology Service Co., Ltd, SGS), and method of testing uses
" Adidas Method 4.13 ", as a result show the slippage intensity of warp-wise and broadwise more than 200N;
(2) the face weave technique is simple, does not have coating in final finishing processing, does not increase production cost additionally;
(3) fabric is in addition to anti-slippage, can also anti-hook silk, fabric is slim and graceful, ventilative, and added value of product is high, is easy to city
Promote field.
Brief description of the drawings
Fig. 1 is the flow chart of the anti-slippage sportswear face weave method of woven nylon of the present invention.
Fig. 2 is the organization chart of the anti-slippage sportswear fabric of woven nylon of the present invention.
Embodiment
The invention discloses a kind of anti-slippage sportswear fabric of woven nylon and its method for weaving, the fabric is to be directed to mesh
The market demand of preceding high-grade sportswear fabric, from nylon fiber, designed by institutional framework selection and thread count, dyeing
A series of production processes such as final finishing processing, are process.
As shown in Fig. 2 the anti-slippage sportswear fabric of woven nylon disclosed by the invention, its raw materials used fabric is nylon
Fully drawn yarn, the warp thread of the nylon fully drawn yarn are 70D/24F, and the weft yarn of the nylon fully drawn yarn is 200D/48F, institute
State anti-slippage fabric through it is close be 180 pieces/inch, the filling density of the anti-slippage fabric is 92 pieces/inch.The fabric tissue knot
Structure is 2 times twills on 2, and the fabric weight weaved is 120~130g/m2。
As shown in figure 1, the anti-slippage sportswear face weave method of woven nylon disclosed by the invention, it includes step:
Select raw material:It is the raw material of fabric to select nylon fully drawn yarn, and wherein warp thread is 70D/24F, weft yarn 200D/
48F;
Warping:Warp thread carries out warping by warp warping machine, and yarn is parallel to each other and is closely wound on warp beam, elongation
Control is 0.5%~0.8%;
Starching:Warp sizing, slurry are mainly 3% polyacrylate and 2.5% PVA-205, add 0.2%
Antistatic additive, 0.5% oil emulsion, the rate of sizing are 3~5%;
Weaving:Warp thread sizing well after gaited denting according to pegging plan and warp count design requirement, loom uses jet
Loom, fabric structure are 2 times twills on 2, and the fabric weight weaved is 120~130g/m2;
Drying and fabric are examined:Length and door width have retraction after drying, beneficial to the shrinkage problem of control dyeing and finishing process, are beneficial to
Thread count is improved, it is 15m/min that fabric, which examines locomotive speed,;
Cold pad--batch:First by fabric alkali immerging at room temperature, the then clot on the cloth beam of draw off mechanism, yardage roll plastics
Film is wrapped up, and prevents cloth cover from air-drying, and last yardage roll is banked up 72 hours at room temperature, during which keeps yardage roll with 6-8r/min speed
Revolution;
Washing:The good yardage roll of cold pad--batch is washed 0.5~1 hour in 60 DEG C of hot water;
Dyeing:Middle acid dyeing, Value in Dyeing Process first is adjusted to 4~6 with acetic acid, and add 1~2% levelling agent,
Dye bath temperature heats up to starting to dye after 40 DEG C and rises to 80~85 degree with the speed of 1 degree/2 minutes, insulation rises again after 15 minutes
Temperature, after dye bath temperature is increased to 95 DEG C, boiling dye 70~90 minutes, then gradually cooling drops to 40 DEG C with 1 degree/min of speed,
Add 1~2% color fixing agent simultaneously;
Drying:Dry and carried out in the cylinder group that surface temperature is 80~90 DEG C, the time 10 that cloth cover is bonded with cylinder~
25 seconds, reach the effect dried substantially, purpose there are two, first, the fabric of drying is to helping in the tank before forming machine
Agent is easier to absorb, while is advantageous to the accuracy of auxiliary agent proportioning, second, drying can efficiently control the washing shrinkage of fabric;
Thermal finalization:In tank before forming machine, anti-agent 1~3% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent are added by proportioning
1~2%, often shape 800~1000 meters, quantitatively supplement waterproofing agent, setting temperature is 130~140 DEG C, and machine rotational speed is 50 yards;
Examine clot, packaging.
The anti-slippage fabric through it is close be that 180 pieces/inch of filling densities are 92 pieces/inch.
With reference to embodiment, the present invention is furture elucidated.
Embodiment 1:
A kind of anti-slippage sportswear fabric of high-grade woven nylon is to use nylon fully drawn yarn, through it is woven, dyeing, after it is whole
What reason was process.
Step 1, it is nylon fully drawn yarn (FDY) that above-mentioned fabric is raw materials used, and wherein warp thread is 70D/24F, and weft yarn is
200D/48F;
Step 2, warping:Warp thread carries out warping by warp warping machine, and yarn is parallel to each other and is closely wound on warp beam,
Elongation is controlled 0.5%;
Step 3, starching:Warp sizing, slurry are mainly 3% polyacrylate and 2.5% PVA-205, are added
0.2% antistatic additive, 0.5% oil emulsion.The rate of sizing is 5%;
Step 4, weave:Warp thread sizing well after gaited denting according to pegging plan and warp count design requirement, loom is adopted
With air-jet loom, fabric structure is 2 time twills on 2, fabric through it is close be 180 pieces/inch, filling density is 92 pieces/inch, is knitted
The fabric weight made is 125g/m2;
Step 5, fabric is examined, locomotive speed 15m/min;
Step 6, cold pad--batch:First by fabric alkali immerging (NaOH 5g/L, 35%H at room temperature2O28ml/L), then
The clot on the cloth beam of draw off mechanism, yardage roll are wrapped up with plastic film and other material, prevent cloth cover from air-drying.Last yardage roll heap at room temperature
Put 72 hours, during which keeping yardage roll, (6r/min) is turned round at a slow speed;
Step 7, wash:The good yardage roll of cold pad--batch is washed 0.5 hour in 60 DEG C of hot water;
Step 8, dye:Middle acid dyeing, Value in Dyeing Process first is adjusted to 4 with acetic acid, and add 1% levelling agent.
Dye bath temperature starts to dye after being increased to 40 DEG C, heats up and rises to 80 degree with the speed of 1 degree/2 minutes, insulation rises again after 15 minutes
Temperature, after dye bath temperature is increased to 95 DEG C, boiling dye 1 hour, 40 DEG C is gradually then cooled to the speed of 1 degree/1 minute, is added simultaneously
1% color fixing agent;
Step 9, dry:Dry and carried out in the cylinder group that surface temperature is 80 DEG C, the time 20 that cloth cover is bonded with cylinder
Second, reach the effect dried substantially;
Step 10, thermal finalization:In tank before forming machine, anti-agent 1% of becoming unwoven or untiwisted is added by proportioning, antistatic additive 0.5%, is prevented
Aqua 1%, often shape 1000 meters, quantitatively supplement waterproofing agent, setting temperature is 140 DEG C, and machine rotational speed is 50 yards;
Step 11, clot, packaging are examined.
Embodiment 2:
A kind of anti-slippage sportswear fabric of high-grade woven nylon is to use nylon fully drawn yarn, through it is woven, dyeing, after it is whole
What reason was process.
Step 1, it is nylon fully drawn yarn (FDY) that above-mentioned fabric is raw materials used, and wherein warp thread is 70D/24F, and weft yarn is
200D/48F,
Step 2, warping:Warp thread carries out warping by warp warping machine, and yarn is parallel to each other and is closely wound on warp beam,
Elongation control 0.6%,
Step 3, starching:Warp sizing, slurry are mainly 3% polyacrylate and 2.5% PVA-205, are added
0.2% antistatic additive, 0.5% oil emulsion, the rate of sizing 4%,
Step 4, weave:Warp thread sizing well after gaited denting according to pegging plan and warp count design requirement, loom is adopted
With air-jet loom, fabric structure is 2 time twills on 2, fabric through it is close be 180 pieces/inch, filling density is 91 pieces/inch, is knitted
The fabric weight made is 124g/m2,
Step 5, fabric is examined, locomotive speed 15m/min,
Step 6, cold pad--batch:First by fabric alkali immerging (NaOH 6g/L, 35%H at room temperature2O28ml/L), then
The clot on the cloth beam of draw off mechanism, yardage roll are wrapped up with plastic film and other material, prevent cloth cover from air-drying, last yardage roll heap at room temperature
Put 72 hours, during which keeping yardage roll, (8r/min) is turned round at a slow speed.
Step 7, wash:The good yardage roll of cold pad--batch is washed 1 hour in 60 DEG C of hot water;
Step 8, dye:Middle acid dyeing, Value in Dyeing Process first is adjusted to 5 with acetic acid, and add 1% levelling agent.
Dye bath temperature starts to dye after being increased to 40 DEG C, heats up and rises to 80 degree with the speed of 1 degree/2 minutes, insulation rises again after 15 minutes
Temperature, after dye bath temperature is increased to 95 DEG C, boiling dye 70 minutes, then gradually cooling drops to 40 DEG C with 1 degree/min of speed, simultaneously
Add 1% color fixing agent color;
Step 9, dry:Dry and carried out in the cylinder group that surface temperature is 85 DEG C, the time 25 that cloth cover is bonded with cylinder
Second, reach the effect dried substantially;
Step 10, thermal finalization:In tank before forming machine, anti-agent 2% of becoming unwoven or untiwisted is added by proportioning, antistatic additive 0.5%, is prevented
Aqua 1%, often shape 800 meters, quantitatively supplement waterproofing agent.Setting temperature is 150 DEG C, and machine rotational speed is 50 yards;
Step 11, clot, packaging are examined.
Embodiment 3:
A kind of anti-slippage sportswear fabric of high-grade woven nylon is to use nylon fully drawn yarn, through it is woven, dyeing, after it is whole
What reason was process.
Step 1, it is nylon fully drawn yarn (FDY) that above-mentioned fabric is raw materials used, and wherein warp thread is 70D/24F, and weft yarn is
200D/48F;
Step 2, warping:Warp thread carries out warping by warp warping machine, and yarn is parallel to each other and is closely wound on warp beam,
Elongation is controlled 0.5%;
Step 3, starching:Warp sizing, slurry are mainly 3% polyacrylate and 2.5% PVA-205, are added
0.2% antistatic additive, 0.5% oil emulsion, the rate of sizing 3%;
Step 4, weave:Warp thread sizing well after gaited denting according to pegging plan and warp count design requirement, loom is adopted
With air-jet loom, fabric structure is 2 time twills on 2, fabric through it is close be 180 pieces/inch, filling density is knitted for 93 pieces/inch
The fabric weight made is 128g/m2;
Step 5, fabric is examined, locomotive speed 15m/min;
Step 6, cold pad--batch:First by fabric alkali immerging (NaOH 6g/L, 35%H at room temperature2O210ml/L), so
The clot on the cloth beam of draw off mechanism, yardage roll are wrapped up with plastic film and other material afterwards, prevent cloth cover from air-drying, and last yardage roll is at room temperature
Bank up 72 hours, during which keeping yardage roll, (6r/min) is turned round at a slow speed;
Step 7, wash:The good yardage roll of cold pad--batch is washed 0.5 hour in 60 DEG C of hot water;
Step 8, dye:Middle acid dyeing, Value in Dyeing Process first is adjusted to 5 with acetic acid, and add 1% levelling agent.
Dye bath temperature starts to dye after being increased to 40 DEG C, heats up and rises to 80 degree with the speed of 1 degree/2 minutes, insulation rises again after 15 minutes
Temperature, after dye bath temperature is increased to 95 DEG C, boiling dye 50 minutes, then gradually cooling drops to 40 DEG C with 1 degree/min of speed, simultaneously
Add 2% color fixing agent;
Step 9, dry:Dry and carried out in the cylinder group that surface temperature is 80 DEG C, the time 25 that cloth cover is bonded with cylinder
Second, reach the effect dried substantially;
Step 10, thermal finalization:In tank before forming machine, anti-agent 1% of becoming unwoven or untiwisted is added by proportioning, antistatic additive 0.5%, is prevented
Aqua 1%, often shape 1000 meters, quantitatively supplement waterproofing agent, setting temperature is 150 DEG C, and machine rotational speed is 50 yards;
Step 11, clot, packaging are examined.
The anti-slippage sportswear fabric of high-grade woven nylon disclosed by the invention is through third party testing agency (logical mark standard skill
Art Services Co., Ltd, SGS) test, method of testing is using " Adidas Method 4.13 ", as a result showing warp-wise and broadwise
Slippage intensity has exceeded 200N.Above three embodiment of the present invention is voluntarily measured by inside, as a result as follows:
Compared with prior art, the beneficial effects of the invention are as follows:
(1) present invention is designed, dyed the processing of final finishing by fabric structure and thread count, makes fabric slippage strong
Degree significantly increases, and is tested through third party testing agency (Tongbiao Standard Technology Service Co., Ltd, SGS), and method of testing uses
" Adidas Method 4.13 ", as a result show the slippage intensity of warp-wise and broadwise more than 200N;
(2) the face weave technique is simple, does not have coating in final finishing processing, does not increase production cost additionally.
(3) fabric is in addition to anti-slippage, can also anti-hook silk, fabric is slim and graceful, ventilative, and added value of product is high, is easy to city
Promote field.
Claims (3)
- A kind of 1. anti-slippage sportswear face weave method of woven nylon, it is characterised in that:Including step:Select raw material:It is the raw material of fabric to select nylon fully drawn yarn, and wherein warp thread is 70D/24F, weft yarn 200D/48F;Warping:Warp thread carries out warping by warp warping machine, and yarn is parallel to each other and is closely wound on warp beam, elongation control 0.5%~0.8%;Starching:Warp sizing, slurry are mainly 3% polyacrylate and 2.5% PVA-205, add 0.2% it is anti-quiet Electric agent, 0.5% oil emulsion, the rate of sizing are 3~5%;Weaving:Warp thread sizing well after gaited denting according to pegging plan and warp count design requirement, loom uses air-jet loom, Fabric structure is 2 times twills on 2, and the fabric weight weaved is 120~130g/m2;Drying and fabric are examined:Length and door width have retraction after drying, and it is 15m/min that fabric, which examines locomotive speed,;Cold pad--batch:First by fabric alkali immerging at room temperature, the then clot on the cloth beam of draw off mechanism, yardage roll plastic sheeting Parcel, prevents cloth cover from air-drying, and last yardage roll is banked up 72 hours at room temperature, during which keeps yardage roll to be returned with 6-8r/min speed Turn;Washing:The good yardage roll of cold pad--batch is washed 0.5~1 hour in 60 DEG C of hot water;Dyeing:Middle acid dyeing, Value in Dyeing Process first is adjusted to 4-6 with acetic acid, and add 1-2% levelling agent, dye bath temperature Spend to starting to dye after 40 DEG C, heat up and rise to 80~85 degree with the speed of 1 degree/2 minutes, insulation heats up again after 15 minutes, dye bath After temperature is increased to 95 DEG C, boiling dye 70~90 minutes, then gradually cooling drops to 40 DEG C with 1 degree/min of speed, while adds 1 ~2% color fixing agent;Drying:Dry and carried out in the cylinder group that surface temperature is 80~90 DEG C, 10~25 seconds time that cloth cover is bonded with cylinder;Thermal finalization:In tank before forming machine, added by proportioning and prevent agent 1~3% of becoming unwoven or untiwisted, antistatic additive 0.5%, waterproofing agent 1~ 2%, often shape 800~1000 meters, quantitatively supplement waterproofing agent, setting temperature is 130~140 DEG C, and machine rotational speed is 50 yards;Examine clot, packaging.
- 2. the anti-slippage sportswear face weave method of woven nylon according to claim 1, it is characterised in that:It is described anti- Slippage fabric through it is close be 180 pieces/inch.
- 3. the anti-slippage sportswear face weave method of woven nylon according to claim 1, it is characterised in that:It is described anti- The filling density of slippage fabric is 92 pieces/inch.