CN105562308B - 一种固化方法、显示面板的制造方法、显示面板及掩模 - Google Patents
一种固化方法、显示面板的制造方法、显示面板及掩模 Download PDFInfo
- Publication number
- CN105562308B CN105562308B CN201610092382.4A CN201610092382A CN105562308B CN 105562308 B CN105562308 B CN 105562308B CN 201610092382 A CN201610092382 A CN 201610092382A CN 105562308 B CN105562308 B CN 105562308B
- Authority
- CN
- China
- Prior art keywords
- mask
- light
- conversion material
- substrate
- curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种固化方法、显示面板的制造方法、显示面板及掩模。所述固化方法包括:提供可固化材料,提供掩模,在所述掩模侧提供入射光以固化所述可固化材料,其中,所述掩模的掩蔽层与可固化材料相对准;所述掩蔽层包括光转换材料;并且其中,所述光转换材料用于将所述入射光转换成能够使所述可固化材料固化的出射光。
Description
技术领域
本发明涉及显示技术领域,尤其涉及一种固化方法、显示面板的制造方法、显示面板及掩模。
背景技术
在现有技术中,对于显示面板,通常采用紫外(UV)光固化和传统热固化的混合固化方法。UV固化胶的特点是可以通过适当功率的紫外光照射将其在短时间内快速硬化。但是对于一些例如由于电极走线遮挡的区域,UV胶不能充分固化。因此,还需要采用热固化方法。
现有的封框胶预固化(UV光固化)工艺采用带有金属图案的玻璃基板作为掩模。该掩模将不需要预固化的部分遮挡住,需要固化的部分暴露在UV光下进行预固化,不同产品需要制作不同的UV掩模玻璃基板。
发明内容
本发明的实施例提供了一种固化方法、显示面板的制造方法、显示面板及掩模,能够解决现有技术中对玻璃基板需求量大、制造成本高且储存使用不便的问题。
本发明的一个目的在于提供一种固化方法。
本发明的第一方面提供了一种固化方法,所述方法包括:在可固化材料之上提供掩模,在所述掩模侧提供入射光以固化所述可固化材料,其中,
所述掩模的掩蔽层与可固化材料相对准;
所述掩蔽层包括光转换材料;其中,
所述光转换材料用于将所述入射光转换成能够使所述可固化材料固化的出射光。
在一种实施方式中,所述光转换材料为上转换材料。
可选地,所述上转换材料用于将可见光转换成紫外光。
可选地,所述上转换材料包括下列材料中的至少一种:NaYF4:Er3+,Yb3+;CaF2(Er3 +);ZrO2(Er3+);Ca3(PO4)2:Tm3+。
在一种实施方式中,所述掩蔽层还包括粘合剂。
可选地,通过下列步骤形成所述掩模:
提供基板;
将所述粘合剂和所述光转换材料混合以形成混合物;
将所述混合物按照特定图案设置在所述基板上以形成所述掩蔽层。
可选地,所述粘合剂包括树脂;
所述基板包括透明基板;
所述可固化材料包括封框胶。
可选地,所述树脂包括环氧树脂;
所述基板包括下列材料中的至少一种:玻璃、PMMA、PET和PC;以及
所述方法还包括在所述掩模侧提供入射光之后,对所述封框胶进行热固化。
本发明的另一个目的在于提供一种显示面板的制造方法。
本发明的第二方面提供了一种显示面板的制造方法,其包括上述的固化方法。
本发明的又一个目的在于提供一种显示面板。
本发明的第三方面提供了一种显示面板,其中,所述显示面板是上述的显示面板的制造方法所制造的。
发明的再一个目的在于提供一种掩模。
本发明的第四方面提供了一种掩模,包括基板和所述基板上的掩蔽层,所述掩蔽层包括光转换材料;其中,所述光转换材料用于将入射光转换成能够使可固化材料固化的出射光。
在一种实施方式中,所述光转换材料为上转换材料。
可选地,所述上转换材料用于将可见光转换成紫外光。
可选地,所述上转换材料包括下列材料中的至少一种:NaYF4:Er3+,Yb3+;CaF2(Er3 +);ZrO2(Er3+);Ca3(PO4)2:Tm3+。
在一种实施方式中,所述掩蔽层还包括粘合剂。
可选地,所述粘合剂包括树脂;
所述基板包括透明基板;
所述可固化材料包括封框胶。
可选地,所述树脂包括热固化树脂;
所述基板包括下列材料中的至少一种:玻璃、PMMA、PET和PC。
本发明的实施例提供的固化方法、显示面板的制造方法、显示面板及掩模,通过在掩模侧提供入射光以固化可固化材料,其中,所述掩模的掩蔽层与可固化材料相对准,所述掩蔽层包括光转换材料,并且其中,所述光转换材料用于将入射光转换成能够使所述可固化材料固化的出射光,节约了基板(例如,玻璃基板),降低了成本,且无需储存调动掩模,节约了生产时间。
附图说明
为了更清楚地说明本发明的实施例的技术方案,下面将对实施例的附图进行简要说明,应当知道,以下描述的附图仅仅涉及本发明的一些实施例,而非对本发明的限制,其中:
图1为现有技术的UV掩模设计的示意图;
图2是根据本发明的一个实施例的掩模的示意图;
图3是根据本发明的一个实施例的固化设计的侧视示意图。
具体实施方式
为了使本发明的实施例的目的、技术方案和优点更加清楚,下面将接合附图,对本发明的实施例的技术方案进行清楚、完整的描述。显然,所描述的实施例是本发明的一部分实施例,而不是全部的实施例。基于所描述的本发明的实施例,本领域技术人员在无需创造性劳动的前提下所获得的所有其他实施例,也都属于本发明保护的范围。
当介绍本发明的元素及其实施例时,冠词“一”、“一个”、“该”和“所述”旨在表示存在一个或者多个要素。用语“包含”、“包括”、“含有”和“具有”旨在包括性的并且表示可以存在除所列要素之外的另外的要素。出于下文表面描述的目的,如其在附图中被标定方向那样,术语“上”、“下”、“左”、“右”“垂直”、“水平”、“顶”、“底”及其派生词应涉及发明。术语“上覆”、“在……顶上”、“定位在……上”或者“定位在……顶上”意味着诸如第一结构的第一要素存在于诸如第二结构的第二要素上,其中,在第一要素和第二要素之间可存在诸如界面结构的中间要素。
图1为现有技术的UV掩模设计的示意图。如图1(a)所示,对于UV掩模,在基板的斜线阴影区域涂覆有遮光金属。图1(b)示出了具有液晶显示区域和封框胶的玻璃基板。遮光金属将不需要UV固化的部分挡住,需要固化的部分能够暴露在UV光下进行预固化。由于紫外光对液晶分子有损伤,所以在固化过程中,必须将液晶显示区域部分遮蔽。对于不同产品,由于需要遮蔽的显示区域不同,需要制作不同的UV掩模玻璃基板。
图2是根据本发明的一个实施例的掩模的示意图。如图2所示,掩模具有基板和掩蔽层。掩蔽层包括光转换材料,该光转换材料可以将入射光转换成能够使可固化材料固化的出射光。
掩模上的图案的形状并非限制于图2中所示的长方形,也可以为任何需要的形状。掩模上的图案的个数也并非限制于图2中所示的6个,也可以为任何需要的数目。此外,可根据实际需要来设置每个图案的边框宽度和大小。
基板可以包括本领域采用的任何基板,优选为透明基板。基板包括下列材料中的至少一种:玻璃、PMMA、PET和PC。
可固化材料可以为本领域采用的任何可固化材料,包括但不限制于紫外固化胶。在一种实施方式中,可固化材料包括封框胶。
容易理解,在使用本实施例的掩模进行固化时,需要将掩模的掩蔽层与可固化材料对准,即,掩蔽层的位置和图案与要被固化的可固化材料的位置和图案相对应。
在一种实施方式中,光转换材料包括上转换材料。优选地,该上转换材料包括用于将可见光转换成紫外光的可见光-紫外光转换材料。以下将以光转换材料为可见光-紫外光转换材料进行示例性说明。需要指出的是,本公开的光转换材料并非仅限于可见光-紫外光转换材料,也可以包括任何其它适合于进行固化的光转换材料。
对于液晶面板的情况,在一种实施方式中,由于可以使用可见光作入射光,而可见光不会像紫外光那样损伤液晶分子,因此与现有技术不同,无需将显示区域所对应的掩模的区域遮蔽,仅需在封框胶对应的掩模的区域处设置具有可见光-紫外光转换材料的掩蔽层。
光转换材料可以包括下列材料中的至少一种:NaYF4:Er3+,Yb3+;CaF2(Er3+);ZrO2(Er3+);Ca3(PO4)2:Tm3+。优选地,光转换材料可以吸收波长480nm左右的蓝光,发射波长332nm、376nm左右的紫外光。
掩蔽层还可以进一步地包括粘合剂。优选使用具有下列性质的材料作为粘合剂:光透过率高、性质稳定、受可见光及紫外光照射不发生分解或聚合、以及易清洗。粘合剂可以包括任何合适的胶状树脂。例如,热固化类的环氧树脂可以用作粘合剂。
在掩蔽层还包括粘合剂的情况下,在一个实施例中,形成掩模可以包括:提供基板;将粘合剂和光转换材料混合以形成混合物;将混合物按照特定图案设置在基板上以形成掩蔽层。
图3是根据本发明的一个实施例的固化设计的侧视示意图。图3所示的固化方法使用了图2所示的掩模。需要注意,图中所示的上下关系仅为示意性的,而非限制本发明。
在图3示出的固化方法中,在可固化材料之上提供掩模,在掩模侧提供入射光以固化可固化材料,掩模的掩蔽层与可固化材料相对准并且包括光转换材料,其中,光转换材料用于将入射光转换成能够使可固化材料固化的出射光。
在一个实施例中,具体地,在显示区域附近设置了包括可固化材料的封框胶,在掩模的透明基板上设置了含有上转换材料的掩蔽层。从光源处朝向掩模发出作为入射光的可见光。一部分入射光穿过掩模的掩蔽层,由于受到隐蔽层的上转换材料的影响,此部分入射光被转换成能够使封框胶固化的紫外光;另一部分入射光则不发生波长改变而直接穿过掩模的除了掩蔽层之外的区域。由于含有上转换材料的隐蔽层与封框胶相对准,封框胶受到从掩蔽层出射的紫外光的影响而固化,因而无需遮蔽对应于诸如液晶显示区域的其他部分,简化了制造工艺并降低制造成本。
上转换材料可以包括下列材料中的至少一种:NaYF4:Er3+,Yb3+;CaF2(Er3+);ZrO2(Er3+);Ca3(PO4)2:Tm3+。
掩蔽层还可以包括粘合剂。粘合剂优选包括诸如环氧树脂的热固化树脂。在一个实施例中,可以将混有上转换材料的胶状树脂涂覆在透明基板上,涂覆图案与需预固化玻璃基板上的封框胶的图案相对应。
在掩模侧提供入射光完成光固化之后,还可以进一步地对可固化材料(例如,封框胶)进行热固化。
与现有技术相比,本技术只需要一块基板(例如,透明基板),针对不同产品,可以涂覆具有不同图案的掩蔽层(例如,树脂),通过掩蔽层发出出射光(例如,紫外光),来对可固化材料(例如,封框胶)进行固化。不同产品之间切换时,只需要将掩蔽层清洗掉然后重新涂覆即可。各产品之间无需制作不同掩模(例如,UV掩模),节约了基板(例如,玻璃基板),降低了成本。且无需储存调动掩模,节约了生产时间。
已经描述了某特定实施例,这些实施例仅通过举例的方式展现,而且不旨在限制本发明的范围。事实上,本文所描述的新颖实施例可以以各种其它形式来实施;此外,可在不脱离本发明的精神下,做出以本文所描述的实施例的形式的各种省略、替代和改变。所附权利要求以及它们的等价物旨在覆盖落在本发明范围和精神内的此类形式或者修改。
Claims (17)
1.一种固化方法,包括:提供可固化材料,提供掩模,在所述掩模侧提供入射光以固化所述可固化材料,其特征在于,
所述掩模的掩蔽层与可固化材料垂直对准;
所述掩蔽层包括光转换材料;其中,
所述光转换材料用于将入射光转换成能够使所述可固化材料固化的出射光。
2.根据权利要求1所述的方法,其中,所述光转换材料为上转换材料。
3.根据权利要求2所述的方法,其中,所述上转换材料用于将可见光转换成紫外光。
4.根据权利要求3所述的方法,其中,所述上转换材料由包含下列的至少一种成份的材料组成:NaYF4:Er3+,Yb3+;CaF2(Er3+);ZrO2(Er3+);Ca3(PO4)2:Tm3+。
5.根据权利要求1-4中任一项所述的方法,其中,所述掩蔽层还包括粘合剂。
6.根据权利要求5所述的方法,其中,提供掩模进一步包括:
提供基板;
将粘合剂和光转换材料混合以形成混合物;
将所述混合物按照特定图案设置在基板上。
7.根据权利要求6所述的方法,其中,所述粘合剂为树脂;
所述基板为透明基板;
所述可固化材料为封框胶。
8.根据权利要求7所述的方法,其中,所述树脂为环氧树脂;
所述基板由选择下列的至少一种材料制成:玻璃、PMMA、PET和PC;
所述方法还包括在所述掩模侧提供入射光之后,对所述封框胶进行热固化。
9.一种制造显示面板的方法,其特征在于,包括权利要求1-8中的任一项所述的固化方法。
10.一种显示面板,其特征在于,所述显示面板是通过权利要求9所述的制造显示面板的方法所制造的。
11.一种掩模,其特征在于,包括基板和掩蔽层,所述掩蔽层包括光转换材料;其中,所述光转换材料用于将入射光转换成能够使可固化材料固化的出射光。
12.根据权利要求11所述的掩模,其中,所述光转换材料为上转换材料。
13.根据权利要求12所述的掩模,其中,所述上转换材料用于将可见光转换成紫外光。
14.根据权利要求13所述的掩模,其中,所述上转换材料由包含下列的至少一种成份的材料组成:NaYF4:Er3+,Yb3+;CaF2(Er3+);ZrO2(Er3+);Ca3(PO4)2:Tm3+。
15.根据权利要求11-14中任一项所述的掩模,其中,所述掩蔽层还包括粘合剂。
16.根据权利要求15所述的掩模,其中,所述粘合剂为树脂;
所述基板为透明基板;
所述可固化材料为封框胶。
17.根据权利要求16所述的掩模,其中,所述树脂为环氧树脂;
所述基板由选择下列的至少一种材料制成:玻璃、PMMA、PET和PC。