CN105507078A - Wallpaper containing a volcanic rock-polylactic acid porous fiber modified acrylic resin emulsion coating - Google Patents
Wallpaper containing a volcanic rock-polylactic acid porous fiber modified acrylic resin emulsion coating Download PDFInfo
- Publication number
- CN105507078A CN105507078A CN201510827400.4A CN201510827400A CN105507078A CN 105507078 A CN105507078 A CN 105507078A CN 201510827400 A CN201510827400 A CN 201510827400A CN 105507078 A CN105507078 A CN 105507078A
- Authority
- CN
- China
- Prior art keywords
- polylactic acid
- emulsion
- volcanic rock
- acrylic resin
- wallpaper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses wallpaper containing a volcanic rock-polylactic acid porous fiber modified acrylic resin emulsion coating. A cellulose acetate-copolymerized modified waterborne acrylic resin emulsion is adopted as a resin adhesive in coating slurry used for the wallpaper, and is stable in performance and free of toxic compounds slow in volatilization such as formaldehyde. The formed coating is smooth and elastic and has waterproof, antifouling and antibacterial functions and other functions. Compared with traditional PVC paste, plasticizing temperature of the coating is lower, and the coating is more energy-saving and environmental friendly. Graphene-doped volcanic rock-polylactic acid porous fibers have functions of high strength, heat preservation, thermal insulation, sound absorption, porosity, formaldehyde removing, and the like. Adsorbability with a substrate is improved. The service lifetime of the wallpaper is effectively prolonged. The wallpaper has a certain indoor air cleaning function.
Description
Technical field
The present invention relates to wallpaper technical field, particularly relate to a kind of wallpaper containing volcanic rock-polylactic acid porous fibre modification emulsion acrylic resin coating.
Background technology
Wallpaper has another name called wallpaper, because of it, to have color various, pattern enriches, the advantage such as luxurious style, safety and environmental protection, easy construction, affordable is applied more and more extensive in house ornamentation, common wallpaper is greatly using the material such as pure paper, nonwoven fabric as base material, at its surperficial coated with resins slurry, make through operations such as high temperature plasticizing, printing embossing.
Modal coating paste is mainly made up of polyvinyl chloride resin and filler in the market, although this coating material has the advantages such as attractive and durable waterproof, but its poor air permeability, and containing organic solvent, long-time use can pollute room air, along with the raising of people's environmental consciousness, require also more and more higher to the feature of environmental protection of wallpaper, this needs to use new coating material to replace polyvinyl chloride resin undoubtedly.In recent years market emerges the water-base resin coating material of a collection of environmental protection, although this kind of material is not containing volatile organic solvent, but its gas permeability, plasticization temperature, additional functional and with the stickiness of base material etc. in still Shortcomings.
Summary of the invention
The object of the invention is exactly the defect in order to make up prior art, provides a kind of wallpaper containing volcanic rock-polylactic acid porous fibre modification emulsion acrylic resin coating.
The present invention is achieved by the following technical solutions:
A kind of wallpaper containing volcanic rock-polylactic acid porous fibre modification emulsion acrylic resin coating, this wallpaper is made up after super-dry, plasticizing, embossing of non-woven fabrics base material and the coating paste being coated on substrate surface, and described coating paste is made up of the raw material of following weight portion: composite water soluble emulsion acrylic resin 80-100, volcanic rock micro mist 2-3, Graphene 0.01-0.02, polylactic acid slice 8-10, vinyl two stearic amide 0.1-0.2, silane coupler kh5500.1-0.2.
Described coating paste preparation method is:
(1) volcanic rock-polylactic acid porous fiber preparation: first polylactic acid slice, volcanic rock micro mist, Graphene, the two stearic amide of vinyl, silane coupler kh550 are carried out melt spinning after being uniformly mixed, making length is 80-100 μm, and diameter is the porous staple fibre of 30-50 μm;
(2) volcanic rock-polylactic acid porous fiber is dropped in composite water soluble emulsion acrylic resin, add other leftover materials after being uniformly mixed 30-50min, strong stirring mixing 4-5h, leave standstill after placing 30-40min subsequently and get final product.
Described composite water soluble emulsion acrylic resin is made up of the raw material of following weight portion: nano silicon 0.5-0.8, cellulose acetate 4-5, N, dinethylformamide 12-15, butyl acrylate 18-25, methyl methacrylate 15-20, acrylic acid 10-15, ammonium persulfate 5-8, emulsifier op-10 2-3, lauryl sodium sulfate 1-3, ammoniacal liquor are appropriate, deionized water 50-60, and preparation method is:
(1) first drop in DMF by cellulose acetate, be stirred to it and dissolve completely, drop in solution subsequently by nano silicon, closed ultrasonic dispersed with stirring 3-4h, the cellulose acetate solution obtaining blending nano silicon is for subsequent use;
(2) emulsifier op-10, lauryl sodium sulfate are dropped in reactor, add the deionized water of 10-15 weight portion subsequently, be stirred to after dissolving completely, material prepared by input step (1) and butyl acrylate, methyl methacrylate, acrylic acid, be warming up to 70-75 DEG C, be uniformly mixed 2-3h, obtain pre-emulsion for subsequent use;
(3) seed emulsion preparation: ammonium persulfate and appropriate ammoniacal liquor are dissolved in the deionized water of surplus, regulator solution pH value is 6.0-7.5, and be heated to 65-75 DEG C, then pre-emulsion prepared by this solution of 2/3 weight portion and 1/4 weight portion step (2) is got respectively, be added drop-wise in reaction vessel simultaneously, rate of addition is that 45-60 drips/min, stops dripping, obtain seed emulsion when question response system is blue-fluorescence;
(4) gained seed emulsion drips ammonium persulfate solution and the pre-emulsion of surplus again after leaving standstill 15-20min, after dropping terminates under 70-75 DEG C of condition constant temperature 50-60min, be heated to 75-80 DEG C subsequently, strong stirring mixing 1.5-2h under constant temperature, stop subsequently stirring, when emulsion naturally cools to below 50 DEG C, ammoniacal liquor regulator solution pH value is 7.0, filters discharging subsequently and get final product.
Resin adhesive in the coating paste that wallpaper of the present invention uses is cellulose acetate modification by copolymerization water-borne acrylic resin emulsion, this resin emulsion stable performance, not containing chronic volatility toxic compounds such as formaldehyde, the coating formed is smooth flexible, possesses water resistant, anti-soil, the function such as antibacterial, lower than traditional PVC paste material plasticization temperature, more energy-conserving and environment-protective, volcanic rock-polylactic acid porous the fiber of blending Graphene has high strength, insulation, heat insulation, sound-absorbing, porous, except effects such as formaldehyde, absorption affinity between enhancement and base material, effectively extend the service life of wallpaper, also certain catharsis is had to the air of indoor.
Detailed description of the invention
This embodiment wallpaper is made up after super-dry, plasticizing, embossing of non-woven fabrics base material and the coating paste being coated on substrate surface, and wherein coating paste is made up of the raw material of following weight portion: composite water soluble emulsion acrylic resin 80, volcanic rock micro mist 2, Graphene 0.01, polylactic acid slice 8, vinyl two stearic amide 0.1, silane coupler kh5500.1.
This coating paste preparation method is:
(1) volcanic rock polylactic acid porous fiber preparation: first polylactic acid slice, volcanic rock micro mist, Graphene, the two stearic amide of vinyl, silane coupler kh550 are carried out melt spinning after being uniformly mixed, making length is 80 μm, and diameter is the porous staple fibre of 30 μm;
(2) polylactic acid porous for volcanic rock fiber is dropped in composite water soluble emulsion acrylic resin, add other leftover materials after being uniformly mixed 30min, strong stirring mixing 4h, leave standstill after placing 30min subsequently and get final product.
Wherein composite water soluble emulsion acrylic resin is made up of the raw material of following weight portion: nano silicon 0.5, cellulose acetate 4, N, dinethylformamide 12, butyl acrylate 18, methyl methacrylate 15, acrylic acid 10, ammonium persulfate 5, polyoxyethylene nonylphenol ether 2, lauryl sodium sulfate 1, ammoniacal liquor are appropriate, deionized water 50, and preparation method is:
(1) first drop in DMF by cellulose acetate, be stirred to it and dissolve completely, drop in solution subsequently by nano silicon, closed ultrasonic dispersed with stirring 3h, the cellulose acetate solution obtaining blending nano silicon is for subsequent use;
(2) polyoxyethylene nonylphenol ether, lauryl sodium sulfate are dropped in reactor, add the deionized water of 10 weight portions subsequently, be stirred to after dissolving completely, material prepared by input step (1) and butyl acrylate, methyl methacrylate, acrylic acid, be warming up to 70 DEG C, be uniformly mixed 2h, obtain pre-emulsion for subsequent use;
(3) seed emulsion preparation: ammonium persulfate and appropriate ammoniacal liquor are dissolved in the deionized water of surplus, regulator solution pH value is 6.0, and be heated to 65 DEG C, then pre-emulsion prepared by this solution of 2/3 weight portion and 1/4 weight portion step (2) is got respectively, be added drop-wise in reaction vessel simultaneously, rate of addition is 45/min, stops dripping, obtain seed emulsion when question response system is blue-fluorescence;
(4) gained seed emulsion drips ammonium persulfate solution and the pre-emulsion of surplus again after leaving standstill 15min, after dropping terminates under 70 DEG C of conditions constant temperature 50min, be heated to 75 DEG C subsequently, strong stirring mixing 1.5h under constant temperature, stop subsequently stirring, when emulsion naturally cools to below 50 DEG C, ammoniacal liquor regulator solution pH value is 7.0, filters discharging subsequently and get final product.
Coating paste is coated in nonwoven fabric base paper surface, control coating weight is 15g/m
2, after its drying, plastify embossing under 135 DEG C of conditions, carry out performance test to product according to relevant criterion after cooling forming, test result is:
Formaldehyde clearance:
0h:45.5%;24h:80.5%;48h:92.8%;72h:95.5%;96h:97.5%;120h:98.0%。
Regain: 0.70%; Air permeability: 10.4L/(m
2s); Tensile strength: 3280N/m, bursting strength: 182KPa.
Antibacterial and mouldproof: can 96.8% be reached to staphylococcus aureus bacteriostasis rate; Can 98.0% be reached to Escherichia coli bacteriostasis rate; It is 0 grade to the antibacterial grade of aspergillus niger, chaetomium globosum, green sticky broom bacterium.
Wallpaper prepared by this embodiment meets the regulation of GB18585-2001, the heavy metal antimony, arsenic, barium, cadmium, chromium, lead, mercury, the selenium that prohibit the use not containing national regulation, not containing formaldehyde, not containing Vinyl Chloride Monomer.
Claims (3)
1. the wallpaper containing volcanic rock-polylactic acid porous fibre modification emulsion acrylic resin coating, this wallpaper is made up after super-dry, plasticizing, embossing of non-woven fabrics base material and the coating paste being coated on substrate surface, it is characterized in that, described coating paste is made up of the raw material of following weight portion: composite water soluble emulsion acrylic resin 80-100, volcanic rock micro mist 2-3, Graphene 0.01-0.02, polylactic acid slice 8-10, vinyl two stearic amide 0.1-0.2, silane coupler kh5500.1-0.2.
2. a kind of wallpaper containing volcanic rock-polylactic acid porous fibre modification emulsion acrylic resin coating as claimed in claim 1, it is characterized in that, described coating paste preparation method is:
(1) volcanic rock-polylactic acid porous fiber preparation: first polylactic acid slice, volcanic rock micro mist, Graphene, the two stearic amide of vinyl, silane coupler kh550 are carried out melt spinning after being uniformly mixed, making length is 80-100 μm, and diameter is the porous staple fibre of 30-50 μm;
(2) volcanic rock-polylactic acid porous fiber is dropped in composite water soluble emulsion acrylic resin, add other leftover materials after being uniformly mixed 30-50min, strong stirring mixing 4-5h, leave standstill after placing 30-40min subsequently and get final product.
3. a kind of wallpaper containing volcanic rock-polylactic acid porous fibre modification emulsion acrylic resin coating as claimed in claim 1 or 2, it is characterized in that, described composite water soluble emulsion acrylic resin is made up of the raw material of following weight portion: nano silicon 0.5-0.8, cellulose acetate 4-5, N, dinethylformamide 12-15, butyl acrylate 18-25, methyl methacrylate 15-20, acrylic acid 10-15, ammonium persulfate 5-8, emulsifier op-10 2-3, lauryl sodium sulfate 1-3, ammoniacal liquor are appropriate, deionized water 50-60, and preparation method is:
(1) first drop in DMF by cellulose acetate, be stirred to it and dissolve completely, drop in solution subsequently by nano silicon, closed ultrasonic dispersed with stirring 3-4h, the cellulose acetate solution obtaining blending nano silicon is for subsequent use;
(2) emulsifier op-10, lauryl sodium sulfate are dropped in reactor, add the deionized water of 10-15 weight portion subsequently, be stirred to after dissolving completely, material prepared by input step (1) and butyl acrylate, methyl methacrylate, acrylic acid, be warming up to 70-75 DEG C, be uniformly mixed 2-3h, obtain pre-emulsion for subsequent use;
(3) seed emulsion preparation: ammonium persulfate and appropriate ammoniacal liquor are dissolved in the deionized water of surplus, regulator solution pH value is 6.0-7.5, and be heated to 65-75 DEG C, then pre-emulsion prepared by this solution of 2/3 weight portion and 1/4 weight portion step (2) is got respectively, be added drop-wise in reaction vessel simultaneously, rate of addition is that 45-60 drips/min, stops dripping, obtain seed emulsion when question response system is blue-fluorescence;
(4) gained seed emulsion drips ammonium persulfate solution and the pre-emulsion of surplus again after leaving standstill 15-20min, after dropping terminates under 70-75 DEG C of condition constant temperature 50-60min, be heated to 75-80 DEG C subsequently, strong stirring mixing 1.5-2h under constant temperature, stop subsequently stirring, when emulsion naturally cools to below 50 DEG C, ammoniacal liquor regulator solution pH value is 7.0, filters discharging subsequently and get final product.