CN103469576A - Coating non-woven fabric - Google Patents
Coating non-woven fabric Download PDFInfo
- Publication number
- CN103469576A CN103469576A CN2013104516255A CN201310451625A CN103469576A CN 103469576 A CN103469576 A CN 103469576A CN 2013104516255 A CN2013104516255 A CN 2013104516255A CN 201310451625 A CN201310451625 A CN 201310451625A CN 103469576 A CN103469576 A CN 103469576A
- Authority
- CN
- China
- Prior art keywords
- coating
- nonwoven fabric
- parts
- drying
- woven fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a coating non-woven fabric. After hydrophilic finishing is carried out on the no-woven fabric, knife coating of water dispersing type acrylic ester copolymer emulsion and a blend coating of aluminum powder, titanium dioxide and cellulose is carried out, then drying is carried out, and therefore the coating non-woven fabric is obtained. Compared with existing heat reflection cloth, the coating non-woven fabric has the advantage that air permeability and abrasion resistance are both improved.
Description
Technical field
The present invention relates to a kind of fabric, be specifically related to a kind of coating nonwoven fabric.
Background technology
The outdoor goods such as tent are except weather-proof basic function, sometimes also need to provide heat-preserving function, the general mode that increases heat reflection liner cloth in inside that adopts solves at present, existing heat reflection liner cloth adopts the mode at polyester material surface chemistry vapour deposition (CVD) thin metal layer to make mostly, although reflecting heat well, Shortcomings aspect permeability and anti-wear performance.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, the invention provides a kind of coating nonwoven fabric heat insulation function and that improved ventilative and anti-wear performance that has.
Technical scheme: for solving the problems of the technologies described above, a kind of coating nonwoven fabric that the present invention proposes is made by following steps:
1) preparation of coating, take 100～150 parts of the water-dispersed acrylic ester copolymer emulsions of solid content 40%, 4～7 parts of aluminium powders, and 2～5 parts of titanium dioxides, 10～15 parts of celluloses also mix, and stir 1～1.5h with electric mixer and obtain coating;
2) adopt hydrophilic finishing agent to be arranged nonwoven fabric;
3) blade coating, the coating blade coating that adopts the method for the direct coating of dry method that step 1) is made is in through step 2) on the nonwoven fabric that arranged;
4) drying at room temperature, by the dry 5～10min at room temperature of the nonwoven fabric after blade coating;
5) dry drying tunnel inner drying 18～30 min by the dried nonwoven fabric of step 4) at 100～130 ℃.
As preferably, the temperature of drying in described step 5) is 120 ℃.
As preferably, in described coating, the parts by weight of each component are 5 parts of aluminium powders, 4 parts of titanium dioxides, 12 parts of celluloses.
As preferably, described nonwoven fabric is spunlace non-woven cloth.
Beneficial effect: the present invention adopts the mode of blade coating acrylate copolymer emulsion to make heat-reflecting material form coating on nonwoven fabric, compares existing insulation processing method, and ABRASION RESISTANCE and the gas permeability of the coating nonwoven fabric obtained have remarkable improvement.
The specific embodiment
Embodiment 1
Get the needle punched non-woven fabrics sample of 1m*1m, according to following steps, make the coating nonwoven fabric
1) preparation of coating, take 150 parts of the water-dispersed acrylic ester copolymer emulsions of solid content 40%, 7 parts of aluminium powders, and 5 parts of titanium dioxides, 15 parts of celluloses also mix, and stir 1h with electric mixer and obtain coating;
2) adopt the special-purpose hydrophilic finishing agent of non-weaving cloth of Zhejiang Province Chuanhua Co., Ltd to be arranged nonwoven fabric;
3) blade coating, the coating blade coating that adopts the method for the direct coating of dry method that step 1) is made is in through step 2) on the nonwoven fabric that arranged;
4) drying at room temperature, by the dry 5min at room temperature of the nonwoven fabric after blade coating;
5) dry drying tunnel inner drying 18 min by the dried nonwoven fabric of step 4) at 130 ℃.
Embodiment 2
Get the spunlace non-woven cloth sample of 1m*1m, according to following steps, make the coating nonwoven fabric
1) preparation of coating, take 150 parts of the water-dispersed acrylic ester copolymer emulsions of solid content 40%, 5 parts of aluminium powders, and 4 parts of titanium dioxides, 12 parts of celluloses, stir 1.5h with electric mixer after mixing and obtain coating;
2) adopt the special-purpose hydrophilic finishing agent of non-weaving cloth of Zhejiang Province Chuanhua Co., Ltd to be arranged nonwoven fabric;
3) blade coating, the coating blade coating that adopts the method for the direct coating of dry method that step 1) is made is in through step 2) on the nonwoven fabric that arranged;
4) drying at room temperature, by the dry 10min at room temperature of the nonwoven fabric after blade coating;
5) dry drying tunnel inner drying 30 min by the dried nonwoven fabric of step 4) at 120 ℃.
Adopt following method of testing to measure respectively system existing heat reflection liner cloth (CVD film), the Air permenbility of embodiment 1 and embodiment 2:
The digital air permeation volume gauge of laboratory apparatus: YG461E
The mensuration of testing standard: GB/T 5453-1997 textile fabric gas permeability
Environmental condition: 20 ℃ of temperature, relative humidity 65 %
Fabric pressure drop: 100Pa
Area of Sample: center clip 20cm*20cm
| The CVD film | Embodiment 1 | Embodiment 2 | |
| Air permenbility (L/s) | 45 | 61.5 | 66.5 |
Visible, coating nonwoven fabric of the present invention is compared existing heat reflection liner cloth and is had gas permeability preferably.
Claims (4)
1. a coating nonwoven fabric is characterized in that being made by following steps:
1) preparation of coating, take 100～150 parts of the water-dispersed acrylic ester copolymer emulsions of solid content 40%, 4～7 parts of aluminium powders, and 2～5 parts of titanium dioxides, 10～15 parts of celluloses also mix, and stir 1～1.5h with electric mixer and obtain coating;
2) adopt hydrophilic finishing agent to be arranged nonwoven fabric;
3) blade coating, the coating blade coating that adopts the method for the direct coating of dry method that step 1) is made is in through step 2) on the nonwoven fabric that arranged;
4) drying at room temperature, by the dry 5～10min at room temperature of the nonwoven fabric after blade coating;
5) dry drying tunnel inner drying 18～30 min by the dried nonwoven fabric of step 4) at 100～130 ℃.
2. coating nonwoven fabric according to claim 1, it is characterized in that: the temperature of drying in described step 5) is 120 ℃.
3. coating nonwoven fabric according to claim 1, it is characterized in that: in described coating, the parts by weight of each component are 5 parts of aluminium powders, 4 parts of titanium dioxides, 12 parts of celluloses.
4. coating nonwoven fabric according to claim 1, it is characterized in that: described nonwoven fabric is spunlace non-woven cloth.