CN105506356A - Water treatment equipment for vibrating membrane - Google Patents
Water treatment equipment for vibrating membrane Download PDFInfo
- Publication number
- CN105506356A CN105506356A CN201510996483.XA CN201510996483A CN105506356A CN 105506356 A CN105506356 A CN 105506356A CN 201510996483 A CN201510996483 A CN 201510996483A CN 105506356 A CN105506356 A CN 105506356A
- Authority
- CN
- China
- Prior art keywords
- tempering
- time
- hours
- alloy material
- room temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water treatment equipment for a vibrating membrane, comprising a pipeline made from alloy material subjected to tempering treatment, wherein the alloy material contains the following components: 1-2% of P, 1.9% of Ti, 0.6% of V, 0.1% of Pm, 0.7% of Li, 0.3% of Pb, and the balance of Cu and unavoidable impurities. The alloy material is subjected to tempering treatment according to the following steps: 1. carrying out first time of tempering at 445 DEG C with tempering duration of 3 hours, and then carrying out air-cooling to room temperature; 2. carrying out second time of tempering at 495 DEG C with tempering duration of 2.5 hours, and then carrying out air-cooling to room temperature; and 3. carrying out third time of tempering at 595 DEG C with tempering duration of 2 hours, and then carrying out air-cooling to room temperature. The pipeline used by the water treatment equipment is high in strength, good in corrosion resistance, abrasion resistance, heat resistance, cold resistance, oxidation resistance and weather resistance, and long in use time.
Description
Technical field
The present invention relates to tympanum water treating equipment.
Background technology
Tympanum water treating equipment are generally provided with some pipelines, and to pipeline performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of tympanum water treating equipment, its pipeline is made up of the alloy material through temper, and pipeline strength is high, corrosion-resistant, abrasion-resistant, heat-resisting, cold-resistant, anti-oxidant, weather resistance is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of tympanum water treating equipment of design, and comprise some pipelines, described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1～2％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Preferably, tympanum water treating equipment, comprise some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Preferably, tympanum water treating equipment, comprise some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：2％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Advantage of the present invention and beneficial effect are: provide a kind of tympanum water treating equipment, its pipeline is made up of the alloy material through temper, and pipeline strength is high, corrosion-resistant, abrasion-resistant, heat-resisting, cold-resistant, anti-oxidant, weather resistance is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of tympanum water treating equipment, comprise some pipelines, described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1～2％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Embodiment 2
Tympanum water treating equipment, comprise some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Embodiment 3
Tympanum water treating equipment, comprise some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：2％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. tympanum water treating equipment, is characterized in that, comprise some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1～2％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
2. tympanum water treating equipment according to claim 1, is characterized in that, comprise some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
3. tympanum water treating equipment according to claim 1, is characterized in that, comprise some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：2％，
Ti：1.9％，
V：0.6％，
Pm：0.1％，
Li：0.7％，
Pb：0.3％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 445 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 495 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 595 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.