CN105369054A - Industrial chemical feeding machine - Google Patents
Industrial chemical feeding machine Download PDFInfo
- Publication number
- CN105369054A CN105369054A CN201510996567.3A CN201510996567A CN105369054A CN 105369054 A CN105369054 A CN 105369054A CN 201510996567 A CN201510996567 A CN 201510996567A CN 105369054 A CN105369054 A CN 105369054A
- Authority
- CN
- China
- Prior art keywords
- tempering
- time
- alloy material
- room temperature
- air cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an industrial chemical feeding machine. The industrial chemical feeding machine comprises a pipeline made of an alloy material subjected to tempering treatment, wherein the alloy material comprises components as follows: 1%-2% of P, 0.6% of At, 0.7% of Cd, 0.9% of In, 0.5% of Zr, 0.7% of Nb and the balance of Cu and inevitable impurities; the alloy material is subjected to the tempering treatment through steps as follows: 1), the alloy material is subjected to first tempering at the temperature of 435 DEG C for 3 h and then is subjected to air cooling to the room temperature; 2), the alloy material is subjected to second tempering at the temperature of 485 DEG C for 2.5 h and then is subjected to air cooling to the room temperature; 3), the alloy material is subjected to third tempering at the temperature of 585 DEG C for 2 h and then is subjected to air cooling to the room temperature. The adopted pipeline is high in strength, resistant to corrosion, wearing, heat, cold and oxidation, good in weather fastness and long in service time.
Description
Technical field
The present invention relates to industrial chemicals feeder.
Background technology
Industrial chemicals feeder is generally provided with some pipelines, and to pipeline performance requriements higher.
Summary of the invention
The object of the present invention is to provide a kind of industrial chemicals feeder, its pipeline is made up of the alloy material through temper, and pipeline strength is high, corrosion-resistant, abrasion-resistant, heat-resisting, cold-resistant, anti-oxidant, weather resistance is good, and duration of service is long.
For achieving the above object, technical scheme of the present invention is a kind of industrial chemicals feeder of design, and comprise some pipelines, described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1～2％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Preferably, industrial chemicals feeder, comprises some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Preferably, industrial chemicals feeder, comprises some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：2％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Advantage of the present invention and beneficial effect are: provide a kind of industrial chemicals feeder, its pipeline is made up of the alloy material through temper, and pipeline strength is high, corrosion-resistant, abrasion-resistant, heat-resisting, cold-resistant, anti-oxidant, weather resistance is good, and duration of service is long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of industrial chemicals feeder, comprise some pipelines, described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1～2％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Embodiment 2
Industrial chemicals feeder, comprises some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
Embodiment 3
Industrial chemicals feeder, comprises some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：2％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. industrial chemicals feeder, is characterized in that, comprises some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1～2％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
2. industrial chemicals feeder according to claim 1, is characterized in that, comprises some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：1％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.
3. industrial chemicals feeder according to claim 1, is characterized in that, comprises some pipelines, and described pipeline is made up of the alloy material through temper, and by weight percentage, the composition of this alloy material is:
P：2％，
At：0.6％，
Cd：0.7％，
In：0.9％，
Zr：0.5％，
Nb：0.7％，
Surplus is Cu and inevitable impurity;
Described alloy material carries out temper as follows:
1) carry out first time tempering in 435 DEG C, tempering time is 3 hours, and then air cooling is to room temperature;
2) carry out second time tempering in 485 DEG C, tempering time is 2.5 hours, and then air cooling is to room temperature;
3) carry out third time tempering in 585 DEG C, tempering time is 2 hours, and then air cooling is to room temperature.