CN105500853A - Double-sided color electric aluminum hot stamping foil and production method thereof - Google Patents
Double-sided color electric aluminum hot stamping foil and production method thereof Download PDFInfo
- Publication number
- CN105500853A CN105500853A CN201410482933.9A CN201410482933A CN105500853A CN 105500853 A CN105500853 A CN 105500853A CN 201410482933 A CN201410482933 A CN 201410482933A CN 105500853 A CN105500853 A CN 105500853A
- Authority
- CN
- China
- Prior art keywords
- coating
- chromatograph
- water
- coated
- sided color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a double-sided color electric aluminum hot stamping foil and a production method thereof. According to the present invention, after the double-sided color electric aluminum hot stamping foil is subjected to hot stamping on a transparent material, the front surface and the back surface of the stamped material can display the same or different colors; after the double-sided color electric aluminum hot stamping foil is used for plastic composite film printing, the hot stamping picture-text can be lined while the printing on the back surface, and the precise chromatograph edition of the hot stamping pattern and the ink printing picture-text can be achieved; and after the product is compounded, the printing layer and the hot stamping layer are positioned on the inner surface of the printed film, the gloss is strong, and the scratch caused by external force cannot be generated.
Description
Technical field
The present invention relates to two-sided color alumite thermoprinting foil and production method thereof.
Background technology
Alumite thermoprinting foil is a kind of material being coated with the film-form for hot transfer printing that the coating of several layers of difference in functionality and vacuum evaporation one deck aluminium coated are made in Plastic film surface, reprocess after being widely used in the printings such as paper plastic, to obtain, there is the brilliant character pattern of metallic luster or color lump.
Traditional making alumite thermoprinting foil technique is:
1. release layer: use biaxially oriented polyester film (BOPET) surface coating release layer.
2. chromatograph: at release layer surface coating chromatograph coating, chromatograph coating is added with 0% ~ 10% colorant and reaches customer personalized color demand.
3. aluminium coated: at the surperficial aluminium coated through vacuum aluminum-plating machine vacuum evaporation 200 ~ 500 dust thickness of chromatograph to obtain gold lustre effect.
4. glue-line: at aluminium coated surface coated glue layer coating.
There is following shortcoming in tradition alumite thermoprinting foil manufacture craft: traditional alumite thermoprinting foil thermoprint when transparent material (as plastic sheeting) only front can manifest the front shades of colour of alumite thermoprinting foil, only can see the canescence of alumite thermoprinting foil reverse side through transparent material reverse side; And be undertake the printing of at film reverse side during the printing of plastic flexible package composite membrane picture and text, again printing-ink face and hot sealing layer dry type compound are made, need to use alumite thermoprinting foil thermoprint pattern can only after dry type compound again thermoprint on the surface of composite membrane, cause and cannot locate alignment with the printed patterns of film reverse side, after thermoprint, picture and text are exposed to film surface and easily abrade.
Summary of the invention
The present invention aims to provide two-sided figuratum alumite thermoprinting foil, all identical or different color can be shown by thermoprint transparent material tow sides, can be applicable to the thermoprint of composite plastic film printing connecting line, line thermoprint picture and text while of when back face printing, accurate chromatography can be realized, after product compound, printed layers and thermoprint layer are all at film inner surface, and reflecting feel is strong, can not abrade by external force affects.
The invention provides two-sided color alumite thermoprinting foil, comprise biaxially oriented polyester film, release layer, chromatograph one, aluminium coated, chromatograph two, glue-line, it is characterized in that: described biaxially oriented polyester film surface uses anilox roll coating release layer, described release layer is coated with chromatograph one, through vacuum aluminum-plating machine vacuum evaporation aluminium coated on described chromatograph one, described aluminium coated is coated with chromatograph two, described chromatograph two upper surface coated glue layer.
Described two-sided color alumite thermoprinting foil production method is:
One, 210 order anilox roll coatings are used to take water as the wax emulsion of dispersion solvent at biaxially oriented polyester film surface, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-145 DEG C-145 DEG C-130 DEG C, and five warm area inner blower frequency conversions are respectively 40-45-50-50-50Hz.
Two, release layer surface coating chromatograph one coating after step one processes, chromatograph one is coated with the water-based chromatograph coating that the coating of use 120-200 order anilox roll take water as solvent, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-150 DEG C-150 DEG C-130 DEG C, and five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Three, chromatograph one surface after step 2 process through the aluminium coated of vacuum aluminum-plating machine vacuum evaporation 200-500 dust thickness to obtain gold lustre effect.
Four, aluminium coated surface coating chromatograph two coating after step 3 process, chromatograph two is coated with the water-based chromatograph coating that the coating of use 120-200 order anilox roll take water as solvent, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-150 DEG C-150 DEG C-130 DEG C, and five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Five, the surperficial coated glue layer coating of the chromatograph two after step 4 process, the coating of glue-line coating use 120-200 order anilox roll take water as the water-base cement coating of solvent, five warm area bake out temperatures 80 DEG C-120 DEG C-145 DEG C-145-130 DEG C, five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Preferably, the releasing layer coating described in step one comprises: wax emulsion 1.7%-7.1%; Water 91.9%-98%; Defoamer 0.5%; Moistening flatting agent 0.5%.
Preferably, the water-based chromatograph coating described in step 2 comprises: water-based chromatograph ready coating (wherein: waterborne polyurethane resin: water-borne acrylic resin=3:1) 45%-50%; Water 45%-50%; The pre-dispersed inclusion enclave of nanoscale organic pigment (the micro-high-tensile strength series of BASF Ciba) 0%-10%; Defoamer: 0.5%; Moistening flatting agent: 0.5%.
Preferably, the water-based chromatograph coating described in step 4 comprises: water-based chromatograph ready coating (wherein: waterborne polyurethane resin: water-borne acrylic resin=4:1) 45%-50%; Water 45%-50%; The pre-dispersed inclusion enclave of nanoscale organic pigment (the micro-high-tensile strength series of BASF Ciba) 0%-10%; Defoamer----0.5%; Moistening flatting agent: 0.5%.
Preferably, the water-base cement coating described in step 5 comprises: water-based glue-line ready coating (main component is aqueous polyurethane thermoplastic resin fat liquor) 45%-50%; Water 45%-50%; Aerosil powder 1%-3%; Defoamer 0.5%; Moistening flatting agent 0.5%.
Beneficial effect of the present invention is: the thermoprint of two-sided color alumite thermoprinting foil is after transparent material, all identical or different color can be shown by thermoprint material tow sides, when being applied to composite plastic film printing can when back face printing simultaneously line thermoprint picture and text, and hot stamping pattern and the accurate chromatography of ink printing picture and text can be realized, after product compound, printed layers and thermoprint layer are all at film inner surface of undertaking the printing of, reflecting feel is strong, can not abrade by external force affects.
Accompanying drawing explanation
Fig. 1 is the structural representation of two-sided color alumite thermoprinting foil.
Wherein: 1. biaxially oriented polyester film; 2. release layer; 3. chromatograph one; 4. aluminium coated; 5. chromatograph two; 6. glue-line.
Detailed description of the invention
Below in conjunction with accompanying drawing, the present invention will be further described.
Embodiment 1
The two-sided color alumite thermoprinting foil of the present invention's design, comprises biaxially oriented polyester film 1, release layer 2, chromatograph 1, aluminium coated 4, chromatograph 25, glue-line 6; Prepare described two-sided color alumite thermoprinting foil according to the following steps:
(1) 210 order anilox roll coatings are used to take water as the wax emulsion of dispersion solvent at biaxially oriented polyester film surface, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-145 DEG C-145 DEG C-130 DEG C, and five warm area inner blower frequency conversions are respectively 40-45-50-50-50Hz.
Described releasing layer coating comprises: wax emulsion 1.7%; Water 97.3%; Defoamer 0.5%; Moistening flatting agent 0.5%.
(2) release layer surface coating chromatograph one coating after step (1) process, chromatograph one is coated with the water-based chromatograph coating that the coating of use 120 order anilox roll take water as solvent, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-150 DEG C-150 DEG C-130 DEG C, and five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Described water-based chromatograph coating comprises: water-based chromatograph ready coating (wherein: waterborne polyurethane resin: water-borne acrylic resin=3:1) 45%; Water 45%; The pre-dispersed inclusion enclave of nanoscale organic pigment (the micro-high-tensile strength series of BASF Ciba) 9%; Defoamer: 0.5%; Moistening flatting agent: 0.5%.
(3) chromatograph one surface after step (2) process through the aluminium coated of vacuum aluminum-plating machine vacuum evaporation 200 dust thickness to obtain gold lustre effect.
(4) aluminium coated surface coating chromatograph two coating after step (3) process, chromatograph two is coated with the water-based chromatograph coating that the coating of use 120 order anilox roll take water as solvent, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-150 DEG C-150 DEG C-130 DEG C, and five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Described water-based chromatograph coating comprises: water-based chromatograph ready coating (wherein: waterborne polyurethane resin: water-borne acrylic resin=4:1) 45%; Water 45%; The pre-dispersed inclusion enclave of nanoscale organic pigment (the micro-high-tensile strength series of BASF Ciba) 9%; Defoamer----0.5%; Moistening flatting agent: 0.5%.
(5) the surperficial coated glue layer coating of chromatograph two after step (4) process, the coating of glue-line coating use 120 order anilox roll take water as the water-base cement coating of solvent, five warm area bake out temperatures 80 DEG C-120 DEG C-145 DEG C-145-130 DEG C, five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Described water-base cement coating comprises: water-based glue-line ready coating (main component is aqueous polyurethane thermoplastic resin fat liquor) 48%; Water 48%; Aerosil powder 3%; Defoamer 0.5%; Moistening flatting agent 0.5%.
Embodiment 2
The two-sided color alumite thermoprinting foil of the present invention's design, comprises biaxially oriented polyester film 1, release layer 2, chromatograph 1, aluminium coated 4, chromatograph 25, glue-line 6; Prepare described two-sided color alumite thermoprinting foil according to the following steps:
(1) 210 order anilox roll coatings are used to take water as the wax emulsion of dispersion solvent at biaxially oriented polyester film surface, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-145 DEG C-145 DEG C-130 DEG C, and five warm area inner blower frequency conversions are respectively 40-45-50-50-50Hz.
Described releasing layer coating comprises: wax emulsion 7.1%; Water 91.9%; Defoamer 0.5%; Moistening flatting agent 0.5%.
(2) release layer surface coating chromatograph one coating after step (1) process, chromatograph one is coated with the water-based chromatograph coating that the coating of use 200 order anilox roll take water as solvent, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-150 DEG C-150 DEG C-130 DEG C, and five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Described water-based chromatograph coating comprises: water-based chromatograph ready coating (wherein: waterborne polyurethane resin: water-borne acrylic resin=3:1) 50%; Water 50%; The pre-dispersed inclusion enclave of nanoscale organic pigment (the micro-high-tensile strength series of BASF Ciba) 0%; Defoamer: 0.5%; Moistening flatting agent: 0.5%.
(3) chromatograph one surface after step (2) process through the aluminium coated of vacuum aluminum-plating machine vacuum evaporation 500 dust thickness to obtain gold lustre effect.
(4) aluminium coated surface coating chromatograph two coating after step (3) process, chromatograph two is coated with the water-based chromatograph coating that the coating of use 200 order anilox roll take water as solvent, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-150 DEG C-150 DEG C-130 DEG C, and five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Described water-based chromatograph coating comprises: water-based chromatograph ready coating (wherein: waterborne polyurethane resin: water-borne acrylic resin=4:1) 50%; Water 50%; The pre-dispersed inclusion enclave of nanoscale organic pigment (the micro-high-tensile strength series of BASF Ciba) 0%; Defoamer----0.5%; Moistening flatting agent: 0.5%.
(5) the surperficial coated glue layer coating of chromatograph two after step (4) process, the coating of glue-line coating use 200 order anilox roll take water as the water-base cement coating of solvent, five warm area bake out temperatures 80 DEG C-120 DEG C-145 DEG C-145-130 DEG C, five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
Described water-base cement coating comprises: water-based glue-line ready coating (main component is aqueous polyurethane thermoplastic resin fat liquor) 48%; Water 50%; Aerosil powder 1%; Defoamer 0.5%; Moistening flatting agent 0.5%.
Claims (6)
1. two-sided color alumite thermoprinting foil, comprise biaxially oriented polyester film, release layer, chromatograph one, aluminium coated, chromatograph two, glue-line, it is characterized in that: described biaxially oriented polyester film surface uses anilox roll coating release layer, described release layer is coated with chromatograph one, through vacuum aluminum-plating machine vacuum evaporation aluminium coated on described chromatograph one, described aluminium coated is coated with chromatograph two, described chromatograph two upper surface coated glue layer.
2. a production method for two-sided color alumite thermoprinting foil according to claim 1, is characterized in that:
(1), 210 order anilox roll coatings are used to take water as the wax emulsion of dispersion solvent at biaxially oriented polyester film surface, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-145 DEG C-145 DEG C-130 DEG C, and five warm area inner blower frequency conversions are respectively 40-45-50-50-50Hz;
(2) release layer surface coating chromatograph one coating, after step one processes, chromatograph one is coated with the water-based chromatograph coating that the coating of use 120-200 order anilox roll take water as solvent, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-150 DEG C-150 DEG C-130 DEG C, and five district's fan frequency conversions are respectively 40-45-50-50-50Hz;
(3) chromatograph one surface, after step 2 process through the aluminium coated of vacuum aluminum-plating machine vacuum evaporation 200-500 dust thickness to obtain gold lustre effect;
(4) aluminium coated surface coating chromatograph two coating, after step 3 process, chromatograph two is coated with the water-based chromatograph coating that the coating of use 120-200 order anilox roll take water as solvent, five warm areas are adopted to dry, five warm area bake out temperatures are respectively 80 DEG C-120 DEG C-150 DEG C-150 DEG C-130 DEG C, and five district's fan frequency conversions are respectively 40-45-50-50-50Hz;
(5) the surperficial coated glue layer coating of the chromatograph two, after step 4 process, the coating of glue-line coating use 120-200 order anilox roll take water as the water-base cement coating of solvent, five warm area bake out temperatures 80 DEG C-120 DEG C-145 DEG C-145-130 DEG C, five district's fan frequency conversions are respectively 40-45-50-50-50Hz.
3. the production method of two-sided color alumite thermoprinting foil according to claim 2, is characterized in that: the releasing layer coating in described step one comprises: wax emulsion 1.7%-7.1%; Water 91.9%-98%; Defoamer 0.5%; Moistening flatting agent 0.5%.
4. the production method of two-sided color alumite thermoprinting foil according to claim 2, is characterized in that: the water-based chromatograph coating in described step 2 comprises: water-based chromatograph ready coating (wherein: waterborne polyurethane resin: water-borne acrylic resin=3:1) 45%-50%; Water 45%-50%; The pre-dispersed inclusion enclave of nanoscale organic pigment (the micro-high-tensile strength series of BASF Ciba) 0%-10%; Defoamer: 0.5%; Moistening flatting agent: 0.5%.
5. the production method of two-sided color alumite thermoprinting foil according to claim 2, is characterized in that: the water-based chromatograph coating in described step 4 comprises: water-based chromatograph ready coating (wherein: waterborne polyurethane resin: water-borne acrylic resin=4:1) 45%-50%; Water 45%-50%; The pre-dispersed inclusion enclave of nanoscale organic pigment (the micro-high-tensile strength series of BASF Ciba) 0%-10%; Defoamer----0.5%; Moistening flatting agent: 0.5%.
6. the production method of two-sided color alumite thermoprinting foil according to claim 2, is characterized in that: the water-base cement coating in described step 5 comprises: water-based glue-line ready coating (main component is aqueous polyurethane thermoplastic resin fat liquor) 45%-50%; Water 45%-50%; Aerosil powder 1%-3%; Defoamer 0.5%; Moistening flatting agent 0.5%.