CN105419397A - Calcium carbonate activating agent containing dipropylene glycol monobutyl ether - Google Patents
Calcium carbonate activating agent containing dipropylene glycol monobutyl ether Download PDFInfo
- Publication number
- CN105419397A CN105419397A CN201510756065.3A CN201510756065A CN105419397A CN 105419397 A CN105419397 A CN 105419397A CN 201510756065 A CN201510756065 A CN 201510756065A CN 105419397 A CN105419397 A CN 105419397A
- Authority
- CN
- China
- Prior art keywords
- parts
- dipropylene glycol
- calcium carbonate
- monobutyl ether
- glycol monobutyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a calcium carbonate activating agent containing dipropylene glycol monobutyl ether. The calcium carbonate activating agent containing the dipropylene glycol monobutyl ether is characterized by comprising, by weight, 5-8 parts of dipropylene glycol monobutyl ether, 3-8 parts of pentaerythritol rosin resin, 25-30 parts of coconut diethanolamide, 5-8 parts of sodium carbonate, 3-5 parts of sodium acrylate-4-vinyl pyridine copolymer, 5-6 parts of glycerol triacetate, 10-12 parts of di-n-octyltin oxide, 3-5 parts of polyvinyl acetal resin, 25-30 parts of gamma-glycidoxypropyl trimethoxysilane, 3-5 parts of dodecyl dimethyl benzyl ammonium bromide, 20-30 parts of ethanol and 550-600 parts of water. The calcium carbonate activating agent containing the dipropylene glycol monobutyl ether has the advantages of scientific and reasonable design, simple technology, safety, reliability, easiness in control, convenience in operation, suitability for large-scale production, low production cost and the like.
Description
Technical field
The invention belongs to a kind of auxiliary agent producing non-metallic powder.
Background technology
At present, calcium carbonate is widely used in papermaking, plastics, plastics film, chemical fibre, rubber, tackiness agent, sealing agent, daily-use chemical industry, makeup, building materials, coating, paint, ink, putty, sealing wax, putty, carpet veneer is packed, medicine, food is (as chewing gum, chocolate), in feed, its effect has: increase small product size, reduce costs, improve processing characteristics (as adjusting viscosity, rheological property, curability), improve dimensional stability, reinforcement or half reinforcement, improve printing performance, improve physicals (as thermotolerance, extinction, wear resistance, flame retardant resistance, whiteness, glossiness) etc., for obtaining more superior performance, auxiliary agent is all adopted to carry out activation treatment.
Summary of the invention
The object of the invention is to; A kind of Dipropylene glycol mono-n-butyl Ether calcium carbonate activator and preparation method thereof is proposed.
Dipropylene glycol mono-n-butyl Ether calcium carbonate activator calcium carbonate activator of the present invention, it is characterized in that: by weight, its formula is by Dipropylene glycol mono-n-butyl Ether 5-8 part, rosin pentaerythritol ester europium resin 3-8 part, cocoanut fatty acid diethanolamide 25-30 part, sodium carbonate 5-8 part, sodium acrylate-4-vinylpridine multipolymer 3-5 part, Vanay 5-6 part, di-n-octyltin oxide 10--12 part, polyvinyl acetal resin 3-5 part, γ-glycidyl ether oxygen propyl trimethoxy silicane 25-30 part, dodecyl dimethyl benzyl ammonium bromide 3-5 part, ethanol 20-30 part, water 550-600 part forms.
The preparation method of Dipropylene glycol mono-n-butyl Ether calcium carbonate activator calcium carbonate activator of the present invention, it is characterized in that: by weight, its formula is by Dipropylene glycol mono-n-butyl Ether 5-8 part, rosin pentaerythritol ester europium resin 3-8 part, cocoanut fatty acid diethanolamide 25-30 part, sodium carbonate 5-8 part, sodium acrylate-4-vinylpridine multipolymer 3-5 part, Vanay 5-6 part, di-n-octyltin oxide 10--12 part, polyvinyl acetal resin 3-5 part, γ-glycidyl ether oxygen propyl trimethoxy silicane 25-30 part, dodecyl dimethyl benzyl ammonium bromide 3-5 part, ethanol 20-30 part, water 550-600 part forms, first with ethanol by rosin europium resin dissolves, after adding water 550-600 part, add whole raw material and mix, at 85 ~ 95 DEG C, stir 20-30 minute, obtain product.
The present invention compared with prior art its beneficial effect is: have design science reasonable, and technique is simple, safe reliability, is easy to control, easy to operate, is applicable to scale operation, the advantages such as production cost is low.
Embodiment
Below in conjunction with embodiment, the invention will be further described, but embodiments of the present invention are not limited thereto.
All raw materials of the present invention can buy acquisition.
Embodiment 1
The preparation method of Dipropylene glycol mono-n-butyl Ether calcium carbonate activator calcium carbonate activator of the present invention, it is characterized in that: by weight, its formula is by Dipropylene glycol mono-n-butyl Ether 5-8 part, rosin pentaerythritol ester europium resin 3-8 part, cocoanut fatty acid diethanolamide 25-30 part, sodium carbonate 5-8 part, sodium acrylate-4-vinylpridine multipolymer 3-5 part, Vanay 5-6 part, di-n-octyltin oxide 10--12 part, polyvinyl acetal resin 3-5 part, γ-glycidyl ether oxygen propyl trimethoxy silicane 25-30 part, dodecyl dimethyl benzyl ammonium bromide 3-5 part, ethanol 20-30 part, water 550-600 part forms, first with ethanol by rosin europium resin dissolves, after adding water 550-600 part, add whole raw material and mix, at 85 ~ 95 DEG C, stir 20-30 minute, obtain product.
Embodiment 2
The preparation method of Dipropylene glycol mono-n-butyl Ether calcium carbonate activator calcium carbonate activator of the present invention, it is characterized in that: by weight, its formula is by Dipropylene glycol mono-n-butyl Ether 5-8 part, rosin pentaerythritol ester europium resin 3 parts, cocoanut fatty acid diethanolamide 25 parts, 5 parts, sodium carbonate, sodium acrylate-4-vinylpridine multipolymer 3 parts, Vanay 5 parts, dioctyl tin 10 parts, polyvinyl acetal resin 3 parts, glycidyl ether oxygen propyl trimethoxy silicane 25 parts, ethanol 20-30 part, water 550-600 part forms; First with ethanol by rosin europium resin dissolves, after adding water 550-600 part, add whole raw material and mix, at 85 ~ 95 DEG C, stir 20-30 minute, obtain product.
Embodiment 3
The preparation method of Dipropylene glycol mono-n-butyl Ether calcium carbonate activator calcium carbonate activator of the present invention, it is characterized in that: by weight, its formula is by Dipropylene glycol mono-n-butyl Ether 5-8 part, rosin pentaerythritol ester europium resin 8 parts, cocoanut fatty acid diethanolamide 30 parts, 8 parts, sodium carbonate, sodium acrylate-4-vinylpridine multipolymer 5 parts, Vanay 6 parts, dioctyl tin 12 parts, polyvinyl acetal resin 5 parts, glycidyl ether oxygen propyl trimethoxy silicane 30 parts, dodecyl dimethyl benzyl ammonium bromide 3-5 part, ethanol 20-30 part, water 550-600 part forms, first with ethanol by rosin europium resin dissolves, after adding water 550-600 part, add whole raw material and mix, at 85 ~ 95 DEG C, stir 20-30 minute, obtain product.
Embodiment 4
The preparation method of Dipropylene glycol mono-n-butyl Ether calcium carbonate activator calcium carbonate activator of the present invention, it is characterized in that: by weight, its formula is by Dipropylene glycol mono-n-butyl Ether 5-8 part, rosin pentaerythritol ester europium resin 3 parts, cocoanut fatty acid diethanolamide 30 parts, 5 parts, sodium carbonate, sodium acrylate-4-vinylpridine multipolymer 5 parts, Vanay 5 parts, dioctyl tin 12 parts, polyvinyl acetal resin 3 parts, glycidyl ether oxygen propyl trimethoxy silicane 25 parts, dodecyl dimethyl benzyl ammonium bromide 3-5 part, ethanol 20-30 part, water 550-600 part forms, first with ethanol by rosin europium resin dissolves, after adding water 550-600 part, add whole raw material and mix, at 85 ~ 95 DEG C, stir 20-30 minute, obtain product.
Product of the present invention, uses through production firm, and produce modified superfine water-ground limestone product, reaction effect is fine.
Part material illustrates:
Described rosin pentaerythritol ester europium resin, the method that can be preferably ZL201410078259.8 by the Chinese patent patent No. obtains.
γ-glycidyl ether oxygen propyl trimethoxy silicane
No. Cas: 2530-83-8
Molecular formula: C9H20O5Si molecular weight: 236.34
Another name: 3-(2,3-epoxy third oxygen) propyl trimethoxy silicane, 3-glycydoxy Trimethoxy silane
γ-glycidyl ether oxygen propyl trimethoxy silicane.
Claims (2)
1. a Dipropylene glycol mono-n-butyl Ether calcium carbonate activator calcium carbonate activator, it is characterized in that: by weight, its formula is by Dipropylene glycol mono-n-butyl Ether 5-8 part, rosin pentaerythritol ester europium resin 3-8 part, cocoanut fatty acid diethanolamide 25-30 part, sodium carbonate 5-8 part, sodium acrylate-4-vinylpridine multipolymer 3-5 part, Vanay 5-6 part, di-n-octyltin oxide 10--12 part, polyvinyl acetal resin 3-5 part, γ-glycidyl ether oxygen propyl trimethoxy silicane 25-30 part, dodecyl dimethyl benzyl ammonium bromide 3-5 part, ethanol 20-30 part, water 550-600 part forms.
2. the preparation method of a Dipropylene glycol mono-n-butyl Ether calcium carbonate activator calcium carbonate activator, it is characterized in that: by weight, its formula is by Dipropylene glycol mono-n-butyl Ether 5-8 part, rosin pentaerythritol ester europium resin 3-8 part, cocoanut fatty acid diethanolamide 25-30 part, sodium carbonate 5-8 part, sodium acrylate-4-vinylpridine multipolymer 3-5 part, Vanay 5-6 part, di-n-octyltin oxide 10--12 part, polyvinyl acetal resin 3-5 part, γ-glycidyl ether oxygen propyl trimethoxy silicane 25-30 part, dodecyl dimethyl benzyl ammonium bromide 3-5 part, ethanol 20-30 part, water 550-600 part forms, first with ethanol by rosin europium resin dissolves, after adding water 550-600 part, add whole raw material and mix, at 85 ~ 95 DEG C, stir 20-30 minute, obtain product.