CN105401082A - 一种铸铁冷作模具材料的配方 - Google Patents
一种铸铁冷作模具材料的配方 Download PDFInfo
- Publication number
- CN105401082A CN105401082A CN201510759826.0A CN201510759826A CN105401082A CN 105401082 A CN105401082 A CN 105401082A CN 201510759826 A CN201510759826 A CN 201510759826A CN 105401082 A CN105401082 A CN 105401082A
- Authority
- CN
- China
- Prior art keywords
- parts
- formula
- cast iron
- copper
- mold material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铸铁冷作模具材料的配方，锌4-6份；镍最大8份；铜从大于3到15份；钙、硅和银中的每一种最大3份；镓0.2-0.5份；锌4-6份；铁70-80份；锶0.01-0.05份。本发明的有益效果是：该冷作模具材料由于铁、铜和镍为主要材料，同时锌、钙、硅和银的加入，模具钢材料加工的模具来说，提高了耐冲击性、断裂韧性和抗破损性，使用寿命延长，性能优越。
Description
技术领域
本发明涉及一种模具材料，尤其涉及一种铸铁冷作模具材料的配方。
背景技术
冷作模具钢侧重硬度、耐磨性。含碳量高，合金元素以增加淬透性，提高耐磨性为主。冷作模具钢包括制造冲裁用的模具（落料冲孔模、修边模、冲头、剪刀）、冷镦模和冷挤压模、压弯模及拉丝模等。目前，国内大中城市高层建筑和各种现浇钢筋混凝土结构工程愈来愈多，对施工质量的要求不断提高，因此建筑钢模板的使用愈来愈广泛，模板工程约占钢筋混凝土总造价的25％、劳动量的35％、工期的50％～60％，模板质量的好坏、施工的方便性，对于加快施工进度、保证施工质量和降低工程成本，起到了关键作用。现有的冷作模具钢在使用过程中由于耐冲击性、断裂韧性和抗破损性差，不能满足需求。
因此，为解决上述问题，特提供一种新的技术方案。
发明内容
本发明提供一种铸铁冷作模具材料的配方。
本发明采用的技术方案是：
一种铸铁冷作模具材料的配方，该模具钢材料的成分及重量份为：
锌4-6份；
镍最大8份；
铜从大于3到15份；
钙、硅和银中的每一种最大3份；
镓0.2-0.5份；
铁70-80份；
锶0.01-0.05份。
进一步地，含有至少3.58份的铜。
进一步地，含有至多13.5份的铜。
进一步地，含有至少1份的钙。
进一步地，含有至少0.5份的银。
进一步地，含有至少0.02份的硅。
进一步地，含有至少1份的镍。
本发明的有益效果是：该冷作模具材料由于铁、铜和镍为主要材料，同时锌、钙、硅和银的加入，模具钢材料加工的模具来说，提高了耐冲击性、断裂韧性和抗破损性，使用寿命延长，性能优越。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明的保护范围的限定。
实施例1
一种铸铁冷作模具材料的配方，该模具钢材料的成分及重量份为：
锌4份；
镍1份；
铜3份；
钙1份；
硅0.02份；
银0.5份；
镓0.2份；
铁70份；
锶0.01份。
实施例2
一种铸铁冷作模具材料的配方，该模具钢材料的成分及重量份为：
锌5份；
镍5份；
铜9份；
钙2份；
硅0.2份；
银2.2份；
镓0.35份；
铁75份；
锶0.03份。
实施例3
一种铸铁冷作模具材料的配方，该模具钢材料的成分及重量份为：
锌6份；
镍8份；
铜15份；
钙3份；
硅3份；
银3份；
镓0.5份；
铁80份；
锶0.05份。
本发明的有益效果是：该冷作模具材料由于铁、铜和镍为主要材料，同时锌、钙、硅和银的加入，模具钢材料加工的模具来说，提高了耐冲击性、断裂韧性和抗破损性，使用寿命延长，性能优越。
以上所述，仅是本发明的较佳实施例而已，并非是对本发明作任何其他形式的限制，而依据本发明的技术实质所作的任何修改或等同变化，仍属于本发明所要求保护的范围。
Claims (7)
1.一种铸铁冷作模具材料的配方，其特征在于：该模具钢材料的成分及重量份为：
锌4-6份；
镍最大8份；
铜从大于3到15份；
钙、硅和银中的每一种最大3份；
镓0.2-0.5份；
铁70-80份；
锶0.01-0.05份。
2.根据权利要求1所述的一种铸铁冷作模具材料的配方，其特征在于：含有至少3.58份的铜。
3.根据权利要求1所述的一种铸铁冷作模具材料的配方，其特征在于：含有至多13.5份的铜。
4.根据权利要求1所述的一种铸铁冷作模具材料的配方，其特征在于：含有至少1份的钙。
5.根据权利要求1所述的一种铸铁冷作模具材料的配方，其特征在于：含有至少0.5份的银。
6.根据权利要求1所述的一种铸铁冷作模具材料的配方，其特征在于：含有至少0.02份的硅。
7.根据权利要求1所述的一种铸铁冷作模具材料的配方，其特征在于：含有至少1份的镍。