CN104674124A - 一种冷冲模用模具钢 - Google Patents

一种冷冲模用模具钢 Download PDF

Info

Publication number
CN104674124A
CN104674124A CN201410823479.9A CN201410823479A CN104674124A CN 104674124 A CN104674124 A CN 104674124A CN 201410823479 A CN201410823479 A CN 201410823479A CN 104674124 A CN104674124 A CN 104674124A
Authority
CN
China
Prior art keywords
parts
die
cold
die steel
steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410823479.9A
Other languages
English (en)
Inventor
高明
刘朋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kunshan Di Saisien Die Design Co Ltd
Original Assignee
Kunshan Di Saisien Die Design Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Di Saisien Die Design Co Ltd filed Critical Kunshan Di Saisien Die Design Co Ltd
Priority to CN201410823479.9A priority Critical patent/CN104674124A/zh
Publication of CN104674124A publication Critical patent/CN104674124A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种冷冲模用模具钢，包括以下重量份的组分：铁80-85份；碳0.1-0.5份；硅1-6份；钼4-5份；磷2-4份；钛0.5-0.8份；铬2-5份；铜3-5份。本发明的有益效果是：添加的铜、锶、钌和铬，能增强模具钢的韧性，从而能延长模具的使用寿命，其它金属元素的添加，使模具的耐磨性能也提高，抗压和冲击力强，满足企业的需求。

Description

一种冷冲模用模具钢
技术领域
本发明涉及一种模具钢，尤其涉及一种冷冲模用模具钢。
背景技术
冷作模具钢在工作时，由于被加工材料的变形抗力比较大，模具的工作部分承受很大的冷作模具钢大的压力、弯曲力、冲击力及摩擦力。因此，冷作模具的正常报废原因一般是磨损。也有因断裂、崩力和变形超差而提前失效的。
冷作模具钢与刃具钢相比有许多共同点。要求模具有高的硬度和耐磨性、高的抗弯强度和足够的韧性，以保证冲压过程的顺利进行、其不同之处在于模具形状及加工艺复杂。而且摩擦面积大。磨损可能性大，所以修磨起来困难。
因此，为解决上述问题，特提供一种新的技术方案。
发明内容
本发明提供一种冷冲模用模具钢。
本发明采用的技术方案是：
一种冷冲模用模具钢，包括以下重量份的组分：
铁    80-85份；
碳    0.1-0.5份；
硅    1-6份；
钼    4-5份；
磷    2-4份；
钛    0.5-0.8份；
铬    2-5份；
铜    3-5份。
进一步的，还包括0.2-0.5重量份的锶。
进一步的，还包括0.12-0.25重量份的钌。
本发明的有益效果是：添加的铜、锶、钌和铬，能增强模具钢的韧性，从而能延长模具的使用寿命，其它金属元素的添加，使模具的耐磨性能也提高，抗压和冲击力强，满足企业的需求。
具体实施方式
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明的保护范围的限定。
实施例1
一种冷冲模用模具钢，包括以下重量份的组分：
铁    80-85份；
碳    0.1-0.5份；
硅    1-6份；
钼    4-5份；
磷    2-4份；
钛    0.5-0.8份；
铬    2-5份；
铜    3-5份。
锶    0.2-0.5份；
钌    0.12-0.25份。
实施例2
一种冷冲模用模具钢，包括以下重量份的组分：
铁    80-85份；
碳    0.1-0.5份；
硅    1-6份；
钼    4-5份；
磷    2-4份；
钛    0.5-0.8份；
铬    2-5份；
铜    3-5份。
锶    0.2-0.5份；
钌    0.12-0.25份。
实施例3
一种冷冲模用模具钢，包括以下重量份的组分：
铁    80-85份；
碳    0.1-0.5份；
硅    1-6份；
钼    4-5份；
磷    2-4份；
钛    0.5-0.8份；
铬    2-5份；
铜    3-5份。
锶    0.2-0.5份；
钌    0.12-0.25份。
本发明的有益效果是：添加的铜、锶、钌和铬，能增强模具钢的韧性，从而能延长模具的使用寿命，其它金属元素的添加，使模具的耐磨性能也提高，抗压和冲击力强，满足企业的需求。
以上所述，仅是本发明的较佳实施例而已，并非是对本发明作任何其他形式的限制，而依据本发明的技术实质所作的任何修改或等同变化，仍属于本发明所要求保护的范围。

Claims (3)

1.一种冷冲模用模具钢，其特征在于：包括以下重量份的组分：
铁    80-85份；
碳    0.1-0.5份；
硅    1-6份；
钼    4-5份；
磷    2-4份；
钛    0.5-0.8份；
铬    2-5份；
铜    3-5份。
2.根据权利要求1所述的一种冷冲模用模具钢，其特征在于：还包括0.2-0.5重量份的锶。
3.根据权利要求1所述的一种冷冲模用模具钢，其特征在于：还包括0.12-0.25重量份的钌。
CN201410823479.9A 2014-12-26 2014-12-26 一种冷冲模用模具钢 Pending CN104674124A (zh)