CN105398122A - SBS modified asphalt waterproof coiled material with anti-ageing layer - Google Patents

SBS modified asphalt waterproof coiled material with anti-ageing layer Download PDF

Info

Publication number
CN105398122A
CN105398122A CN201510947675.1A CN201510947675A CN105398122A CN 105398122 A CN105398122 A CN 105398122A CN 201510947675 A CN201510947675 A CN 201510947675A CN 105398122 A CN105398122 A CN 105398122A
Authority
CN
China
Prior art keywords
layer
coiled material
woven fabrics
modified asphalt
ageing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510947675.1A
Other languages
Chinese (zh)
Inventor
杨磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHUCHENG INFORMATION TECHNOLOGY Co Ltd
Original Assignee
ANHUI ZHUCHENG INFORMATION TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHUCHENG INFORMATION TECHNOLOGY Co Ltd filed Critical ANHUI ZHUCHENG INFORMATION TECHNOLOGY Co Ltd
Priority to CN201510947675.1A priority Critical patent/CN105398122A/en
Publication of CN105398122A publication Critical patent/CN105398122A/en
Pending legal-status Critical Current

Abstract

The invention provides an SBS modified asphalt waterproof coiled material with an anti-ageing layer. The waterproof coiled material possesses a layered structure, and successively comprises a TPO anti-ageing layer, an upper non-woven fabrics enhancement layer, an SBS waterproof layer and a lower non-woven fabrics enhancement layer from top to bottom, the upper non-woven fabrics enhancement layer and the lower non-woven fabrics enhancement layer are both prepared from mutually-staggered-laminated polyester fiber, glass fiber and carbon fiber, and the weight fractions of polyester fiber, glass fiber and carbon fiber are 30%-40%, 30%-40% and 20%-40%. The TPO anti-ageing layer is additionally added, because TPO resin is a blended product of EPDM and PP, the coiled material is extremely excellent in ozone ageing resistance and waterproofness. By taking the TPO anti-ageing layer as the surface layer of SBS modified asphalt, an anti-ageing layer does not need constructing on the coiled material applied to roofing engineering, the roof weight is mitigated, and engineering cost is saved.

Description

With the SBS modified asphalt waterproof coiled material of anti-aging layer
Technical field
The invention belongs to waterproof roll technical field, especially relate to a kind of SBS modified asphalt waterproof coiled material with anti-aging layer.
Background technology
SBS modified asphalt waterproof coiled material, this coiled material has good resistance to elevated temperatures, can use, have higher elasticity and fatigue durability in the temperature range of-25 to+100 DEG C, and up to 1500% percentage elongation and stronger puncture-resistant ability, tear-resistant ability.Be suitable for cold district, and the waterproofing work of distortion and the larger industry of vibration and civil buildings.
Existing SBS modified asphalt waterproof coiled material is aging in order to prevent, and must cover 20mm solid cement mortar anti-aging layer, adding the weight of roofing when being applied to roofworks, and engineering cost is higher simultaneously.
Summary of the invention
The object of the invention is to the above problem overcoming prior art existence, a kind of SBS modified asphalt waterproof coiled material with anti-aging layer is provided.
For realizing above-mentioned technical purpose, reach above-mentioned technique effect, the present invention is achieved through the following technical solutions:
A kind of SBS modified asphalt waterproof coiled material with anti-aging layer, this waterproof roll is layer structure, comprise TPO anti-aging layer, upper non-woven fabrics enhancement layer, SBS watertight composition and lower non-woven fabrics enhancement layer from top to bottom successively, described upper non-woven fabrics enhancement layer and lower non-woven fabrics enhancement layer are formed by the interlaced compacting of polyester fiber, glass fibre and carbon fiber, and weight percent proportioning shared by wherein said polyester fiber, glass fibre and carbon fiber is 30% ~ 40%:30% ~ 40%:20% ~ 40%.
Further, the thickness of described TPO anti-aging layer is 0.8 ~ 1.2mm.
Further, the thickness of described SBS watertight composition is 0.5 ~ 0.7mm.
The invention has the beneficial effects as follows:
The present invention has set up TPO anti-aging layer, because TPO resin is by the blended product of EPDM/PP, therefore resistance to ozone aging and resistance to water splendid, using the top layer of TPO anti-aging layer as SBS modified pitch, this materials application it goes without doing when roofworks anti-aging layer, alleviate the weight of roofing, save engineering cost.
Accompanying drawing explanation
Accompanying drawing described herein is used to provide a further understanding of the present invention, and form a application's part, schematic description and description of the present invention, for explaining the present invention, does not form inappropriate limitation of the present invention.In the accompanying drawings:
Fig. 1 is structural representation of the present invention.
Detailed description of the invention
Below with reference to the accompanying drawings and in conjunction with the embodiments, describe the present invention in detail.
The SBS modified asphalt waterproof coiled material of the band anti-aging layer described in the present embodiment, as shown in Figure 1, this waterproof roll is layer structure, comprise TPO anti-aging layer 1, upper non-woven fabrics enhancement layer 2, SBS watertight composition 3 and lower non-woven fabrics enhancement layer 4 from top to bottom successively, described upper non-woven fabrics enhancement layer 2 and lower non-woven fabrics enhancement layer 4 are formed by the interlaced compacting of polyester fiber, glass fibre and carbon fiber, and weight percent proportioning shared by wherein said polyester fiber, glass fibre and carbon fiber is 30% ~ 40%:30% ~ 40%:20% ~ 40%.
Further, the thickness of described TPO anti-aging layer 1 is 0.8 ~ 1.2mm.
Further, the thickness of described SBS watertight composition 3 is 0.5 ~ 0.7mm.
The present invention has set up TPO anti-aging layer 1, because TPO resin is by the blended product of EPDM/PP, therefore resistance to ozone aging and resistance to water splendid, using the top layer of TPO anti-aging layer 1 as SBS modified pitch, this materials application it goes without doing when roofworks anti-aging layer, alleviate the weight of roofing, save engineering cost.

Claims (3)

1. the SBS modified asphalt waterproof coiled material with anti-aging layer, this waterproof roll is layer structure, it is characterized in that: comprise TPO anti-aging layer (1), upper non-woven fabrics enhancement layer (2), SBS watertight composition (3) and lower non-woven fabrics enhancement layer (4) from top to bottom successively, described upper non-woven fabrics enhancement layer (2) and lower non-woven fabrics enhancement layer (4) are formed by the interlaced compacting of polyester fiber, glass fibre and carbon fiber, and weight percent proportioning shared by wherein said polyester fiber, glass fibre and carbon fiber is 30% ~ 40%:30% ~ 40%:20% ~ 40%.
2. the SBS modified asphalt waterproof coiled material of band anti-aging layer according to claim 1, is characterized in that: the thickness of described TPO anti-aging layer (1) is 0.8 ~ 1.2mm.
3. the SBS modified asphalt waterproof coiled material of band anti-aging layer according to claim 1, is characterized in that: the thickness of described SBS watertight composition (3) is 0.5 ~ 0.7mm.
CN201510947675.1A 2015-12-17 2015-12-17 SBS modified asphalt waterproof coiled material with anti-ageing layer Pending CN105398122A (en)