CN105395306A - Sterilization type condom and preparation method thereof - Google Patents
Sterilization type condom and preparation method thereof Download PDFInfo
- Publication number
- CN105395306A CN105395306A CN201510899394.3A CN201510899394A CN105395306A CN 105395306 A CN105395306 A CN 105395306A CN 201510899394 A CN201510899394 A CN 201510899394A CN 105395306 A CN105395306 A CN 105395306A
- Authority
- CN
- China
- Prior art keywords
- condom
- type condom
- rubber latex
- silver
- disinfection type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a sterilization type condom and a preparation process thereof. The sterilization type condom is made of silver powder and natural rubber latex; the preparation method comprises the following steps: refining silver to be 1-2 nm to obtain nanoscale silver powder; mixing the nanoscale silver powder with the natural rubber latex containing a conventional material, stirring uniformly, curing for forming, and adding sulphur to the formed condom, thus obtaining the sterilization type condom. The silver in the sterilization type condom has the efficacies of disinfection and sterilization, can effectively kill viruses and pathogenic bacteria, and has wide sociality, practicability and safety, as well as good social benefit and economic benefit.
Description
Technical field
The present invention relates to condom, particularly relate to a kind of disinfection type condom and preparation method thereof.
Background technology
Since the condom appearance last 100 years that Du Leisi produces, be subject to global consumer always and welcome.Du Leisi condom to family planning, avoid unplanned pregnancy and use health, be reduced by sexual life infect function of diseases etc. make it have market greatly.
But this rubber condoms does not have sterilizing function, the condom up to now with sterilizing function does not occur in market yet.The disease infected by sexual life has a lot, as trichomoniasis, vaginitis etc.The most serious sexually transmitted disease is acquired immune deficiency syndrome (AIDS), is the pernicious infectious disease that can not be cured.General Purpose Rubber condom, has certain buffer action to infectious disease pathogenic bacterias such as HIV (human immunodeficiency virus), but condom is once poorly sealed, and this quasi-microorganism will be infected with human body, works the mischief to people.
Summary of the invention
For above-mentioned shortcomings and deficiencies, the invention provides a kind of disinfection type condom killing diversity transmitted virus pathogenic bacteria.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
A kind of disinfection type condom, its raw material packet is containing argentum powder and nature rubber latex, and described argentum powder is 1-2nm.
Above-mentioned disinfection type condom, raw material packet is containing argentum powder 0.5-1g, nature rubber latex 10Kg.
Another object of the present invention is to provide the preparation method of above-mentioned disinfection type condom.
A preparation method for disinfection type condom, step is as follows:
Step one: by silver micronization processes at 80-100 DEG C of temperature, refinement causes 1-2nm and obtains nano-scale silver powder;
Step 2: by the nano-scale silver powder of step one with add nature rubber latex and mix mutually, stir after fixing molding;
Step 3: the condom after step 2 molding is concentrated dehydration, then puts into and add sulfur device, the sulfur adding the 1%-3% of contoured contraceptive cover quality carries out sulfur adding treatment, obtains disinfection type condom.
In the present invention, disinfection type condom adopts the silver-colored advantage for biocide to be:
1, silver is active metal, with other composition chemical combination or when mixing, active large, even if become compound with other chemical combination, still has sterilizing function.
2, silver is when entering the design's formula, and be refined into the fine powder of 1-2 nanometer, these fine powders are evenly distributed in condom, high with bacterial virus contact probability, and it is thorough that this kind of nuisance is killed, the safety of available protecting end user.
3, nano-scale silver powder does not affect the elasticity comfortableness of condom.
With prior art ratio, beneficial effect of the present invention is:
1, disinfection type condom of the present invention, use safety, comfortable, adapt to male consumer.
2, the silver in disinfection type condom of the present invention, after contacting, can block its nutrient protein chain with microorganism in body cavity (bacterial virus), makes it dead and reaches sterilization, sterilizing object, having effective killing action to the disease virus pathogenic bacteria infected by sexual intercourse.In formula, silver is refined to 1-2 nanometer body footpath, and large with bacterial virus contact surface, probability is high, kills the successful of this kind of harmful live body, has realistic meaning to protection health.
3, disinfection type condom of the present invention has social, practicality, safety widely, and Social benefit and economic benefit is better.
Detailed description of the invention
Describe technical scheme of the present invention in detail below in conjunction with embodiment and experimental example, but protection domain is not by this restriction.
embodiment 1a kind of disinfection type condom, its raw material packet is containing argentum powder 1g, nature rubber latex 10Kg.
The preparation technology of above-mentioned disinfection type condom, step is as follows:
Step one: by silver micronization processes at 100 DEG C of temperature, refinement causes 1nm and obtains nano-scale silver powder;
Step 2: the argentum powder of step one and the nature rubber latex adding conventional material are mixed mutually, stir after fixing molding;
Step 3: the condom after step 2 molding is concentrated dehydration, then puts into and add sulfur device, add 100g sulfur and carry out sulfur adding treatment, obtain the condom that 10Kg argentiferous is 0.0001g, each heavy 1g, totally 10000.
The argentum powder that this example adds, than great, is stronger sterilizing ability product, is suitable for ill suspicion or has suffered from the consumer of genital organ disease, infectious disease.
embodiment 2a kind of disinfection type condom, its raw material packet is containing argentum powder 0.5g, nature rubber latex 10Kg.
The preparation technology of above-mentioned disinfection type condom, step is as follows:
Step one: by silver micronization processes at 80 DEG C of temperature, refinement causes 2nm and obtains nano-scale silver powder;
Step 2: the argentum powder of step one and the nature rubber latex adding conventional material are mixed mutually, stir after fixing molding;
Step 3: the condom after step 2 molding is concentrated dehydration, then puts into and add sulfur device, add 300g sulfur and carry out sulfur adding treatment, obtain the condom that 10Kg argentiferous is 0.00005g, each heavy 1g, totally 10000.
This example adds argentum powder 0.5g, is applicable to dailyly to use for preventive infectious disease.
Claims (3)
1. a disinfection type condom, is characterized in that: raw material packet is containing argentum powder and nature rubber latex, and described argentum powder is 1-2nm.
2. a kind of disinfection type condom according to claim 1, is characterized in that: raw material packet is containing argentum powder 0.5-1g, nature rubber latex 10Kg.
3. the preparation technology of a kind of disinfection type condom according to claim 1, is characterized in that: step is as follows:
Step one: by silver micronization processes at 80-100 DEG C of temperature, refinement causes 1-2nm and obtains nano-scale silver powder;
Step 2: the argentum powder of step one and the nature rubber latex adding conventional material are mixed mutually, stir after fixing molding;
Step 3: the condom after step 2 molding is concentrated dehydration, then puts into and add sulfur device, the sulfur adding the 1%-3% of contoured contraceptive cover quality carries out sulfur adding treatment, obtains disinfection type condom.