CN105349070A - Ceramic tile sticking anti-falling reinforcing agent - Google Patents
Ceramic tile sticking anti-falling reinforcing agent Download PDFInfo
- Publication number
- CN105349070A CN105349070A CN201510645394.0A CN201510645394A CN105349070A CN 105349070 A CN105349070 A CN 105349070A CN 201510645394 A CN201510645394 A CN 201510645394A CN 105349070 A CN105349070 A CN 105349070A
- Authority
- CN
- China
- Prior art keywords
- ceramic tile
- weight percent
- toughener
- tile
- peel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a ceramic tile sticking anti-falling reinforcing agent. The ceramic tile sticking anti-falling reinforcing agent comprises the following raw materials in percentage by weight: 50-60% of polyacrylic emulsion, 20-30% of styrene-butadiene emulsion, 5-10% of a binding agent, 3-6% of a coalescing agent, 0.5-3% of a defoaming agent and 0.5-3% of a preservative. The ceramic tile sticking anti-falling reinforcing agent disclosed by the invention can enable a ceramic tile to be agglomerated with cement mortar more firmly and be more stable in performance.
Description
Technical field
The present invention relates to stickup toughener, relate in particular to a kind of tile paste peel toughener for the paving of ceramic tile mortar cement.
Background technology
Sand-cement slurry is material of construction the most frequently used in construction work, and in material of construction, occupy very large proportion, is one of indispensable material of construction.
When paving ceramic tile, if common building mortar gel material, because north and south, winter in the summer weather temperature difference are too large, prolonged and repeatedly to expand with heat and contract with cold, often occur that adhesive (ceramic tile, marble etc.) is pasted loosely, hollowing, ftracture, the defect such as come off, in addition, also may occur the problems such as sand-cement slurry performance is relatively unstable, these defects bring an a lot of difficult problem all to the technician of building operation.Meanwhile, also very large puzzlement is brought to human consumer.
Therefore, need badly in prior art and occur that one can overcome the above-mentioned defect of sand-cement slurry, bonding firmly, the ceramic tile peel sand-cement slurry binding agent of not easily hollowing, not easy to crack, difficult drop-off and stable performance.
Summary of the invention
In order to overcome the deficiencies in the prior art, the object of the present invention is to provide a kind of can make ceramic tile and sand-cement slurry bonding firmly, the tile paste peel toughener of stable performance.
Object of the present invention is achieved through the following technical solutions:
A kind of tile paste peel toughener, comprises the raw material of following weight percent: ACRYLIC EMULSION 50-60%, styrene-butadiene emulsion 20-30%, binding agent 5-10%, film coalescence aid 3-6%, defoamer 0.5-3%, sanitas 0.5-3%.
Preferably, described ACRYLIC EMULSION weight percent content is 50%.
Preferably, described styrene-butadiene emulsion weight percent content is 30%.
Preferably, described caking agent weight percent content is 9%.
Preferably, described film coalescence aid weight percent content is 5%.
Preferably, the weight percent content of defoamer is 1%.
Preferably, the weight percent content of sanitas is 1%.
Compared with prior art, the present invention has following beneficial effect:
Brushing of the present invention can change the snappiness of contact surface at ceramic tile (stone material) back side, and sand-cement slurry and ceramic tile have and expand with heat and contract with cold, the yielding characteristic of appearance of base material and ceramic tile, this characteristic is the major cause that ceramic tile decoration material comes off, therefore the present invention is by flexible lifting, can make that sand-cement slurry bonds more firmly, performance is more stable.Secondly, the present invention also can work as interfacial agents effect, improves the cohesive strength of mortar and ornament.
Embodiment
The present invention is described in further detail for specific embodiment below.
Embodiment 1
A kind of tile paste peel toughener, by weight percentage, by the emulsion that 50% ACRYLIC EMULSION, 30% styrene-butadiene emulsion, 9% caking agent, 6% film coalescence aid, 3% defoamer and 3% sanitas are mixed with, evenly fully brush at thing to be pasted (marble, the ceramic tile etc.) back side and surface of wall, and make it as transparence.Keep solid, smooth, clean (without the wax without oil stain) of to be bonded (marble, ceramic tile, body of wall etc.), drying.
The present invention is single-component Green Product, nontoxic, non-stimulated smell, pollution-free, performance is remarkable, significantly can strengthen the stickup dynamics of motar, effectively prevent mortar premature hardening, reduce mortar cracking simultaneously, promote waterproof infiltration effect, there is superpower stickup effect, material of construction (marble, ceramic tile etc.) hollowing can be prevented to greatest extent, fall the generation of brick phenomenon.
The present invention has easy construction (can use without the need to stirring), simple, use cost is low, the characteristics such as adherence force is superpower.
In addition, the intensity contrast that comes off when this tile paste peel toughener and conventional cement mortar, glue for tile paving ceramic tile is as table one:
As shown in Table 1, the peel intensity adding the sand-cement slurry of this tile paste peel is the highest.
The economic performance of this tile paste peel toughener and common glue for tile is to such as table two:
Embodiment 2
A kind of embodiment of tile paste peel toughener of the present invention, by weight percentage, comprises the raw material of following weight percent:
55% ACRYLIC EMULSION, 25% styrene-butadiene emulsion, 10% caking agent, 6% film coalescence aid, 2% defoamer and 2% sanitas.Other process of the test is identical with embodiment 1 with effect comparison result, repeats no more herein.
Embodiment 3
A kind of embodiment of tile paste peel toughener of the present invention, by weight percentage, comprises the raw material of following weight percent:
60% ACRYLIC EMULSION, 25% styrene-butadiene emulsion, 8% caking agent, 5% film coalescence aid, 1% defoamer and 1% sanitas.Other process of the test is identical with embodiment 1 with effect comparison result, repeats no more herein.
Embodiment 4
A kind of embodiment of tile paste peel toughener of the present invention, by weight percentage, comprises the raw material of following weight percent:
60% ACRYLIC EMULSION, 30% styrene-butadiene emulsion, 5% caking agent, 3% film coalescence aid, 1% defoamer and 1% sanitas.Other process of the test is identical with embodiment 1 with effect comparison result, repeats no more herein.
Embodiment 5
A kind of embodiment of tile paste peel toughener of the present invention, by weight percentage, comprises the raw material of following weight percent:
60% ACRYLIC EMULSION, 30% styrene-butadiene emulsion, 5% caking agent, 4% film coalescence aid, 0.5% defoamer and 0.5% sanitas.Other process of the test is identical with embodiment 1 with effect comparison result, repeats no more herein.
Embodiment 6
A kind of embodiment of tile paste peel toughener of the present invention, by weight percentage, comprises the raw material of following weight percent:
60% ACRYLIC EMULSION, 20% styrene-butadiene emulsion, 9% caking agent, 6% film coalescence aid, 3% defoamer and 2% sanitas.Other process of the test is identical with embodiment 1 with effect comparison result, repeats no more herein.
Embodiments of the present invention are not limited thereto; according to foregoing of the present invention; utilize ordinary technical knowledge and the customary means of this area; do not departing under the present invention's above-mentioned basic fundamental thought prerequisite; the present invention can also make the amendment of other various ways, replacement or change, all drops within rights protection scope of the present invention.
Claims (7)
1. a tile paste peel toughener, is characterized in that, comprises the raw material of following weight percent: ACRYLIC EMULSION 50-60%, styrene-butadiene emulsion 20-30%, binding agent 5-10%, film coalescence aid 3-6%, defoamer 0.5-3%, sanitas 0.5-3%.
2. tile paste peel toughener according to claim 1, is characterized in that, described ACRYLIC EMULSION weight percent content is 50%.
3. tile paste peel toughener according to claim 1, is characterized in that, described styrene-butadiene emulsion weight percent content is 30%.
4. tile paste peel toughener according to claim 1, is characterized in that, described caking agent weight percent content is 9%.
5. tile paste peel toughener according to claim 1, is characterized in that, described film coalescence aid weight percent content 5%.
6. tile paste peel toughener according to claim 1, is characterized in that, the weight percent content of defoamer is 1%.
7. tile paste peel toughener according to claim 1, is characterized in that, the weight percent content of sanitas is 1%.