CN105314966A - 小分子水陶瓷容器的制作工艺 - Google Patents
小分子水陶瓷容器的制作工艺 Download PDFInfo
- Publication number
- CN105314966A CN105314966A CN201410635829.9A CN201410635829A CN105314966A CN 105314966 A CN105314966 A CN 105314966A CN 201410635829 A CN201410635829 A CN 201410635829A CN 105314966 A CN105314966 A CN 105314966A
- Authority
- CN
- China
- Prior art keywords
- pug
- clay
- purple
- micromolecular water
- porcelain receptacle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种小分子水陶瓷容器的制作工艺,包括泥料处理工序:所述泥料由紫砂泥和粘土泥组成,其中紫砂泥占泥料总重量的80~90%,粘土泥由含铁质粉砂岩和泥土组成;首先将泥料混合粉碎,之后采用压滤工艺将泥料中的多余水分滤除后,再进行炼泥。坯料成型工序。烧制成型工序:将制得的坯料放入炉窑中,且控制炉窑内的烧制温度从初始温度逐渐升高到1200℃,其中初始温度到100℃用时1~2小时,100℃到400℃用时1~2小时,400℃到600℃用时5~6小时,600℃到1200℃用时5~6小时;而且在炉窑内温度逐渐升高的过程中,让炉窑内的坯料依次在氧化气氛中烧制6~7小时,在还原气氛中烧制2~4小时,在中性气氛中烧制4~5小时。使用本发明制作出来的砂壶能够烧出对人体有利的弱碱性小分子水。
Description
技术领域
本发明涉及一种小分子水陶瓷容器的制作工艺。
背景技术
目前市面上的烧水容器,为普通的瓷土、陶土、或铁制的烧水容器,所有市面上出现的烧水容器,均不能产生小分子水。
发明内容
本发明目的是:针对上述问题,提供一种小分子水陶瓷容器的制作工艺,使用本发明制作出来的小分子水陶瓷容器能够烧出对人体有利的弱碱性小分子水。
本发明的技术方案是:一种小分子水陶瓷容器的制作工艺,包括以下工序:
工序一、泥料处理:
所述泥料由紫砂泥和粘土泥组成,其中紫砂泥占泥料总重量的80~90%,粘土泥由含铁质粉砂岩和泥土组成;首先将作为制作原料的泥料混合粉碎,之后采用压滤工艺将泥料中的多余水分滤除后,再进行炼泥;
工序二、坯料成型;
工序三、烧制成型:
将工序二制得的坯料放入炉窑中,且控制炉窑内的烧制温度从初始温度逐渐升高到1200℃,其中初始温度到100℃用时2小时,100℃到400℃用时2小时,400℃到600℃用时5~6小时,600℃到1200℃用时6小时;而且在炉窑内温度逐渐升高的过程中,让炉窑内的坯料依次在氧化气氛中烧制6~7小时,在还原气氛中烧制2~4小时,在中性气氛中烧制4~5小时;从而制得小分子水陶瓷容器成品。
本发明在上述技术方案的基础上,还包括一下优选技术方案:
所述紫砂泥为宜兴黄龙山紫砂泥。
所述粘土泥为宜兴粘土泥,且该粘土泥的含铁量在8%以上。
在所述工序一中,所述紫砂泥占泥料总重量的90%。
所述小分子水陶瓷容器为紫砂壶。
所述小分子水陶瓷容器为紫砂容器。
所述紫砂容器为紫砂杯、紫砂锅、紫砂罐、紫砂瓶或紫砂壶。
本发明的优点是:使用本发明的工艺能够制作出来的陶瓷容器(如紫砂壶),可以改变水质,使水呈弱碱性,且不含砷,汞等重金属。一般的水含水分子团108赫兹,而本发明制作的砂壶烧出来的水分子团变小,为46赫兹左右的小分子水,小分子团水能保护肠内微生物急速排除细胞内的赃物。
直接饮用小分子团水能保护肠内微生物急速排除细胞内的赃物。
用小分子水陶瓷容器烧水,煮茶,能将茶叶中的儿茶素有效分解,茶水醇厚回味,且其有丰富的铁离子,对存放茶水有良好的保鲜功能,煮咖啡,能将咖啡较多有效成分释出,使咖啡更可口醇香。
具体实施方式
本发明这种小分子水陶瓷容器的制作工艺,主要用于制作紫砂容器(紫砂容器为陶瓷容器的一个小类,陶瓷容器包括紫砂容器),可以用来制作紫砂壶,也可以用来制作紫砂杯,还可以用来制作紫砂锅、紫砂罐或紫砂瓶等其他各种容器。本实施例具体为小分子水紫砂壶的制作工艺,该工艺包括以下三大工序:
工序一、泥料处理:
所述泥料由紫砂泥和粘土泥两种材料组成,其中紫砂泥占泥料总重量的80~90%(优选为90%。),粘土泥由含铁质粉砂岩和泥土组成;首先将作为制作原料的泥料(即紫砂泥和粘土泥)混合粉碎,之后采用压滤工艺将泥料中的多余水分滤除后,再进行炼泥;
为了保证烧制出来的砂壶成品具有较高的质量,一般将所述紫砂泥选用为宜兴黄龙山紫砂泥,或者将所述粘土泥选用为含铁量不低于8%(重量百分比)的宜兴粘土泥。而且在选用紫砂泥和粘土泥时,需精挑细选,去除那些质量较差的泥料。
紫砂泥料,透而不漏,有双重气孔的特性,透水性好。
工序二、坯料成型。该工序与传统的坯料成型工序相同,在此不再赘述。
工序三、烧制成型:
将工序二制得的坯料放入炉窑中,且控制炉窑内的烧制温度从初始温度逐渐升高到1200℃,其中初始温度到100℃用时1~2小时,100℃到400℃用时1~2小时,400℃到600℃用时5~6小时,600℃到1200℃用时5~6小时;而且在炉窑内温度逐渐升高的过程中,让炉窑内的坯料依次在氧化气氛中烧制4~5小时,在还原气氛中烧制1~2小时,在中性气氛中烧制2~3小时;从而制得小分子水紫砂壶成品。
采用传统工艺之所以烧制不出能出小分子水的砂壶,一方面是因为传统工艺采用单种材料粉碎,第二方面是因为泥料处理不够精细,第三方面是因为烧制气氛和烧制温度不合理。所以传统工艺烧制出来的砂壶很容易开裂,且不能产生小分子水。
制作紫砂杯、紫砂锅、紫砂罐、紫砂瓶的工艺与本本实施例这种制造紫砂壶的工艺基本相同,区别仅在于工序二中坯料成型制得的坯料形状不同,不再是本实施例中的壶形,而是杯形、锅形、罐形或瓶形。
当然,上述实施例只为说明本发明的技术构思及特点,其目的在于让人们能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明主要技术方案的精神实质所做的等效变换或修饰,都应涵盖在本发明的保护范围之内。
Claims (7)
1.一种小分子水陶瓷容器的制作工艺,其特征在于包括以下工序:
工序一、泥料处理:
所述泥料由紫砂泥和粘土泥组成,其中紫砂泥占泥料总重量的80~90%,粘土泥由含铁质粉砂岩和泥土组成;首先将作为制作原料的泥料混合粉碎,之后采用压滤工艺将泥料中的多余水分滤除后,再进行炼泥;
工序二、坯料成型;
工序三、烧制成型:
将工序二制得的坯料放入炉窑中,且控制炉窑内的烧制温度从初始温度逐渐升高到1200℃,其中初始温度到100℃用时1~2小时,100℃到400℃用时1~2小时,400℃到600℃用时5~6小时,600℃到1200℃用时5~6小时;而且在炉窑内温度逐渐升高的过程中,让炉窑内的坯料依次在氧化气氛中烧制6~7小时,在还原气氛中烧制2~4小时,在中性气氛中烧制4~5小时;从而制得小分子水陶瓷容器成品。
2.根据权利他要求1所述的小分子水陶瓷容器的制作工艺,其特征在于:所述紫砂泥为宜兴黄龙山紫砂泥。
3.根据权利他要求1所述的小分子水陶瓷容器的制作工艺,其特征在于:所述粘土泥为宜兴粘土泥,且该粘土泥的含铁量在8%以上。
4.根据权利他要求1所述的小分子水陶瓷容器的制作工艺,其特征在于:在所述工序一中,所述紫砂泥占泥料总重量的90%。
5.根据权利他要求1所述的小分子水陶瓷容器的制作工艺,其特征在于:所述小分子水陶瓷容器为紫砂壶。
6.根据权利他要求1所述的小分子水陶瓷容器的制作工艺,其特征在于:所述小分子水陶瓷容器为紫砂容器。
7.根据权利他要求6所述的小分子水陶瓷容器的制作工艺,其特征在于:所述紫砂容器为紫砂杯、紫砂锅、紫砂罐、紫砂瓶或紫砂壶。