CN105296103A - 一种机械零件包装用防锈油 - Google Patents

一种机械零件包装用防锈油 Download PDF

Info

Publication number
CN105296103A
CN105296103A CN201510688587.4A CN201510688587A CN105296103A CN 105296103 A CN105296103 A CN 105296103A CN 201510688587 A CN201510688587 A CN 201510688587A CN 105296103 A CN105296103 A CN 105296103A
Authority
CN
China
Prior art keywords
parts
oil
powder
15min
rust
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510688587.4A
Other languages
English (en)
Inventor
米文彪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIESHOU JIABAO PACKAGING MATERIALS Co Ltd
Original Assignee
JIESHOU JIABAO PACKAGING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIESHOU JIABAO PACKAGING MATERIALS Co Ltd filed Critical JIESHOU JIABAO PACKAGING MATERIALS Co Ltd
Priority to CN201510688587.4A priority Critical patent/CN105296103A/zh
Publication of CN105296103A publication Critical patent/CN105296103A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种机械零件包装用防锈油，涉及包装材料技术领域，由如下重量份数的原料制成：纳米二氧化钛2-5份、磁铁矿粉6-10份、菜籽粕12-17份、膨润土10-15份、十二碳醇酯8-13份、乙二醇苯醚4-7份、羧甲基纤维素钠5-8份、松香5-8份、陈皮3-6份、樟树籽6-10份、芦苇秸秆2-4份、棕榈油30-40份、米糠油15-20份、乙醇15-20份。本发明所制防锈油具有较强的防锈效果，涂抹于零件表面后能快速性能一层致密保护膜，起到防潮、防腐蚀和抗氧化作用，并且防锈周期长，从而有效保护零件。

Description

一种机械零件包装用防锈油
技术领域：
本发明涉及包装材料技术领域，具体涉及一种机械零件包装用防锈油。
背景技术：
在工厂生产的机械零件在包装封存时，需要在其表面涂抹一层防锈油，以防止零件生锈，然后用石蜡纸包裹，这样就可以保证零件在一定时间内不生锈。而现有的防锈油效果一般，防锈周期较短，不能起到长时间防锈的作用。
发明内容：
本发明所要解决的技术问题在于提供一种防锈效果好且防锈时间长的机械零件包装用防锈油。
本发明所要解决的技术问题采用以下的技术方案来实现：
一种机械零件包装用防锈油，由如下重量份数的原料制成：
纳米二氧化钛2-5份、磁铁矿粉6-10份、菜籽粕12-17份、膨润土10-15份、十二碳醇酯8-13份、乙二醇苯醚4-7份、羧甲基纤维素钠5-8份、松香5-8份、陈皮3-6份、樟树籽6-10份、芦苇秸秆2-4份、棕榈油30-40份、米糠油15-20份、乙醇15-20份；
其制备方法如下：
(1)先将纳米二氧化钛和磁铁矿粉分散于乙醇中，研磨10-15min后于微波频率2450MHz、功率800W下微波处理10-15min，然后经浓缩后制成膏体，再向膏体中加入羧甲基纤维素钠，充分混合均匀后进行烘干，最后经粉碎后得到粉体I；
(2)将陈皮、樟树籽和芦苇秸秆加热至70-80℃保温翻炒10-15min，然后粉碎成粉末，混合均匀后得到粉料II；
(3)将粉料I、粉料II、菜籽粕和膨润土加入棕榈油中，混合物加热至60-70℃保温搅拌15-20min，然后加入松香和米糠油，继续保温搅拌10-15min，冷却至室温后再加入十二碳醇酯和乙二醇苯醚，充分混合均匀后加入球磨机中，球磨至细度小于0.1mm即可。
所述膨润土使用前需要经过改性处理，其处理方法为：先向膨润土中加入0.01倍量浓硫酸，混合均匀后升温至60-65℃保温搅拌15-20min，然后水洗三次，再加入0.05倍量活性炭和0.1倍量预胶化淀粉，于微波频率2450MHz、功率600W下微波处理10-15min，最后经烘干后粉碎成粉末。经改性后的膨润土，能有效提高防锈膜的机械性能。
本发明的有益效果是：本发明利于纳米二氧化钛和磁铁矿粉制得纳米防锈剂，并辅以多种防锈助剂制得机械零件包装用防锈油，该防锈油具有较强的防锈效果，涂抹于零件表面后能快速性能一层致密保护膜，起到防潮、防腐蚀和抗氧化作用，并且防锈周期长，从而有效保护零件。其中，天然植物陈皮、樟树籽和芦苇秸秆的加入，提高了防锈效果和降低了生产成本。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施例，进一步阐述本发明。
膨润土的改性：先向膨润土中加入0.01倍量浓硫酸，混合均匀后升温至60-65℃保温搅拌20min，然后水洗三次，再加入0.05倍量活性炭和0.1倍量预胶化淀粉，于微波频率2450MHz、功率600W下微波处理15min，最后经烘干后粉碎成粉末。
实施例1
(1)先将3份纳米二氧化钛和8份磁铁矿粉分散于15份乙醇中，研磨10min后于微波频率2450MHz、功率800W下微波处理10min，然后经浓缩后制成膏体，再向膏体中加入5-8份羧甲基纤维素钠，充分混合均匀后进行烘干，最后经粉碎后得到粉体I；
(2)将3份陈皮、7份樟树籽和2份芦苇秸秆加热至70-80℃保温翻炒15min，然后粉碎成粉末，混合均匀后得到粉料II；
(3)将粉料I、粉料II、12份菜籽粕和10份膨润土加入30份棕榈油中，混合物加热至65-70℃保温搅拌20min，然后加入5份松香和15份米糠油，继续保温搅拌15min，冷却至室温后再加入9份十二碳醇酯和5份乙二醇苯醚，充分混合均匀后加入球磨机中，球磨至细度小于0.1mm即可。
实施例2
(1)先将4份纳米二氧化钛和10份磁铁矿粉分散于20份乙醇中，研磨15min后于微波频率2450MHz、功率800W下微波处理15min，然后经浓缩后制成膏体，再向膏体中加入7份羧甲基纤维素钠，充分混合均匀后进行烘干，最后经粉碎后得到粉体I；
(2)将5份陈皮、8份樟树籽和3份芦苇秸秆加热至75-80℃保温翻炒15min，然后粉碎成粉末，混合均匀后得到粉料II；
(3)将粉料I、粉料II、15份菜籽粕和12份膨润土加入35份棕榈油中，混合物加热至65-70℃保温搅拌20min，然后加入7份松香和18份米糠油，继续保温搅拌15min，冷却至室温后再加入10份十二碳醇酯和5份乙二醇苯醚，充分混合均匀后加入球磨机中，球磨至细度小于0.1mm即可。
实施例3
(1)先将5份纳米二氧化钛和10份磁铁矿粉分散于20份乙醇中，研磨15min后于微波频率2450MHz、功率800W下微波处理15min，然后经浓缩后制成膏体，再向膏体中加入8份羧甲基纤维素钠，充分混合均匀后进行烘干，最后经粉碎后得到粉体I；
(2)将5份陈皮、10份樟树籽和3份芦苇秸秆加热至75-80℃保温翻炒15min，然后粉碎成粉末，混合均匀后得到粉料II；
(3)将粉料I、粉料II、16份菜籽粕和15份膨润土加入40份棕榈油中，混合物加热至65-70℃保温搅拌20min，然后加入8份松香和20份米糠油，继续保温搅拌15min，冷却至室温后再加入13份十二碳醇酯和6份乙二醇苯醚，充分混合均匀后加入球磨机中，球磨至细度小于0.1mm即可。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (2)

1.一种机械零件包装用防锈油，其特征在于，由如下重量份数的原料制成：
纳米二氧化钛2-5份、磁铁矿粉6-10份、菜籽粕12-17份、膨润土10-15份、十二碳醇酯8-13份、乙二醇苯醚4-7份、羧甲基纤维素钠5-8份、松香5-8份、陈皮3-6份、樟树籽6-10份、芦苇秸秆2-4份、棕榈油30-40份、米糠油15-20份、乙醇15-20份；
其制备方法如下：
(1)先将纳米二氧化钛和磁铁矿粉分散于乙醇中，研磨10-15min后于微波频率2450MHz、功率800W下微波处理10-15min，然后经浓缩后制成膏体，再向膏体中加入羧甲基纤维素钠，充分混合均匀后进行烘干，最后经粉碎后得到粉体I；
(2)将陈皮、樟树籽和芦苇秸秆加热至70-80℃保温翻炒10-15min，然后粉碎成粉末，混合均匀后得到粉料II；
(3)将粉料I、粉料II、菜籽粕和膨润土加入棕榈油中，混合物加热至60-70℃保温搅拌15-20min，然后加入松香和米糠油，继续保温搅拌10-15min，冷却至室温后再加入十二碳醇酯和乙二醇苯醚，充分混合均匀后加入球磨机中，球磨至细度小于0.1mm即可。
2.根据权利要求1所述的机械零件包装用防锈油，其特征在于：所述膨润土使用前需要经过改性处理，其处理方法为：先向膨润土中加入0.01倍量浓硫酸，混合均匀后升温至60-65℃保温搅拌15-20min，然后水洗三次，再加入0.05倍量活性炭和0.1倍量预胶化淀粉，于微波频率2450MHz、功率600W下微波处理10-15min，最后经烘干后粉碎成粉末。
CN201510688587.4A 2015-10-19 2015-10-19 一种机械零件包装用防锈油 Pending CN105296103A (zh)