CN105295502A - 一种水性涂料分散剂 - Google Patents

一种水性涂料分散剂 Download PDF

Info

Publication number
CN105295502A
CN105295502A CN201510773263.0A CN201510773263A CN105295502A CN 105295502 A CN105295502 A CN 105295502A CN 201510773263 A CN201510773263 A CN 201510773263A CN 105295502 A CN105295502 A CN 105295502A
Authority
CN
China
Prior art keywords
parts
initiator
hour
add
dispersant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510773263.0A
Other languages
English (en)
Other versions
CN105295502B (zh
Inventor
程聚光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xuancheng City Trooyawn Refined Chemical Industry Co Ltd
Original Assignee
Xuancheng City Trooyawn Refined Chemical Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xuancheng City Trooyawn Refined Chemical Industry Co Ltd filed Critical Xuancheng City Trooyawn Refined Chemical Industry Co Ltd
Priority to CN201510773263.0A priority Critical patent/CN105295502B/zh
Publication of CN105295502A publication Critical patent/CN105295502A/zh
Application granted granted Critical
Publication of CN105295502B publication Critical patent/CN105295502B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

发明公开了一种水性涂料分散剂，由以下成分制成，丙烯酸、甲基丙烯酸甲酯、白炭黑、乙二醇、有机溶剂、正戊醇、丙二酸、引发剂、亚硫酸钠、中和剂；本发明分散剂能够降低水性涂料的表面张力,增强对颜料颗粒的润湿作用,使颜料颗粒在液相中稳定的分散，并且能够与涂料表面基团迅速牢固的结合,使颜料粒子稳定的悬浮在水溶剂中,使颜料获得较好的分散,达到最佳的分散效果，通过添加改性白炭黑，来提高分散效果和分散速度；本发明分散剂在制作过程中，通过改变以往一次性添加引发剂换成分次添加引发剂，改变了生成物的分子量和产物的分布，使得制成的分散剂不仅具有良好的分散性能，还具有良好的耐环境温度变化的能力。

Description

一种水性涂料分散剂
技术领域
本发明涉及化工品领域，特别是涉及一种水性涂料分散剂。
背景技术
分散剂是一种在分子内同时具有亲油性和亲水性两种相反性质的界面活性剂，可均一分散难溶于液体的无机、有机颜料的固体颗粒，同时防止固体颗粒的沉降和凝聚。人们对健康环保要求的提高,水性环保涂料成为建筑装饰领域的新宠。但水的表面张力要比有机溶剂大很多,就需要添加一些助剂降低水的表面张力,增强对颜料颗粒的润湿作用,使颜料颗粒在液相中稳定的分散。然而，现有市场上生产的许多分散剂，分散效果不明显，效率低。
发明内容
本发明的目的是提供一种水性涂料分散剂。
本发明通过以下技术方案实现：
一种水性涂料分散剂，按重量份计由以下成分制成，丙烯酸15份、甲基丙烯酸甲酯15份、白炭黑2份、乙二醇10份、有机溶剂60份、正戊醇1份、丙二酸3份、引发剂2份、亚硫酸钠4份、中和剂4份；其由以下制作步骤制成：
1）在反应釜中添加有机溶剂，加热至65-70℃，恒温处理1-1.5小时，再添加丙烯酸、甲基丙烯酸甲酯，在6-10Mpa压力，95-100℃下添加引发剂，反应8-9小时；
2）将正戊醇、丙二酸与白炭黑在55-60℃，15-18MPa压力下通入氮气反应40-45分钟；
3）将1）和2）中所得原料混合，加热至60℃时，添加乙二醇，当温度上升至85℃时，添加亚硫酸钠，当温度升高到105℃时，停止升温，反应1-2小时后，快速冷却至35-40℃，取出物料；
4）将3）中取出的物料放入胶体磨中研磨1小时后，再放入搅拌缸中，搅拌1-1.5分钟；
5）将4）中的物料添加中和剂后，除去有机溶剂，搅拌30分钟后，密封1小时，再放入均质机中均质45分钟，即可。
进一步地，所述有机溶剂为丙酮。
进一步地，所述引发剂为过硫酸铵。
进一步地，所述中和剂为氢氧化钠。
进一步地，所述步骤1）中引发剂添加速度为每隔1小时添加0.5重量份引发剂。
本发明的有益效果是，与现有技术相比：
本发明分散剂能够降低水性涂料的表面张力,增强对颜料颗粒的润湿作用,使颜料颗粒在液相中稳定的分散，并且能够与涂料表面基团迅速牢固的结合,使颜料粒子稳定的悬浮在水溶剂中,使颜料获得较好的分散,达到最佳的分散效果，通过添加改性白炭黑，来提高分散效果和分散速度；本发明分散剂在制作过程中，通过改变以往一次性添加引发剂换成分次添加引发剂，改变了生成物的分子量和产物的分布，使得制成的分散剂不仅具有良好的分散性能，还具有良好的耐环境温度变化的能力。
具体实施方式
一种水性涂料分散剂，按重量份计由以下成分制成，丙烯酸15份、甲基丙烯酸甲酯15份、白炭黑2份、乙二醇10份、有机溶剂60份、正戊醇1份、丙二酸3份、引发剂2份、亚硫酸钠4份、中和剂4份；其由以下制作步骤制成：
1）在反应釜中添加有机溶剂，加热至65-70℃，恒温处理1-1.5小时，再添加丙烯酸、甲基丙烯酸甲酯，在6-10Mpa压力，95-100℃下添加引发剂，反应8-9小时；
2）将正戊醇、丙二酸与白炭黑在55-60℃，15-18MPa压力下通入氮气反应40-45分钟；
3）将1）和2）中所得原料混合，加热至60℃时，添加乙二醇，当温度上升至85℃时，添加亚硫酸钠，当温度升高到105℃时，停止升温，反应1-2小时后，快速冷却至35-40℃，取出物料；
4）将3）中取出的物料放入胶体磨中研磨1小时后，再放入搅拌缸中，搅拌1-1.5分钟；
5）将4）中的物料添加中和剂后，除去有机溶剂，搅拌30分钟后，密封1小时，再放入均质机中均质45分钟，即可。
进一步地，所述有机溶剂为丙酮。
进一步地，所述引发剂为过硫酸铵。
进一步地，所述中和剂为氢氧化钠。
进一步地，所述步骤1）中引发剂添加速度为每隔1小时添加0.5重量份引发剂。
当pH≈9.0时，分散剂的分散效果最好。
用本发明分散剂制备的涂料在30℃下具有25mPa·s的粘度，在室温下存储60天，涂料的粘度、微观分散相、分散度和沉降时间表现的均较为出色。

Claims (5)

1.一种水性涂料分散剂，其特征在于，按重量份计由以下成分制成，丙烯酸15份、甲基丙烯酸甲酯15份、白炭黑2份、乙二醇10份、有机溶剂60份、正戊醇1份、丙二酸3份、引发剂2份、亚硫酸钠4份、中和剂4份；其由以下制作步骤制成：
1）在反应釜中添加有机溶剂，加热至65-70℃，恒温处理1-1.5小时，再添加丙烯酸、甲基丙烯酸甲酯，在6-10Mpa压力，95-100℃下添加引发剂，反应8-9小时；
2）将正戊醇、丙二酸与白炭黑在55-60℃，15-18MPa压力下通入氮气反应40-45分钟；
3）将1）和2）中所得原料混合，加热至60℃时，添加乙二醇，当温度上升至85℃时，添加亚硫酸钠，当温度升高到105℃时，停止升温，反应1-2小时后，快速冷却至35-40℃，取出物料；
4）将3）中取出的物料放入胶体磨中研磨1小时后，再放入搅拌缸中，搅拌1-1.5分钟；
5）将4）中的物料添加中和剂后，除去有机溶剂，搅拌30分钟后，密封1小时，再放入均质机中均质45分钟，即可。
2.根据权利要求1所述的一种水性涂料分散剂，其特征在于，所述有机溶剂为丙酮。
3.根据权利要求1所述的一种水性涂料分散剂，其特征在于，所述引发剂为过硫酸铵。
4.根据权利要求1所述的一种水性涂料分散剂，其特征在于，所述中和剂为氢氧化钠。
5.根据权利要求1所述的一种水性涂料分散剂，其特征在于，所述步骤1）中引发剂添加速度为每隔1小时添加0.5重量份引发剂。
CN201510773263.0A 2015-11-13 2015-11-13 一种水性涂料分散剂 Active CN105295502B (zh)