CN105294029A - 一种耐腐蚀防火门芯制备方法 - Google Patents

一种耐腐蚀防火门芯制备方法 Download PDF

Info

Publication number
CN105294029A
CN105294029A CN201510802480.8A CN201510802480A CN105294029A CN 105294029 A CN105294029 A CN 105294029A CN 201510802480 A CN201510802480 A CN 201510802480A CN 105294029 A CN105294029 A CN 105294029A
Authority
CN
China
Prior art keywords
parts
high speed
corrosion
carrying
door core
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510802480.8A
Other languages
English (en)
Inventor
张斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TAIXING HEQING MACHINERY FITTINGS FACTORY
Original Assignee
TAIXING HEQING MACHINERY FITTINGS FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TAIXING HEQING MACHINERY FITTINGS FACTORY filed Critical TAIXING HEQING MACHINERY FITTINGS FACTORY
Priority to CN201510802480.8A priority Critical patent/CN105294029A/zh
Publication of CN105294029A publication Critical patent/CN105294029A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种耐腐蚀防火门芯，将聚乙烯醇30-40份和水100-140份混合制成胶水，胶水置于高速剪切机内加入开孔膨胀珍珠岩5-10份、硅酸镁铝3-6份、三氧化二铝3-5份、改性纳米二氧化钛5-10份、纳米氧化锌5-10份、硫铝酸盐水泥70-95份和胺醇类阻锈剂2-3份高速剪切搅拌，剪切速度6000-8000RPM，剪切时间5-10min，转移至高速搅拌机，加入高铝水泥发泡剂0.5-2份，搅拌转速1000-1500r/min，搅拌时间10-15min，最后加入PVA短丝20-30份搅拌，搅拌转速800-1000r/min，搅拌时间5-10min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。

Description

一种耐腐蚀防火门芯制备方法
技术领域
本发明涉及一种耐腐蚀防火门芯及其制备方法。
背景技术
传统的卤素发泡门芯防火性能差，易蹿火、返卤，高温易碳化、变形，且在高温受热过程中会释放有害气体，严重影响其使用寿命、安全性能和稳定性能。
发明内容
针对现有技术中的上述不足，本发明提供了一种轻质、高强，耐火性能优异，高温受热无有害气体，隔音抗震、性能稳定、使用安全、寿命长的耐腐蚀防火门芯及其制备方法。
本发明采用的技术方案是：一种耐腐蚀防火门芯，其特征在于：按质量份数包括：聚乙烯醇30-40份、硫铝酸盐水泥70-95份、开孔膨胀珍珠岩5-10份、硅酸镁铝3-6份、胺醇类阻锈剂2-3份、改性纳米二氧化钛5-10份、纳米氧化锌5-10份、三氧化二铝3-5份、PVA短丝20-30份、高铝水泥发泡剂0.5-2份、水100-140份。
一种耐腐蚀防火门芯制备方法，其特征在于：首先将聚乙烯醇30-40份和水100-140份混合制成胶水，胶水置于高速剪切机内加入开孔膨胀珍珠岩5-10份、硅酸镁铝3-6份、三氧化二铝3-5份、改性纳米二氧化钛5-10份、纳米氧化锌5-10份、硫铝酸盐水泥70-95份和胺醇类阻锈剂2-3份高速剪切搅拌，剪切速度6000-8000RPM，剪切时间5-10min，转移至高速搅拌机，加入高铝水泥发泡剂0.5-2份，搅拌转速1000-1500r/min，搅拌时间10-15min，最后加入PVA短丝20-30份搅拌，搅拌转速800-1000r/min，搅拌时间5-10min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。
本发明客服了现有卤素防火门填充芯材防火性能差、易蹿火、返卤，高温易碳化、变形，在高温受热过程中会释放有害气体的根本性缺点，具有轻质高强，耐火性能优异，在高温受热过程中无有害产生，强度稳定，容重达340-380kg/m3，不粉化，符合GB8624-2006A1级不燃标准，以及GB/T20285-2006AQ1《材料产烟毒性危险分级》，性能明显优于卤素发泡防火门芯材料。且本发明的制备工艺具有材料浪费少、计量精确，发泡效率高、发泡稳定、效果好的优点，结合PVA短丝和钢丝笼，稳定发泡结构以及整体强度，进一步提高使用强度；结合改性纳米二氧化钛和纳米氧化锌促进抗菌、抗霉效果，配合三氧化二铝提高其防腐蚀性能。
具体实施方式
以下结合实施例对本发明作进一步说明。
实施例一
一种耐腐蚀防火门芯，按质量份数包括：聚乙烯醇30份、硫铝酸盐水泥100份、开孔膨胀珍珠岩5份、硅酸镁铝3份、胺醇类阻锈剂2份、改性纳米二氧化钛5份、纳米氧化锌5份、三氧化二铝3份、PVA短丝3份、高铝水泥发泡剂0.5份、水100份。
一种耐腐蚀防火门芯制备方法，首先将聚乙烯醇和水混合制成胶水，胶水置于高速剪切机内加入三氧化二铝、改性纳米二氧化钛、纳米氧化锌、硫铝酸盐水泥和胺醇类阻锈剂高速剪切搅拌，剪切速度6000RPM，剪切时间5min，转移至高速搅拌机，加入高铝水泥发泡剂，搅拌转速1000r/min，搅拌时间10min，最后加入PVA短丝搅拌，搅拌转速800r/min，搅拌时间5min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。
实施例二
一种耐腐蚀防火门芯，按质量份数包括：聚乙烯醇40份、硫铝酸盐水泥120份、开孔膨胀珍珠岩10份、硅酸镁铝6份、胺醇类阻锈剂3份、改性纳米二氧化钛10份、纳米氧化锌10份、三氧化二铝5份、PVA短丝5份、高铝水泥发泡剂2份、水140份。
一种耐腐蚀防火门芯制备方法，首先将聚乙烯醇和水混合制成胶水，胶水置于高速剪切机内加入三氧化二铝、改性纳米二氧化钛、纳米氧化锌、硫铝酸盐水泥和胺醇类阻锈剂高速剪切搅拌，剪切速度8000RPM，剪切时间10min，转移至高速搅拌机，加入高铝水泥发泡剂，搅拌转速1500r/min，搅拌时间15min，最后加入PVA短丝搅拌，搅拌转速1000r/min，搅拌时间10min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。
实施例三
一种耐腐蚀防火门芯，按质量份数包括：聚乙烯醇35份、硫铝酸盐水泥110份、开孔膨胀珍珠岩8份、硅酸镁铝5份、胺醇类阻锈剂2份、改性纳米二氧化钛8份、纳米氧化锌8份、三氧化二铝4份、PVA短丝4份、高铝水泥发泡剂1.5份、水130份。
一种耐腐蚀防火门芯制备方法，首先将聚乙烯醇和水混合制成胶水，胶水置于高速剪切机内加入三氧化二铝、改性纳米二氧化钛、纳米氧化锌、硫铝酸盐水泥和胺醇类阻锈剂高速剪切搅拌，剪切速度7000RPM，剪切时间8min，转移至高速搅拌机，加入高铝水泥发泡剂，搅拌转速1200r/min，搅拌时间12min，最后加入PVA短丝搅拌，搅拌转速900r/min，搅拌时间8min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。

Claims (1)

1.一种耐腐蚀防火门芯制备方法，其特征在于：首先将聚乙烯醇30-40份和水100-140份混合制成胶水，胶水置于高速剪切机内加入开孔膨胀珍珠岩5-10份、硅酸镁铝3-6份、三氧化二铝3-5份、改性纳米二氧化钛5-10份、纳米氧化锌5-10份、硫铝酸盐水泥70-95份和胺醇类阻锈剂2-3份高速剪切搅拌，剪切速度6000-8000RPM，剪切时间5-10min，转移至高速搅拌机，加入高铝水泥发泡剂0.5-2份，搅拌转速1000-1500r/min，搅拌时间10-15min，最后加入PVA短丝20-30份搅拌，搅拌转速800-1000r/min，搅拌时间5-10min，出料至模具内，模具内方正堆积满10dm3钢丝笼，模具内静至固化成型后，取出烘干至含水率12%即可。
CN201510802480.8A 2015-11-19 2015-11-19 一种耐腐蚀防火门芯制备方法 Pending CN105294029A (zh)