CN105271987A - 一种新型加气砖用砂浆 - Google Patents

一种新型加气砖用砂浆 Download PDF

Info

Publication number
CN105271987A
CN105271987A CN201510640472.8A CN201510640472A CN105271987A CN 105271987 A CN105271987 A CN 105271987A CN 201510640472 A CN201510640472 A CN 201510640472A CN 105271987 A CN105271987 A CN 105271987A
Authority
CN
China
Prior art keywords
mortar
aerated bricks
cement
powder
diatomite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510640472.8A
Other languages
English (en)
Inventor
沈圣祥
李凤必
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Kunlong Building Materials Co Ltd
Original Assignee
Anhui Kunlong Building Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Kunlong Building Materials Co Ltd filed Critical Anhui Kunlong Building Materials Co Ltd
Priority to CN201510640472.8A priority Critical patent/CN105271987A/zh
Publication of CN105271987A publication Critical patent/CN105271987A/zh
Pending legal-status Critical Current

Abstract

发明公开了一种新型加气砖用砂浆，按重量百分比计由以下成分制成：石英砂60%、粉煤灰10%、沸石粉4%、海泡石2%、羟乙基甲基纤维素0.5%、硅藻土3%、生石灰4%、水泥8%、铝粉2%、可再分散乳胶粉4.5%、减水剂1%、添加剂1%。本发明生产工艺简单，成本低，制成的砂浆强度好、导热系数低、抗裂效果非常好、节能环保，满足建筑工程的需要，符合环保的需求；本发明通过向水泥中添加膨胀土进行煅烧改性，使得水泥在砂浆中的粘接性增强；通过添加工艺改性后的硅藻土，改善了砂浆的性能，使得砂浆干缩变形小；本发明采用1%重量百分比的纤维素醚做添加剂，提高各成分的结合性，从而进一步提高加气砖的强度。

Description

一种新型加气砖用砂浆
技术领域
本发明涉及建筑材料制作领域，特别是涉及一种新型加气砖用砂浆。
背景技术
加气混凝土砖因具有重量轻、保温性能和吸音效果好、以及有一定强度等诸多优点，现有的加气砖长期存在的建筑墙体渗漏、开裂、强度低等问题；加气砖用砂浆吸水率大，很难具有较好的抗裂、耐久性、抗冲击、抗震和抗火灾的综合性能。
发明内容
本发明的目的是提供一种新型加气砖用砂浆，通过以下技术方案实现：
一种新型加气砖用砂浆，按重量百分比计由以下成分制成：石英砂60%、粉煤灰10%、沸石粉4%、海泡石2%、羟乙基甲基纤维素0.5%、硅藻土3%、生石灰4%、水泥8%、铝粉2%、可再分散乳胶粉4.5%、减水剂1%、添加剂1%。
进一步地，所述海泡石需粉碎至50-100目，与羟乙基甲基纤维素均匀混合，在有氧条件下加热至75-80℃，持续0.5-1小时，冷却至室温。
进一步地，所述生石灰与铝粉需在180-200℃温度下煅烧研磨2-3小时。
进一步地，所述可再分散乳胶粉为丙烯酸酯与苯乙烯共聚胶粉。
进一步地，所述减水剂为密胺系减水剂。
进一步地，所述添加剂为纤维素醚。
进一步地，所述硅藻土经过工艺改性处理：将硅藻土采用1%浓度的盐酸浸泡30分钟后，过滤，再采用5%氢氧化钠溶液浸泡，并加热并进行研磨30-40分钟，自然冷却至室温，过滤，干燥。
进一步地，所述水泥经过煅烧处理：向水泥中添加其重量1%的膨胀土，混合均匀，在300-350℃下进行煅烧1-1.5小时。
本发明的有益效果是：与现有的加气砖用砂浆制作技术相比，
（1）本发明生产工艺简单，成本低，制成的砂浆强度好、导热系数低、抗裂效果非常好、节能环保，满足建筑工程的需要，符合环保的需求；
（2）本发明通过向水泥中添加膨胀土进行煅烧改性，使得水泥在砂浆中的粘接性增强；通过添加工艺改性后的硅藻土，改善了砂浆的性能，使得砂浆干缩变形小；
（3）本发明采用1%重量百分比的纤维素醚做添加剂，提高各成分的结合性，从而进一步提高加气砖的强度；
（4）具有良好的耐水，耐高低温性能，解决普通一般加气砖用砂浆的干缩变形大，抗裂性、抗冻性差等问题。
具体实施方式
一种新型加气砖用砂浆，按重量百分比计由以下成分制成：石英砂60%、粉煤灰10%、沸石粉4%、海泡石2%、羟乙基甲基纤维素0.5%、硅藻土3%、生石灰4%、水泥8%、铝粉2%、可再分散乳胶粉4.5%、减水剂1%、添加剂1%。
进一步地，所述海泡石需粉碎至50-100目，与羟乙基甲基纤维素均匀混合，在有氧条件下加热至75-80℃，持续0.5-1小时，冷却至室温。
进一步地，所述生石灰与铝粉需在180-200℃温度下煅烧研磨2-3小时。
进一步地，所述可再分散乳胶粉为丙烯酸酯与苯乙烯共聚胶粉。
进一步地，所述减水剂为密胺系减水剂。
进一步地，所述添加剂为纤维素醚。
进一步地，所述硅藻土经过工艺改性处理：将硅藻土采用1%浓度的盐酸浸泡30分钟后，过滤，再采用5%氢氧化钠溶液浸泡，并加热并进行研磨30-40分钟，自然冷却至室温，过滤，干燥。
进一步地，所述水泥经过煅烧处理：向水泥中添加其重量1%的膨胀土，混合均匀，在300-350℃下进行煅烧1-1.5小时。
对本发明砂浆与一般加气砖用砂浆同强度等级上进行测试对比：
表1
由表1可以看出，本发明砂浆在相同强度等级下比一般砂浆在性能上要提高很多。

Claims (8)

1.一种新型加气砖用砂浆，其特征在于，按重量百分比计由以下成分制成：石英砂60%、粉煤灰10%、沸石粉4%、海泡石2%、羟乙基甲基纤维素0.5%、硅藻土3%、生石灰4%、水泥8%、铝粉2%、可再分散乳胶粉4.5%、减水剂1%、添加剂1%。
2.根据权利要求1所述的一种新型加气砖用砂浆，其特征在于，所述海泡石需粉碎至50-100目，与羟乙基甲基纤维素均匀混合，在有氧条件下加热至75-80℃，持续0.5-1小时，冷却至室温。
3.根据权利要求1所述的一种新型加气砖用砂浆，其特征在于，所述生石灰与铝粉需在180-200℃温度下煅烧研磨2-3小时。
4.根据权利要求1所述的一种新型加气砖用砂浆，其特征在于，所述可再分散乳胶粉为丙烯酸酯与苯乙烯共聚胶粉。
5.根据权利要求1所述的一种新型加气砖用砂浆，其特征在于，所述减水剂为密胺系减水剂。
6.根据权利要求1所述的一种新型加气砖用砂浆，其特征在于，所述添加剂为纤维素醚。
7.根据权利要求1所述的一种新型加气砖用砂浆，其特征在于，所述硅藻土经过工艺改性处理：将硅藻土采用1%浓度的盐酸浸泡30分钟后，过滤，再采用5%氢氧化钠溶液浸泡，并加热并进行研磨30-40分钟，自然冷却至室温，过滤，干燥。
8.根据权利要求1所述的一种新型加气砖用砂浆，其特征在于，所述水泥经过煅烧处理：向水泥中添加其重量1%的膨胀土，混合均匀，在300-350℃下进行煅烧1-1.5小时。
CN201510640472.8A 2015-09-30 2015-09-30 一种新型加气砖用砂浆 Pending CN105271987A (zh)