CN105219312A - 胶粘剂及胶粘剂制品 - Google Patents
胶粘剂及胶粘剂制品 Download PDFInfo
- Publication number
- CN105219312A CN105219312A CN201510575065.3A CN201510575065A CN105219312A CN 105219312 A CN105219312 A CN 105219312A CN 201510575065 A CN201510575065 A CN 201510575065A CN 105219312 A CN105219312 A CN 105219312A
- Authority
- CN
- China
- Prior art keywords
- tackiness agent
- adhesive product
- adhesive
- layer
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种胶粘剂及胶粘剂制品,所述胶粘剂按重量计包括以下组分,90-95%聚丙烯酸酯聚合物,1-3%交联剂,0.5-3%抗氧剂,0.1-1%光稳定剂。通过胶粘剂涂布而成的胶粘剂胶带能够很好的贴合于光伏组件边缘,能实现良好的贴合功能,并且具备优良的抗UV老化性能、密封性、耐磨性、耐水性、耐温性。
Description
技术领域
本发明涉及胶粘剂及胶粘剂制品技术领域,尤其涉及一种胶粘剂及胶粘剂制品。
背景技术
光伏技术是指在太阳能电池的帮助下将辐射能(主要为太阳能)直接转化为电能的技术。存在的各种太阳能电池的具体实例,最普遍的为硅电池,如单晶硅电池或者多晶硅电池,日益发展的是薄膜电池以及有机太阳能电池和染料电池等。
光伏组件制作流程一般为:经电池片分选-单焊接-串焊接-拼接(即将串焊好的电池片定位,拼接在一起)-中间测试(中间测试分:红外线测试和外观检查)-层压-削边-层后外观-层后红外-装框(一般为铝边框)-装接线盒-清洗-测试(此环节也分红外线测试和外观检查、判定该组件的等级)-包装。
光伏电池组件在生产过程中,边缘的保护一般通过铝合金边框来实现,密封在通过硅胶或者一些泡沫胶带,工序复杂,生产过程较为繁琐。随着技术的发展,薄膜组件越来越普及,目前薄膜组件使用的电池片的厚度最低已在150μm左右,这种薄膜组件的优点是工艺过程大大简化,硅材料消耗很少,电耗更低,并且在弱光条件也能发电;这种结构组件外边缘则不需要厚、重的铝边框保护,直接用保护胶带贴合即可实现对组件的保护,但同时对保护组件的胶带也提出了更高的要求:耐老化性能、抗UV效果更好,对组件材料有更好的粘结效果,轻柔,有很强的力的缓冲效果,耐摩擦,对气体和水蒸气渗透率低,即拥有优良的抗UV、阻气、水、油及异味性能等。
发明内容
本发明的目的在于提供一种胶粘剂及胶粘剂制品,该胶粘剂制品具备抗UV老化性能佳、粘结效果佳、耐磨、耐温等优良特性。
为实现上述发明目的,本发明提供了:
一种胶粘剂,其特征在于按重量计包括以下组分,
90-95%聚丙烯酸酯聚合物,
1-3%交联剂,
0.5-3%抗氧剂,
0.1-1%光稳定剂。
作为本发明的进一步改进,所述交联剂为金属氧化物类交联剂,包括氧化锌、氧化铅、氧化镁中的一种或多种。
作为本发明的进一步改进,所述抗氧剂包括主抗氧剂和辅助抗氧剂两种,主抗氧剂为四[甲基-β-(3,5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯和三(2,4-二叔丁基苯基)亚磷酸酯中的一种或者多种;辅助抗氧剂为硫代二丙酸双酯类中的一种或几种。
作为本发明的进一步改进,所述光稳定剂包括丁二酸与(4-羟基-2,2,6,6-四甲基-1-哌啶醇的聚合物)、双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯或者双(3,5-二叔丁基-4羟基苄基磷酸单乙酯)镍中的一种或者多种。
一种胶粘剂制品,包括如上所述的胶粘剂涂布而成的胶粘剂层。
作为本发明的进一步改进,所述胶粘剂制品自其一侧至另一侧依次包括离型层、第一胶粘剂层、泡沫层、第二胶粘剂层、载体层。
作为本发明的进一步改进,所述胶粘剂制品中第一胶粘剂层和第二胶粘剂层均由所述胶粘剂涂布而成。
作为本发明的进一步改进,所述胶粘剂层干胶厚度为55-65μm。
作为本发明的进一步改进,所述胶粘剂制品180°剥离力不小于1.2kg。
与现有技术相比,本发明的有益效果是:
本发明中光伏组件贴合胶粘剂制品能够很好的贴合于光伏组件边缘,能实现良好的贴合功能,并且具备优良的抗UV老化性能、密封性、耐磨性、耐水性、耐温性。
附图说明
图1为本发明光伏组件贴合胶粘剂制品结构示意图;
图2为本发明实施方式中湿热实验进程图;
图3为本发明实施方式中热循环实验进程图;
图4为本发明实施方式中湿冻实验进程图。
具体实施方式
下面通过具体实施方式来对本发明进行进一步的阐述:
本实施方式提供了一种一种胶粘剂,其特征在于按重量计包括以下组分,
90-95%聚丙烯酸酯聚合物,
1-3%交联剂,
0.5-3%抗氧剂,
0.1-1%光稳定剂。
所述交联剂为金属盐类交联剂,包括氧化锌、氧化铅、氧化镁中的一种或多种。
所述抗氧剂包括主抗氧剂和辅助抗氧剂两种,主抗氧剂为四[甲基-β-(3,5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯和三(2,4-二叔丁基苯基)亚磷酸酯中的一种或者多种;辅助抗氧剂为硫代二丙酸双酯类中的一种或几种。
所述光稳定剂包括丁二酸与(4-羟基-2,2,6,6-四甲基-1-哌啶醇的聚合物)、双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯或者双(3,5-二叔丁基-4羟基苄基磷酸单乙酯)镍中的一种或者多种。
本实施方式还提供一种胶粘剂制品(如图1),所述胶粘剂制品自其一侧至另一侧依次包括离型层、第一胶粘剂层、泡沫层、第二胶粘剂层、载体层,所述胶粘剂制品中第一胶粘剂层和第二胶粘剂层均由所述胶粘剂涂布而成。所述胶粘剂层干胶厚度为55-65μm,所述胶粘剂制品180°剥离力不小于1.2kg。
该胶粘剂制品的制备工艺,具体包括以下步骤:
a、将离型层、泡沫层、载体层材料进行电晕预处理,
b、将涂布机烤箱干燥温度设定在60~110℃,并将此温度设定成6~8段不同的干燥区域,
c、将载体层经过电晕处理的表面涂布胶粘剂,然后将其经过烤箱烘干,再将其涂布有胶粘剂的表面贴合转移至泡沫层的一面上,并与离型层一起完成收卷,组成复合基材层,
d、在离型层一面上涂布胶粘剂,然后将其经过烤箱烘干,再将其涂布有胶粘剂的表面贴合于泡沫层的另一面上,并与复合基材层一起完成收卷。
其中,步骤c中收卷的机速为20~50m/min,步骤d中收卷的机速为10~30m/min。
为了更好的体现本发明的有益效果,下面通过具体实验来作进一步验证。
验证实施例:
耐水实验:
将本发明胶粘剂胶带贴合于光伏组件边缘,随后将光伏组件整体放置于水中,水温为常温,浸泡时间不低于360h,然后观察是否有水汽进入光伏组件内部,初步验证组件的密封性。
湿热实验:
将经过耐水实验的光伏组件进行湿热实验,随后先将光伏组件放置于温度为85℃、湿度85%±5%的环境中至少1200小时,湿热实验进程图参图2。
热循环实验:
将经过湿热实验的光伏组件进行热循环实验,环境初始温度设置为25℃,然后迅速降温至-40℃,降温速率为0~-100℃/h,保持-40℃至少10min,随后升温至85℃,升温速率为0~100℃/h,保持85℃至少10min,接着再降温至-40℃,降温速率为0~-100℃/h,保持-40℃至少10min,然后再升温至85℃,升温速率为0~100℃/h,保持85℃至少10min,如此循环至6h为热循环一次,连续重复热循环200次,热循环实验进程图参图3。
湿冻实验:
将讲过热循环实验的光伏组件进行湿冻实验,环境初始温度设置为0℃,湿度控制在85%±5%,然后升温至85℃,升温速率为0~100℃/h,保持85℃至少20h,然后降温至-40℃,降温速率为0~-200℃/h,保持-40℃不超过4h,整个过程不超过24h,接着重复循环至少10次,湿冻实验进程图参图4。
抗UV老化实验:
将经过湿冻实验的光伏组件进行抗UV老化实验,将实验环境光波波长设置在280nm~385nm范围之内,辐射强度设置在15kWh/m2,其中280nm~320nm的紫外光辐射强度不低于5kWh/m2,辐射时间不低于168h。
在经过耐水实验之后,将胶粘剂制品从光伏组件上剥离,然后观察光伏组件内发现并没有出现水汽,即证明本发明胶粘剂制品具备优良的密封耐水性能。
在经过湿热实验、热循环实验、湿冻实验以及抗UV老化实验之后,将贴合于光伏组件边缘的进行观察,经目测观察,本发明光伏组件贴合胶带依旧完整牢固的贴合于光伏组件边缘,没有出现裂痕、翘起、脱落的现象,由此可见,本发明提供的光伏组件贴合胶带能够在恶劣环境之下具备优良的使用效果,具备优良的密封性、耐磨性、耐水性、耐温性、抗UV老化实验。
应当理解,虽然本说明书按照实施方式加以描述,但并非每个实施方式仅包含一个独立的技术方案,说明书的这种叙述方式仅仅是为清楚起见,本领域技术人员应当将说明书作为一个整体,各实施方式中的技术方案也可以经适当组合,形成本领域技术人员可以理解的其他实施方式。
上文所列出的一系列的详细说明仅仅是针对本发明的可行性实施方式的具体说明,它们并非用以限制本发明的保护范围,凡未脱离本发明技艺精神所作的等效实施方式或变更均应包含在本发明的保护范围之内。
Claims (9)
1.一种胶粘剂,其特征在于按重量计包括以下组分,
90-95%聚丙烯酸酯聚合物,
1-3%交联剂,
0.5-3%抗氧剂,
0.1-1%光稳定剂。
2.根据权利要求1所述的胶粘剂,其特征在于:所述交联剂为金属氧化物类交联剂,包括氧化锌、氧化铅、氧化镁中的一种或多种。
3.根据权利要求1所述的胶粘剂,其特征在于:所述抗氧剂包括主抗氧剂和辅助抗氧剂两种,主抗氧剂为四[甲基-β-(3,5-二叔丁基-4-羟基苯基)丙酸酯]季戊四醇酯、β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯和三(2,4-二叔丁基苯基)亚磷酸酯中的一种或者多种;辅助抗氧剂为硫代二丙酸双酯类中的一种或几种。
4.根据权利要求1所述的胶粘剂,其特征在于:所述光稳定剂包括丁二酸与(4-羟基-2,2,6,6-四甲基-1-哌啶醇的聚合物)、双(2,2,6,6-四甲基-4-哌啶基)癸二酸酯或者双(3,5-二叔丁基-4羟基苄基磷酸单乙酯)镍中的一种或者多种。
5.一种胶粘剂制品,包括如权利要求1所述的胶粘剂涂布而成的胶粘剂层。
6.根据权利要求5所述的胶粘剂制品,其特征在于:所述胶粘剂制品自其一侧至另一侧依次包括离型层、第一胶粘剂层、泡沫层、第二胶粘剂层、载体层。
7.根据权利要求6所述的胶粘剂制品,其特征在于:所述胶粘剂制品中第一胶粘剂层和第二胶粘剂层均由所述胶粘剂涂布而成。
8.根据权利要求5所述的胶粘剂制品,其特征在于:所述胶粘剂层干胶厚度为55-65μm。
9.根据权利要求5所述的胶粘剂制品,其特征在于:所述胶粘剂制品180°剥离力不小于1.2kg。