CN105218140A - A kind of ventilative upper water flowerpot and material thereof and preparation method - Google Patents
A kind of ventilative upper water flowerpot and material thereof and preparation method Download PDFInfo
- Publication number
- CN105218140A CN105218140A CN201510636315.XA CN201510636315A CN105218140A CN 105218140 A CN105218140 A CN 105218140A CN 201510636315 A CN201510636315 A CN 201510636315A CN 105218140 A CN105218140 A CN 105218140A
- Authority
- CN
- China
- Prior art keywords
- flowerpot
- upper water
- ventilative
- cement
- ventilative upper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of ventilative upper water flowerpot and material thereof and preparation method, described preparation method is, by get and get cement 100 parts according to parts by weight, perlite 10-20 part, cement blowing agent 5-7 part, water 50-70 part and anti-crack fiber 2-5 part, for subsequent use; By water intaking and cement blowing agent be placed in container, puddle evenly, after having a large amount of foam to occur, add cement and perlite, after again stirring 15-20min, add anti-crack fiber, stir 5-20 minute, obtain mixture I, be the material for ventilative upper water flowerpot.Take the material in ventilative upper water flowerpot, be placed in mould and make flowerpot, namely obtain ventilative upper water flowerpot.Flowerpot of the present invention meet ventilative needs, there is certain upper water function, and can from draining.
Description
Technical field
The present invention relates to a kind of flowerpot, specifically a kind of ventilative upper water flowerpot and material thereof and preparation method.
Background technology
Along with improving constantly of living standards of the people, the requirement of people to quality of life is also more and more higher, all wants to enjoy green living, but due to the quickening of work rhythm and the increase of operating pressure, has no time to take quality of life into account.Potted plant more and more receives an acclaim.Normal flower pot material be generally pottery, porcelain, watt, plastics etc., it is ventilative, drainage performance is poor, needs bottom opening etc., but is difficult to avoid spending soil to outflow with water, and especially supports family room in and plants, cause environmental pollution, should not health.The flowerpot (CN86207239) that a kind of permeability of patent is good is flowerpot wall hollow out, the tubular cloth back boxing that inner side chemical fiber cloth or glasscloth are manufactured, and increases ventilation property.Production cost is higher, needs to regularly replace back boxing.Mostly what other was similar is also adopt the absorbent articles such as cotton strap from upper water flowerpot, automatically can supplement plant water sources.But how simultaneously can not meet infiltration and upper water, and ventilative function.
Summary of the invention
The present invention seeks to the deficiency for solving the problems of the technologies described above, a kind of ventilative upper water flowerpot and material thereof and preparation method be provided, this flowerpot meet ventilative needs, there is certain upper water function, and can from draining.
The present invention for solving the problems of the technologies described above adopted technical scheme is:
For a preparation method for the material of ventilative upper water flowerpot, comprise the following steps:
Step one, get cement 100 parts according to parts by weight, perlite 10-20 part, cement blowing agent 5-7 part, water 50-70 part and anti-crack fiber 2-5 part, for subsequent use;
Step 2, by water intaking and cement blowing agent be placed in container, puddle evenly, after having a large amount of foam to occur, add cement and perlite, after again stirring 15-20min, add anti-crack fiber, stir 5-20 minute, obtain mixture I, be the material for ventilative upper water flowerpot.
Utilize described material to prepare the method for ventilative upper water flowerpot, take the material in ventilative upper water flowerpot, be placed in mould and make flowerpot, namely obtain ventilative upper water flowerpot.Flowerpot mouth diameter is greater than 20cm, fills rack and reinforce in flowerpot wall.
Beneficial effect is:
The present invention adopts a kind of porousness composite, meets the ventilative needs of flowerpot, and has certain upper water function, and can accomplish from drain function, can realize the unattended and automatic irrigation of short-term.This design can also further genralrlization to the potted plant crop in industrialized agriculture, promote the development of industrialized agriculture, provide a new thinking to installment agriculture growth.The ventilative upper water flowerpot of this invention, automatically fills with draining, has practicality, saves time, the laborsaving and advantage of saving worry, and obviously reducing family potted plant plant need water water problems at regular time and quantity, facilitates the realization that family afforests and beautifies.
Accompanying drawing explanation
Fig. 1 is the photo figure of the ventilative upper water flowerpot prepared by the present invention;
Fig. 2 this patent is breathed freely the section amplification figure of upper water flowerpot.
Embodiment
For a preparation method for the material of ventilative upper water flowerpot, comprise the following steps:
Step one, get cement 100 parts according to parts by weight, perlite 10 parts, cement blowing agent 5 parts, 50 parts, water and anti-crack fiber 2 parts, for subsequent use;
Step 2, by water intaking and cement blowing agent be placed in container, puddle evenly, after having a large amount of foam to occur, add cement and perlite, after again stirring 15min, add anti-crack fiber, stir 5 minutes, obtain mixture I, be the material for ventilative upper water flowerpot.
Utilize described material to prepare the method for ventilative upper water flowerpot, take the material in ventilative upper water flowerpot, be placed in mould and make flowerpot, namely obtain ventilative upper water flowerpot.Flowerpot mouth diameter is greater than 20cm, fills rack and reinforce in flowerpot wall.
embodiment 1
For a preparation method for the material of ventilative upper water flowerpot, comprise the following steps:
Step one, get cement 100 parts according to parts by weight, perlite 20 parts, cement blowing agent 7 parts, 70 parts, water and anti-crack fiber 5 parts, for subsequent use;
Step 2, by water intaking and cement blowing agent be placed in container, puddle evenly, after having a large amount of foam to occur, add cement and perlite, after again stirring 20min, add anti-crack fiber, stir 20 minutes, obtain mixture I, be the material for ventilative upper water flowerpot.
Utilize described material to prepare the method for ventilative upper water flowerpot, take the material in ventilative upper water flowerpot, be placed in mould and make flowerpot, namely obtain ventilative upper water flowerpot.Flowerpot mouth diameter is greater than 20cm, fills rack and reinforce in flowerpot wall.
embodiment 2
For a preparation method for the material of ventilative upper water flowerpot, comprise the following steps:
Step one, get cement 100 parts according to parts by weight, perlite 20 parts, cement blowing agent 7 parts, water 50-70 part and anti-crack fiber 5 parts, for subsequent use;
Step 2, by water intaking and cement blowing agent be placed in container, puddle evenly, after having a large amount of foam to occur, add cement and perlite, after again stirring 20min, add anti-crack fiber, stir 5-20 minute, obtain mixture I, be the material for ventilative upper water flowerpot.
Utilize described material to prepare the method for ventilative upper water flowerpot, take the material in ventilative upper water flowerpot, be placed in mould and make flowerpot, namely obtain ventilative upper water flowerpot.Flowerpot mouth diameter is greater than 20cm, fills rack and reinforce in flowerpot wall.
embodiment 3
For a preparation method for the material of ventilative upper water flowerpot, comprise the following steps:
Step one, get cement 100 parts according to parts by weight, perlite 15 parts, cement blowing agent 6 parts, 60 parts, water and anti-crack fiber 4 parts, for subsequent use;
Step 2, by water intaking and cement blowing agent be placed in container, puddle evenly, after having a large amount of foam to occur, add cement and perlite, after again stirring 15-20min, add anti-crack fiber, stir 5-20 minute, obtain mixture I, be the material for ventilative upper water flowerpot.
Utilize described material to prepare the method for ventilative upper water flowerpot, take the material in ventilative upper water flowerpot, be placed in mould and make flowerpot, namely obtain ventilative upper water flowerpot.Flowerpot mouth diameter is greater than 20cm, fills rack and reinforce in flowerpot wall.
Claims (3)
1., for a preparation method for the material of ventilative upper water flowerpot, it is characterized in that: comprise the following steps:
Step one, get cement 100 parts according to parts by weight, perlite 10-20 part, cement blowing agent 5-7 part, water 50-70 part and anti-crack fiber 2-5 part, for subsequent use;
Step 2, by water intaking and cement blowing agent be placed in container, puddle evenly, after having a large amount of foam to occur, add cement and perlite, after again stirring 15-20min, add anti-crack fiber, stir 5-20 minute, obtain mixture I, be the material for ventilative upper water flowerpot.
2. utilize the method for the ventilative upper water flowerpot of material preparation described in claim 1, it is characterized in that: take the material in ventilative upper water flowerpot, be placed in mould and make flowerpot, namely obtain ventilative upper water flowerpot.
3. the ventilative upper water flowerpot prepared by method of upper water flowerpot as ventilative in claim 2 preparation, is characterized in that: flowerpot mouth diameter is greater than 20cm, fills rack reinforcing in flowerpot wall.