CN105206184A - 用于显示装置的覆盖窗、包括该覆盖窗的显示装置以及制造该覆盖窗的方法 - Google Patents

用于显示装置的覆盖窗、包括该覆盖窗的显示装置以及制造该覆盖窗的方法 Download PDF

Info

Publication number
CN105206184A
CN105206184A CN201510354072.0A CN201510354072A CN105206184A CN 105206184 A CN105206184 A CN 105206184A CN 201510354072 A CN201510354072 A CN 201510354072A CN 105206184 A CN105206184 A CN 105206184A
Authority
CN
China
Prior art keywords
initiating agent
coating composition
agent based
iodine
display device
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510354072.0A
Other languages
English (en)
Other versions
CN105206184B (zh
Inventor
郑镛铁
南承郁
任志爀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Samsung Display Co Ltd
Original Assignee
Samsung Display Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Samsung Display Co Ltd filed Critical Samsung Display Co Ltd
Publication of CN105206184A publication Critical patent/CN105206184A/zh
Application granted granted Critical
Publication of CN105206184B publication Critical patent/CN105206184B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本申请涉及覆盖窗、显示装置以及制造覆盖窗的方法，所述覆盖窗包括基膜；以及在所述基膜上的涂层，其中通过涂覆涂料组合物来形成所述涂层，所述涂料组合物包含基于碘的引发剂和基于硼酸的引发剂中的至少一种。

Description

用于显示装置的覆盖窗、包括该覆盖窗的显示装置以及制造该覆盖窗的方法
相关申请的交叉引用
于2014年6月24日向韩国知识产权局提交并且名称为“用于显示装置的覆盖窗、包括该覆盖窗的显示装置以及制造该覆盖窗的方法”的第10-2014-0077608号韩国专利申请通过引用整体并入本文。
技术领域
实施方案涉及用于显示装置的窗、包括该窗的显示装置以及制造用于显示装置的窗的方法。
背景技术
移动电子装置包括移动电话、导航***、数码相机、电子书、便携式游戏机及各种终端机。移动电子装置可以包括用作显示装置的液晶显示器(LCD)或有机发光二极管(OLED)显示器。
用于此类移动电子装置的显示装置可以具有透明的窗，该窗设置在显示面板的前面并且使用者通过该窗可以看到显示单元。可以在装置的最外面的位置处形成窗，并且该窗可以抵抗外部冲击以保护显示装置内的显示面板。
在本背景技术部分中公开的上述信息仅用于增强对本发明的背景的理解，并因此其可能包括不构成本领域普通技术人员在本国已知的现有技术的信息。
发明内容
实施方案涉及用于显示装置的窗、包括该窗的显示装置以及制造用于显示装置的窗的方法。
实施方案可以通过提供覆盖窗而实现，所述覆盖窗包括基膜；以及在所述基膜上的涂层，其中所述涂层通过涂覆涂料组合物而形成，所述涂料组合物包含基于碘的引发剂和基于硼酸的引发剂中的至少一种。
所述涂料组合物还可以包含单体和溶剂。
所述单体可以包括由式1表示的化合物：
其中，在式1中，R可以为CH3，并且R'可以为含环氧基的基团。
所述涂料组合物可以包含基于碘的引发剂，所述基于碘的引发剂包括由式2表示的化合物：
所述涂料组合物可以包含基于硼酸的引发剂，所述基于硼酸的引发剂包括由式3表示的化合物：
所述涂料组合物可以包含基于碘的引发剂，所述基于碘的引发剂为光硬化的引发剂。
所述涂料组合物可以包含基于硼酸的引发剂，所述基于硼酸的引发剂为光硬化和热硬化的引发剂。
基于所述涂料组合物的总重量，所述基于碘的引发剂和所述基于硼酸的引发剂中的至少一种可以以约0.5重量％至约8.0重量％的量包含在所述涂料组合物中。
基于所述涂料组合物的总重量，所述单体可以以约40重量％至约90重量％的量包含在所述涂料组合物中。
所述溶剂可以包括甲基乙基酮。
实施方案可以通过提供显示装置而实现，所述显示装置包括显示面板；以及在所述显示面板上的覆盖窗，其中所述覆盖窗包括基膜以及在所述基膜上的涂层，所述涂层通过涂覆涂料组合物而形成，所述涂料组合物包含基于碘的引发剂和基于硼酸的引发剂中的至少一种。
所述涂料组合物还可以包含单体和溶剂。
所述单体可以包括由式1表示的化合物：
其中，在式1中，R可以为CH3，并且R'可以为含环氧基的基团。
所述涂料组合物可以包含基于碘的引发剂，所述基于碘的引发剂包括由式2表示的化合物：
所述涂料组合物可以包含基于硼酸的引发剂，所述基于硼酸的引发剂包括由式3表示的化合物：
所述涂料组合物可以包含基于碘的引发剂，所述基于碘的引发剂为光硬化的引发剂。
所述涂料组合物可以包含基于硼酸的引发剂，所述基于硼酸的引发剂为光硬化和热硬化的引发剂。
所述基于碘的引发剂和所述基于硼酸的引发剂中的至少一种可以以约0.5重量％至约8.0重量％的量包含在所述涂料组合物中，并且所述单体可以以约40重量％至约90重量％的量包含在所述涂料组合物中，所有重量％均基于所述涂料组合物的总重量。
实施方案可以通过提供制造覆盖窗的方法而实现，所述方法包括提供基膜；在所述基膜上涂覆涂料组合物；干燥并硬化所述涂料组合物；以及将所述硬化的涂料组合物退火。
所述退火可以在与提供所述基膜、在所述基膜上涂覆所述涂料组合物、或干燥并硬化所述涂料组合物时的湿度相同的湿度下进行。
附图说明
通过参考附图详细描述示例性实施方案，特征对于本领域技术人员而言会是显而易见的，其中：
图1示出根据示例性实施方案的显示装置的分解透视图。
图2示出根据示例性实施方案的覆盖窗的横截面视图。
图3示出根据示例性实施方案的覆盖窗的制造过程中的阶段。
图4示出示例性实施方案和比较例的黄化指数图。
图5示出示例性实施方案和比较例的黄化指数图。
具体实施方式
现在将参考附图在下文中更全面地描述示例实施方案，然而，它们可以以不同的形式实施，并且不应解释为局限于本文所述的实施方案。相反，提供这些实施方案，以使得本公开将变得全面和完整，并且将向本领域技术人员完整地表达示例性实施。
在附图中，为了例示清楚，可以放大层和区域的尺寸。全文中相同的参考数字指代相同的元件。
应理解，当诸如层、膜、区域或衬底的元件被称为在另一元件“上”时，其可以直接在其他元件上或还可以存在中介元件。相反，当元件被称为“直接在”另一元件“上”时，不存在中介元件。
首先，将参考图1描述根据示例性实施方案的显示装置。
图1示出根据示例性实施方案的显示装置的分解透视图。
参考图1，根据示例性实施方案的显示装置100可以包括显示面板10(用于显示图像)和在显示面板10的前侧上并保护显示面板10的覆盖窗20。
在实施中，显示面板10可以为有机发光面板。在另一实施中，显示面板10可以为另一类型的显示器，例如液晶显示器(LCD)，并且显示面板10可以为包括下衬底、场发生电极和液晶层而不包括单独的上衬底的显示面板。在本示例性实施方案中，为了便于描述，描述有机发光面板作为实例。
显示面板10可以通过柔性印刷电路30与印刷电路板(PCB)50电连接。
像素，例如用于表达图像的基础单元，可以以矩阵形式布置在显示面板10的第一衬底13上，并且第二衬底14可以通过密封件(未示出)与第一衬底13结合以保护像素。第一衬底13可以为后衬底，并且第二衬底14可以为前衬底。
例如，在有源矩阵有机发光显示面板中，每一像素可以包括有机发光元件(未示出)和驱动该有机发光元件的驱动电路单元(未示出)，所述有机发光元件包括阳极电极、有机发光层和阴极电极。驱动电路单元可以为薄膜晶体管(TFT)。数据线可以连接至该TFT的源端子，并且栅极线可以连接至该TFT的栅端子。有机发光元件的阳极电极和阴极电极中的任一个可以连接至该TFT的漏端子。
数据线和栅极线可以通过柔性印刷电路30连接至PCB50。当电信号通过PCB50输入至TFT的源端子和栅端子时，该TFT可以根据信号输入而打开或关闭，从而向漏端子输出用于驱动像素的电信号。
集成电路(IC)芯片26可以安装在第一衬底13上，以控制显示面板10。IC芯片26可以生成定时信号以采用合适的定时施加数据驱动信号和栅极驱动信号。IC芯片26可以分别向显示面板10的数据线和栅极线施加所产生的定时信号。可以在IC芯片26周围形成保护层25以保护IC芯片26。
用于处理驱动信号的电子元件(未示出)可以安装在PCB50上。PCB50可以包括连接器51和延伸部件52。延伸部件52可以安装在连接器51的一端以向PCB50传输外部信号。
覆盖窗20(保护显示面板10)可以位于显示面板10的前面。覆盖窗20可以保护显示面板10，以使显示面板10不会由于例如外部冲击而破碎。覆盖窗20可以通过粘合层(未示出)而连接至显示面板10。在实施中，显示面板10和覆盖窗20可以被形成为利用在二者之间形成的空气层彼此间隔开。
覆盖窗20可以包括基膜21和在基膜21上的涂层22。
基膜21可以包括：透明部分211，其在对应于或覆盖显示面板10的显示单元11的区域中，以使显示单元11对于外部是可见的；以及不透明部分212，其在对应于或覆盖显示面板10的非显示部分12的区域中，以防止非显示部分12对于外部是可见的。不透明部分212可以遮盖在显示面板10的非显示部分12中的布线、组件等，以使它们对于外部是不可见的。不透明部分212可以包括例如产品的标识、装饰图案等。在实施中，基膜21可以包括透明部分211和不透明部分212，或者基膜21可以仅包括透明部分211。
基膜21可以由例如聚对苯二甲酸乙二醇酯(PET)、三乙酰纤维素(TAC)、聚酰亚胺(PI)、聚碳酸酯(PC)、热塑性聚氨酯(TPU)或硅橡胶制成。
可以通过在基膜21上涂覆并硬化涂料组合物来形成涂层22。根据示例性实施方案的涂层22可以具有高于预定程度的硬度，由此减少可能在涂层22中由UV产生或响应于UV而产生的黄化现象。下文将描述涂层22。
根据本示例性实施方案的显示装置100可以由能够弯曲的材料形成。例如，显示装置100可以沿着线A-A弯曲，并由此覆盖窗20也可以沿着线A-A弯曲。
接下来，将参考图2来描述根据示例性实施方案的显示装置100的覆盖窗20。
图2示出根据示例性实施方案的覆盖窗20的横截面视图。如图2所示，覆盖窗20可以包括基膜21和在基膜21上的涂层22。
在实施中，涂层22可以仅在基膜21上，或者任何形状的覆盖窗是可能的。例如，在本说明书中描述的构造可以包括涂膜、基膜以及粘合涂膜和基膜的粘合层。
可以通过在基膜21上涂覆并硬化涂料组合物来形成根据示例性实施方案的涂层22。
根据示例性实施方案的涂料组合物可以包含单体、引发剂和溶剂。
根据示例性实施方案的单体可以是作为有机-无机杂化材料的杂化物(hybrimer)。在实施中，单体可以包括由以下式1表示的化合物。
在式1中，R可以为CH3，并且R'可以为含环氧基的基团。R'的环氧基可以是开环的，并且可以通过开环的环氧基来实现交联。
基于涂料组合物的总重量，单体可以以约40重量％至约90重量％、例如约60重量％的量包含在该涂料组合物中。
根据示例性实施方案的涂料组合物可以包含引发剂，例如可以包含基于碘的引发剂和基于硼酸的引发剂中的至少一种。
在实施中，基于碘的引发剂可以包括由以下式2表示的化合物。在实施中，基于硼酸的引发剂可以包括由以下式3表示的化合物。
基于碘的引发剂可以为光硬化的。基于硼酸的引发剂可以为光硬化和热硬化的。例如，引发剂可以在形成涂层的过程中由光或热来活化，并且单体可以通过活化的引发剂而聚合。
引发剂可以以约0.5重量％至约8.0重量％、例如约2重量％的量包含在涂料组合物中。以所述的量包含引发剂可以有助于确保适当地控制对光或热的反应速率。
根据示例性实施方案的溶剂可以包括例如甲基乙基酮(MEK)。
由所述涂料组合物形成的涂层22可以不仅具有适于显示装置的外表面的硬度，而且还可以有助于减少和/或防止由长时间暴露于UV而产生的黄化现象。例如，可以改善覆盖窗的可靠性和耐久性。
图3示出根据示例性实施方案的覆盖窗的制造过程中的阶段。
首先，可以通过使用例如聚对苯二甲酸乙二醇酯(PET)、三乙酰纤维素(TAC)、聚酰亚胺(PI)、聚碳酸酯(PC)、热塑性聚氨酯(TPU)或硅橡胶来形成基膜21。
接下来，用于形成涂层22的涂料组合物可以被涂覆在基膜21上，并且可以随后通过加热而干燥，然后可以通过照射UV而硬化。
接下来，可以在硬化的涂料组合物上进行退火过程以形成涂层22。此处，如果退火过程不需要额外的高湿度条件，则退火过程可以在常见的湿度条件中进行。例如，退火过程可以在与先前进行的步骤(例如涂覆、干燥和/或UV硬化)时的湿度条件相同的湿度条件下(在相同的湿度下)进行。因此，可以通过与所述涂料组合物的涂覆和干燥的过程相同的(单动式)设备来制造涂层。根据该制造过程，可以有利地降低制造时间和成本。
提供下列实施例和比较例以突出一个或多个实施方案的特征，但应理解，实施例和比较例不应解释为限制实施方案的范围，并且比较例不应解释为在实施方案的范围之外。此外，应理解实施方案不限于在实施例和比较例中描述的特定细节。
接下来，将参考图4和图5来描述实施例和比较例的黄化指数。图4的图基于以下表1，并且图5的图基于以下表2。
首先，参考图4和表1，使用包含基于碘的引发剂的涂料组合物形成根据实施例的涂层，并且使用包含基于硫的引发剂的涂料组合物形成比较例的涂层。
对于比较例的包含基于硫的引发剂的涂层，作为通过微分在涂料组合物中包含的引发剂的含量来检查黄化指数(ΔYI)的结果，随着引发剂的含量增加，明显出现黄化现象。当包含最低含量时，可看到出现了黄化指数为约1.53的程度。
相反，对于使用包含基于碘的引发剂的涂料组合物制备的涂层，根据引发剂含量的黄化指数的变化程度小。例如，其中出现最大值的黄化指数的情况(引发剂含量为8重量％)与比较例的最低指数值的情况(引发剂的含量为0.5重量％)相似。
例如，当包含根据示例性实施方案的基于碘的引发剂时，可看到由UV导致的黄化现象可以显著减少。
表1
接下来，参考表2和图5，比较例是其中由包含基于硫的引发剂的涂料组合物制备涂层的情况，并且实施例1是其中由包含基于碘的引发剂的涂料组合物制备涂层的情况。实施例2是其中由包含基于硼酸的引发剂的涂料组合物制备涂层的情况，并且实施例3是其中由包含基于碘的引发剂和基于硼酸的引发剂的涂料组合物制备涂层的情况。
表2
参考表2和图5，与比较例相比，可看到根据实施例的涂层的黄化指数显著降低。例如，当包含基于碘的引发剂或基于硼酸的引发剂时，可以减少和/或防止由UV造成的涂层的黄化现象。
如表2所示，在其中涂料组合物仅包含基于碘的引发剂的实施例1中，硬度可能稍微降低。如在其中涂料组合物包含基于硼酸的引发剂的实施例2和实施例3中所示，可以提供预定程度的硬度，由此通过控制基于硼酸的引发剂的含量来控制硬度以及黄化的可靠性。
通过总结和回顾，结构可以采用具有在其中集成的显示屏的触摸面板。因此，窗的表面与根据相关领域的移动装置相比可能更频繁地与手指等接触，并且窗可能需要更高的强度。
最近，已经考虑柔性装置，并且应用于显示装置的覆盖窗可以由具有柔性的构件制成，以使其可以弯曲。
实施方案可以提供用于显示装置的覆盖窗，其有助于减少和/或防止黄化现象，并且在弯曲时具有比预定程度更大的表面硬度。
例如，通过在基膜上形成根据实施方案的涂层，覆盖窗可以有助于抑制黄化现象，同时还具有预定程度的表面硬度。
根据示例性实施方案的涂层可以不仅具有适于显示装置的外表面的硬度，而且还可以减少和/或防止当长时间暴露于UV时产生的黄化现象，由此提供具有改善的可靠性和耐久性的覆盖窗。
本文已经公开了示例实施方案，并且尽管使用具体术语，但它们仅应以上位且描述性含义来使用和解释，并且不用于限定的目的。在一些情形中，如自提交本申请起本领域技术人员所显而易见的，对于特定实施方案而描述的特征、特性和/或元件可以单独使用或与对于其他实施方案而描述的特征、特性和/或元件组合使用，除非另外具体指明。因此，本领域技术人员应理解在不背离权利要求所述的本发明的精神和范围的情况下，可以进行形式和细节的各种改变。
符号说明
10:显示面板
20:覆盖窗
21:基膜
22:涂层
30:柔性印刷电路
50:印刷电路板(PCB)

Claims (20)

1.覆盖窗，其包括：
基膜；以及
在所述基膜上的涂层，
其中所述涂层通过涂覆涂料组合物而形成，所述涂料组合物包含基于碘的引发剂和基于硼酸的引发剂中的至少一种。
2.如权利要求1所述的覆盖窗，其中所述涂料组合物还包含：
单体，和
溶剂。
3.如权利要求2所述的覆盖窗，其中所述单体包括由式1表示的化合物：
其中，在式1中，R为CH3，并且R'为含环氧基的基团。
4.如权利要求1所述的覆盖窗，其中所述涂料组合物包含所述基于碘的引发剂，所述基于碘的引发剂包括由式2表示的化合物：
5.如权利要求1所述的覆盖窗，其中所述涂料组合物包含所述基于硼酸的引发剂，所述基于硼酸的引发剂包括由式3表示的化合物：
6.如权利要求1所述的覆盖窗，其中所述涂料组合物包含所述基于碘的引发剂，所述基于碘的引发剂为光硬化的引发剂。
7.如权利要求1所述的覆盖窗，其中所述涂料组合物包含所述基于硼酸的引发剂，所述基于硼酸的引发剂为光硬化和热硬化的引发剂。
8.如权利要求2所述的覆盖窗，其中基于所述涂料组合物的总重量，所述基于碘的引发剂和所述基于硼酸的引发剂中的至少一种以0.5重量％至8.0重量％的量包含在所述涂料组合物中。
9.如权利要求2所述的覆盖窗，其中基于所述涂料组合物的总重量，所述单体以40重量％至90重量％的量包含在所述涂料组合物中。
10.如权利要求2所述的覆盖窗，其中所述溶剂包括甲基乙基酮。
11.显示装置，其包括：
显示面板；以及
在所述显示面板上的覆盖窗，其中所述覆盖窗包括：
基膜，以及
在所述基膜上的涂层，所述涂层通过涂覆涂料组合物而形成，所述涂料组合物包含基于碘的引发剂和基于硼酸的引发剂中的至少一种。
12.如权利要求11所述的显示装置，其中所述涂料组合物还包含：
单体，和
溶剂。
13.如权利要求12所述的显示装置，其中所述单体包括由式1表示的化合物：
其中，在式1中，R为CH3，并且R'为含环氧基的基团。
14.如权利要求11所述的显示装置，其中所述涂料组合物包含所述基于碘的引发剂，所述基于碘的引发剂包括由式2表示的化合物：
15.如权利要求11所述的显示装置，其中所述涂料组合物包含所述基于硼酸的引发剂，所述基于硼酸的引发剂包括由式3表示的化合物：
16.如权利要求11所述的显示装置，其中所述涂料组合物包含所述基于碘的引发剂，所述基于碘的引发剂为光硬化的引发剂。
17.如权利要求11所述的显示装置，其中所述涂料组合物包含所述基于硼酸的引发剂，所述基于硼酸的引发剂为光硬化和热硬化的引发剂。
18.如权利要求12所述的显示装置，其中：
所述基于碘的引发剂和所述基于硼酸的引发剂中的至少一种以0.5重量％至8.0重量％的量包含在所述涂料组合物中，以及
所述单体以40重量％至90重量％的量包含在所述涂料组合物中，所有重量％均基于所述涂料组合物的总重量。
19.制造覆盖窗的方法，所述方法包括：
提供基膜；
在所述基膜上涂覆涂料组合物；
干燥并硬化所述涂料组合物；以及
将所述硬化的涂料组合物退火。
20.如权利要求19所述的方法，其中所述退火在与提供所述基膜、在所述基膜上涂覆所述涂料组合物、或干燥并硬化所述涂料组合物时的湿度相同的湿度下进行。
CN201510354072.0A 2014-06-24 2015-06-24 用于显示装置的覆盖窗、包括该覆盖窗的显示装置以及制造该覆盖窗的方法 Active CN105206184B (zh)