CN105199578B - The upper color technique of color calligraphy and painting on a kind of cinnabar - Google Patents
The upper color technique of color calligraphy and painting on a kind of cinnabar Download PDFInfo
- Publication number
- CN105199578B CN105199578B CN201510650411.XA CN201510650411A CN105199578B CN 105199578 B CN105199578 B CN 105199578B CN 201510650411 A CN201510650411 A CN 201510650411A CN 105199578 B CN105199578 B CN 105199578B
- Authority
- CN
- China
- Prior art keywords
- cinnabar
- parts
- color
- painting
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The upper color technique of color calligraphy and painting on a kind of cinnabar provided by the invention, including portrayed specific figure, aqua calcis rinses, clear water cleaning, color and baking step on cinnabar coating.By using the upper color technique of color calligraphy and painting on the cinnabar, and use unique cinnabar coating, the cinnabar coating for being can be bonded on cinnabar on color calligraphy and painting well, be not in phenomena such as coming off, meanwhile to spraying the clear dope of uniqueness after coloured silk on cinnabar so that the picture is bright and new glossy, the effect of cinnabar coating is sealed simultaneously, further avoid the generation of the phenomenon of cinnabar Paint Falling.
Description
Technical field
The present invention relates to a kind of upper color technique of color calligraphy and painting on cinnabar.
Background technology
Cinnabar is mercuric sulphide, chemical name HgS；Cinnabar is also known as cinnabar, cinnabar, Chi Dan, mercury sand, is the natural of mercuric sulphide
Ore, large red, there is adamantine luster to metallic luster, belong to trigonal system.Cinnabar Main Ingredients and Appearance is mercuric sulphide, but is often mingled with hero
Huang, apatite, asphalitine etc..Color calligraphy and painting on cinnabar, using numerical controlled carving technology, works with great care, using color on first-class cinnabar
Into, color technique easily easily drops in the case of by external force on conventional cinnabar, although while cinnabar have detoxifying and anticorrosive etc. work
, human body excessively takes in cinnabar, can cause to cause hepatorenal damage, and can pass through blood-brain barrier, directly damages central nervous system
System etc., so, in colour painting on making cinnabar, it is necessary to which, in one layer of paraffin of surface smear, the effect of paraffin has so that color on cinnabar
Smooth interaction, and the effect of isolation cinnabar are drawn, but the physical arrangement stability of paraffin is bad.
The content of the invention
In order to solve the above technical problems, the invention provides a kind of upper color technique of color calligraphy and painting on cinnabar.
The present invention is achieved by the following technical programs.
The upper color technique of color calligraphy and painting on a kind of cinnabar provided by the invention, including following technique：
1) specific figure has been portrayed with Numeric Control Technology in specific stone part；
2) visuals is rinsed using the aqua calcis that pH value is 11~12, rinses 2~10min；
3) stone part after being cleaned with clear water, then dries；
4) upper coloured silk is carried out to visuals using cinnabar coating, then as in 40~45 DEG C of closed environment dry 3~
4h。
Further, described cinnabar coating is made up of the raw material of following parts by weight：80~100 parts of cinnabar powder, ripe height
5~8 parts of aluminium powder, 10~15 parts of modified Nano crystal whisker materials, polyurethane resin 3-8 parts, polytetrafluoroethylene (PTFE) 1-5 parts, zinc stearate
3-8 parts, 3~8 parts of octamethylcy-clotetrasiloxane, white oil 5-10 parts, 50~80 parts of organic solvent.
Further, the one kind or several of the solvent in alcohols, fat hydrocarbon, arene, ketone, esters solvent
Kind.
Further, after coloured silk is dried on described step 4) cinnabar, layer of transparent coating also is sprayed to Cinnabar picture, after allowing extremely
3~4h in 60~65 DEG C of closed environment.
Further, described clear dope is made up of the raw material of following parts by weight：20~30 parts of organosilicon-modified styrene-acrylics
Emulsion, 10~15 parts of triethylamines, 5~8 parts of modified Nano tin-antiomony oxides, 3~6 parts of zinc oxide, 4~7 parts of polyurethane finishing agents, 15
~25 parts of absolute ethyl alcohols.
The beneficial effects of the present invention are：By using the upper color technique of color calligraphy and painting on the cinnabar, and use uniqueness
Cinnabar coating, the cinnabar coating for being can be bonded on cinnabar on color calligraphy and painting well, be not in phenomena such as coming off, meanwhile,
Clear dope to spraying uniqueness after coloured silk on cinnabar so that the picture is bright and new glossy, while seals the effect of cinnabar coating, further
Avoid the generation of the phenomenon of cinnabar Paint Falling.
Embodiment
Be described further below technical scheme, but claimed scope be not limited to it is described.
Embodiment one
A kind of upper color technique of color calligraphy and painting on cinnabar is present embodiments provided, is comprised the following steps：
1) cinnabar coating prepares, and cinnabar coating is made up of following raw material：Cinnabar powder 80kg, ripe high-alumina fly 5kg, modification are received
It is rice crystal whisker materials 10kg, polyurethane resin 3kg, polytetrafluoroethylene (PTFE) 1kg, zinc stearate 3kg, octamethylcy-clotetrasiloxane 3kg, white
Oily 5kg, organic solvent 50kg；One kind in alcohols, fat hydrocarbon, arene, ketone, esters solvent of the solvent or
It is several, the present embodiment selection esters solvent；
2) specific figure has been portrayed with Numeric Control Technology in specific stone part；
3) visuals is rinsed using the aqua calcis that pH value is 11, rinses 2min；
4) stone part after being cleaned with clear water, then dries；
5) upper coloured silk is carried out to visuals using cinnabar coating, then as dry 3h in 40 DEG C of closed environment.
Embodiment two
A kind of upper color technique of color calligraphy and painting on cinnabar is present embodiments provided, is comprised the following steps：
1) cinnabar coating prepares, and cinnabar coating is made up of following raw material：Cinnabar powder 100kg, ripe high-alumina fly 8kg, modification
Nano crystal whisker material 15kg, polyurethane resin 8kg, polytetrafluoroethylene (PTFE) 5kg, zinc stearate 8kg, octamethylcy-clotetrasiloxane 8kg,
White oil 10kg, organic solvent 80kg；The solvent in alcohols, fat hydrocarbon, arene, ketone, esters solvent one
Kind is several, the present embodiment selection fat hydrocarbon；
2) specific figure has been portrayed with Numeric Control Technology in specific stone part；
3) visuals is rinsed using the aqua calcis that pH value is 12, rinses 10min；
4) stone part after being cleaned with clear water, then dries；
5) upper coloured silk is carried out to visuals using cinnabar coating, then as dry 4h in 45 DEG C of closed environment.
Embodiment three
A kind of upper color technique of color calligraphy and painting on cinnabar is present embodiments provided, is comprised the following steps：
1) cinnabar coating prepares, and cinnabar coating is made up of following raw material：Cinnabar powder 90kg, ripe high-alumina fly 6kg, modification are received
It is rice crystal whisker materials 12kg, polyurethane resin 5kg, polytetrafluoroethylene (PTFE) 3kg, zinc stearate 5kg, octamethylcy-clotetrasiloxane 5kg, white
Oily 8kg, organic solvent 70kg；One kind in alcohols, fat hydrocarbon, arene, ketone, esters solvent of the solvent or
It is several, the present embodiment selection alcohols, specifically chosen, ethanol；
2) specific figure has been portrayed with Numeric Control Technology in specific stone part；
3) visuals is rinsed using the aqua calcis that pH value is 11, rinses 10min；
4) stone part after being cleaned with clear water, then dries；
5) upper coloured silk is carried out to visuals using cinnabar coating, then as dry 3.5h in 43 DEG C of closed environment.
Example IV
A kind of upper color technique of color calligraphy and painting on cinnabar is present embodiments provided, is comprised the following steps：
1) cinnabar coating prepares, and cinnabar coating is made up of following raw material：Cinnabar powder 90kg, ripe high-alumina fly 6kg, modification are received
It is rice crystal whisker materials 12kg, polyurethane resin 5kg, polytetrafluoroethylene (PTFE) 3kg, zinc stearate 5kg, octamethylcy-clotetrasiloxane 5kg, white
Oily 8kg, organic solvent 70kg；One kind in alcohols, fat hydrocarbon, arene, ketone, esters solvent of the solvent or
It is several, the present embodiment selection alcohols, specifically chosen, ethanol；
2) preparation of clear dope, it is made up of raw material：20~30kg silicone modified styrene-acrylate emulsions, 10~15kg tri-
Ethamine, 5~8kg modified Nanos tin-antiomony oxide, 3~6kg zinc oxide, 4~7kg polyurethane finishing agents, 15~25kg absolute ethyl alcohols；
3) specific figure has been portrayed with Numeric Control Technology in specific stone part；
4) visuals is rinsed using the aqua calcis that pH value is 11, rinses 10min；
5) stone part after being cleaned with clear water, then dries；
6) upper coloured silk is carried out to visuals using cinnabar coating, then as dry 3.5h in 43 DEG C of closed environment；
7) on cinnabar it is color dry after, layer of transparent coating also is sprayed to Cinnabar picture, as 60~65 DEG C of closed loop after allowing
3~4h in border.
Claims (3)
- A kind of 1. upper color technique of color calligraphy and painting on cinnabar, it is characterised in that：Including following technique：1) specific figure has been portrayed with Numeric Control Technology in specific stone part；2) visuals is rinsed using the aqua calcis that pH value is 11~12, rinses 2~10min3) stone part after being cleaned with clear water, then dries；4) upper coloured silk is carried out to visuals using cinnabar coating, then as dry 3~4h in 40~45 DEG C of closed environment；Described cinnabar coating is made up of the raw material of following parts by weight：80~100 parts of cinnabar powder, ripe 5~8 parts of high-alumina fly, change 10~15 parts of nano crystal whisker material of property, polyurethane resin 3-8 parts, polytetrafluoroethylene (PTFE) 1-5 parts, zinc stearate 3-8 parts, prestox ring 3~8 parts of tetrasiloxane, white oil 5-10 parts, 50~80 parts of organic solvent.After coloured silk is dried on described step 4) cinnabar, layer of transparent coating also is sprayed to Cinnabar picture, as 60~65 DEG C after allowing 3~4h in closed environment.
- 2. the upper color technique of color calligraphy and painting on cinnabar as claimed in claim 1, it is characterised in that：The solvent is selected from alcohols, fat One or more in fat hydro carbons, arene, ketone, vinegar class solvent.
- 3. the upper color technique of color calligraphy and painting on cinnabar as claimed in claim 1, it is characterised in that：Described clear dope is by following The raw material composition of parts by weight：20~30 parts of silicone modified styrene-acrylate emulsions, 10~15 parts of triethylamines, 5~8 parts of modified Nano oxidations Tin antimony, 3~6 parts of zinc oxide, 4~7 parts of polyurethane finishing agents.