CN105199578A - Coloring technique of cinnabar colored handwriting/painting - Google Patents
Coloring technique of cinnabar colored handwriting/painting Download PDFInfo
- Publication number
- CN105199578A CN105199578A CN201510650411.XA CN201510650411A CN105199578A CN 105199578 A CN105199578 A CN 105199578A CN 201510650411 A CN201510650411 A CN 201510650411A CN 105199578 A CN105199578 A CN 105199578A
- Authority
- CN
- China
- Prior art keywords
- cinnabar
- parts
- painting
- color
- technique
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a coloring technique of a cinnabar colored handwriting/painting, which comprises the following steps: etching a specific pattern, flushing with a calcium hydroxide solution, cleaning with clear water, coloring with a cinnabar paint and drying. By using the coloring technique and unique cinnabar paint, the cinnabar paint can be well bound to the cinnabar colored handwriting/painting without shedding or the like. A unique transparent paint is sprayed after cinnabar coloring, so that the painting is bright and glossy, and the cinnabar paint is sealed, thereby further preventing the cinnabar paint from shedding.
Description
Technical field
The present invention relates to the upper color technique of color calligraphy and painting on a kind of cinnabar.
Background technology
Cinnabar and zunsober, chemical name HgS; Cinnabar is also known as cinnabar, cinnabar, Chi Dan, mercury sand, and be the natural crystal of zunsober, large red, has adamantine luster to metalluster, belongs to trigonal system.Cinnabar major ingredient is zunsober, but is often mingled with realgar, phosphatic rock, bituminous matter etc.Color calligraphy and painting on cinnabar, adopt numerical controlled carving technology, work with great care, coloured silk on first-class cinnabar is adopted to form, on conventional cinnabar, color technique is easily being subject to easily dropping in external force situation, although cinnabar has the anticorrosion effect such as grade of removing toxic substances simultaneously, human body too much takes in cinnabar, can cause causing hepatorenal damage, and can pass through hemato encephalic barrier, direct infringement central nervous system etc., so, when making colour painting on cinnabar, must at surface smear one deck paraffin, the effect of paraffin makes colour painting smooth interaction on cinnabar, and the effect of isolated cinnabar, but the physical structure stability of paraffin is bad.
Summary of the invention
For solving the problems of the technologies described above, the invention provides the upper color technique of color calligraphy and painting on a kind of cinnabar.
The present invention is achieved by the following technical programs.
The upper color technique of color calligraphy and painting on a kind of cinnabar provided by the invention, comprises following technique:
1) specific figure is portrayed in specific stone part Numeric Control Technology;
2) use pH value is the aqua calcis flushing visuals of 11 ~ 12, rinses 2 ~ 10min;
3) with stone part after clean water, then dry;
4) cinnabar coating is used to carry out upper coloured silk to visuals, then as 3 ~ 4h dry in the closed environment of 40 ~ 45 DEG C.
Further, described cinnabar coating is made up of the raw material of following weight part: cinnabar powder 80 ~ 100 parts, ripe high-alumina fly 5 ~ 8 parts, modified Nano crystal whisker materials 10 ~ 15 parts, urethane resin 3-8 part, tetrafluoroethylene 1-5 part, Zinic stearas 3-8 part, octamethylcyclotetrasiloxane 3 ~ 8 parts, white oil 5-10 part, organic solvent 50 ~ 80 parts.
Further, described solvent is selected from one or more in alcohols, fat hydrocarbon, arene, ketone, esters solvent.
Further, described step 4) on cinnabar after color drying, also to Cinnabar picture spraying layer of transparent coating, as 3 ~ 4h in the closed environment of 60 ~ 65 DEG C after allowing.
Further, described Clear paint is made up of the raw material of following weight part: 20 ~ 30 parts of silicone modified styrene-acrylate emulsions, 10 ~ 15 parts of triethylamines, 5 ~ 8 parts of modified Nano tin-antiomony oxides, 3 ~ 6 parts of zinc oxide, 4 ~ 7 parts of polyurethane finishing agents, 15 ~ 25 parts of dehydrated alcohols.
Beneficial effect of the present invention is: by using the upper color technique of color calligraphy and painting on this cinnabar, and use unique cinnabar coating, the cinnabar coating being can be bonded on cinnabar on color calligraphy and painting well, there will not be phenomenons such as coming off, meanwhile, after color on cinnabar, spray unique Clear paint, make this picture bright and new glossy, seal the effect of cinnabar coating simultaneously, further avoid the generation of the phenomenon of cinnabar Paint Falling.
Embodiment
Further describe technical scheme of the present invention below, but described in claimed scope is not limited to.
Embodiment one
Present embodiments provide the upper color technique of color calligraphy and painting on a kind of cinnabar, comprise the following steps:
1) cinnabar coating prepares, and cinnabar coating is made up of following raw material: cinnabar powder 80kg, ripe high-alumina fly 5kg, modified Nano crystal whisker materials 10kg, urethane resin 3kg, tetrafluoroethylene 1kg, Zinic stearas 3kg, octamethylcyclotetrasiloxane 3kg, white oil 5kg, organic solvent 50kg; Described solvent is selected from one or more in alcohols, fat hydrocarbon, arene, ketone, esters solvent, and the present embodiment selects esters solvent;
2) specific figure is portrayed in specific stone part Numeric Control Technology;
3) use pH value is the aqua calcis flushing visuals of 11, rinses 2min;
4) with stone part after clean water, then dry;
5) cinnabar coating is used to carry out upper coloured silk to visuals, then as dry 3h in the closed environment of 40 DEG C.
Embodiment two
Present embodiments provide the upper color technique of color calligraphy and painting on a kind of cinnabar, comprise the following steps:
1) cinnabar coating prepares, and cinnabar coating is made up of following raw material: cinnabar powder 100kg, ripe high-alumina fly 8kg, modified Nano crystal whisker materials 15kg, urethane resin 8kg, tetrafluoroethylene 5kg, Zinic stearas 8kg, octamethylcyclotetrasiloxane 8kg, white oil 10kg, organic solvent 80kg; Described solvent is selected from one or more in alcohols, fat hydrocarbon, arene, ketone, esters solvent, and the present embodiment selects fat hydrocarbon;
2) specific figure is portrayed in specific stone part Numeric Control Technology;
3) use pH value is the aqua calcis flushing visuals of 12, rinses 10min;
4) with stone part after clean water, then dry;
5) cinnabar coating is used to carry out upper coloured silk to visuals, then as dry 4h in the closed environment of 45 DEG C.
Embodiment three
Present embodiments provide the upper color technique of color calligraphy and painting on a kind of cinnabar, comprise the following steps:
1) cinnabar coating prepares, and cinnabar coating is made up of following raw material: cinnabar powder 90kg, ripe high-alumina fly 6kg, modified Nano crystal whisker materials 12kg, urethane resin 5kg, tetrafluoroethylene 3kg, Zinic stearas 5kg, octamethylcyclotetrasiloxane 5kg, white oil 8kg, organic solvent 70kg; Described solvent is selected from one or more in alcohols, fat hydrocarbon, arene, ketone, esters solvent, and the present embodiment selects alcohols, specifically selects, ethanol;
2) specific figure is portrayed in specific stone part Numeric Control Technology;
3) use pH value is the aqua calcis flushing visuals of 11, rinses 10min;
4) with stone part after clean water, then dry;
5) cinnabar coating is used to carry out upper coloured silk to visuals, then as dry 3.5h in the closed environment of 43 DEG C.
Embodiment four
Present embodiments provide the upper color technique of color calligraphy and painting on a kind of cinnabar, comprise the following steps:
1) cinnabar coating prepares, and cinnabar coating is made up of following raw material: cinnabar powder 90kg, ripe high-alumina fly 6kg, modified Nano crystal whisker materials 12kg, urethane resin 5kg, tetrafluoroethylene 3kg, Zinic stearas 5kg, octamethylcyclotetrasiloxane 5kg, white oil 8kg, organic solvent 70kg; Described solvent is selected from one or more in alcohols, fat hydrocarbon, arene, ketone, esters solvent, and the present embodiment selects alcohols, specifically selects, ethanol;
2) preparation of Clear paint, it is made up of raw material: 20 ~ 30kg silicone modified styrene-acrylate emulsion, 10 ~ 15kg triethylamine, 5 ~ 8kg modified Nano tin-antiomony oxide, 3 ~ 6kg zinc oxide, 4 ~ 7kg polyurethane finishing agent, 15 ~ 25kg dehydrated alcohol;
3) specific figure is portrayed in specific stone part Numeric Control Technology;
4) use pH value is the aqua calcis flushing visuals of 11, rinses 10min;
5) with stone part after clean water, then dry;
6) cinnabar coating is used to carry out upper coloured silk to visuals, then as dry 3.5h in the closed environment of 43 DEG C;
7) on cinnabar after color drying, also to Cinnabar picture spraying layer of transparent coating, as 3 ~ 4h in the closed environment of 60 ~ 65 DEG C after allowing.
Claims (5)
1. the upper color technique of color calligraphy and painting on cinnabar, is characterized in that: comprise following technique:
1) specific figure is portrayed in specific stone part Numeric Control Technology;
2) use pH value is the aqua calcis flushing visuals of 11 ~ 12, rinses 2 ~ 10min;
3) with stone part after clean water, then dry;
4) cinnabar coating is used to carry out upper coloured silk to visuals, then as 3 ~ 4h dry in the closed environment of 40 ~ 45 DEG C.
2. the upper color technique of color calligraphy and painting on cinnabar as claimed in claim 1, it is characterized in that: described cinnabar coating is made up of the raw material of following weight part: cinnabar powder 80 ~ 100 parts, ripe high-alumina fly 5 ~ 8 parts, modified Nano crystal whisker materials 10 ~ 15 parts, urethane resin 3-8 part, tetrafluoroethylene 1-5 part, Zinic stearas 3-8 part, octamethylcyclotetrasiloxane 3 ~ 8 parts, white oil 5-10 part, organic solvent 50 ~ 80 parts.
3. the upper color technique of color calligraphy and painting on cinnabar as claimed in claim 1, is characterized in that: described solvent is selected from one or more in alcohols, fat hydrocarbon, arene, ketone, esters solvent.
4. the upper color technique of color calligraphy and painting on cinnabar as claimed in claim 1, is characterized in that: described step 4) on cinnabar after color drying, also to Cinnabar picture spraying layer of transparent coating, as 3 ~ 4h in the closed environment of 60 ~ 65 DEG C after allowing.
5. the upper color technique of color calligraphy and painting on cinnabar as claimed in claim 4, is characterized in that: described Clear paint is made up of the raw material of following weight part: 20 ~ 30 parts of silicone modified styrene-acrylate emulsions, 10 ~ 15 parts of triethylamines, 5 ~ 8 parts of modified Nano tin-antiomony oxides, 3 ~ 6 parts of zinc oxide, 4 ~ 7 parts of polyurethane finishing agents, 15 ~ 25 parts of dehydrated alcohols.