CN105199364B - 一种阻燃耐老化ppo‑hips高分子合金及其制备方法 - Google Patents
一种阻燃耐老化ppo‑hips高分子合金及其制备方法 Download PDFInfo
- Publication number
- CN105199364B CN105199364B CN201510708826.8A CN201510708826A CN105199364B CN 105199364 B CN105199364 B CN 105199364B CN 201510708826 A CN201510708826 A CN 201510708826A CN 105199364 B CN105199364 B CN 105199364B
- Authority
- CN
- China
- Prior art keywords
- ppo
- hips
- high polymer
- retardant
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种阻燃耐老化PPO‑HIPS高分子合金及其制备方法,涉及一种高分子合金及其制备方法,高分子合金组成成份以质量份数表示如下:PPO80‑90;HIPS10‑20;三位一体膨胀型阻燃剂10‑40;高效防老剂0.5‑20;抗菌剂0.5‑3;增容剂SEBS‑g‑MAH10‑50;云母粉1‑20;氧化锌0.1‑5。步骤:将PPO和HIPS在真空干燥箱中干燥1‑5小时;按照所述质量配比将PPO、HIPS以及其它加工助剂混合;将混合好的原料投入到双螺杆挤出机加料斗中,熔融挤出,造粒即可。本发明可以很好的与聚合物基体相容,并且能高效阻燃PPO‑HIPS高分子合金,具有良好的耐氧化性、抗紫外线能力、抗自由基破坏能力,具有优异的机械性能的同时,也具备了很好的加工流动性能。
Description
技术领域
本发明涉及一种高分子合金及其制备方法,特别是涉及一种阻燃耐老化PPO-HIPS高分子合金及其制备方法。
背景技术
聚苯醚,是世界五大通用工程塑料之一。它具有刚性大、耐热性高、强度较高电性能优良等优点。另外,聚苯醚还具有耐磨、无毒、耐污染等优点。PPO广泛应用于汽车工业、机械工业以及化工行业等领域。但是PPO的不足之处也很明显,纯的PPO料熔融流动性较差、价格过高。高抗冲聚苯乙烯,是一种工程塑料,是苯乙烯和丁二烯的嵌段共聚物。将PPO于HIPS进行机械共混,制成PPO-HIPS高分子合金可以有效的改善PPO的加工流动性和抗冲击性能。
PPO合金应用十分广泛,但是阻燃性能差,耐老化性能不理想严重限制了其应用范围。传统的阻燃方法大多采用卤系阻燃剂或膨胀型阻燃剂,卤系阻燃剂不符合环保的发展趋势,而传统的膨胀型阻燃剂由三源组成,在基体中的分散性和抗迁移性能差,所以急需一种稳定性好、分散均匀的“三位一体”膨胀型阻燃剂来解决该不足。PPO-HIPS的耐老化性能并不理想,而目前所实用的小分子防老剂的抗迁移能力、抗自由基、抗紫外线破坏能力不强。
发明内容
本发明的目的在于提供一种阻燃耐老化PPO-HIPS高分子合金及其制备方法,本发明可以很好的与聚合物基体相容,并且能高效阻燃PPO-HIPS高分子合金,具有良好的耐氧化性、抗紫外线能力、抗自由基破坏能力,具有优异的机械性能的同时,也具备了很好的加工流动性能。
本发明的目的是通过以下技术方案实现的:
一种阻燃耐老化PPO-HIPS高分子合金,其组成成份以质量份数表示如下 :
PPO80-90;HIPS10-20;三位一体膨胀型阻燃剂10-40;高效防老剂0.5-20;抗菌剂0.5-3;增容剂SEBS-g-MAH10-50;云母粉1-20;氧化锌0.1-5。
所述的一种阻燃耐老化PPO-HIPS高分子合金,所述防老剂组成成份以质量份数表示如下:水滑石0.1-10;抗氧剂(330) 2-5;原花青素 0.1 -3;二氧化钛 10-20。
一种阻燃耐老化PPO-HIPS高分子合金其制备方法,所述方法包括以下步骤:
a:将PPO和HIPS在真空干燥箱中干燥1-5小时;
b:按照所述质量配比将PPO、HIPS以及其它加工助剂投入到高速混合机中;
c:将b中混合好的原料投入到双螺杆挤出机加料斗中,在220-300℃下,压力为10-15MPa,停留时间1-3min条件下熔融挤出,造粒。
所述的一种阻燃耐老化PPO-HIPS高分子合金及其制备方法,所述三位一体膨胀型阻燃剂是一种集碳源、酸源、气源与一体的膨胀型阻燃剂,其合成方法如下:将壳聚糖与三氯氧磷以1:(2-10)质量比加入到装有甲磺酸的三口瓶中,在50-120℃搅拌条件下冷凝回流反应1-5个小时,后洗涤干燥,再将产物与三聚氰胺以1:(0.2-0.7)质量比加入装有乙二醇三口瓶中,常温搅拌反应2-6小时,洗涤干燥。
本发明的优点与效果是:
1.本发明的新型膨胀型阻燃剂是集三源于一体的膨胀型阻燃剂,可以很好的与聚合物基体相容,并且能高效阻燃PPO-HIPS高分子合金。
2.本发明制得的PPO-HIPS高分子合金具有优异的耐老化性能,具有良好的耐氧化性、抗紫外线能力、抗自由基破坏能力。
3.本发明制备的PPO-HIPS高分子合金在具有优异的机械性能的同时,也具备了很好的加工流动性能。
4.本发明公开的PPO-HIPS高分子合金制备工艺简单,能耗低,易于生产。
附图说明
图1为三位一体膨胀型阻燃剂合成机理图。
具体实施方式
实施例1
本发明所采用的“三位一体”膨胀型阻燃剂自制合成方法如下:将壳聚糖与三氯氧磷以1:(2-10)质量比加入到装有甲磺酸的三口瓶中,在50-120℃搅拌条件下冷凝回流反应1-5个小时,后洗涤干燥,再将产物与三聚氰胺以1:(0.2-0.7)质量比加入装有乙二醇三口瓶中,常温搅拌反应2-6小时,洗涤干燥。
本发明所采用的的防老剂是由:水滑石0.1-10份 ,抗氧剂330 2-5份,原花青素0.1 -3份 ,二氧化钛10-20份。
本发明公开的一种阻燃耐老化PPO-HIPS高分子合金,其制备方法如下:
a:将PPO和HIPS在真空干燥箱中干燥1-5小时。
b:按照一定的权利要求1所述质量配比将PPO、HIPS以及其它加工助剂投入到高速混合机中。
c:将b中混合好的原料投入到双螺杆挤出机中加料斗,在220-300℃下,压力为10-15MPa,停留时间1-3min条件下熔融挤出,造粒。
“三位一体”膨胀型阻燃剂合成机理如下式所示:
阻燃剂的合成:将壳聚糖与三氯氧磷以1:2.5质量比加入到装有甲磺酸三口瓶中,在60℃搅拌条件下冷凝回流反应4个小时,后洗涤干燥,再将产物与三聚氰胺以1:0.5的质量比加入装有乙二醇的三口瓶中常温搅拌反应6小时,离心洗涤干燥。
将PPO-HIPS100份、阻燃剂35份、防老剂40份、抗菌剂2份、增容剂SEBS-g-MAH 30份、云母粉15份、氧化锌4份,加入到高速混合机中,室温下控制转速在350转/分钟,混合8分钟,取出后转入双螺杆挤出机加料斗中,在240℃下,压力为15MPa,停留时间3min条件下,熔融挤出,造粒,获得阻燃抗老化 PPO-HIPS塑料合金。
Claims (2)
1.一种阻燃耐老化PPO-HIPS高分子合金的制备方法,其特征在于,所述方法包括以下步骤:
a:将PPO和HIPS在真空干燥箱中干燥1-5小时;
b: 按照质量配比将PPO、HIPS以及其它加工助剂投入到高速混合机中;
c:将b中混合好的原料投入到双螺杆挤出机加料斗中,在220-300℃下,压力为10-15MPa,停留时间1-3min条件下熔融挤出,造粒;
所述的质量配比为:PPO80-90;HIPS10-20;三位一体膨胀型阻燃剂10-40;高效防老剂0.5-20;抗菌剂0.5-3;增容剂SEBS-g-MAH10-50;云母粉1-20;氧化锌0.1-5;
所述防老剂组成成份以质量份数表示如下:水滑石0.1-10;抗氧剂330 2-5;原花青素0.1 -3;二氧化钛 10-20。
2.如权利要求1所述的一种阻燃耐老化PPO-HIPS高分子合金的制备方法,其特征在于,所述三位一体膨胀型阻燃剂是一种集碳源、酸源、气源于 一体的膨胀型阻燃剂,其合成方法如下:将壳聚糖与三氯氧磷以1:(2-10)质量比加入到装有甲磺酸的三口瓶中,在50-120℃搅拌条件下冷凝回流反应1-5个小时,后洗涤干燥,再将产物与三聚氰胺以1:(0.2-0.7)质量比加入装有乙二醇三口瓶中,常温搅拌反应2-6小时,洗涤干燥。