CN105199364A - 一种阻燃耐老化ppo-hips高分子合金及其制备方法 - Google Patents

一种阻燃耐老化ppo-hips高分子合金及其制备方法 Download PDF

Info

Publication number
CN105199364A
CN105199364A CN201510708826.8A CN201510708826A CN105199364A CN 105199364 A CN105199364 A CN 105199364A CN 201510708826 A CN201510708826 A CN 201510708826A CN 105199364 A CN105199364 A CN 105199364A
Authority
CN
China
Prior art keywords
hips
ppo
polymer alloy
parts
retardant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510708826.8A
Other languages
English (en)
Other versions
CN105199364B (zh
Inventor
王娜
王升
张静
亢萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shenyang Li Yang Sealing Technology Co., Ltd.
Original Assignee
Shenyang University of Chemical Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang University of Chemical Technology filed Critical Shenyang University of Chemical Technology
Priority to CN201510708826.8A priority Critical patent/CN105199364B/zh
Publication of CN105199364A publication Critical patent/CN105199364A/zh
Application granted granted Critical
Publication of CN105199364B publication Critical patent/CN105199364B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种阻燃耐老化PPO-HIPS高分子合金及其制备方法，涉及一种高分子合金及其制备方法，高分子合金组成成份以质量份数表示如下：PPO80-90；HIPS10-20；三位一体膨胀型阻燃剂10-40；高效防老剂0.5-20；抗菌剂0.5-3；增容剂SEBS-g-MAH10-50；云母粉1-20；氧化锌0.1-5。步骤：将PPO和HIPS在真空干燥箱中干燥1-5小时；按照所述质量配比将PPO、HIPS以及其它加工助剂混合；将混合好的原料投入到双螺杆挤出机加料斗中，熔融挤出，造粒即可。本发明可以很好的与聚合物基体相容，并且能高效阻燃PPO-HIPS高分子合金，具有良好的耐氧化性、抗紫外线能力、抗自由基破坏能力，具有优异的机械性能的同时，也具备了很好的加工流动性能。

Description

一种阻燃耐老化PPO-HIPS高分子合金及其制备方法
技术领域
本发明涉及一种高分子合金及其制备方法，特别是涉及一种阻燃耐老化PPO-HIPS高分子合金及其制备方法。
背景技术
聚苯醚，是世界五大通用工程塑料之一。它具有刚性大、耐热性高、强度较高电性能优良等优点。另外，聚苯醚还具有耐磨、无毒、耐污染等优点。PPO广泛应用于汽车工业、机械工业以及化工行业等领域。但是PPO的不足之处也很明显，纯的PPO料熔融流动性较差、价格过高。高抗冲聚苯乙烯，是一种工程塑料，是苯乙烯和丁二烯的嵌段共聚物。将PPO于HIPS进行机械共混，制成PPO-HIPS高分子合金可以有效的改善PPO的加工流动性和抗冲击性能。
PPO合金应用十分广泛，但是阻燃性能差，耐老化性能不理想严重限制了其应用范围。传统的阻燃方法大多采用卤系阻燃剂或膨胀型阻燃剂，卤系阻燃剂不符合环保的发展趋势，而传统的膨胀型阻燃剂由三源组成，在基体中的分散性和抗迁移性能差，所以急需一种稳定性好、分散均匀的“三位一体”膨胀型阻燃剂来解决该不足。PPO-HIPS的耐老化性能并不理想，而目前所实用的小分子防老剂的抗迁移能力、抗自由基、抗紫外线破坏能力不强。
发明内容
本发明的目的在于提供一种阻燃耐老化PPO-HIPS高分子合金及其制备方法，本发明可以很好的与聚合物基体相容，并且能高效阻燃PPO-HIPS高分子合金，具有良好的耐氧化性、抗紫外线能力、抗自由基破坏能力，具有优异的机械性能的同时，也具备了很好的加工流动性能。
本发明的目的是通过以下技术方案实现的：
一种阻燃耐老化PPO-HIPS高分子合金，其组成成份以质量份数表示如下：
PPO80-90；HIPS10-20；三位一体膨胀型阻燃剂10-40；高效防老剂0.5-20；抗菌剂0.5-3；增容剂SEBS-g-MAH10-50；云母粉1-20；氧化锌0.1-5。
所述的一种阻燃耐老化PPO-HIPS高分子合金，所述防老剂组成成份以质量份数表示如下：水滑石0.1-10；抗氧剂（330）2-5；原花青素0.1-3；二氧化钛10-20。
一种阻燃耐老化PPO-HIPS高分子合金其制备方法，所述方法包括以下步骤：
a：将PPO和HIPS在真空干燥箱中干燥1-5小时；
b：按照所述质量配比将PPO、HIPS以及其它加工助剂投入到高速混合机中；
c：将b中混合好的原料投入到双螺杆挤出机加料斗中，在220-300℃下，压力为10-15MPa，停留时间1-3min条件下熔融挤出，造粒。
所述的一种阻燃耐老化PPO-HIPS高分子合金及其制备方法，所述三位一体膨胀型阻燃剂是一种集碳源、酸源、气源与一体的膨胀型阻燃剂，其合成方法如下：将壳聚糖与三氯氧磷以1:（2-10）质量比加入到装有甲磺酸的三口瓶中，在50-120℃搅拌条件下冷凝回流反应1-5个小时，后洗涤干燥，再将产物与三聚氰胺以1：（0.2-0.7）质量比加入装有乙二醇三口瓶中，常温搅拌反应2-6小时，洗涤干燥。
本发明的优点与效果是：
1.本发明的新型膨胀型阻燃剂是集三源于一体的膨胀型阻燃剂，可以很好的与聚合物基体相容，并且能高效阻燃PPO-HIPS高分子合金。
2.本发明制得的PPO-HIPS高分子合金具有优异的耐老化性能，具有良好的耐氧化性、抗紫外线能力、抗自由基破坏能力。
3.本发明制备的PPO-HIPS高分子合金在具有优异的机械性能的同时，也具备了很好的加工流动性能。
4.本发明公开的PPO-HIPS高分子合金制备工艺简单，能耗低，易于生产。
附图说明
图1为三位一体膨胀型阻燃剂合成机理图。
具体实施方式
实施例1
本发明所采用的“三位一体”膨胀型阻燃剂自制合成方法如下：将壳聚糖与三氯氧磷以1:（2-10）质量比加入到装有甲磺酸的三口瓶中，在50-120℃搅拌条件下冷凝回流反应1-5个小时，后洗涤干燥，再将产物与三聚氰胺以1：（0.2-0.7）质量比加入装有乙二醇三口瓶中，常温搅拌反应2-6小时，洗涤干燥。
本发明所采用的的防老剂是由：水滑石0.1-10份，抗氧剂3302-5份，原花青素0.1-3份，二氧化钛10-20份。
本发明公开的一种阻燃耐老化PPO-HIPS高分子合金，其制备方法如下：
a：将PPO和HIPS在真空干燥箱中干燥1-5小时。
b：按照一定的权利要求1所述质量配比将PPO、HIPS以及其它加工助剂投入到高速混合机中。
c：将b中混合好的原料投入到双螺杆挤出机中加料斗，在220-300℃下，压力为10-15MPa，停留时间1-3min条件下熔融挤出，造粒。
“三位一体”膨胀型阻燃剂合成机理如下式所示：
阻燃剂的合成：将壳聚糖与三氯氧磷以1:2.5质量比加入到装有甲磺酸三口瓶中，在60℃搅拌条件下冷凝回流反应4个小时，后洗涤干燥，再将产物与三聚氰胺以1：0.5的质量比加入装有乙二醇的三口瓶中常温搅拌反应6小时，离心洗涤干燥。
将PPO-HIPS100份、阻燃剂35份、防老剂40份、抗菌剂2份、增容剂SEBS-g-MAH30份、云母粉15份、氧化锌4份，加入到高速混合机中，室温下控制转速在350转/分钟，混合8分钟，取出后转入双螺杆挤出机加料斗中，在240℃下，压力为15MPa，停留时间3min条件下，熔融挤出，造粒，获得阻燃抗老化PPO-HIPS塑料合金。

Claims (4)

1.一种阻燃耐老化PPO-HIPS高分子合金，其特征在于，其组成成份以质量份数表示如下：
PPO80-90；HIPS10-20；三位一体膨胀型阻燃剂10-40；高效防老剂0.5-20；抗菌剂0.5-3；增容剂SEBS-g-MAH10-50；云母粉1-20；氧化锌0.1-5。
2.如权利要求1所述的一种阻燃耐老化PPO-HIPS高分子合金，其特征在于，所述防老剂组成成份以质量份数表示如下：水滑石0.1-10；抗氧剂（330）2-5；原花青素0.1-3；二氧化钛10-20。
3.一种阻燃耐老化PPO-HIPS高分子合金其制备方法，其特征在于，所述方法包括以下步骤：
a：将PPO和HIPS在真空干燥箱中干燥1-5小时；
b:按照所述质量配比将PPO、HIPS以及其它加工助剂投入到高速混合机中；
c:将b中混合好的原料投入到双螺杆挤出机加料斗中，在220-300℃下，压力为10-15MPa，停留时间1-3min条件下熔融挤出，造粒。
4.如权利要求1或3所述的阻燃耐老化PPO-HIPS高分子合金及其制备方法，其特征在于，所述三位一体膨胀型阻燃剂是一种集碳源、酸源、气源与一体的膨胀型阻燃剂，其合成方法如下：将壳聚糖与三氯氧磷以1:（2-10）质量比加入到装有甲磺酸的三口瓶中，在50-120℃搅拌条件下冷凝回流反应1-5个小时，后洗涤干燥，再将产物与三聚氰胺以1：（0.2-0.7）质量比加入装有乙二醇三口瓶中，常温搅拌反应2-6小时，洗涤干燥。
CN201510708826.8A 2015-10-28 2015-10-28 一种阻燃耐老化ppo‑hips高分子合金及其制备方法 Active CN105199364B (zh)