CN105176263A - 一种水性五金烤漆 - Google Patents
一种水性五金烤漆 Download PDFInfo
- Publication number
- CN105176263A CN105176263A CN201510660246.6A CN201510660246A CN105176263A CN 105176263 A CN105176263 A CN 105176263A CN 201510660246 A CN201510660246 A CN 201510660246A CN 105176263 A CN105176263 A CN 105176263A
- Authority
- CN
- China
- Prior art keywords
- water
- acrylic resin
- butyl peroxide
- cellaburate
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种水性五金烤漆,其原料成分的重量百分比为:丙烯酸树脂6-20%;晶须硅10-20%;消泡剂0.5-2%;聚酰胺固化剂0.5-0.8%;二叔丁基过氧化物1-2%;醋丁纤维素2-4%;交联树脂10-20%;余量为去离子水。
Description
技术领域
本发明属于五金加工技术领域,具体涉及一种喷涂于电脑机壳等表面的水性五金烤漆。
背景技术
水性丙烯酸氨基烤漆由于具有高光泽、硬度、保色保光、耐热等优点成为重要的工业涂料,广泛应用于汽车,家电,包装桶,自行车,缝纫机,订书机,书架等制品行业,起到金属装饰和保护作用;但现有的水性烤漆在硬度、耐冲击性、柔韧性、附着力,耐水性和耐醇性上都存在不足,导致现有的水性烤漆寿命较短。
发明内容
发明目的:针对上述现有技术存在的问题和不足,本发明的目的是提供一种水性五金烤漆,具有高光泽、高硬度等优点的同时,具有较长的使用寿命。
技术方案:本发明公开了一种水性五金烤漆,其原料成分的重量百分比为:丙烯酸树脂6-20%;晶须硅10-20%;消泡剂0.5-2%;聚酰胺固化剂0.5-0.8%;二叔丁基过氧化物1-2%;醋丁纤维素2-4%;交联树脂10-20%;余量为去离子水。
作为本发明的进一步优化,本发明的原料成分的重量百分比为:丙烯酸树脂9%;晶须硅10%;消泡剂0.5%;聚酰胺固化剂0.8%;二叔丁基过氧化物2%;醋丁纤维素3.5%;交联树脂20%,余量为去离子水。
作为本发明的进一步优化,本发明的原料成分的重量百分比为:丙烯酸树脂15%;晶须硅15%;消泡剂1.0%;聚酰胺固化剂0.8%;二叔丁基过氧化物1%;醋丁纤维素3%;交联树脂10%;,余量为去离子水。
作为本发明的进一步优化,本发明的原料成分的重量百分比为:丙烯酸树脂12%;晶须硅20%;消泡剂1.5%;聚酰胺固化剂0.8%;二叔丁基过氧化物1.5%;醋丁纤维素2%;丙烯酸树脂55%;交联树脂15%,余量为去离子水。
有益效果:本发明与现有技术相比,具有以下优点:本发明的烤漆光泽度高,硬度强,且重涂性强附着力好。
具体实施方式
以下结合具体的实施例对本发明进行详细说明,但同时说明本发明的保护范围并不局限于本实施例的具体范围,基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
需要说明的是,在本发明的描述中,除非另有说明,“多个”的含义是两个或两个以上;术语“上”、“下”、“左”、“右”、“内”、“外”、“前端”、“后端”、“头部”、“尾部”等指示的方位或位置关系为基于附图所示的方位或位置关系,仅是为了便于描述本发明和简化描述,而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作,因此不能理解为对本发明的限制。此外,术语“第一”、“第二”、“第三”等仅用于描述目的,而不能理解为指示或暗示相对重要性。
实施例1
本实施例的一种水性五金烤漆,原料成分的重量百分比为:丙烯酸树脂9%;晶须硅10%;消泡剂0.5%;聚酰胺固化剂0.8%;二叔丁基过氧化物2%;醋丁纤维素3.5%;交联树脂20%,余量为去离子水。
实施例2
本实施例的一种水性五金烤漆,原料成分的重量百分比为:丙烯酸树脂15%;晶须硅15%;消泡剂1.0%;聚酰胺固化剂0.8%;二叔丁基过氧化物1%;醋丁纤维素3%;交联树脂10%;,余量为去离子水。
实施例3
本实施例的一种水性五金烤漆,原料成分的重量百分比为:丙烯酸树脂12%;晶须硅20%;消泡剂1.5%;聚酰胺固化剂0.8%;二叔丁基过氧化物1.5%;醋丁纤维素2%;丙烯酸树脂55%;交联树脂15%,余量为去离子水。
本发明的实施例是为了示例和描述起见而给出的,而并不是无遗漏的或者将本发明限于所公开的形式。很多修改和变化对于本领域的普通技术人员而言是显而易见的。选择和描述实施例是为了更好说明本发明的原理和实际应用,并且使本领域的普通技术人员能够理解本发明从而设计适于特定用途的带有各种修改的各种实施例。
Claims (4)
1.一种水性五金烤漆,其特征在于:其原料成分的重量百分比为:丙烯酸树脂6-20%;晶须硅10-20%;消泡剂0.5-2%;聚酰胺固化剂0.5-0.8%;二叔丁基过氧化物1-2%;醋丁纤维素2-4%;交联树脂10-20%;余量为去离子水。
2.根据权利要求1所述的一种水性五金烤漆,其特征在于:其原料成分的重量百分比为:丙烯酸树脂9%;晶须硅10%;消泡剂0.5%;聚酰胺固化剂0.8%;二叔丁基过氧化物2%;醋丁纤维素3.5%;交联树脂20%,余量为去离子水。
3.根据权利要求1所述的一种水性五金烤漆,其特征在于:其原料成分的重量百分比为:丙烯酸树脂15%;晶须硅15%;消泡剂1.0%;聚酰胺固化剂0.8%;二叔丁基过氧化物1%;醋丁纤维素3%;交联树脂10%;,余量为去离子水。
4.根据权利要求1所述的一种水性五金烤漆,其特征在于:其原料成分的重量百分比为:丙烯酸树脂12%;晶须硅20%;消泡剂1.5%;聚酰胺固化剂0.8%;二叔丁基过氧化物1.5%;醋丁纤维素2%;丙烯酸树脂55%;交联树脂15%,余量为去离子水。