CN105133137A - Ceiba and wool fiber bicolor denim and production technology thereof - Google Patents
Ceiba and wool fiber bicolor denim and production technology thereof Download PDFInfo
- Publication number
- CN105133137A CN105133137A CN201510503170.6A CN201510503170A CN105133137A CN 105133137 A CN105133137 A CN 105133137A CN 201510503170 A CN201510503170 A CN 201510503170A CN 105133137 A CN105133137 A CN 105133137A
- Authority
- CN
- China
- Prior art keywords
- denim
- kapok
- wool fibre
- tension
- double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses ceiba and wool fiber bicolor denim and production technology thereof. The invention is aimed at providing high-grade denim fabric and production technology. By giving higher-level technology content to conventional denim fabric, denim fabric has fine hygroscopicity, elasticity, heat-retaining property, skin-friendly performance and excellent spinnability and feels soft and smooth with natural color.The ceiba and wool fiber bicolor denim and production technology thereof have following beneficial effects: by utilization of production technology, level of denim fabric of the manufactured ceiba/wool fiber bicolor denim is increased; higher-level technical content is given to conventional denim; a product is soft, smooth and bright-colored and has performance such as anti-static electricity, moisture absorbent and transfer performance and mildew-proof and decay-proof performance and has excellent spinnability so that the ceiba and wool fiber bicolor denim is in accord with the theory of green and environmental protection in people's dressing and satisfies the ever-growing fashionable requirement for pursuit of nature, comfortableness and beauty of people; and the ceiba and wool fiber bicolor denim has a bright market prospect.
Description
Technical field
The present invention relates to textile technology field, be specifically related to a kind of kapok, the double-colored denim of wool fibre and production technology thereof.
Background technology
The production of denim originates from the U.S., and Li Wei Astrid Strauss is the founder of jeans.The welcome that jeans wear is rough with style, comfortable and easy to wear, tough and hard wear resistant obtains consumers in general is popular so far more than 150 year.Jeans are a kind of major consumers product of people, and its demand is considerable.According to american cotton corporate statistics, global consumer has 7 pairs of jeans per capita, and Chinese Consumer's is 4 per capita, and has the consumer of 90% at least to have 1 pair of jeans all over the world, has the consumer of 64% to like wearing jeans.
Along with the raising of expanding economy and the level of consumption, denim breaches textile indigo thick number twill traditional style already, on rough, random basis, gradually to the future development that light-duty, soft type, colourful colour bar, jacquard knitting etc. are with high content of technology.First the innovation of cowboy's product shows differential, the functionalization aspect of the application of new raw material and the diversification of raw material and fiber. in the selection of raw material, breached the general layout based on cotton, from single Pure cotton Product to blending type, elastic-type, non-cottonizing development.Present jeans cloth is abundant, permeability extreme difference, to often moist, scorching hot, pathogenic bacteria multiplied in a large number, breeds, and makes application on human skin produce itch, shouting pain, affects the normal dress of people.
Summary of the invention
In order to solve the problem, the invention provides the double-colored denim of kapok/wool fibre and production technology thereof, its object is to: denim fabric and preparation technology thereof that a kind of top grade is provided, give the technology content that traditional denim fabric is higher, make denim fabric hygroscopicity better, good springiness, good heat preservation performance, soft cunning is glutinous, natural in color, have the performances such as affinity, spinning property is excellent.
The technology of the present invention solution:
The double-colored denim of kapok/wool fibre, is characterized in that: the content of described bombax cotton is 50%-90%, and wool fibre content is 10%-50%.
The double-colored denim of described kapok/wool fibre, is characterized in that, described kapok: the blending ratio of wool fibre is 70:30.
The double-colored denim of described kapok/wool fibre, is characterized in that, described kapok: the blending ratio of wool fibre is 65:35.
The double-colored denim of described kapok/wool fibre, is characterized in that, described kapok: the blending ratio of wool fibre is 80:20.
The double-colored denim manufacturing technique of kapok/wool fibre, comprises the steps:
1, winder: use 1332M bobbin winder to produce, be equipped with DQSS-4 type Capacitance Clearer and waxing attachment, the convoluting speed of bobbin winder is 800-1000m/min, and workshop humid control is 60-70%;
2, warping: for ensureing that warp tension is consistent, tension in Warping layer and section be made to configure, and tension washer weight is configured to proparea 5.0g, Qian Zhong district 4.6g, middle back zone 3.8g, back zone 3.3g; The upper and lower, proparea 5.5g, middle level, proparea 6.0g, Zhong Qu the upper and lower: 5.0g, Zhong Qu middle level 5.5g; The upper and lower, back zone: 4.5g, middle level, back zone: 5.0g, rear row limit yarn: 7.0g, and note increasing limit yarn tension, reduce woven slack list phenomenon, improve beam of a loom quality;
3, pulp: add sodium chloride in dyestuff, sodium chloride can ionize out negative ions, neutralized bombax cotton with part electricity, play short dye effect, the process conditions of dyeing are: sodium chloride 25-30g/L, calcium carbonate 18-20g/L; bath raio: 1:50-1:60; temperature: 55-60 DEG C, time 70-75min, carry out aftertreatment technology after dyeing is good;
4, gait: adopt 12 to combine, gait along the method for wearing;
5, weave: adopt Rapier looms to weave, adopt early opening, hightension technique, be conducive to urgent weft yarn and obtain neat and well spaced appearance effect, technological parameter is opening time 270 °, cloth machine tension force 4200N, loom speed 550r/min, warp stop frame: front and back 90mm, high 120mm, hightension when weaving easily producing the fault of the unrepairable such as Starting Mark and driving ripple time long through, latitude down time, therefore requires that the good axial ratio of sizing wants high, and taping head, lappers will lack, reduce longitude and latitude as far as possible and stop platform, improve the weavability of warp thread to greatest extent.）。Weft yarn adopts dyed yarn, makes the fabric weaving out present two kinds of colors, the relative humidity in workshop will be strict controlled in 65%-70% simultaneously;
6, running repair: carry out perching by cloth inspecting machine to the grey cloth woven, defectively knits flaw point by manually to repair;
7, singe: process conditions are flame temperature 800-900 DEG C, the fabric speed of a motor vehicle 90-100m/min, number of times two positive two of singing is anti-, flame and cloth distance 0.8 centimetre;
8, determine: can put in storage after finished product package.
Adopt sizing-dyeing machine to carry out pulp in described step 3, in order to ensure to contaminate quality, strictly must control the unwinding tension of yarn, and keeping the unwinding tension between warp beam even.Moisture and the dyestuff of warp thread after dyeing, thus starching midge ability, should adopt the sizing technique of high temperature, high pressure, low viscosity, low starching and middle moisture regain, little elongation, Technological Parameters of Sizing is high temperature 95 DEG C, high pressure 23kN, viscosity 8
s-10
sconcentration 6%, sizing is drawn from stock tank, is divided into upper and lower two-layer before entering drying room, enter two groups of drying cylinders respectively, upper and lower two-layer warp thread is because of the change of tension force, the speed of a motor vehicle, and folding repeatedly, adhesion mutually, make filoplume regenerate, wet yarn not only separates by the use of hygroscopic water strand in time, reduce adhesion, and smooth-going under yarn hygrometric state, submissive filoplume, to raising loom opening sharpness successful.
In described step 3, the technical recipe of dyestuff is: Lanasol dyestuff 4%(owf), ammonium sulfate 4%(owf), the acetic acid 2%-3%(owf of 80%) and, upper dye pH value 4-5, natrium carbonicum calcinatum 2%-3%(owf), fixation pH value: 8-9, bath raio: 1:5.
Aftertreatment technology in described step 3 is: (soda ash 2g/L, 80 DEG C × 15min) → soap (soaping agent 1%(owf) in fixation washing, 75 DEG C × 10min) → washing (70 DEG C × 10min).
Beneficial effect of the present invention:
The double-colored denim of kapok/wool fibre that the present invention produces improves the class of denim, and give the technology content of traditional cowboy Geng Gao, this product has softness, smooth, bright-coloured, antistatic, moisture absorption, the not mould performance such as not eat into, spinning property is excellent, both the theory of people's dressing environmental protection had been met, meet again people and day by day pursue nature, fashion demand comfortable, attractive in appearance, there are good market prospects.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further.
Embodiment one:
Adopt kapok: the blending ratio of wool fibre is 70:30, processing step:
Winder: use 1332M bobbin winder to produce, be equipped with DQSS-4 type Capacitance Clearer and waxing attachment, removes the large tieing on warp thread, large impurity, adopts air splicer, realize knotless, keep the fineness of cloth cover.For reducing the filoplume that doff process produces, adopt waxing attachment, reduce thread friction coefficient, the convoluting speed of bobbin winder is 800m/min, and workshop humid control is 60%.
2, warping: for ensureing that warp tension is consistent, tension in Warping layer and section be made to configure, and tension washer weight is configured to proparea 5.0g, Qian Zhong district 4.6g, middle back zone 3.8g, back zone 3.3g; The upper and lower, proparea 5.5g, middle level, proparea 6.0g, Zhong Qu the upper and lower 5.0g; Zhong Qu middle level 5.5g, the upper and lower, back zone 4.5g, middle level, back zone 5.0g, rear row limit yarn 7.0g, and note increasing limit yarn tension, reduce woven slack list phenomenon, improve beam of a loom quality.
3, pulp: add sodium chloride in dyestuff, , sodium chloride can ionize out negative ions, neutralized bombax cotton with part electricity, thus play short dye effect, the process conditions of dyeing are: sodium chloride 25g/L, calcium carbonate 18g/L, bath raio 1:50, temperature 55 DEG C, time 70min, dyeing is filled a prescription: Lanasol dyestuff 4%(owf), ammonium sulfate 4%(owf), the acetic acid 2%(owf of 80%), upper dye pH value 4, natrium carbonicum calcinatum 2%(owf), fixation pH value 8, bath raio 1:5, aftertreatment technology is carried out after dyeing, treatment process is: fixation washing (soda ash 2g/L, 80 DEG C × 15min) → soap (soaping agent 1%(owf), 75 DEG C × 10min) → washing (70 DEG C × 10min), pulp adopts sizing-dyeing machine, in order to ensure to contaminate quality, strictly must control the unwinding tension of yarn, and keep the unwinding tension between warp beam even.Moisture and the dyestuff of warp thread after dyeing, thus starching midge ability, should adopt the sizing technique of high temperature, high pressure, low viscosity, low starching and middle moisture regain, little elongation.Sizing technique is: high temperature 95 DEG C, high pressure 23kN, viscosity 8
sconcentration 6%, sizing is drawn from stock tank, be divided into upper and lower two-layer before entering drying room, enter two groups of drying cylinders respectively, upper and lower two-layer warp thread is because of the change of tension force, the speed of a motor vehicle, folding repeatedly, adhesion mutually, make filoplume regenerate, and wet yarn not only separates by the use of hygroscopic water strand in time, reduce adhesion, and smooth-going under yarn hygrometric state, submissive filoplume, to raising loom opening sharpness successful, otherwise, because Squeezing Weighting Percentage reduces, adhesion strength when can cause sizing layering between adjacent yarn improves and increases filoplume.
4, gait: adopt 12 to combine, gait along the method for wearing.
5, weave: adopt Rapier looms to weave, adopt early opening, hightension technique, be conducive to urgent weft yarn and obtain neat and well spaced appearance effect, weaving process is: opening time 270 °, cloth machine tension force 4200N, loom speed 550r/min, 90mm before and after warp stop frame, high 120mm, hightension when weaving easily producing the fault of the unrepairable such as Starting Mark and driving ripple time long through, latitude down time, therefore requires that the good axial ratio of sizing wants high, and taping head, lappers will lack, reduce longitude and latitude as far as possible and stop platform, improve the weavability of warp thread to greatest extent.Weft yarn adopts dyed yarn, makes the fabric weaving out present two kinds of colors, the relative humidity in workshop will be strict controlled in 65% simultaneously.
6, running repair: carry out perching by cloth inspecting machine to the grey cloth woven, defectively knits flaw point by manually to repair.
7, singe: process conditions: flame temperature 800 DEG C, fabric speed of a motor vehicle 100m/min, number of times two positive two of singing is anti-, flame and cloth distance 0.8 centimetre.
8, determine: can put in storage after finished product package.
Embodiment two:
Adopt kapok: the blending ratio of wool fibre is 65:35, processing step:
Winder: use 1332M bobbin winder to produce, be equipped with DQSS-4 type Capacitance Clearer and waxing attachment, removes the large tieing on warp thread, large impurity, adopts air splicer, realize knotless, keep the fineness of cloth cover.For reducing the filoplume that doff process produces, adopt waxing attachment, reduce thread friction coefficient, the convoluting speed of bobbin winder is 900m/min, and workshop humid control is 65%.
2, warping: for ensureing that warp tension is consistent, tension in Warping layer and section be made to configure, and tension washer weight is configured to proparea 5.0g, Qian Zhong district 4.6g, middle back zone 3.8g, back zone 3.3g; The upper and lower, proparea 5.5g, middle level, proparea 6.0g, Zhong Qu the upper and lower 5.0g; Zhong Qu middle level 5.5g, the upper and lower, back zone 4.5g, middle level, back zone 5.0g, rear row limit yarn 7.0g, and note increasing limit yarn tension, reduce woven slack list phenomenon, improve beam of a loom quality.
3, pulp: add sodium chloride in dyestuff, , sodium chloride can ionize out negative ions, neutralized bombax cotton with part electricity, thus play short dye effect, the process conditions of dyeing are: sodium chloride 28g/L, calcium carbonate 19g/L, bath raio 1:55, temperature 57 DEG C, time 72min, dyeing is filled a prescription: Lanasol dyestuff 4%(owf), ammonium sulfate 4%(owf), the acetic acid 2%(owf of 80%), upper dye pH value 4, natrium carbonicum calcinatum 2%(owf), fixation pH value 8, bath raio 1:5, aftertreatment technology is carried out after dyeing, treatment process is: fixation washing (soda ash 2g/L, 80 DEG C × 15min) → soap (soaping agent 1%(owf), 75 DEG C × 10min) → washing (70 DEG C × 10min), pulp adopts sizing-dyeing machine, in order to ensure to contaminate quality, strictly must control the unwinding tension of yarn, and keep the unwinding tension between warp beam even.Moisture and the dyestuff of warp thread after dyeing, thus starching midge ability, should adopt the sizing technique of high temperature, high pressure, low viscosity, low starching and middle moisture regain, little elongation.Sizing technique is: high temperature 95 DEG C, high pressure 23kN, viscosity 9
sconcentration 6%, sizing is drawn from stock tank, be divided into upper and lower two-layer before entering drying room, enter two groups of drying cylinders respectively, upper and lower two-layer warp thread is because of the change of tension force, the speed of a motor vehicle, folding repeatedly, adhesion mutually, make filoplume regenerate, and wet yarn not only separates by the use of hygroscopic water strand in time, reduce adhesion, and smooth-going under yarn hygrometric state, submissive filoplume, to raising loom opening sharpness successful, otherwise, because Squeezing Weighting Percentage reduces, adhesion strength when can cause sizing layering between adjacent yarn improves and increases filoplume.
4, gait: adopt 12 to combine, gait along the method for wearing.
5, weave: adopt Rapier looms to weave, adopt early opening, hightension technique, be conducive to urgent weft yarn and obtain neat and well spaced appearance effect, weaving process is: opening time 270 °, cloth machine tension force 4200N, loom speed 550r/min, 90mm before and after warp stop frame, high 120mm, hightension when weaving easily producing the fault of the unrepairable such as Starting Mark and driving ripple time long through, latitude down time, therefore requires that the good axial ratio of sizing wants high, and taping head, lappers will lack, reduce longitude and latitude as far as possible and stop platform, improve the weavability of warp thread to greatest extent.Weft yarn adopts dyed yarn, makes the fabric weaving out present two kinds of colors, the relative humidity in workshop will be strict controlled in 65% simultaneously.
6, running repair: carry out perching by cloth inspecting machine to the grey cloth woven, defectively knits flaw point by manually to repair.
7, singe: process conditions: flame temperature 850 DEG C, fabric speed of a motor vehicle 95m/min, number of times two positive two of singing is anti-, flame and cloth distance 0.8 centimetre.
8, determine: can put in storage after finished product package.
Implementation column three:
Adopt kapok: the blending ratio of wool fibre is 80:20, processing step:
Winder: use 1332M bobbin winder to produce, be equipped with DQSS-4 type Capacitance Clearer and waxing attachment, removes the large tieing on warp thread, large impurity, adopts air splicer, realize knotless, keep the fineness of cloth cover.For reducing the filoplume that doff process produces, adopt waxing attachment, reduce thread friction coefficient, the convoluting speed of bobbin winder is 1000m/min, and workshop humid control is 70%.
2, warping: for ensureing that warp tension is consistent, tension in Warping layer and section be made to configure, and tension washer weight is configured to proparea 5.0g, Qian Zhong district 4.6g, middle back zone 3.8g, back zone 3.3g; The upper and lower, proparea 5.5g, middle level, proparea 6.0g, Zhong Qu the upper and lower 5.0g; Zhong Qu middle level 5.5g, the upper and lower, back zone 4.5g, middle level, back zone 5.0g, rear row limit yarn 7.0g, and note increasing limit yarn tension, reduce woven slack list phenomenon, improve beam of a loom quality.
3, pulp: add sodium chloride in dyestuff, , sodium chloride can ionize out negative ions, neutralized bombax cotton with part electricity, thus play short dye effect, the process conditions of dyeing are: sodium chloride 30g/L, calcium carbonate 20g/L, bath raio 1:60, temperature 57 DEG C, time 75min, dyeing is filled a prescription: Lanasol dyestuff 4%(owf), ammonium sulfate 4%(owf), the acetic acid 3%(owf of 80%), upper dye pH value 5, natrium carbonicum calcinatum 3%(owf), fixation pH value 9, bath raio 1:5, aftertreatment technology is carried out after dyeing, treatment process is: fixation washing (soda ash 2g/L, 80 DEG C × 15min) → soap (soaping agent 1%(owf), 75 DEG C × 10min) → washing (70 DEG C × 10min), pulp adopts sizing-dyeing machine, in order to ensure to contaminate quality, strictly must control the unwinding tension of yarn, and keep the unwinding tension between warp beam even.Moisture and the dyestuff of warp thread after dyeing, thus starching midge ability, should adopt the sizing technique of high temperature, high pressure, low viscosity, low starching and middle moisture regain, little elongation.Sizing technique is: high temperature 95 DEG C, high pressure 23kN, viscosity 10
sconcentration 6%, sizing is drawn from stock tank, be divided into upper and lower two-layer before entering drying room, enter two groups of drying cylinders respectively, upper and lower two-layer warp thread is because of the change of tension force, the speed of a motor vehicle, folding repeatedly, adhesion mutually, make filoplume regenerate, and wet yarn not only separates by the use of hygroscopic water strand in time, reduce adhesion, and smooth-going under yarn hygrometric state, submissive filoplume, to raising loom opening sharpness successful, otherwise, because Squeezing Weighting Percentage reduces, adhesion strength when can cause sizing layering between adjacent yarn improves and increases filoplume.
4, gait: adopt 12 to combine, gait along the method for wearing.
5, weave: adopt Rapier looms to weave, adopt early opening, hightension technique, be conducive to urgent weft yarn and obtain neat and well spaced appearance effect, weaving process is: opening time 270 °, cloth machine tension force 4200N, loom speed 550r/min, 90mm before and after warp stop frame, high 120mm, hightension when weaving easily producing the fault of the unrepairable such as Starting Mark and driving ripple time long through, latitude down time, therefore requires that the good axial ratio of sizing wants high, and taping head, lappers will lack, reduce longitude and latitude as far as possible and stop platform, improve the weavability of warp thread to greatest extent.Weft yarn adopts dyed yarn, makes the fabric weaving out present two kinds of colors, the relative humidity in workshop will be strict controlled in 65% simultaneously.
6, running repair: carry out perching by cloth inspecting machine to the grey cloth woven, defectively knits flaw point by manually to repair.
7, singe: process conditions: flame temperature 900 DEG C, fabric speed of a motor vehicle 90m/min, number of times two positive two of singing is anti-, flame and cloth distance 0.8 centimetre.
8, determine: can put in storage after finished product package.
Claims (8)
1. the double-colored denim of kapok/wool fibre, is characterized in that: the content of described bombax cotton is 50%-90%, and wool fibre content is 10%-50%.
2. the double-colored denim of kapok/wool fibre as claimed in claim 1, is characterized in that, described kapok: the blending ratio of wool fibre is 70:30.
3. the double-colored denim of kapok/wool fibre as claimed in claim 1, is characterized in that, described kapok: the blending ratio of wool fibre is 65:35.
4. the double-colored denim of kapok/wool fibre as claimed in claim 1, is characterized in that: described kapok: the blending ratio of wool fibre is 80:20.
5. the double-colored denim manufacturing technique of kapok/wool fibre, comprises the steps:
(1), winder: use 1332M bobbin winder to produce, be equipped with DQSS-4 type Capacitance Clearer and waxing attachment, the convoluting speed of bobbin winder is 800-1000m/min, and workshop humid control is 60-70%;
(2), warping: for ensureing that warp tension is consistent, tension in Warping layer and section be made to configure, and tension washer weight is configured to proparea 5.0g, Qian Zhong district 4.6g, middle back zone 3.8g, back zone 3.3g; The upper and lower, proparea 5.5g, middle level, proparea 6.0g, Zhong Qu the upper and lower: 5.0g, Zhong Qu middle level 5.5g; The upper and lower, back zone: 4.5g, middle level, back zone: 5.0g, rear row limit yarn: 7.0g, and note increasing limit yarn tension, reduce woven slack list phenomenon, improve beam of a loom quality;
(3), pulp: add sodium chloride in dyestuff, sodium chloride can ionize out negative ions, neutralized bombax cotton with part electricity, play short dye effect, the process conditions of dyeing are: sodium chloride 25-30g/L, calcium carbonate 18-20g/L; bath raio: 1:50-1:60; temperature: 55-60 DEG C, time 70-75min, carry out aftertreatment technology after dyeing is good;
(4), gait: adopt 12 to combine, gait along the method for wearing;
(5), weave: adopt Rapier looms to weave, adopt early opening, hightension technique, be conducive to urgent weft yarn and obtain neat and well spaced appearance effect, technological parameter is opening time 270 °, cloth machine tension force 4200N, loom speed 550r/min, warp stop frame: front and back 90mm, high 120mm, is strict controlled in 65%-70% by the relative humidity in workshop;
(6), running repair: by cloth inspecting machine, perching is carried out to the grey cloth woven, defectively knits flaw point by manually to repair;
(7), singe: process conditions are flame temperature 800-900 DEG C, the fabric speed of a motor vehicle 90-100m/min, number of times two positive two of singing is anti-, flame and cloth distance 0.8 centimetre;
(8), determine: can put in storage after finished product package.
6. the double-colored denim manufacturing technique of kapok/wool fibre as claimed in claim 5, it is characterized in that: in described step 3, adopt sizing-dyeing machine to carry out pulp, in order to ensure to contaminate quality, strictly must control the unwinding tension of yarn, and keep the unwinding tension between warp beam even, moisture and the dyestuff of warp thread after dyeing, thus starching midge ability, the sizing technique of high temperature, high pressure, low viscosity, low starching and middle moisture regain, little elongation should be adopted, Technological Parameters of Sizing is high temperature 95 DEG C, high pressure 23kN, viscosity 8
s-10
sconcentration 6%, sizing is drawn from stock tank, is divided into upper and lower two-layer before entering drying room, enter two groups of drying cylinders respectively, upper and lower two-layer warp thread is because of the change of tension force, the speed of a motor vehicle, and folding repeatedly, adhesion mutually, make filoplume regenerate, wet yarn not only separates by the use of hygroscopic water strand in time, reduce adhesion, and smooth-going under yarn hygrometric state, submissive filoplume, to raising loom opening sharpness successful.
7. the double-colored denim manufacturing technique of kapok/wool fibre as claimed in claim 5, it is characterized in that, in described step 3, the technical recipe of dyestuff is: Lanasol dyestuff 4%(owf), ammonium sulfate 4%(owf), the acetic acid 2%-3%(owf of 80%), upper dye pH value 4-5, natrium carbonicum calcinatum 2%-3%(owf), fixation pH value: 8-9, bath raio is 1:5.
8. the double-colored denim manufacturing technique of kapok/wool fibre as claimed in claim 5, it is characterized in that, aftertreatment technology in described step 3 is: (soda ash 2g/L, 80 DEG C × 15min) → soap (soaping agent 1%(owf) in fixation washing, 75 DEG C × 10min) → washing (70 DEG C × 10min).