CN105131537A - Flame-retardant acid-and-alkali-resistant waterproof fire hose material - Google Patents
Flame-retardant acid-and-alkali-resistant waterproof fire hose material Download PDFInfo
- Publication number
- CN105131537A CN105131537A CN201510562507.0A CN201510562507A CN105131537A CN 105131537 A CN105131537 A CN 105131537A CN 201510562507 A CN201510562507 A CN 201510562507A CN 105131537 A CN105131537 A CN 105131537A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire hose
- acid
- alkali
- hose material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a flame-retardant acid-and-alkali-resistant waterproof fire hose material. The fire hose material is composed of the following ingredients, by weight, 38-42 parts of acrylic acid ester, 40-44 parts of dioctyl phthalate, 36-40 parts of polyvinyl chloride, 40-44 parts of stearic acid, 36-40 parts of diisocyanate, 40-44 parts of chloroprene rubber, 36-40 parts of hexanedioic acid pentaerythritol ester, 42-46 parts of polyester silk, 36-40 parts of calcium carbonate, 40-44 parts of aluminum hydroxide, 36-40 parts of imvite, 40-44 parts of vinyl acetate, 36-40 parts of styrene-acrylic emulsion, 40-44 parts of sodium pyrophosphate, 36-40 parts of forsterite, 40-44 parts of white oil, 36-40 parts of sodium tetraborate, 40-44 parts of phenolic resin, 36-40 parts of zinc stearate, 40-44 parts of silicon carbide micro powder, 36-40 parts of long stapled cotton fibers, 40-44 parts of maleic anhydride and 36-40 parts of calcium plumbite. The fire hose material has excellent flame retardation, corrosion resistance and waterproof performance. The fire hose material is used for preparation of a fire hose, and the product performances are improved.
Description
Technical field
The present invention relates to a kind of fire-retardant acid and alkali-resistance waterproof fire hose material, belong to fire-fighting material technical field.
Background technology
Fire hose is used to the flexible pipe transporting the anti-flaming liquid such as high pressure water or foam, and it is convenient to lay during use, has become one of topmost Fire extinguisher in daily life.Because environment different during fire can produce unpredictable high calorie, some combustionmaterial can produce higher radiant heat, thus causes fire hose heat damage.Improve existing fire hose, make water-band high pressure resistant, wear-resistant, high temperature resistant, durable in use, and not easy to leak, resistance is little, also can bending fold arbitrarily, easy to use, can play better effect in fire fighting operation.
Summary of the invention
The object of the present invention is to provide a kind of fire-retardant acid and alkali-resistance waterproof fire hose material, to realize the function of fire hose flame-proof abrasion-resistant better.
To achieve these goals, technical scheme of the present invention is as follows.
A kind of fire-retardant acid and alkali-resistance waterproof fire hose material, be made up of the component of following mass fraction: acrylate 38 ~ 42 parts, dioctyl phthalate (DOP) 40 ~ 44 parts, polyvinyl chloride 36 ~ 40 parts, stearic acid 40 ~ 44 parts, vulcabond 36 ~ 40 parts, chloroprene rubber 40 ~ 44 parts, adipic acid pentaerythritol ester 36 ~ 40 parts, POLYESTER YARNS 42 ~ 46 parts, 36 ~ 40 parts, calcium carbonate, 40 ~ 44 parts, aluminium hydroxide, polynite 36 ~ 40 parts, vinyl-acetic ester 40 ~ 44 parts, benzene emulsion 36 ~ 40 parts, trisodium phosphate 40 ~ 44 parts, forsterite 36 ~ 40 parts, white oil 40 ~ 44 parts, sodium tetraborate 36 ~ 40 parts, 40 ~ 44 parts, resol, Zinic stearas 36 ~ 40 parts, silicon carbide micro-powder 40 ~ 44 parts, long-staple cotton fiber 36 ~ 40 parts, MALEIC ANHYDRIDE 40 ~ 44 parts, calcium plumbite 36 ~ 40 parts.
Further, above-mentioned fire-retardant acid and alkali-resistance waterproof fire hose material, be made up of the component of following mass fraction: acrylate 38 parts, dioctyl phthalate (DOP) 40 parts, polyvinyl chloride 36 parts, stearic acid 40 parts, vulcabond 36 parts, chloroprene rubber 40 parts, adipic acid pentaerythritol ester 36 parts, POLYESTER YARNS 42 parts, 36 parts, calcium carbonate, 40 parts, aluminium hydroxide, polynite 36 parts, vinyl-acetic ester 40 parts, benzene emulsion 36 parts, trisodium phosphate 40 parts, forsterite 36 parts, white oil 40 parts, sodium tetraborate 36 parts, 40 parts, resol, Zinic stearas 36 parts, silicon carbide micro-powder 40 parts, long-staple cotton fiber 36 parts, MALEIC ANHYDRIDE 40 parts, calcium plumbite 36 parts.
Further, above-mentioned fire-retardant acid and alkali-resistance waterproof fire hose material, be made up of the component of following mass fraction: acrylate 40 parts, dioctyl phthalate (DOP) 42 parts, polyvinyl chloride 38 parts, stearic acid 42 parts, vulcabond 38 parts, chloroprene rubber 42 parts, adipic acid pentaerythritol ester 38 parts, POLYESTER YARNS 44 parts, 38 parts, calcium carbonate, 42 parts, aluminium hydroxide, polynite 38 parts, vinyl-acetic ester 42 parts, benzene emulsion 38 parts, trisodium phosphate 42 parts, forsterite 38 parts, white oil 42 parts, sodium tetraborate 38 parts, 42 parts, resol, Zinic stearas 38 parts, silicon carbide micro-powder 42 parts, long-staple cotton fiber 38 parts, MALEIC ANHYDRIDE 42 parts, calcium plumbite 38 parts.
Further, above-mentioned fire-retardant acid and alkali-resistance waterproof fire hose material, be made up of the component of following mass fraction: acrylate 42 parts, dioctyl phthalate (DOP) 44 parts, polyvinyl chloride 40 parts, stearic acid 44 parts, vulcabond 40 parts, chloroprene rubber 44 parts, adipic acid pentaerythritol ester 40 parts, POLYESTER YARNS 46 parts, 40 parts, calcium carbonate, 44 parts, aluminium hydroxide, polynite 40 parts, vinyl-acetic ester 44 parts, benzene emulsion 40 parts, trisodium phosphate 44 parts, forsterite 40 parts, white oil 44 parts, sodium tetraborate 40 parts, 44 parts, resol, Zinic stearas 40 parts, silicon carbide micro-powder 44 parts, long-staple cotton fiber 40 parts, MALEIC ANHYDRIDE 44 parts, calcium plumbite 40 parts.
Further, above-mentioned fire-retardant acid and alkali-resistance waterproof fire hose material preparation method step is as follows:
(1) acrylate of described mass fraction, dioctyl phthalate (DOP), polyvinyl chloride, stearic acid, vulcabond, chloroprene rubber, adipic acid pentaerythritol ester, POLYESTER YARNS, calcium carbonate, aluminium hydroxide, polynite, vinyl-acetic ester, trisodium phosphate, forsterite, white oil, sodium tetraborate, resol, Zinic stearas, long-staple cotton fiber, MALEIC ANHYDRIDE, calcium plumbite are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min;
(2) add the benzene emulsion of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the silicon carbide micro-powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix this product that rear obtained solid content is about 20 ~ 70%.
Above-mentioned each component function is as follows:
(1) acrylate: sterling is white, needle-shaped crystals.Be insoluble in water and common organic solvents, can be dissolved in hot ethanol, be slightly dissolved in hot water, be soluble in diluted acid, dilute alkaline aqueous solution.Stable in soda acid.Transparent, low toxicity, is easy to preparation, cementability widely, water tolerance, weather resistance.Rubber based on this product, oil resistant, thermotolerance are better.
(2) dioctyl phthalate (DOP): colourless transparent liquid, water insoluble, be dissolved in ethanol, ether, the most of organic solvent of mineral wet goods.This product is important universal softening agent, and have good over-all properties, good mixing property, plasticizing efficiency is high, and volatility is lower, and low-temperature pliability is better, water-fast extraction, and electric property is high, thermotolerance and weathering resistance good.Be mainly used in the processing of polyvinyl chloride (PVC) RESINS, also can be used for the processing of the superpolymer such as chemical fibre resin, acetate resin, ABS resin and rubber, also can be used for making paint, dyestuff, dispersion agent etc.
(3) polyvinyl chloride: this product is that vinyl chloride monomer is at the initiator such as superoxide, azo-compound; Or by the polymkeric substance that mechanism of free-radical polymerization is polymerized under light, heat effect.True qualities are that micro-yellow is translucent, glossy.Transparency is better than polyethylene, polypropylene, is worse than polystyrene, and different with auxiliary dosage, be divided into soft, rigid polyvinyl chloride, soft goods is soft and tough, and feel is glued, and the hardness of boardy product is higher than Low Density Polyethylene, and lower than polypropylene, in flexion, place there will be albinism.Stable; Not easily by acid, caustic corrosion; Ratio of specific heat is comparatively tolerated.Have fire-retardant, chemical proofing is high, physical strength and the good advantage of electrical insulating property.All be widely used in material of construction, mechanicals, daily necessities, flooring laminate, floor tile, leatheroid, tubing, electric wire, packing film, bottle, foam material, sealing material, fiber etc.
(4) stearic acid: sterling is the wax-like small pieces xln of white slightly gloss, is slightly soluble in cold water, is dissolved in alcohol, acetone, be soluble in benzene, chloroform, ether, tetracol phenixin, dithiocarbonic anhydride, amyl acetate-n and toluene etc.Nontoxic.Being widely used in the manufacture of PVC plastic pipe, sheet material, section bar, film, is PVC heat stabilizer, has good oilness and good light, heat stabilization.Play an important role in the synthesis and the course of processing of rubber, be the vulcanization leveller of widespread use in natural gum, synthetic rubber and latex, also can be used as softening agent and tenderizer.
(5) vulcabond: this product is mainly used as the raw material manufacturing polyurethane material.Polyurethane material is obtained through being polymerized with polyether glycol or polyester polyol by this product, has non yellowing and good application performance, is widely used as the polyurethane coating of industry and automobile.
(6) chloroprene rubber: outward appearance is sheet or the block of oyster white, beige or light brown, is dissolved in toluene, dimethylbenzene, ethylene dichloride, three vanadium ethene, is slightly soluble in acetone, methylethylketone, vinyl acetic monomer, hexanaphthene, is insoluble to normal hexane, industrial naptha.There is good physical and mechanical properties, oil resistant, heat-resisting, resistance to combustion, resistance to daylight, resistance to ozone, acid and alkali-resistance, chemical-resistant reagent.Have higher tensile strength, elongation and reversible crystallinity, cementability is good, is widely used in weathering resistance product, viscose glue sole, coating and rocket fuel.
(7) adipic acid pentaerythritol ester: there is excellent lubricity, viscosity index is high, non-flame properties good; Acid esters has good surface filming, can be used in soft, hard PVC sheet, sheet material conductivity type material, tubing, clear vial material and heat-shrinkable film.
(8) POLYESTER YARNS: the characteristic of this product can be supported by chemical substance and often be washed, reduces clothing and to fade and decolour phenomenon, so hotel uniform, stone mill blue jeans clothing, Sportswear or garment for children all can manufacture by POLYESTER YARNS.The polyester thread that toughness is high can bear larger pulling force; And its fire line is high; Even if clothing is close to flame; Also not easily fire is touched.
(9) calcium carbonate: white solid, tasteless, odorless.Have good consistency with rubber, there is reinforcement, performance that filling, toning, improvement add technique and goods, can make rubber easily mixing, easily disperse, mixing rear colloid is soft, and rubber surface is smooth; The extensibility of goods, tensile strength, tear strength etc. can be made to have the raising of essence.
(10) aluminium hydroxide: this product is the maximum and most widely used inorganic fire-retarded additive of consumption, can not only be fire-retardant as fire retardant, and can prevent from being fuming, do not produce dropping, do not produce toxic gas, therefore, obtain and apply more widely, usage quantity is also increasing year by year.Use range comprises the industries such as thermosetting resin, thermoplastics, synthetic rubber, coating and building materials.
(11) polynite: a kind of natural mineral of silicate is the essential mineral component of bentonite ore.There is unique one dimension layered nano-structure and cationic exchange characteristic, thus give the many modifications of polynite may with the expansion of Application Areas.Polynite through modification has very strong adsorptive power, good dispersing property, can widespread use macromolecular material industry as the additive of nanometer polymer macromolecular material, mechanical properties of polymer, flame retardant properties, thermal stability are improved, have a extensive future.Deng, thus play the effect strengthening polymkeric substance comprehensive physical performance, improve materiel machining performance simultaneously.
(12) vinyl-acetic ester: colourless liquid, has sweet ether taste; Be slightly soluble in water, be dissolved in alcohol, acetone, benzene, chloroform.Mainly for the production of polyvinyl alcohol resin and synthon.The copolymerization of monomer whose energy can produce multiple use tackiness agent; The high molecular synthetic material of different performance can also be made with vinylchlorid, vinyl cyanide, butenoic acid, vinylformic acid, vinyl monomer energy copolymerized grafting, block etc.
(13) benzene emulsion: this product is obtained through emulsion copolymerization by vinylbenzene and acrylate monomer, milky white liquid, band blue light.It is water-fast, alkaline-resisting, scrub resistance can be good, and resistance to outdoor aging, is widely used in the field such as tackiness agent, coating.
(14) trisodium phosphate: water white transparency crystallization or white crystalline powder.Soluble in water, its aqueous solution is in alkalescence; Be insoluble to alcohol.It has the phosphatic general character of General polymeric, and the being knotted property of the protein that namely has emulsifying property, dispersiveness, prevents fats oxidn, improves, also has and suppress the oxidation of food and the effect of fermentation at a high ph.Dispersion agent and emulsifying agent is used as in Chemical Manufacture.Also can be used for the aspect such as water conditioner, oil drilling, in the food industry as quality improver, emulsifying agent, buffer reagent, sequestrant etc.
(15) forsterite: as refractory materials.Make forsterite brick, for ladle, in glass melter; As filler for tap holes of electric furnace main raw material; As soaking pit siege ramming material.
(16) white oil: this product is by the mixture of oil gained refining liquid hydrocarbon, is mainly saturated naphthenic hydrocarbon and alkane mixture, crude oil through normal pressure and vacuum fractionation, solvent extraction and dewaxing, hydrofining and obtaining.Semi-transparent clear oily liquids, nothing or almost unstressed configuration, odorless time cold, tasteless, slightly oil sample smell during heating, water insoluble, ethanol, is dissolved in volatile oil, miscible in most nonvolatile oil, stable to light, heat, acid etc., for the manufacture of washing powder, synthetic detergent, synthetic petroleum albumen, farm chemical emulgent etc.
(17) sodium tetraborate: very important containing boron mineral and boron compound.Be generally the white powder containing clear crystal, soluble in water.This product has been widely used, and can be used as sanitising agent, makeup, sterilant, also can be used for configuration buffered soln and produces other boron compounds etc.
(18) resol: yellow, transparent, amorphous cake mass, because being blush containing free phenol, is soluble in alcohol, water insoluble, stablizes water, weak acid, weak caustic solution.There is good acid resistance, mechanical property, resistance toheat, be widely used in the industries such as anticorrosion engineering, tackiness agent, fire retardant material, grinding wheel manufacture.
(19) Zinic stearas: white powder, water insoluble, be dissolved in ethanol, benzene, toluene, the turpentine wet goods organic solvent of heat.The main lubricant as styrene resin, resol, amine resin and releasing agent.In rubber, also there is vulcanization leveller, the function of tenderizer simultaneously.
(20) silicon carbide micro-powder: in green, crystalline structure, hardness is high, and cutting power is comparatively strong, and stable chemical nature, good heat conductivity is the engineering work material of solar photovoltaic industry, semiconductor industry, piezoquartz industry.
(21) long-staple cotton fiber: long stapled cotton is best in quality, its fiber is soft and long, is generally 33 ~ 39 millimeters, the longlyest reaches 64 millimeters; Fineness is 7000 ~ 8500 meters/gram, width 15 ~ 16 microns; Intensity is higher, is 4 ~ 5 gram forces/root, length of fracture 33 ~ 40 km; Turning bent more, is 80 ~ 120/centimetre.For senior giant tyre cord fabrics of weaving.
(22) MALEIC ANHYDRIDE: colourless crystallization, has intense stimulus smell, easily distils.Obtaining primarily of the normal butane in benzene or C-4-fraction or butylene oxidation, is the raw material producing unsaturated polyester and organic synthesis.Plastics industry is for the manufacture of softening agent.Paper industry is for the manufacture of paper treating agent.Synthetic resin industry is for the manufacture of unsaturated polyester resin, Synolac etc.Coatings industry is for the manufacture of insullac, white enamel paint, baking finish, varnish etc.Pesticide industry is for the manufacture of agricultural chemicals Phosphothion and higher effective and lower toxic pesticide 4049 etc.Medicine industry is for the manufacture of long-acting sulfonamide.Oil prodution industry is used as fat, oily sanitas.Organic industry is for the manufacture of fumaric acid and tetrahydrofuran (THF) etc.Chemical reagent is used as in analytical chemistry.
(23) calcium plumbite: in faint yellow, chemical structure and red lead close.Its corrosion inhibition is alkalescence and forms calcium soap.Be widely used on iron and steel and galvanized workpiece.Also can be used for the seal coat of inorganic zinc.
This beneficial effect of the invention is: this fire-retardant acid and alkali-resistance waterproof fire hose material preparation process method is simple, and prepared product has comparatively superior fire-retardant, burn into water resistance, for fire hose preparation, improves product performance.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
embodiment 1
Fire-retardant acid and alkali-resistance waterproof fire hose material in the present embodiment, be made up of the component of following mass fraction: acrylate 38 parts, dioctyl phthalate (DOP) 40 parts, polyvinyl chloride 36 parts, stearic acid 40 parts, vulcabond 36 parts, chloroprene rubber 40 parts, adipic acid pentaerythritol ester 36 parts, POLYESTER YARNS 42 parts, 36 parts, calcium carbonate, 40 parts, aluminium hydroxide, polynite 36 parts, vinyl-acetic ester 40 parts, benzene emulsion 36 parts, trisodium phosphate 40 parts, forsterite 36 parts, white oil 40 parts, sodium tetraborate 36 parts, 40 parts, resol, Zinic stearas 36 parts, silicon carbide micro-powder 40 parts, long-staple cotton fiber 36 parts, MALEIC ANHYDRIDE 40 parts, calcium plumbite 36 parts.
Above-mentioned fire-retardant acid and alkali-resistance waterproof fire hose material preparation method step is as follows:
(1) acrylate of described mass fraction, dioctyl phthalate (DOP), polyvinyl chloride, stearic acid, vulcabond, chloroprene rubber, adipic acid pentaerythritol ester, POLYESTER YARNS, calcium carbonate, aluminium hydroxide, polynite, vinyl-acetic ester, trisodium phosphate, forsterite, white oil, sodium tetraborate, resol, Zinic stearas, long-staple cotton fiber, MALEIC ANHYDRIDE, calcium plumbite are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, jitter time is 60min;
(2) add the benzene emulsion of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min;
(3) add the silicon carbide micro-powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min; Mix this product that rear obtained solid content is about 20%.
embodiment 2
Fire-retardant acid and alkali-resistance waterproof fire hose material in the present embodiment, be made up of the component of following mass fraction: acrylate 40 parts, dioctyl phthalate (DOP) 42 parts, polyvinyl chloride 38 parts, stearic acid 42 parts, vulcabond 38 parts, chloroprene rubber 42 parts, adipic acid pentaerythritol ester 38 parts, POLYESTER YARNS 44 parts, 38 parts, calcium carbonate, 42 parts, aluminium hydroxide, polynite 38 parts, vinyl-acetic ester 42 parts, benzene emulsion 38 parts, trisodium phosphate 42 parts, forsterite 38 parts, white oil 42 parts, sodium tetraborate 38 parts, 42 parts, resol, Zinic stearas 38 parts, silicon carbide micro-powder 42 parts, long-staple cotton fiber 38 parts, MALEIC ANHYDRIDE 42 parts, calcium plumbite 38 parts.
Above-mentioned fire-retardant acid and alkali-resistance waterproof fire hose material preparation method step is as follows:
(1) acrylate of described mass fraction, dioctyl phthalate (DOP), polyvinyl chloride, stearic acid, vulcabond, chloroprene rubber, adipic acid pentaerythritol ester, POLYESTER YARNS, calcium carbonate, aluminium hydroxide, polynite, vinyl-acetic ester, trisodium phosphate, forsterite, white oil, sodium tetraborate, resol, Zinic stearas, long-staple cotton fiber, MALEIC ANHYDRIDE, calcium plumbite are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, jitter time is 45min;
(2) add the benzene emulsion of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min;
(3) add the silicon carbide micro-powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min; Mix this product that rear obtained solid content is about 35%.
embodiment 3
Fire-retardant acid and alkali-resistance waterproof fire hose material in the present embodiment, be made up of the component of following mass fraction: acrylate 42 parts, dioctyl phthalate (DOP) 44 parts, polyvinyl chloride 40 parts, stearic acid 44 parts, vulcabond 40 parts, chloroprene rubber 44 parts, adipic acid pentaerythritol ester 40 parts, POLYESTER YARNS 46 parts, 40 parts, calcium carbonate, 44 parts, aluminium hydroxide, polynite 40 parts, vinyl-acetic ester 44 parts, benzene emulsion 40 parts, trisodium phosphate 44 parts, forsterite 40 parts, white oil 44 parts, sodium tetraborate 40 parts, 44 parts, resol, Zinic stearas 40 parts, silicon carbide micro-powder 44 parts, long-staple cotton fiber 40 parts, MALEIC ANHYDRIDE 44 parts, calcium plumbite 40 parts.
Above-mentioned fire-retardant acid and alkali-resistance waterproof fire hose material preparation method step is as follows:
(1) acrylate of described mass fraction, dioctyl phthalate (DOP), polyvinyl chloride, stearic acid, vulcabond, chloroprene rubber, adipic acid pentaerythritol ester, POLYESTER YARNS, calcium carbonate, aluminium hydroxide, polynite, vinyl-acetic ester, trisodium phosphate, forsterite, white oil, sodium tetraborate, resol, Zinic stearas, long-staple cotton fiber, MALEIC ANHYDRIDE, calcium plumbite are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min;
(2) add the benzene emulsion of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) add the silicon carbide micro-powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min; Mix this product that rear obtained solid content is about 70%.
Carry out performance measurement for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured data are as shown in table 1.Fire protection flame retarding level estimate adopts UL94 standard.
Table 1 the performance test results
Visible, material of the present invention has corrosion-resistant, fire protection flame retarding, water resistance preferably.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (5)
1. a fire-retardant acid and alkali-resistance waterproof fire hose material, it is characterized in that: be made up of the component of following mass fraction: acrylate 38 ~ 42 parts, dioctyl phthalate (DOP) 40 ~ 44 parts, polyvinyl chloride 36 ~ 40 parts, stearic acid 40 ~ 44 parts, vulcabond 36 ~ 40 parts, chloroprene rubber 40 ~ 44 parts, adipic acid pentaerythritol ester 36 ~ 40 parts, POLYESTER YARNS 42 ~ 46 parts, 36 ~ 40 parts, calcium carbonate, 40 ~ 44 parts, aluminium hydroxide, polynite 36 ~ 40 parts, vinyl-acetic ester 40 ~ 44 parts, benzene emulsion 36 ~ 40 parts, trisodium phosphate 40 ~ 44 parts, forsterite 36 ~ 40 parts, white oil 40 ~ 44 parts, sodium tetraborate 36 ~ 40 parts, 40 ~ 44 parts, resol, Zinic stearas 36 ~ 40 parts, silicon carbide micro-powder 40 ~ 44 parts, long-staple cotton fiber 36 ~ 40 parts, MALEIC ANHYDRIDE 40 ~ 44 parts, calcium plumbite 36 ~ 40 parts.
2. fire-retardant acid and alkali-resistance waterproof fire hose material according to claim 1, it is characterized in that: described fire-retardant acid and alkali-resistance waterproof fire hose material is made up of the component of following mass fraction: acrylate 38 parts, dioctyl phthalate (DOP) 40 parts, polyvinyl chloride 36 parts, stearic acid 40 parts, vulcabond 36 parts, chloroprene rubber 40 parts, adipic acid pentaerythritol ester 36 parts, POLYESTER YARNS 42 parts, 36 parts, calcium carbonate, 40 parts, aluminium hydroxide, polynite 36 parts, vinyl-acetic ester 40 parts, benzene emulsion 36 parts, trisodium phosphate 40 parts, forsterite 36 parts, white oil 40 parts, sodium tetraborate 36 parts, 40 parts, resol, Zinic stearas 36 parts, silicon carbide micro-powder 40 parts, long-staple cotton fiber 36 parts, MALEIC ANHYDRIDE 40 parts, calcium plumbite 36 parts.
3. according to the fire-retardant acid and alkali-resistance waterproof fire hose material described in claim 1 to 2, it is characterized in that: described fire-retardant acid and alkali-resistance waterproof fire hose material is made up of the component of following mass fraction: acrylate 40 parts, dioctyl phthalate (DOP) 42 parts, polyvinyl chloride 38 parts, stearic acid 42 parts, vulcabond 38 parts, chloroprene rubber 42 parts, adipic acid pentaerythritol ester 38 parts, POLYESTER YARNS 44 parts, 38 parts, calcium carbonate, 42 parts, aluminium hydroxide, polynite 38 parts, vinyl-acetic ester 42 parts, benzene emulsion 38 parts, trisodium phosphate 42 parts, forsterite 38 parts, white oil 42 parts, sodium tetraborate 38 parts, 42 parts, resol, Zinic stearas 38 parts, silicon carbide micro-powder 42 parts, long-staple cotton fiber 38 parts, MALEIC ANHYDRIDE 42 parts, calcium plumbite 38 parts.
4. the fire-retardant acid and alkali-resistance waterproof fire hose material according to claims 1 to 3, it is characterized in that: described fire-retardant acid and alkali-resistance waterproof fire hose material is made up of the component of following mass fraction: acrylate 42 parts, dioctyl phthalate (DOP) 44 parts, polyvinyl chloride 40 parts, stearic acid 44 parts, vulcabond 40 parts, chloroprene rubber 44 parts, adipic acid pentaerythritol ester 40 parts, POLYESTER YARNS 46 parts, 40 parts, calcium carbonate, 44 parts, aluminium hydroxide, polynite 40 parts, vinyl-acetic ester 44 parts, benzene emulsion 40 parts, trisodium phosphate 44 parts, forsterite 40 parts, white oil 44 parts, sodium tetraborate 40 parts, 44 parts, resol, Zinic stearas 40 parts, silicon carbide micro-powder 44 parts, long-staple cotton fiber 40 parts, MALEIC ANHYDRIDE 44 parts, calcium plumbite 40 parts.
5. the fire-retardant acid and alkali-resistance waterproof fire hose material according to claim 1 or 4, is characterized in that: described fire-retardant acid and alkali-resistance waterproof fire hose material preparation method step is as follows:
(1) acrylate of described mass fraction, dioctyl phthalate (DOP), polyvinyl chloride, stearic acid, vulcabond, chloroprene rubber, adipic acid pentaerythritol ester, POLYESTER YARNS, calcium carbonate, aluminium hydroxide, polynite, vinyl-acetic ester, trisodium phosphate, forsterite, white oil, sodium tetraborate, resol, Zinic stearas, long-staple cotton fiber, MALEIC ANHYDRIDE, calcium plumbite are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min;
(2) add the benzene emulsion of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the silicon carbide micro-powder of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix this product that rear obtained solid content is about 20 ~ 70%.