CN105116697A - 非磁性负电激光打印机墨粉 - Google Patents
非磁性负电激光打印机墨粉 Download PDFInfo
- Publication number
- CN105116697A CN105116697A CN201410458559.9A CN201410458559A CN105116697A CN 105116697 A CN105116697 A CN 105116697A CN 201410458559 A CN201410458559 A CN 201410458559A CN 105116697 A CN105116697 A CN 105116697A
- Authority
- CN
- China
- Prior art keywords
- ink powder
- laser printer
- adhesive resin
- negative electricity
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种非磁性负电激光打印机墨粉,粘合剂树脂为苯乙烯-丙烯酸共聚物,颜料为炭黑,电荷调节剂选用水杨酸锌,所述的内添剂选用低分子聚丙烯蜡,所述的外添剂选用疏水性二氧化硅,各组分的重量百分比为:粘合剂树脂78~90%,颜料3~9%,电荷调节剂2.1~8%,内添剂0.4~2.8%,外添剂0.1~4%。粘合剂树脂选用苯乙烯-丙烯酸共聚物,既包容了两种不间组分成分,提高了墨粉的性能指标,又简化了生产工艺降低了成本。另外对疏水性二氧化硅的疏水度加以控制,以防调色剂吸潮结团影响打印效果。使用本发明的非磁性负电激光打印机墨粉获得的打印图像分辨率高、底灰小。
Description
技术领域
本发明涉及激光打印机墨粉的技术领域,具体说是一种非磁性负电激光打印机墨粉。
背景技术
激光打印机的墨粉按分为电性能可以分为正电粉和负电粉,按磁性能可以分为有磁粉和非磁粉,按组份可以分为单组份和双组分,由于单组份磁性墨粉中含有黑褐色的铁粉,所以不能够用于彩色打印机中,所以为保证墨粉在打印机中的通用性,单组份非磁性墨粉的开发越来越受到重视,单组份非磁性负电墨粉在循环使用及几乎无废粉,使得感光鼓不用清洁刮板,鼓组件没有废粉仓,结构大大简化。但在单组份非磁性负电墨粉的使用中,墨粉的迁移全靠墨粉自身的流动性和带电稳定性,因此对墨粉的粒度分布、球形化、带电均匀性及起电速率、稳定性都比单组份磁性显影方式高的多。
发明内容
本发明要解决的技术问题是提供一种非磁性负电激光打印机墨粉。
本发明为解决公知技术中存在的技术问题所采取的技术方案是:
本发明的非磁性负电激光打印机墨粉,由粘合剂树脂、颜料、电荷调节剂、内添剂及外添剂组成,上述粘合剂树脂为苯乙烯-丙烯酸共聚物,颜料为炭黑,所述的电荷调节剂选用水杨酸锌,所述的内添剂选用低分子聚丙烯蜡,所述的外添剂选用经环氧烷处理过的疏水性二氧化硅,上述各组分的重量百分比为:
粘合剂树脂78~90%,
颜料3~9%,
电荷调节剂2.1~8%,
内添剂0.4~2.8%,
外添剂0.1~4%。
本发明还可以采用以下技术措施:
粘合剂树脂中苯乙烯-丙烯酸共聚物的熔融指数MI为1.5~5.5。
所述疏水性二氧化硅的疏水度为20~40。
本发明具有的优点和积极效果是:
本发明的非磁性负电激光打印机墨粉中,粘合剂树脂选用苯乙烯-丙烯酸共聚物,既包容了两种不间组分成分,提高了墨粉的性能指标,又简化了生产工艺降低了成本。另外对疏水性二氧化硅的疏水度加以控制,以防调色剂吸潮结团影响打印效果。使用本发明的非磁性负电激光打印机墨粉获得的打印图像分辨率高、底灰小。
具体实施方式
以下参照实施例对本发明进行详细的说明。
实施例1、本发明的非磁性负电激光打印机墨粉中,粘合剂树脂为MI为1.5的苯乙烯-丙烯酸共聚物,颜料为炭黑,电荷调节剂选用水杨酸锌,内添剂选用低分子聚丙烯蜡,外添剂选用疏水度为30疏水性二氧化硅,上述各组分的重量百分比为:
苯乙烯-丙烯酸共聚物占90%,
炭黑占6%,
水杨酸锌占2.1%,
低分子聚丙烯蜡占1.8%,
疏水性二氧化硅占0.1%。
将苯乙烯-丙烯酸共聚物、炭黑、水杨酸锌、低分子聚丙烯蜡混合后,使用专用的高精度混炼设备恒温混炼,把聚丙烯、电荷调节剂等物质均匀地分散到混合物中,原料经过混炼后,再经冷却、预粉碎、粗粉碎及微粉碎、分级后得到如下粒度分布的分级品:
个数平均径:9.61μm,6.35μm以下:23.57%,
体积平均径:10.37μm,16.Oμm以上:1.17%
将疏水性二氧化硅外添剂加入上述分级品中,充分混合即获得所需的墨粉。
实施例2、本发明的非磁性负电激光打印机墨粉中,粘合剂树脂为MI为5.5的苯乙烯-丙烯酸共聚物,颜料为炭黑,电荷调节剂选用水杨酸锌,内添剂选用低分子聚丙烯蜡,外添剂选用疏水度为20疏水性二氧化硅,上述各组分的重量百分比为:
苯乙烯-丙烯酸共聚物占78%,
炭黑占9%,
水杨酸锌占8%,
低分子聚丙烯蜡占2.8%,
疏水性二氧化硅占2.2%。
将苯乙烯-丙烯酸共聚物、炭黑、水杨酸锌、低分子聚丙烯蜡混合后,使用专用的高精度混炼设备恒温混炼,把聚丙烯、电荷调节剂等物质均匀地分散到混合物中,原料经过混炼后,再经冷却、预粉碎、粗粉碎及微粉碎、分级后得到如下粒度分布的分级品:
个数平均径:9.57μm,6.35μm以下:27.57%,
体积平均径:10.24μm,16.Oμm以上:1.20%
将疏水性二氧化硅外添剂加入上述分级品中,充分混合即获得所需的墨粉。
实施例3、本发明的非磁性负电激光打印机墨粉中,粘合剂树脂为MI为5.5的苯乙烯-丙烯酸共聚物,颜料为炭黑,电荷调节剂选用水杨酸锌,内添剂选用低分子聚丙烯蜡,外添剂选用疏水度为20疏水性二氧化硅,上述各组分的重量百分比为:
苯乙烯-丙烯酸共聚物占86.6%,
炭黑占3%,
水杨酸锌占6%,
低分子聚丙烯蜡占0.4%,
疏水性二氧化硅占4%。
将苯乙烯-丙烯酸共聚物、炭黑、水杨酸锌、低分子聚丙烯蜡混合后,使用专用的高精度混炼设备恒温混炼,把聚丙烯、电荷调节剂等物质均匀地分散到混合物中,原料经过混炼后,再经冷却、预粉碎、粗粉碎及微粉碎、分级后得到如下粒度分布的分级品:
个数平均径:9.77μm,6.35μm以下:26.48%,
体积平均径:10.43μm,16.Oμm以上:1.16%
将疏水性二氧化硅外添剂加入上述分级品中,充分混合即获得所需的墨粉。
以上所述,仅是本发明的较佳实施例而已,并非对本发明作任何形式上的限制,虽然本发明已以较佳实施例公开如上,然而,并非用以限定本发明,任何熟悉本专业的技术人员,在不脱离本发明技术方案范围内,当然会利用揭示的技术内容作出些许更动或修饰,成为等同变化的等效实施例,但凡是未脱离本发明技术方案的内容,依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰,均属于本发明技术方案的范围内。
Claims (3)
1.一种非磁性负电激光打印机墨粉,由粘合剂树脂、颜料、电荷调节剂、内添剂及外添剂组成,其特征在于:上述粘合剂树脂为苯乙烯-丙烯酸共聚物,颜料为炭黑,所述的电荷调节剂选用水杨酸锌,所述的内添剂选用低分子聚丙烯蜡,所述的外添剂选用经环氧烷处理过的疏水性二氧化硅,上述各组分的重量百分比为:
粘合剂树脂78~90%,
颜料3~9%,
电荷调节剂2.1~8%,
内添剂0.4~2.8%,
外添剂0.1~4%。
2.根据权利要求1所述的非磁性负电激光打印机墨粉,其特征在于:粘合剂树脂中苯乙烯-丙烯酸共聚物的熔融指数MI为1.5~5.5。
3.根据权利要求1所述的非磁性负电激光打印机墨粉,其特征在于:所述疏水性二氧化硅的疏水度为20~40。