CN105110716A - Binding mortar for flexible facing bricks and preparation method thereof - Google Patents
Binding mortar for flexible facing bricks and preparation method thereof Download PDFInfo
- Publication number
- CN105110716A CN105110716A CN201510564999.7A CN201510564999A CN105110716A CN 105110716 A CN105110716 A CN 105110716A CN 201510564999 A CN201510564999 A CN 201510564999A CN 105110716 A CN105110716 A CN 105110716A
- Authority
- CN
- China
- Prior art keywords
- parts
- flexible
- water
- agent
- adhesive mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a binding mortar for flexible facing bricks and a preparation method thereof. The technical scheme is as follows: the binding mortar for flexible facing bricks is prepared from the following components in parts by weight: 20-30 parts of cementing material cement, 60-70 parts of quartz sand, 5-10 parts of filler heavy calcium carbonate, 0.3-0.4 part of water-retaining and wetting agent, 0.05-0.1 part of anti-slipping assistant, 0.3-0.5 part of crack-resistant water-retaining fiber, 3-5 parts of redispersible latex powder, 0.1-0.2 part of water repellent and 0.05-0.1 part of dispersing agent. The binding mortar for flexible facing bricks has the advantages of low material consumption, higher construction efficiency, high binding strength and low shedding tendency. The binding mortar for flexible facing bricks especially makes up the deformation generated by shrinkage due to temperature changes, resists cracks and has the function of joint filling, thereby being an environment-friendly flexible binding mortar applicable to different climatic conditions.
Description
Technical field
The present invention relates to the sticking mortar of a kind of architectural exterior insulation industry flexible clay facing tile, flexible patch, flexible porcelain tendre, particularly a kind of flexible clay facing tile adhesive mortar and preparation method thereof.
Background technology
Flexible clay facing tile is using inorganic materials as main base material, be equipped with high molecular polymer, again through the special a kind of novel inner-outer wall decoration plane material processed, flexible face brick look abundant, thickness is thin, quality is light, flexible, waterproof, seepage control, good endurance, easy construction, be used in the interior/exterior decoration finishing of various buildings, the flexible finishing material such as flexible face brick, flexible patch, flexible porcelain tendre is widely applied the decorations that decorating outer wall of building finishing is particularly suitable for external wall outer insulation on the market in recent years.
Traditional facing tile adhesive mortar generally adopts the back of the body bonding cement, sand to be added water stirring according to certainweight per-cent, criticize to scrape and be then affixed on base material in the face brick back side, the thickness of tack coat is at 5-10mm, its shortcoming be cohesive strength not high, easily come off, consumption of materials is large, easily produce shrinkage crack by temperature head change, particularly can not bond joint filling integration.
Summary of the invention
Object of the present invention is exactly in view of the foregoing defects the prior art has, provides a kind of flexible clay facing tile adhesive mortar and preparation method thereof, and consumption of materials is little, raising operating efficiency, cohesive strength are high, difficult drop-off.Particularly make up difference variation shrink produce deformation, opposing crackle has joint filling function concurrently, is suitable for environmentally friendly flexible adhesion mortar under Different climate condition.
Its technical scheme is: the component comprising following weight part is made: gelling material cement 20 ~ 30 parts, quartz sand 60 ~ 70 parts, filler coarse whiting 5 ~ 10 parts, water conservation wetting agent 0.3 ~ 0.4 part, anti-downslide auxiliary agent 0.05 ~ 0.1 part, anticracking water conservation fiber 0.3 ~ 0.5 part, redispersable latex powder 3 ~ 5 parts, hydrophober 0.1 ~ 0.2 part, dispersion agent 0.05 ~ 0.1 part.
Also pigment toner is comprised in above-mentioned flexible face brick binding agent.
Above-mentioned redispersable latex powder is ethene-vinyl acetate fat;
Above-mentioned water conservation wetting agent is ethoxyl methyl cellulose ether.
Above-mentioned hydrophober is silane.
Above-mentioned dispersion agent is polycarboxylate water-reducer.
A kind of preparation method of flexible clay facing tile adhesive mortar is: comprise the steps:
(1) by weight, take following component: gelling material cement 20 ~ 30 parts, quartz sand 60 ~ 70 parts, filler coarse whiting 5 ~ 10 parts, water conservation wetting agent 0.3 ~ 0.4 part, redispersable latex powder 3 ~ 5 parts, hydrophober 0.1 ~ 0.2 part, get its functional agent: in anticracking water conservation fiber 0.3 ~ 0.5 part, dispersion agent 0.05 ~ 0.1 part, anti-downslide auxiliary agent 0.05 ~ 0.1 part of loading container, after above metering, enter forced action type high speed dispersor in certain sequence respectively and carry out action of forced stirring;
(2) finely dispersed powder enters packaging facilities and packs, and packed weight is 25+0.3Kg;
(3) packaged flexible adhesion mortar at the construction field (site) with water according to 4.5: 1 weight percent mixing and stirring, during mixing, first add water and add flexible adhesion mortar again, the even post curing of slurry to be mixed is stirred for 5 minutes more again, make slurry reach even thickening effectiveness, can use.
Above-mentioned high speed dispersor carries out the pigment toner that can add 3 ~ 5 parts in action of forced stirring process.
The invention has the beneficial effects as follows: consumption of materials is little, raising operating efficiency, cohesive strength are high, difficult drop-off.Particularly make up difference variation shrink produce deformation, opposing crackle has joint filling function concurrently, is suitable for environmentally friendly flexible adhesion mortar under Different climate condition.
Embodiment
In conjunction with the embodiments, the invention will be further described:
Embodiment one:
The component that a kind of flexible clay facing tile adhesive mortar that the present invention mentions comprises following weight part is made: gelling material cement 20 parts, quartz sand 60 parts, filler coarse whiting 5 parts, water conservation wetting agent 0.3 part, anti-downslide auxiliary agent 0.05 part, anticracking water conservation fiber 0.3 part, redispersable latex powder 3 parts, hydrophober 0.1 part, dispersion agent 0.05 part.
Wherein, also pigment toner is comprised in flexible face brick binding agent.
Wherein, redispersable latex powder is ethene-vinyl acetate fat;
Wherein, water conservation wetting agent is ethoxyl methyl cellulose ether.
Wherein, hydrophober is silane.
Wherein, dispersion agent is polycarboxylate water-reducer.
A kind of preparation method of flexible clay facing tile adhesive mortar is: comprise the steps:
(1) by weight, take following component: gelling material cement 20 parts, quartz sand 60 parts, filler coarse whiting 5 parts, water conservation wetting agent 0.3 part, redispersable latex powder 3 parts, hydrophober 0.1 part, get its functional agent: in anticracking water conservation fiber 0.3 part, dispersion agent 0.05 part, anti-downslide auxiliary agent 0.05 part of loading container, after above metering, enter forced action type high speed dispersor in certain sequence respectively and carry out action of forced stirring;
(2) finely dispersed powder enters packaging facilities and packs, and packed weight is 25+0.3Kg;
(3) packaged flexible adhesion mortar at the construction field (site) with water according to 4.5: 1 weight percent mixing and stirring, during mixing, first add water and add flexible adhesion mortar again, the even post curing of slurry to be mixed is stirred for 5 minutes more again, make slurry reach even thickening effectiveness, can use.
Above-mentioned high speed dispersor carries out the pigment toner that can add 3 ~ 5 parts in action of forced stirring process.
Embodiment two:
The component that a kind of flexible clay facing tile adhesive mortar that the present invention mentions comprises following weight part is made: gelling material cement 25 parts, quartz sand 65 parts, filler coarse whiting 7.5 parts, water conservation wetting agent 0.35 part, anti-downslide auxiliary agent 0.55 part, anticracking water conservation fiber 0.4 part, redispersable latex powder 4 parts, hydrophober 0.15 part, dispersion agent 0.55 part.
A kind of preparation method of flexible clay facing tile adhesive mortar is: comprise the steps:
(1) by weight, take following component: gelling material cement 25 parts, quartz sand 65 parts, filler coarse whiting 7.5 parts, water conservation wetting agent 0.35 part, redispersable latex powder 4 parts, hydrophober 0.15 part, gets its functional agent: anticracking water conservation fiber 0.4 part, dispersion agent 0.55 part, in anti-downslide auxiliary agent 0.55 part of loading container, after above metering, enter forced action type high speed dispersor in certain sequence respectively and carry out action of forced stirring;
(2) finely dispersed powder enters packaging facilities and packs, and packed weight is 25+0.3Kg;
(3) packaged flexible adhesion mortar at the construction field (site) with water according to 4.5: 1 weight percent mixing and stirring, during mixing, first add water and add flexible adhesion mortar again, the even post curing of slurry to be mixed is stirred for 5 minutes more again, make slurry reach even thickening effectiveness, can use.
Embodiment three:
The component that a kind of flexible clay facing tile adhesive mortar that the present invention mentions comprises following weight part is made: gelling material cement 30 parts, quartz sand 70 parts, filler coarse whiting 10 parts, water conservation wetting agent 0.4 part, anti-downslide auxiliary agent 0.1 part, anticracking water conservation fiber 0.5 part, redispersable latex powder 5 parts, hydrophober 0.2 part, dispersion agent 0.1 part.
A kind of preparation method of flexible clay facing tile adhesive mortar is: comprise the steps:
(1) by weight, take following component: gelling material cement 30 parts, quartz sand 70 parts, filler coarse whiting 10 parts, water conservation wetting agent 0.4 part, redispersable latex powder 5 parts, hydrophober 0.2 part, gets its functional agent: anticracking water conservation fiber 0.5 part, dispersion agent 0.1 part, in anti-downslide auxiliary agent 0.1 part of loading container, after above metering, enter forced action type high speed dispersor in certain sequence respectively and carry out action of forced stirring;
(2) finely dispersed powder enters packaging facilities and packs, and packed weight is 25+0.3Kg;
(3) packaged flexible adhesion mortar at the construction field (site) with water according to 4.5: 1 weight percent mixing and stirring, during mixing, first add water and add flexible adhesion mortar again, the even post curing of slurry to be mixed is stirred for 5 minutes more again, make slurry reach even thickening effectiveness, can use.
Above-mentioned three embodiments, all can make the good flexible clay facing tile adhesive mortar of effect, the bonding tensile strength of mortar can be improved in adhesive mortar by redispersable latex powder, reduce Young's modulus, improve the deformation behavior with difference variation, promote abrasive wear resistance, improve cohesive strength, reduce carbonation depth, reduce material water-absorbent, construct under can meeting differing temps envrionment conditions, add hydrophober makes material have the infiltration of hydrophobic nature minimizing external environment water simultaneously, decrease the possibility of secondary hydration, owing to adding water conservation wetting agent---ethoxyl methyl cellulose ether makes polymer mortar have certain uniform and stable bubble and thickening effectiveness, improve the effect of application property and anti-downslide, due to the water retention of ether of cellulose, the water that the ether of cellulose of certain volume keeps has time enough can impel cement continuous hydration in adhesive mortar, the sticking power of base material under raising adhesive mortar.
Using method:
By will the redispersable latex powder of preparation and other gelling material and various aggregate, filler and other additive ethoxyl methyl cellulose ether, starch ethers, wood fibre, the dry-mixed mortar that hydrophober physical mixed is made, when this powder stirs by adding water, under the effect of hydrophilic protective colloid and mechanical shearing, latex powder Granular composite is in water, to be soaked equably by the effect latex powder of various additive and in the surrounding being distributed to various powder and gap, when moisture evaporation, polymer emulsion powder draws close mutually formation film gradually, along with step volatilization under the entering of moisture and minimizing---the absorption of basic unit, the consumption of hydrated reaction of cement, surface-moisture volatilizees in air, latex powder particle is close gradually, interface is merged gradually mutually, finally become continuous print macromolecule membrane, redispersable latex powder can improve the bonding tensile strength of mortar in adhesive mortar, reduce Young's modulus, improve the deformation behavior with difference variation, promote abrasive wear resistance, improve cohesive strength, reduce carbonation depth, reduce material water-absorbent, construct under can meeting differing temps envrionment conditions, add hydrophober makes material have the infiltration of hydrophobic nature minimizing external environment water simultaneously, decrease the possibility of secondary hydration, owing to adding water conservation wetting agent---ethoxyl methyl cellulose ether makes polymer mortar have certain uniform and stable bubble and thickening effectiveness, improve the effect of application property and anti-downslide, due to the water retention of ether of cellulose, the water that the ether of cellulose of certain volume keeps has time enough can impel cement continuous hydration in adhesive mortar, the sticking power of base material under raising adhesive mortar, in addition due to bonding and the integrated material of joint filling of face brick adhesive mortar, joint filling part will be grown it and be exposed in external environment, in bonding face brick construction process, along with the volatilization of moisture and hydrated cementitious will produce very large contraction, the dry shrinkage of flexible adhesion mortar is required it will will be very high, therefore prevent the material ftractureed from preventing dry shrinkage and later stage cement secondary hydration in a large number by adding, the strain that cohesive strength change produces is shunk, crack resistence and the long durability of flexible adhesion agent can be improved.In addition, in order to meet flexible adhesion mortar dispersed with stirring in use, add poly carboxylic acid dispersiveness, this dispersion agent is nonionogenic tenside, newly mixing in adhesive mortar the interfacial tension that can reduce between the surface tension of liquid and solid-liquid, liquid is easily launched on the surface at powder, reach the rapid dispersion wetting action in system, thus improve the application property of adhesive mortar, strengthen the tinting strength of pigment toner, reduce the generation of bubble in mortar, wetting defend and split fibre surface, enhancing system improves the snappiness of mortar, poly carboxylic acid dispersiveness is cement surfactant simultaneously, have and reduce the effect that hydrated cementitious water consumption improves adhesive mortar intensity, the minimizing of hydrated cementitious water consumption, same viscosity water consumption cement consumption reduces, cement consumption reduces the deformation retract of hydrated cementitious shrinkage strain and secondary hydration, thus reduce probability and the possibility of later stage adhesive mortar generation crackle, extend the endurance of adhesive mortar,
In addition, this flexible adhesion slurry is sticky directly criticize in advance with profile of tooth spatula scrape brick to be pasted substrate surface on, then combing is carried out with profile of tooth spatula, it is made to form convex stripe and the uniform screed of thickness, then by flexible face brick by above being pressed in, can according to the position of design paper or arranging situation adjustment face brick, the thickness of binding paste is 2-4mm, reduce the effect that materials consumption consumption plays environmental protection and energy saving, be applicable to applying;
Certainly this flexible adhesion mortar can use according to concrete the best effect that the effect of face brick adjusts mortar slurry grating, system formulation reaches applicable bonding face brick, this flexible adhesion mortar can according to the concrete tone using face brick, and the pigment colorant consumption of adjustment mortar slurry reaches best decorative effect.
The innovative point contrasted with existing like product:
1, the high and low accumulation of salt in the surface soil of intensity or without the accumulation of salt in the surface soil
Contrast with existing like product, the characteristic early stage hydrated cementitious of binding agent in use due to cement cementitious material of the similar cement based that existing like product uses is insufficient, incomplete, there is the calcium ion of unbound state, hydroxide ion and other alkaline-earth metal ions, react with the carbonic acid gas in air, there is salting-out phenomenon or the accumulation of salt in the surface soil, and there is secondary hydration and long-term aquation in the medium-term and long-term exposure of later stage application process, there is a large amount of accumulation of salt in the surface soil phenomenons in the environment.This flexible adhesion agent improves owing to having carried out adjusting in formula, add the filler suppressing the accumulation of salt in the surface soil to improve early stage hydrated cementitious, the calcium ion that there is unbound state, hydroxide ion and other alkaline-earth metal ions changed in filler and cement is fully reacted, abundant hydrated cementitious, improve early strength and decrease the chance that later stage hydrated reaction of cement produces the accumulation of salt in the surface soil, make this flexible adhesion agent be consistent in long-term color developing, solve the problem of the cement base products accumulation of salt in the surface soil for a long time;
2, make up difference variation shrink produce deformation, opposing crackle have joint filling function concurrently
Contrast with existing like product, existing like product due to each side reason ubiquity chronicity expose there is adhesive mortar crackle or Tile falling problem in the environment, mainly because adhesive mortar long-term exposure is subject to humiture change in the environment, freeze-thaw cycle impact and secondary hydration cannot make up difference variation and shrink the deformation and the crackle that causes that produce, and such flexible adhesion agent is improved by the adjustment of formula, prevent the material of flexible auxiliary agent and cracking from preventing dry shrinkage and later stage cement secondary hydration in a large number by adding, the strain that cohesive strength change produces is shunk, make up difference variation and shrink generation deformation, opposing crackle, improve crack resistence and the long durability of flexible adhesion agent,
Contrast with existing like product simultaneously, existing like product binding agent is only used in bonding face brick, and such flexible adhesion agent meets the performance index requirement of spackling each side simultaneously, improve construction technology, one-off construction can be reached, do not need secondary joint filling, have certain improvement from the aspect such as artificial, cost, efficiency;
3, to contrast water-fast bonding tensile strength high for the present invention and existing like product
Due to the water-intake rate of exposed wall facing brick and smooth surface degree different, contrast with existing like product, the water-fast intensity of existing like product binding agent is substantially on the low side, this flexible adhesion agent is improved by the adjustment of formula, with the addition of the adjustment of a certain amount of hydrophober, filler and adhesive mortar grating, the compaction rate of adhesive mortar is improved, and adding the tensile strength impact of adhesive mortar of hydrophober is comparatively large, and water-fast intensity reaches 0.67MPa and meets JGJ110-2008 standard-required.
In sum, the present invention compared with similar products, its early strength is high, make up difference variation and shrink generation deformation, opposing crackle (snappiness is good), water-fast bonding tensile strength high hydrophobic is good, material consumption is low, and the present invention's flexible face brick product that bonds obviously is better than existing conventional products, and Data Comparison is as follows:
The above, be only part preferred embodiment of the present invention, any those of ordinary skill in the art all may utilize the technical scheme correct of above-mentioned elaboration or are revised as equivalent technical scheme.Therefore, any simple modification of carrying out according to technical scheme of the present invention or substitute equivalents, belong to the scope of protection of present invention to the greatest extent.
Claims (8)
1. a flexible clay facing tile adhesive mortar, it is characterized in that: the component comprising following weight part is made: gelling material cement 20 ~ 30 parts, quartz sand 60 ~ 70 parts, filler coarse whiting 5 ~ 10 parts, water conservation wetting agent 0.3 ~ 0.4 part, anti-downslide auxiliary agent 0.05 ~ 0.1 part, anticracking water conservation fiber 0.3 ~ 0.5 part, redispersable latex powder 3 ~ 5 parts, hydrophober 0.1 ~ 0.2 part, dispersion agent 0.05 ~ 0.1 part.
2. a kind of flexible clay facing tile adhesive mortar according to claim 1, is characterized in that: also comprise component pigment toner in described flexible face brick binding agent.
3. a kind of flexible clay facing tile adhesive mortar according to claim 1, is characterized in that: described redispersable latex powder is ethene-vinyl acetate fat.
4. a kind of flexible clay facing tile adhesive mortar according to claim 1, is characterized in that: described water conservation wetting agent is ethoxyl methyl cellulose ether.
5. a kind of flexible clay facing tile adhesive mortar according to claim 1, is characterized in that: described hydrophober is silane.
6. a kind of flexible clay facing tile adhesive mortar according to claim 1, is characterized in that: described dispersion agent is polycarboxylate water-reducer.
7. the preparation method of a kind of flexible clay facing tile adhesive mortar according to any one of claim 1-6 is: it is characterized in that: comprise the steps:
(1) by weight, take following component: gelling material cement 20 ~ 30 parts, quartz sand 60 ~ 70 parts, filler coarse whiting 5 ~ 10 parts, water conservation wetting agent 0.3 ~ 0.4 part, redispersable latex powder 3 ~ 5 parts, hydrophober 0.1 ~ 0.2 part, get its functional agent: in anticracking water conservation fiber 0.3 ~ 0.5 part, dispersion agent 0.05 ~ 0.1 part, anti-downslide auxiliary agent 0.05 ~ 0.1 part of loading container, after above metering, enter forced action type high speed dispersor in certain sequence respectively and carry out action of forced stirring;
(2) finely dispersed powder enters packaging facilities and packs, and packed weight is 25+0.3Kg;
(3) packaged flexible adhesion mortar at the construction field (site) with water according to 4.5: 1 weight percent mixing and stirring, during mixing, first add water and add flexible adhesion mortar again, the even post curing of slurry to be mixed is stirred for 5 minutes more again, make slurry reach even thickening effectiveness, can use.
8. the preparation method of a kind of flexible clay facing tile adhesive mortar according to claim 7: it is characterized in that: described high speed dispersor is carrying out adding the pigment toner that weight part is 1 ~ 3 part in action of forced stirring process.