CN105086876A - 一种植物分子粉末粘合剂及其制备方法 - Google Patents

一种植物分子粉末粘合剂及其制备方法 Download PDF

Info

Publication number
CN105086876A
CN105086876A CN201510578034.3A CN201510578034A CN105086876A CN 105086876 A CN105086876 A CN 105086876A CN 201510578034 A CN201510578034 A CN 201510578034A CN 105086876 A CN105086876 A CN 105086876A
Authority
CN
China
Prior art keywords
powder
starch
plant molecular
sepiolite
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510578034.3A
Other languages
English (en)
Other versions
CN105086876B (zh
Inventor
薛松涛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shaanxi biting Zhihua Biotechnology Co., Ltd
Original Assignee
Xi'an Xiang Hai Glutinous Rice Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xi'an Xiang Hai Glutinous Rice Coating Co Ltd filed Critical Xi'an Xiang Hai Glutinous Rice Coating Co Ltd
Priority to CN201510578034.3A priority Critical patent/CN105086876B/zh
Publication of CN105086876A publication Critical patent/CN105086876A/zh
Application granted granted Critical
Publication of CN105086876B publication Critical patent/CN105086876B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种植物分子粉末粘合剂,按照质量百分比由以下原料组成：糯米淀粉29％～31％，大豆淀粉19％～21％，淀粉醚14％～16％，硅藻土14％～16％，负离子粉9％～11％，海泡石粉末9％～11％，以上组分质量百分比之和为100％。本发明还公开了上述植物分子粉末粘合剂的制备方法。本发明植物分子粉末粘合剂，由各种天然原材料组成，具有无毒无害，可用于墙纸、瓷砖、地板等各种室内装修粘结，具有操作简单、粘结力强、快速干燥、不易脱落的特点，并且能够净化室内空气。

Description

一种植物分子粉末粘合剂及其制备方法
技术领域
本发明属于建筑装修材料技术领域，涉及一种植物分子粉末粘合剂，本发明还涉及上述植物分子粉末粘合剂的制备方法。
背景技术
在房屋室内装修过程中，不可避免的需要使用到乳胶等粘合剂进行瓷砖、地板、壁纸等的粘结粘贴工作，而这些建筑装修粘合剂，均由各种化学添加剂混合而成，并且大多数中含有甲醛等有毒物质。这类粘合剂的粘结性能较低，耐水性差，容易脱落，更重要的是这类粘合剂在使用过程中会散发有害气体，危害施工人员的身体健康，同时粘合剂与建材粘合后有害气体不易挥发，而是长期存在于室内环境中，危害住户的身体健康。
发明内容
本发明的目的是提供一种植物分子粉末粘合剂，解决了建筑装修粘合剂中均含有甲醛等化学添加剂，危害人体健康的问题。
本发明的另一目的是提供上述植物分子粉末粘合剂的制备方法。
本发明所采用的技术方案是，一种植物分子粉末粘合剂，按照质量百分比由以下原料组成：糯米淀粉29％～31％，大豆淀粉19％～21％，淀粉醚14％～16％，硅藻土14％～16％，负离子粉9％～11％，海泡石粉末9％～11％，以上组分质量百分比之和为100％。
本发明所采用的另一技术方案是，上述植物分子粉末粘合剂的制备方法，具体按以下步骤实施：
步骤1，取糯米淀粉、大豆淀粉、淀粉醚、硅藻土、负离子粉和海泡石，将所有原料进行打磨为粉末，并将海泡石粉末烘干；
步骤2，按比例称取步骤所述原料，均匀混合，即得到植物分子粉末粘合剂。
本发明的特点还在于，
步骤1中各原料粉末的打磨粒度为800～1200目。
步骤1中海泡石粉末的烘干温度为40～50℃，烘干时间至少30min。
步骤2中各原料按照质量百分比分别为：糯米淀粉29％～31％，大豆淀粉19％～21％，淀粉醚14％～16％，硅藻土14％～16％，负离子粉9％～11％，海泡石粉末9％～11％，以上组分质量百分比之和为100％。
本发明的有益效果是，本发明植物分子粉末粘合剂，由各种天然原材料组成，具有无毒无害，可用于墙纸、瓷砖、地板等各种室内装修粘结，具有操作简单、粘结力强、快速干燥、不易脱落的特点，并且能够净化室内空气。
具体实施方式
下面结合具体实施方式对本发明进行详细说明。
本发明提供了一种植物分子粉末粘合剂，按照质量百分比由以下原料组成：糯米淀粉29％～31％，大豆淀粉19％～21％，淀粉醚14％～16％，硅藻土14％～16％，负离子粉9％～11％，海泡石粉末9％～11％，以上组分质量百分比之和为100％。
本发明上述植物分子粉末粘合剂的制备方法,具体按以下步骤实施：
步骤1，取糯米淀粉、大豆淀粉、淀粉醚、硅藻土、负离子粉和海泡石，将所有原料打磨至粒度为800～1200目，并将海泡石粉末在40～50℃烘干至少30min；
步骤2，按质量百分比分别称糯米淀粉29％～31％，大豆淀粉19％～21％，淀粉醚14％～16％，硅藻土14％～16％，负离子粉9％～11％，海泡石9％～11％，以上组分质量百分比之和为100％；
步骤3，将步骤2称取的原料均匀混合，即得到植物分子粉末粘合剂。
植物分子粉末粘合剂中，糯米淀粉、大豆淀粉，能够降低粘合剂的表面张力，增加表面自由能浸润，同时扩展物质分子间作用力，进而使界面静电引子的作用能极好的粘接和附着。
淀粉醚与粘合剂中其他原料具有良好的相容性，能够明显提高粘合剂的流动性能，同时其良好的润滑性能，使粘合剂具有更强的操作性。
海泡石遇水变柔，干燥***，具有非金属矿物中最大的比表面积和独特的内部孔道结构，对甲醛、苯等有害气体具有强的吸附作用，并且海泡石还能与淀粉醚相互作用增加粘合剂的耐水性能。
负离子粉为电气石粉+镧系元素或者稀土元素的混合物，其中稀土元素的配比比例大大超过了电气石粉，占到了60％以上，负离子粉能够释放空气负离子，输送负电荷给细菌、灰尘，烟雾微粒以及水滴等，电荷与这些微粒相结合聚成球而下沉，从而达到净化空气的目的。负离子粉对装潢材料挥发出来的苯、甲醛、酮、氨等刺激性气体以及日常生活中空气异味等都具有良好的吸附作用。
粘合剂中硅藻土的加入，使其除了具有除湿、除臭、净化室内空气的作用，同时由于硅藻土具有较大的孔体积，能够有效缩短粘合剂的干燥时间。
本发明植物分子粉末粘合剂，由各种天然原材料组成，具有无毒无害，并且能够净化室内空气的特点。使用时与水按1：2的质量比混合，即可用于墙纸、瓷砖、地板等各种室内装修粘结，具有操作简单、粘结力强、快速干燥、不易脱落的特点。
实施例1
步骤1，取糯米淀粉、大豆淀粉、淀粉醚、硅藻土、负离子粉和海泡石，将所有原料打磨至粒度为800～1200目，并将海泡石粉末在50℃烘干30min；
步骤2，按质量百分比分别称糯米淀粉31％，大豆淀粉21％，淀粉醚14％，硅藻土14％，负离子粉9％，海泡石11％，以上组分质量百分比之和为100％；
步骤3，将步骤2称取的原料均匀混合，即得到植物分子粉末粘合剂。
实施例2
步骤1，取糯米淀粉、大豆淀粉、淀粉醚、硅藻土、负离子粉和海泡石，将所有原料打磨至粒度为800～1200目，并将海泡石粉末在40℃烘干50min；
步骤2，按质量百分比分别称糯米淀粉29％，大豆淀粉19％，淀粉醚16％，硅藻土16％，负离子粉11％，海泡石9％，以上组分质量百分比之和为100％；
步骤3，将步骤2称取的原料均匀混合，即得到植物分子粉末粘合剂。
实施例3
步骤1，取糯米淀粉、大豆淀粉、淀粉醚、硅藻土、负离子粉和海泡石，将所有原料打磨至粒度为800～1200目，并将海泡石粉末在45℃烘干至少40min；
步骤2，按质量百分比分别称糯米淀粉30％，大豆淀粉20％，淀粉醚15％，硅藻土15％，负离子粉10％，海泡石10％，以上组分质量百分比之和为100％；
步骤3，将步骤2称取的原料均匀混合，即得到植物分子粉末粘合剂。

Claims (5)

1.一种植物分子粉末粘合剂，其特征在于，按照质量百分比由以下原料组成：糯米淀粉29％～31％，大豆淀粉19％～21％，淀粉醚14％～16％，硅藻土14％～16％，负离子粉9％～11％，海泡石粉末9％～11％，以上组分质量百分比之和为100％。
2.一种植物分子粉末粘合剂的制备方法，其特征在于，具体按以下步骤实施：
步骤1，取糯米淀粉、大豆淀粉、淀粉醚、硅藻土、负离子粉和海泡石，将所有原料进行打磨为粉末，并将海泡石粉末烘干；
步骤2，按比例称取步骤所述原料，均匀混合，即得到植物分子粉末粘合剂。
3.根据权利要求2所述的一种植物分子粉末粘合剂的制备方法，其特征在于，步骤1中所述各原料粉末的打磨粒度为800～1200目。
4.根据权利要求2所述的一种植物分子粉末粘合剂的制备方法，其特征在于，步骤1中所述海泡石粉末的烘干温度为40～50℃，烘干时间至少30min。
5.根据权利要求2所述的一种植物分子粉末粘合剂的制备方法，其特征在于，步骤2中所述各原料按照质量百分比分别为：糯米淀粉29％～31％，大豆淀粉19％～21％，淀粉醚14％～16％，硅藻土14％～16％，负离子粉9％～11％，海泡石粉末9％～11％，以上组分质量百分比之和为100％。
CN201510578034.3A 2015-09-11 2015-09-11 一种植物分子粉末粘合剂及其制备方法 Expired - Fee Related CN105086876B (zh)