CN105236881B - 一种硅藻泥内墙装饰壁材及其制备方法 - Google Patents
一种硅藻泥内墙装饰壁材及其制备方法 Download PDFInfo
- Publication number
- CN105236881B CN105236881B CN201510559532.3A CN201510559532A CN105236881B CN 105236881 B CN105236881 B CN 105236881B CN 201510559532 A CN201510559532 A CN 201510559532A CN 105236881 B CN105236881 B CN 105236881B
- Authority
- CN
- China
- Prior art keywords
- parts
- diatom ooze
- wall material
- dry powder
- wall decoration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种硅藻泥内墙装饰壁材,本发明由以下组分和重量份数比配制而成:硅藻土10‑25份、重钙45‑55份、白水泥20‑30份、可再分散乳胶粉4‑8份、纤维素1.0‑1.4份、色粉0.5‑1.0份、海泡石0.5‑1.0份、触变润滑剂0.2‑0.4份、杀菌防霉剂0.2‑0.4份、2‑咪唑烷酮0.1‑0.9份、干粉消泡剂0.2‑0.4份。本发明的有益效果:采用本发明的硅藻泥内墙装饰壁材不仅具有色彩多样、图案丰富、施工方便、安全环保等特点外,而且还可以吸附分解空气中的异味、甲醛等各种污染物,具有调湿、透气、防霉除臭、净化空气防火阻燃等功能,而且有着优异的甲醛净化率和甲醛净化效果持久性。
Description
技术领域
本发明涉及一种室内用建筑装饰材料,尤其涉及一种硅藻泥内墙装饰壁材及其制备方法。
背景技术
壁材是指有关墙体粉刷施工,对普通的砂浆表面进行处理的一类材料。随着现今环境生态呈现不稳定性,诸多的环境污染问题和环境污染形态层出不穷,人们对与自身息息相关的室内墙面装饰的要求也日益增高,室内墙面装饰逐渐成为家居装修的重头戏,市场上流行着各种各样的室内墙面装饰壁材。目前,市场上具有代表性的墙面装饰壁材有乳胶漆、壁纸、瓷砖等,这些装饰壁材给人们带来众多选择的同时也带了些危害,乳胶漆虽比较环保,但刚涂在墙上时不可避免会有一些可挥发性的有害物质;壁纸虽色彩多样、图案丰富,但铺贴不环保、防火阻燃性差,瓷砖虽易清洁,但会加重对墙体的负载,易脱落。因此,一种新型环保壁材——硅藻泥壁材近几年流行起来,硅藻泥壁材主要原材料是天然硅藻土,具有消除甲醛、净化空气、防火阻燃等功能,然而市场上绝大多数的硅藻泥壁材存在着消除甲醛的效率低,甲醛净化效果持久性差的问题,导致不能有效的净化室内空气,产品质量不能满足消费者的需求。
发明内容
为了解决市场上绝大多数的硅藻泥壁材存在着消除甲醛的效率低,甲醛净化效果持久性差的问题,本发明提供一种硅藻泥内墙装饰壁材及其制备方法。本发明产品可以吸附分解空气中的的异味、甲醛等各种污染物,具有调湿、透气、防霉除臭、净化空气、防火阻燃等功能,并且有着优异的甲醛净化率和甲醛净化效果持久性。
本发明的技术方案一如下:
一种硅藻泥内墙装饰壁材,由以下组分和重量份数比配制而成:
进一步地,所述硅藻土是由生长在海湖中的植物遗骸堆积数百万年变迁而成的具有功能性过滤材料的海洋浮游硅藻土,其主要成分为硅酸质,表面有无数细孔,松散密度为0.25-0.50g/cm3,空隙率达85%以上,吸水率可达200-400%。
进一步地,所述重钙粒径为80-800目,所述优质白水泥粒径为275-525目。
进一步地,所述可再分散乳胶粉为乙烯/醋酸乙烯酯共聚物、醋酸乙烯/叔碳酸乙烯共聚物或丙烯酸共聚物中的任意一种。
进一步地,所述纤维素羟丙基甲基纤维素、羟乙基纤维素、羧甲基纤维素中的任意一种。
进一步地,所述海泡石为一种具层链状结构的含水富镁硅酸盐黏土矿物,其比表面积大,吸附性强,可吸附空气中的甲醛、异味等。
进一步地,所述触变润滑剂为一种经过特殊加工处理,适用于干粉料***的添加剂,主要成分为硅酸盐矿物材料。它可以提高施工润滑性、延长开放时间、提高触变性和减少流动阻力。
进一步地,所述杀菌防霉剂为用于控制微生物繁殖的一种涂料助剂,它是通过阻碍菌体呼吸,或干扰病原菌的生物合成等的一类干粉类杀菌防霉剂。
进一步地,所述干粉消泡剂为非离子表面活性剂,主要成分为特种改性聚硅氧烷,适合于干粉体系中添加。
本发明的技术方案二如下:
一种硅藻泥内墙装饰壁材的制备方法,它包括如下依序进行的步骤:
准确称量10-25份硅藻土与45-55份重钙、20-30份白水泥、4-8份可再分散乳胶粉、1.0-1.4份纤维素、0.5-1.0份色粉、0.5-1.0份海泡石、0.2-0.4份触变润滑剂、0.2-0.4份杀菌防霉剂、0.1-0.9份2-咪唑烷酮、0.2-0.4份干粉消泡剂充分混合。
将上述混匀后的干粉与水按照质量比为1:0.8-1:1.2搅拌10-20分钟,搅拌速度控制在1000-1500r/min。
本发明制备的一种硅藻泥内墙装饰壁材具有如下优点:采用本发明所述的组分及配比结合制备的一种硅藻泥内墙装饰壁材不仅具有色彩多样、图案丰富、施工方便、安全环保等特点外,而且还可以吸附分解空气中的的异味、甲醛等各种污染物,具有调湿、透气、防霉除臭、净化空气防火阻燃等功能,而且有着优异的甲醛净化率和甲醛净化效果持久性。
本发明一种硅藻泥内墙装饰壁材与现有的技术相比具有如下优点:本发明的一种硅藻泥内墙装饰壁材及其制备方法,采用具有多孔且吸附能力强的硅藻土、海泡石等材料,再与具有极强甲醛去除能力的2-咪唑烷酮复配,经过合理的配比制备了具有多孔、极强吸附性能与离子交换性能的硅藻泥。通过硅藻泥这些独特的功能,可以有效的驱除空气中的化学物质——甲醛,以及一些吸烟、生活垃圾等产生的空气异味,本发明的硅藻泥内墙装饰壁材对甲醛的净化率与净化效果持久率分别达到95%和85%以上,并且透气、调湿、色彩多样等特点,使室内墙面美观又会“呼吸”。
具体实施方式
下述组分中所述硅藻土采用长白山优质硅藻土。所述重钙采用三友化工的200目重钙。所述优质白水泥采用南银牌325目的优质白水泥。所述可再分散乳胶粉采用德国瓦克的5010N可再分散乳胶粉。所述纤维素采用中维的10000SMK羟丙基甲基纤维素。所述海泡石采用煜成矿业的YF-A海泡石。所述触变润滑剂采用中畅化工的602触变润滑剂。所述杀菌防霉剂采用埃迪特化学的AB-254干粉杀菌防霉剂。所述干粉消泡剂采用埃迪特化学的BX-832干粉消泡剂。
所述每种组分也可采用同类其它型号产品。
具体实施案例1:
一种硅藻泥内墙装饰壁材,由以下组分和重量份数比配制而成:
一种硅藻泥内墙装饰壁材的制备方法,它包括如下依序进行的步骤:
准确称量25份硅藻土与45份重钙、20份白水泥、8份可再分散乳胶粉、1.4份纤维素、1.0份色粉、1.0份保水剂、0.4份触变润滑剂、0.4份杀菌防霉剂、0.1份2-咪唑烷酮、0.4份干粉消泡剂充分混合。将上述混匀后的干粉与水按照质量比为1:0.8搅拌10分钟,搅拌速度控制在1000r/min。
具体实施案例2:
一种硅藻泥内墙装饰壁材,由以下组分和重量份数比配制而成:
一种硅藻泥内墙装饰壁材的制备方法,它包括如下依序进行的步骤:
准确称量10份硅藻土与55份重钙、30份白水泥、4份可再分散乳胶粉、1.0份纤维素、0.5份色粉、1.0份保水剂、0.2份触变润滑剂、0.2份杀菌防霉剂、0.9份2-咪唑烷酮、0.2份干粉消泡剂充分混合。将上述混匀后的干粉与水按照质量比为1:1.2搅拌20分钟,搅拌速度控制在1500r/min。
具体实施案例3:
一种硅藻泥内墙装饰壁材,由以下组分和重量份数比配制而成:
一种硅藻泥内墙装饰壁材的制备方法,它包括如下依序进行的步骤:
准确称量17.5份硅藻土与50份重钙、25份白水泥、6份可再分散乳胶粉、1.2份纤维素、0.75份色粉、0.75份保水剂、0.3份触变润滑剂、0.3份杀菌防霉剂、0.5份2-咪唑烷酮、0.3份干粉消泡剂充分混合。将上述混匀后的干粉与水按照质量比为1:1搅拌15分钟,搅拌速度控制在1200r/min。
本发明所制备的硅藻泥内墙装饰壁材的各个实施例中的甲醛净化率和甲醛净化效果持久性按照JC/T1074-2008《室内空气净化功能涂覆材料净化性能》II类材料的各项性能指标测试。
表1是本发明制备的硅藻泥内墙装饰壁材的各实施例中按照JC/T1074-2008《室内空气净化功能涂覆材料净化性能》II类材料中测试甲醛净化率试验方法测得的甲醛净化率指标实验数据:
表1甲醛净化率测试结果
检测项目 | 标准要求 | 实施例1 | 实施例2 | 实施例3 |
甲醛净化率 | ≥80% | 95.5% | 95.8% | 96.1% |
从表1可以明显看出,本发明各实施例的甲醛净化率均超过JC/T1074-2008《室内空气净化功能涂覆材料净化性能》II类材料的标准要求,甲醛净化率均大于或等于95%。
表2本发明所制备的硅藻泥内墙装饰壁材的甲醛净化效果持久性测试实验数据:
表2甲醛净化效果持久性测试结果
检测项目 | 标准要求 | 实施例1 | 实施例2 | 实施例3 |
甲醛净化效果持久性 | ≥65% | 85.3% | 86.2% | 87.5% |
从表2可以明显看出,本发明各实施例的甲醛净化效果持久性均超过JC/T1074-2008《室内空气净化功能涂覆材料净化性能》II类材料的标准要求,甲醛净化效果持久性均大于等于85%。
综上,本发明制备的一种硅藻泥内墙装饰壁材不仅具有色彩多样、图案丰富、施工方便、安全环保等特点外,而且还可以吸附分解空气中的的异味、甲醛等各种污染物,具有调湿、透气、防霉除臭、净化空气、防火阻燃等功能,而且有着优异的甲醛净化率和甲醛净化效果持久性。
以上所述仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种硅藻泥内墙装饰壁材,其特征在于,由以下组分和重量份数比配制而成:
所述硅藻土松散密度为0.25-0.50g/cm3,空隙率达85%以上,吸水率达200-400%;
所述可再分散乳胶粉为醋酸乙烯/叔碳酸乙烯共聚物或丙烯酸共聚物中的任意一种;
所述纤维素为羟丙基甲基纤维素、羟乙基纤维素、羧甲基纤维素中的任意一种;
所述海泡石为具层链状结构的含水富镁硅酸盐黏土矿物;
所述杀菌防霉剂为干粉类杀菌防霉剂;
所述干粉消泡剂为非离子表面活性剂,主要成分为特种改性聚硅氧烷;
所述重钙粒径为80-800目,所述白水泥为粒径为275-525目的优质白水泥;
所述的硅藻泥内墙装饰壁材是按照以下方法制备而成的:称量10-25份硅藻土、45-55份重钙、20-30份优质白水泥、4-8份可再分散乳胶粉、1.0-1.4份纤维素、0.5-1.0份色粉、0.5-1.0份海泡石、0.2-0.4份触变润滑剂、0.2-0.4份杀菌防霉剂、0.1-0.9份2-咪唑烷酮、0.2-0.4份干粉消泡剂充分混合。
2.一种硅藻泥内墙装饰壁材的制备方法,其特征在于:它包括以下步骤:
称量10-25份硅藻土、45-55份重钙、20-30份优质白水泥、4-8份可再分散乳胶粉、1.0-1.4份纤维素、0.5-1.0份色粉、0.5-1.0份海泡石、0.2-0.4份触变润滑剂、0.2-0.4份杀菌防霉剂、0.1-0.9份2-咪唑烷酮、0.2-0.4份干粉消泡剂充分混合。
3.根据权利要求2所述的一种硅藻泥内墙装饰壁材的制备方法,其特征在于:将上述混匀后的干粉与水按照质量比为1:0.8-1:1.2搅拌10-20分钟,搅拌速度控制在1000-1500r/min。