CN105084829A - Anti-seepage leakage stop material and preparation method thereof - Google Patents
Anti-seepage leakage stop material and preparation method thereof Download PDFInfo
- Publication number
- CN105084829A CN105084829A CN201510481641.8A CN201510481641A CN105084829A CN 105084829 A CN105084829 A CN 105084829A CN 201510481641 A CN201510481641 A CN 201510481641A CN 105084829 A CN105084829 A CN 105084829A
- Authority
- CN
- China
- Prior art keywords
- cotton seed
- seed hulls
- blocking material
- cement
- fragment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an anti-seepage leakage stop material and a preparation method thereof. Raw materials of the anti-seepage leakage stop material comprise cottonseed hull fragments, gypsum, an expanding agent, cement and water. By adding the cottonseed hull fragments into the cement, the tensile strength of cement mortar is improved; meanwhile, by using the cottonseed hull fragments, the cost of the anti-seepage leakage stop material can be greatly lowered, and the anti-seepage leakage stop material is widely applied to tunnel and underground structure projects, mine excavation projects, water conservancy and hydropower foundation reinforcement projects and the like.
Description
Technical field
The present invention relates to material of construction, more specifically, relate to a kind of impervious blocking material and preparation method thereof.
Background technology
House, tunnel, dykes and dams and underground pipeline etc. all there will be the situation broken or damage, thus dykes and dams or underground pipeline etc. there will be the situation of leaking, seeping water, for tackling above-mentioned situation, the place of breakage is blocked by usual employing anti-seeping grouting material, causes breaking-up to avoid leaking for a long time or seep water to dykes and dams or underground pipeline.
Anti-seeping grouting material can be divided into cement grouting material (the granular injection material based on cement) and chemical grouting material two kinds according to the state of slurries, wherein, cement grouting material has that consolidating strength is high, price is low, transport and storage is convenient and grouting process is simple etc. advantage, but also also exist simultaneously time of coagulation long, easily by shortcoming that current dilute, therefore, be usually restricted when cement grouting material is used for leak stopping; The time of coagulation of chemical grouting material can regulate according to the needs of duration, chemical grouting material as polyurethanes can produce gel with water direct reaction, thus the impervious leakage-stopping of flowing water is gone for, but chemical grouting material is expensive, construction process requirement is high, is unfavorable for large-scale leak stopping.
At present, in general impervious leakage-stopping engineering, biliquid is usually adopted to control grouting technique, i.e. the grouting technique of cementation process and the combined chemistry of cement matrix material of chemical grouting.The setting time that biliquid controls the cement-chemical composite grouting material that grouting technique adopts is longer than the setting time of cement grouting material, and the tensile strength of cement-chemical composite grouting material is also enhanced simultaneously.But, when run into flow and be large and flow velocity high water burst time, the tensile strength of cement-chemical composite grouting material does not often reach construction requirement, and the slurries of sand-cement slurry are easily washed away, have a strong impact on water plugging effect.Therefore, can only take to accelerate slurries injection speed in the construction of reality and leak stopping is carried out in the measure strengthening slurries injection rates, but this can cause the huge wasting of resources, and then make the cost up of leak stopping.
Summary of the invention
The object of this invention is to provide a kind of impervious blocking material and preparation method thereof, with solve large to flow described in background technology and the water burst that flow velocity is high carries out leak stopping time slurries easily washed away problems.
In order to solve the problems of the technologies described above, the invention provides following technical scheme:
A kind of impervious blocking material, the raw material of described impervious blocking material comprises cotton seed hulls fragment, gypsum, swelling agent, cement and water.
Preferably, the raw materials by weight of described impervious blocking material is: cotton seed hulls fragment 0.3%-0.5%, gypsum 3%-8%, swelling agent 2%-3.2%, cement 35%-50%, water 40%-55%.
Preferably, the raw materials by weight of described impervious blocking material is: cotton seed hulls fragment 0.3%, gypsum 5%, swelling agent 3%, cement 40%, water 51.7%.
Preferably, the length of described cotton seed hulls fragment is 6-20mm, and wide is 1-6mm.
Preferably, described swelling agent is alumite plumping agent, sulphoaluminate expander, calcium oxide swelling agent or iron filings swelling agent.
A preparation method for impervious blocking material, the preparation method of described impervious blocking material comprises the following steps:
S01: select inclusion-free, without the cotton seed hulls rotted, fragmentation carried out to cotton seed hulls, obtains cotton seed hulls fragment; Select gypsum, swelling agent and the cement in described impervious blocking material raw material simultaneously;
S02: cotton seed hulls fragment, gypsum, swelling agent and the cement after selecting is put into dispersion machine and stirs 3-5min, obtain the siccative mixed;
S03: joined by water in the siccative mixed, continues to stir 3-10min, obtains described impervious blocking material.
Preferably, described step S01 comprises: select the cement that weight percent is respectively the cotton seed hulls fragment of 0.3%-0.5%, the gypsum of 3%-8%, the swelling agent of 2%-3.2% and 35%-50%.
Preferably, describedly carry out fragmentation to cotton seed hulls and comprise: use pulverizer that 6-20mm is grown in cotton seed hulls fragmentation, wide be the fragment of 1-6mm, and cotton seed hulls fragment is put in the NaOH solution immersion 30min that concentration is 1%, wash away clean with water again and dry, obtaining cotton seed hulls fragment.
Impervious blocking material provided by the invention comprises cotton seed hulls, gypsum, swelling agent, cement and water.Can harden in atmosphere or in water after cement and gypsum add water, and cemented together securely for the materials such as sand, stone.Swelling agent in this impervious blocking material adds after in cement, and when cement setting hardens, swelling agent can expand and volume becomes large, swelling agent while expanding can compensate for shrinkage and the prestress of tension reinforcing steel bar, the gap fully between filling concrete.Cotton seed hulls fragment after fragmentation adds in sand-cement slurry to increase pulls power between cotton seed hulls fragment and sand-cement slurry and cotton seed hulls fragment, thus the tensile strength of this impervious blocking material is strengthened, and then the large and reactive force of the water burst that flow velocity is high of flow can be resisted, avoid the slurries of sand-cement slurry to be diluted by current.Meanwhile, the output zone of cotton seed hulls is wide, and wide material sources are cheap, thus can reduce the raw materials cost of impervious blocking material.
Accompanying drawing explanation
In order to be illustrated more clearly in the technical scheme in the embodiment of the present invention, below the accompanying drawing used required in describing embodiment is briefly described, apparently, for those of ordinary skills, under the prerequisite not paying creative work, other accompanying drawing can also be obtained according to these accompanying drawings.
Fig. 1 is the schema of the impervious blocking material preparation method that the embodiment of the present invention provides.
Embodiment
Impervious blocking material that the embodiment of the present invention provides and preparation method thereof, solves the problem that when large to flow and that flow velocity is high water burst carries out leak stopping, slurries are easily washed away.
Technical scheme in the embodiment of the present invention is understood better in order to make those skilled in the art person, and enable the above-mentioned purpose of the embodiment of the present invention, feature and advantage become apparent more, below in conjunction with accompanying drawing, the technical scheme in the embodiment of the present invention is described in further detail.
The schema of the impervious blocking material preparation method that Fig. 1 provides for the embodiment of the present invention, has illustrated the primary process preparing impervious blocking material in Fig. 1.Below in conjunction with specific embodiment, the preparation process preparing impervious blocking material is described.
Embodiment 1
The raw materials by weight of the impervious blocking material that the embodiment of the present invention provides is:
Cotton seed hulls fragment 0.3%, gypsum 5%, alumite plumping agent 3%, cement 40%, water 51.7%.
The preparation method of the impervious blocking material that the embodiment of the present invention provides comprises the following steps:
S101: select inclusion-free, without the cotton seed hulls rotted, use pulverizer that 6mm is grown in cotton seed hulls fragmentation, wide be the fragment of 1mm, and cotton seed hulls fragment is put in the NaOH solution immersion 30min that concentration is 1%, wash away clean with water again and dry, obtaining cotton seed hulls fragment; Select the gypsum of powdery, alumite plumping agent and cement simultaneously;
S102: cotton seed hulls fragment, gypsum, alumite plumping agent and cement after selecting are weighed according to aforementioned proportion, and the gypsum of the cotton seed hulls fragment after weighing, powdery, alumite plumping agent and cement are put into dispersion machine stir 3min, obtain the siccative mixed;
S103: join in the siccative mixed by the water after weighing, continues to stir 3min, obtains described impervious blocking material.
Embodiment 2
The raw materials by weight of the impervious blocking material that the embodiment of the present invention provides is:
Cotton seed hulls fragment 0.5%, gypsum 3%, sulphoaluminate expander 2%, cement 45%, water 49.5%.
The preparation method of the impervious blocking material that the embodiment of the present invention provides comprises the following steps:
S201: select inclusion-free, without the cotton seed hulls rotted, use pulverizer that 10mm is grown in cotton seed hulls fragmentation, wide be the fragment of 3mm, and cotton seed hulls fragment is put in the NaOH solution immersion 30min that concentration is 1%, wash away clean with water again and dry, obtaining cotton seed hulls fragment; Select the gypsum of powdery, sulphoaluminate expander and cement simultaneously;
S202: cotton seed hulls fragment, gypsum, sulphoaluminate expander and cement after selecting are weighed according to aforementioned proportion, and the gypsum of the cotton seed hulls fragment after weighing, powdery, sulphoaluminate expander and cement are put into dispersion machine stir 5min, obtain the siccative mixed;
S203: join in the siccative mixed by the water after weighing, continues to stir 10min, obtains described impervious blocking material.
Embodiment 3
The raw materials by weight of the impervious blocking material that the embodiment of the present invention provides is:
Cotton seed hulls fragment 0.5%, gypsum 8%, calcium oxide swelling agent 3.2%, cement 35%, water 53.3%.
The preparation method of the impervious blocking material that the embodiment of the present invention provides comprises the following steps:
S301: select inclusion-free, without the cotton seed hulls rotted, use pulverizer that 20mm is grown in cotton seed hulls fragmentation, wide be the fragment of 6mm, and cotton seed hulls fragment is put in the NaOH solution immersion 30min that concentration is 1%, wash away clean with water again and dry, obtaining cotton seed hulls fragment; Select the gypsum of powdery, calcium oxide swelling agent and cement simultaneously;
S302: cotton seed hulls fragment, gypsum, calcium oxide swelling agent and cement after selecting are weighed according to aforementioned proportion, and the gypsum of the cotton seed hulls fragment after weighing, powdery, calcium oxide swelling agent and cement are put into dispersion machine stir 4min, obtain the siccative mixed;
S303: join in the siccative mixed by the water after weighing, continues to stir 8min, obtains described impervious blocking material.
Embodiment 4
The raw materials by weight of the impervious blocking material that the embodiment of the present invention provides is:
Cotton seed hulls fragment 0.4%, gypsum 4%, iron filings swelling agent 2.1%, cement 38.5%, water 55%.
The preparation method of the impervious blocking material that the embodiment of the present invention provides comprises the following steps:
S401: select inclusion-free, without the cotton seed hulls rotted, use pulverizer that 17mm is grown in cotton seed hulls fragmentation, wide be the fragment of 4mm, and cotton seed hulls fragment is put in the NaOH solution immersion 30min that concentration is 1%, wash away clean with water again and dry, obtaining cotton seed hulls fragment; Select the gypsum of powdery, iron filings swelling agent and cement simultaneously;
S402: cotton seed hulls fragment, gypsum, iron filings swelling agent and cement after selecting are weighed according to aforementioned proportion, and the gypsum of the cotton seed hulls fragment after weighing, powdery, iron filings swelling agent and cement are put into dispersion machine stir 5min, obtain the siccative mixed;
S403: join in the siccative mixed by the water after weighing, continues to stir 5min, obtains described impervious blocking material.
Embodiment 5
The raw materials by weight of the impervious blocking material that the embodiment of the present invention provides is:
Cotton seed hulls fragment 0.3%, gypsum 4%, calcium oxide swelling agent 2%, cement 50%, water 43.7%.
The preparation method of the impervious blocking material that the embodiment of the present invention provides comprises the following steps:
S501: select inclusion-free, without the cotton seed hulls rotted, use pulverizer that 9mm is grown in cotton seed hulls fragmentation, wide be the fragment of 4mm, and cotton seed hulls fragment is put in the NaOH solution immersion 30min that concentration is 1%, wash away clean with water again and dry, obtaining cotton seed hulls fragment; Select the gypsum of powdery, calcium oxide swelling agent and cement simultaneously;
S502: cotton seed hulls fragment, gypsum, calcium oxide swelling agent and cement after selecting are weighed according to aforementioned proportion, and the gypsum of the cotton seed hulls fragment after weighing, powdery, calcium oxide swelling agent and cement are put into dispersion machine stir 3min, obtain the siccative mixed;
S503: join in the siccative mixed by the water after weighing, continues to stir 6min, obtains described impervious blocking material.
Embodiment 6
The raw materials by weight of the impervious blocking material that the embodiment of the present invention provides is:
Cotton seed hulls fragment 0.5%, gypsum 7%, sulphoaluminate expander 3.2%, cement 49.3%, water 40%.
The preparation method of the impervious blocking material that the embodiment of the present invention provides comprises the following steps:
S601: select inclusion-free, without the cotton seed hulls rotted, use pulverizer that 12mm is grown in cotton seed hulls fragmentation, wide be the fragment of 5mm, and cotton seed hulls fragment is put in the NaOH solution immersion 30min that concentration is 1%, wash away clean with water again and dry, obtaining cotton seed hulls fragment; Select the gypsum of powdery, sulphoaluminate expander and cement simultaneously;
S602: cotton seed hulls fragment, gypsum, sulphoaluminate expander and cement after selecting are weighed according to aforementioned proportion, and the gypsum of the cotton seed hulls fragment after weighing, powdery, sulphoaluminate expander and cement are put into dispersion machine stir 5min, obtain the siccative mixed;
S603: join in the siccative mixed by the water after weighing, continues to stir 9min, obtains described impervious blocking material.
Impervious blocking material provided by the invention by adding cotton seed hulls fragment in sand-cement slurry, greatly can improve the tensile strength of sand-cement slurry, this is mainly due under the water burst condition comparatively large at flow, flow velocity is higher, power of pullling between cotton seed hulls fragment and sand-cement slurry and cotton seed hulls fragment is enhanced, thus the tensile strength of this impervious blocking material is strengthened, and then the large and reactive force of the water burst that flow velocity is high of flow can be resisted, avoid the slurries of sand-cement slurry to be diluted by current.
Impervious blocking material provided by the invention is by pouring into by the mode of high pressure pouring after concrete preparation.
Above-mentioned specific embodiment is only the section Example that the present invention proposes, and those skilled in the art is understood or realizes the present invention.To be apparent to one skilled in the art to the multiple amendment of these embodiments, General Principle as defined herein can without departing from the spirit or scope of the present invention, realize in other embodiments.Therefore, the present invention can not be restricted to these embodiments shown in this article, but will meet the widest scope consistent with principle disclosed herein and features of novelty.
Above-described embodiment of the present invention, does not form limiting the scope of the present invention.Any amendment done within the spirit and principles in the present invention, equivalent replacement and improvement etc., all should be included within protection scope of the present invention.
Claims (8)
1. an impervious blocking material, is characterized in that, the raw material of described impervious blocking material comprises cotton seed hulls fragment, gypsum, swelling agent, cement and water.
2. impervious blocking material according to claim 1, is characterized in that, the raw materials by weight of described impervious blocking material is:
Cotton seed hulls fragment 0.3%-0.5%, gypsum 3%-8%, swelling agent 2%-3.2%, cement 35%-50%, water 40%-55%.
3. impervious blocking material according to claim 2, is characterized in that, the raw materials by weight of described impervious blocking material is:
Cotton seed hulls fragment 0.3%, gypsum 5%, swelling agent 3%, cement 40%, water 51.7%.
4. impervious blocking material according to claim 3, is characterized in that, the length of described cotton seed hulls fragment is 6-20mm, and wide is 1-6mm.
5. impervious blocking material according to claim 3, is characterized in that, described swelling agent is alumite plumping agent, sulphoaluminate expander, calcium oxide swelling agent or iron filings swelling agent.
6. a preparation method for impervious blocking material, is characterized in that, the preparation method of described impervious blocking material comprises the following steps:
S01: select inclusion-free, without the cotton seed hulls rotted, fragmentation carried out to cotton seed hulls, obtains cotton seed hulls fragment; Select gypsum, swelling agent and the cement in described impervious blocking material raw material simultaneously;
S02: cotton seed hulls fragment, gypsum, swelling agent and the cement after selecting is put into dispersion machine and stirs 3-5min, obtain the siccative mixed;
S03: joined by water in the siccative mixed, continues to stir 3-10min, obtains described impervious blocking material.
7. the preparation method of impervious blocking material according to claim 6, it is characterized in that, described step S01 comprises: select the cement that weight percent is respectively the cotton seed hulls fragment of 0.3%-0.5%, the gypsum of 3%-8%, the swelling agent of 2%-3.2% and 35%-50%.
8. the preparation method of impervious blocking material according to claim 6, is characterized in that, describedly carries out fragmentation to cotton seed hulls and comprises:
Use pulverizer that 6-20mm is grown in cotton seed hulls fragmentation, wide be the fragment of 1-6mm, and cotton seed hulls fragment is put in concentration be 1% NaOH solution soak 30min, then wash away totally with water and dry, obtaining cotton seed hulls fragment.