CN105060820A - 一种经济型c60高强混凝土的制备 - Google Patents

一种经济型c60高强混凝土的制备 Download PDF

Info

Publication number
CN105060820A
CN105060820A CN201510489985.3A CN201510489985A CN105060820A CN 105060820 A CN105060820 A CN 105060820A CN 201510489985 A CN201510489985 A CN 201510489985A CN 105060820 A CN105060820 A CN 105060820A
Authority
CN
China
Prior art keywords
concrete
strength concrete
sand
strength
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510489985.3A
Other languages
English (en)
Inventor
王力威
张明
章敏燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changzhou University
Original Assignee
Changzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changzhou University filed Critical Changzhou University
Priority to CN201510489985.3A priority Critical patent/CN105060820A/zh
Publication of CN105060820A publication Critical patent/CN105060820A/zh
Pending legal-status Critical Current

Abstract

一种经济型C60高强混凝土的制备，本发明公开了一种配合比优化的C60级高强混凝土，主要采用材料为粉煤灰、矿渣粉、砂、碎石、外加剂、水，经过配合比和正交试验设计、试验、分析优选，得到若干拟定的配合比，然后按配合比进行强度试验。试验结果和比选得到一种C60级高强混凝土，其特征在于：每立米混凝土用胶凝材料533kg，砂609kg，碎石1082kg。高效减水剂占混凝土总质量的0.305％，外加剂按胶凝材料总量1.375％加入。其水胶比为0.32。配制的混凝土满足C60高强混凝土要求。此配合比可在工程实际中参考应用。

Description

一种经济型C60高强混凝土的制备
技术领域
本发明涉及建筑工程上的高强度混凝土应用技术领域。
背景技术
建筑工程中，随着高层建筑飞发展，对高强混凝土的需要越来越多，然而高强混凝土一般成本较高，如何配制经济效果较好的满足高层建筑需要的高强混凝土是一个普遍需要解决的问题。C60强度等级的混凝土是应用比较多的一种高强混凝土，因此尽可能经济地制备这种混凝土有着较大的实用意义和经济效果。
发明内容
本发明的目的是为混凝土结构工程提出一种实用的，具有较好技术性和经济性的C60混凝土制备方法。
为了达到上述目的，本发明提出了一种经济型C60高强混凝土制备方法，在混凝土配合比设计中，进行了多方案比较，采用矿粉和粉煤灰双掺方法，并加如高效减水剂配制了C60高强混凝土，保证了供应的C60高强混凝土质量并取得了较好经济效果。得到的优选配合比如下表。
表1每立方米混凝土材料用量kg/m3
所述高效减水剂占混凝土总质量的0.305％，外加剂按胶凝材料总量1.375％加入。其水胶比为0.32。
所述的水泥采用江苏常州扬子水泥P·042.5，符合现行的国家标准《通用硅酸盐水泥》(GB175-2007)的规定。其主要性能见表2。
表2水泥物理性能指标
所述的砂为长江天然砂，其物理性能技术指标如表3。
表3砂物理性能技术指标
粗骨料采用的碎石为溧阳戴埠产，碎石级配属于连续级配，其物理性能技术指标如表4。
表4碎石物理性能技术指标
所述粉煤灰采用常州国电C类II级灰；采用江苏溧阳产S95级矿粉。
本发明的优势在于：利用成本很低的工业副产品粉煤灰和矿渣粉，通过多种配合比拟定和试验，从中优选出了满足设计和施工要求的强度等级为C60高强高性能混凝土，试验得到的混凝土28天抗压强度达到71.8MPa，抗渗等级达到了P12。混凝土工程实际应用表明，配制的混凝土很好满足了建筑工程上对C60高强混凝土的需要，配合比在使用中达到很好的强度等指标，同时由于掺用了矿粉和粉煤灰，节约了成本，每立方米混凝土比不掺的节省约29元，取得了较好的经济效益。
具体实施方式
现结合实施例对本发明做进一步说明。
实例：按每立米混凝土各种材料的用量进行配制，每立米混凝土用粉煤灰53kg，矿渣粉160kg，水泥320kg，砂609kg，碎石1082kg，高效减水剂7.33kg，加水171kg。针对拌合机械的每次拌合量，确定各种材料的一次投料量，注意投料前对天然存放的砂石应测定含水率，实际用水量要减去砂石中的水量，而砂石实际用量要考虑到本身水分的变化，保证砂石干质量符合配比要求不变。各种材料要混合均匀，高效减水剂应先加入水中混合均匀后一起使用，减水剂按每立米混凝土7.33kg加入水中混合好后，即可加入混合均匀的其它各种材料中，采用机械搅拌的方式，将所有材料拌合均匀，灌入模板内，按施工技术要求进行振捣、养生。

Claims (5)

1.一种经过配合比优化的C60高强混凝土，采用主要材料水泥、粉煤灰、矿渣粉、砂、碎石、外加剂、水。经过配合比试验设计，得到若干拟定的配合比，然后按配合比进行试验。通过试验结果的比选得到一种C60级高强混凝土。其特征在于：每立米混凝土用粉煤灰53kg，矿渣粉160kg，水泥320kg，砂609kg，碎石1082kg，高效减水剂7.33kg，加水171kg。配制的混凝土达到C60高强混凝土的标准。
2.根据权利要求1所述的一种C60高强混凝土，其特征在于：所述高效减水剂占混凝土总质量的0.305％，并按胶凝材料总量1.375％加入，所述高效减水剂产自江苏苏博特新材料股份有限公司。
3.根据权利要求1所述的一种C60高强混凝土，其特征在于：所述的混凝土水胶比为0.32。
4.根据权利要求1所述的混凝土，其特征在于：采用江苏常州扬子水泥P·042.5，符合现行的国家标准《通用硅酸盐水泥》(GB175-2007)的规定；粉煤灰采用常州国电C类II级灰；采用江苏溧阳产S95级矿粉；砂采用天然级配的河砂，处于2区，级配良好，为细度模数2.7中砂，堆积密度1540kg/m3；采用的粗骨料为采用连续级配的直径5-31.5mm的碎石、高料。粗细骨料均符合现行行业标准《普通混凝土用砂、石质量及检验方法标准》(JGJ52-2006)的规定。
5.根据权利要求1所述的一种C60高强混凝土，其特征在于：在配制所需的各种材料要按一定的投料顺序依次将各种材料混合均匀，但外加剂要首先加入水中，采用机械搅拌的方式，将所有材料拌合均匀，灌入模板，振捣密实，养生。
CN201510489985.3A 2015-08-08 2015-08-08 一种经济型c60高强混凝土的制备 Pending CN105060820A (zh)