CN105058537A - Processing method for primarily treated green thin sliced moso bamboo strips used for decoration - Google Patents
Processing method for primarily treated green thin sliced moso bamboo strips used for decoration Download PDFInfo
- Publication number
- CN105058537A CN105058537A CN201510417689.2A CN201510417689A CN105058537A CN 105058537 A CN105058537 A CN 105058537A CN 201510417689 A CN201510417689 A CN 201510417689A CN 105058537 A CN105058537 A CN 105058537A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- green
- blue
- processing method
- mao bamboon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a processing method for primarily treated green thin sliced moso bamboo strips used for decoration. After fresh flawless moso bamboos are cut into bamboo segments, convex bamboo joints are planed away, and the bamboo segments are split into bamboo slices with the width of 1.2 cm; after inner joints are removed, the bamboo slices are split into bamboo slices with the width of 0.6 cm; then the bamboo slices are pressurized, soaked and subjected to color retaining, and after that, the bamboo slices are subjected to drying, fine planning, side edge gluing assembly and hot-pressing board forming; afterwards, the bamboo slices are planed into the primarily treated green thin sliced strips; and the obtained primarily treated green thin sliced strips are further subjected to compound hot-pressing with polypropylene non-woven fabrics, so that finished products are obtained. The processing method is simple and the obtained primarily treated green thin sliced moso bamboo strips have the characteristics of elegant appearance and durable service. The obtained primarily treated green thin sliced moso bamboo strips are further processed into bamboo furniture, so that the limitation that existing bamboo furniture is not green is overcome, and the bamboo furniture is applicable to hotels, offices, homes and other various places. In addition, the application area of bamboo can be broadened; the technological content and the product added value of the bamboo processing industry can be fully enhanced; the sustainable development of bamboo resources and the bamboo industry can be achieved, and the primarily treated green thin sliced moso bamboo strips have broad development prospects.
Description
Technical field
The invention belongs to bamboo class processing technique field, be specifically related to a kind of processing method of decorating with the blue or green slicing veneer of mao bamboon two.
Background technology
The title that China have " bamboo kingdom ", North gets Liaoning, reach in the south Hainan, east up to Taiwan, be dispersed with more than 400 ten thousand hm to the wide territory in Tibet
2bamboo grove and 39 belong to more than 500 plant bamboo kind, be topmost Chan Zhu state in the world, bamboo class germ plasm resource, bamboo grove area, accumulation and output all occupy first place in the world.Bamboo is a kind of totemism in China, is a kind of spirit.Bamboo is all liked by many men of literature and writing.To revive the Northern Song Dynasty verse of the horizontal bar in the front of a carriage used as an armrest: " would rather have no meat at meals than no bamboos round one's residence ", visible people are to the favorable rating of bamboo.The area of bamboo is abounded with in south, bamboo is seen everywhere especially in the daily life of people, bamboo tower, bamboo bed, bamboo stool, bamboo basket, bamboo raft, the figure of bamboo everywhere, and along with the raising of social progress and people's living standard, bamboo obtains liking of more and more people, has come into huge numbers of families.
" two is blue or green " i.e. bamboo removes the head blue or green Hou bis-road thin bamboo strip, its matter is crisp easily broken, due to the restriction by processing technology, easily damaged in process, therefore sold in the market bamboo furniture, for making finished color even, is all removed surf green part and makes product redgreen.The present invention utilizes aboundresources, cheap mao bamboon is raw material, through special process process, produce the decoration two blue or green slicing veneer materials with special decorative effect, its preparation method is simple, products obtained therefrom can the naturally verdant form of simulation bamboo to greatest extent, it is processed into bamboo furniture further, the limitation of existing bamboo furniture redgreen can be overcome, be applicable to hotel, office, the various occasion such as family, and have elegant in appearance, long-lived feature, the application of bamboo wood can be widened, the scientific and technological content of General Promotion Bamboo processing enterprise and added value of product, realize the sustainable development of bamboo timber resource and bamboo wood industry, also help and optimize the structure of production, create more jobs number, increase farmers' income, therefore there is vast potential for future development.
Summary of the invention
The object of the present invention is to provide a kind of processing method of decorating with the blue or green slicing veneer of mao bamboon two, its preparation method is simple, the blue or green slicing veneer of gained mao bamboon two has elegant in appearance, long-lived feature, it is processed into bamboo furniture further, the limitation of existing bamboo furniture redgreen can be overcome, widen the application of bamboo wood.
For achieving the above object, the present invention adopts following technical scheme:
Decorate the processing method with the blue or green slicing veneer of mao bamboon two, comprise the steps:
Step 1) fells the fresh mao bamboon of diameter at 8 ~ 12cm, with slighing the flat branch of pruning of cutter, is cut into the bamboo section of 1 ~ 3 meter long on request;
Step 2) with hand plane by after in bamboo section, the ring of evagination neatly digs, feeding is cutd open bamboo machine and is cutd open into the wide bamboo chip of 1.2cm, it is split on wafer separator the wide bamboo chip of 0.6cm again after removing bamboo chip internal segment, in planing process should as far as possible by the planing of evagination ring to bamboo surf green section transitions flat smooth, note not staying the pit defect of bossed ring or planing;
Step 3) by mass concentration be 0.1 ~ 1.0% keeping color agent stir after pour in impregnating autoclave, by step 2) bamboo chip that processes puts into impregnating autoclave, weighting material makes bamboo chip be immersed in completely in keeping color agent, then the opening of impregnating autoclave is closed, opening air compressor machine, in impregnating autoclave, be forced into pressure in tank be 0.2 ~ 1MPa, makes bamboo chip protect look process under an increased pressure 1 ~ 10 hour;
It is dry that the bamboo chip protected after look is sent into lumber kiln by step 4), makes the moisture control of dry rear bamboo chip below 6%;
Dried bamboo chip is sent into improved bamboo chip adjustable cast iron planes machine by step 5), other three surfaces of scraping except bamboo strip, and after scraping, the width of gained bamboo cane is 0.5cm;
Step 6) by the marshalling on the table of the bamboo cane after adjustable cast iron planes, and makes bamboo strip place upward, and side gluing carries out assembly;
The fine finishining bamboo cane completing assembly is sent into and is deposited between constant temperature and humidity after being hot pressed into plywood made from green bamboo in the hot press of side pressure by step 7);
Step 8) takes out plywood made from green bamboo, with PUR, the back side of plywood made from green bamboo is fixed on the prepackage substrate surface of vertical veneer slicer, after plywood made from green bamboo surface sprinkling makes surface wettability, first by less planing operation amount, plywood made from green bamboo surface head green grass or young crops is removed, then planing operation goes out two blue or green slicing veneers;
Step 9) is after plane out the two blue or green slicing veneer back sides evenly brush one deck adhesive, and itself and polypropylene is molded without imitative cloth compound thermal, makes drum or tabular.
Wherein, fresh mao bamboon selected by step 1) answers outward appearance verdant attractive in appearance, without worm channel, rotten, aberration, injures the defects such as bending outward, and should handle with care in mao bamboon transport and process, prevents that mao bamboon and hard object from colliding and scratch surf green is surperficial.
Keeping color agent described in step 3) is that copper naphthenate and copper sulphate is formulated by weight adding water after 1:1 mixes.
Improved bamboo chip adjustable cast iron planes machine described in step 5) is removed the top cutter group of traditional bamboo chip adjustable cast iron planes machine, and substitute original metal pineapple roller by nylon roller.
The temperature of hot pressing described in step 7) is 105 ~ 120 DEG C, and pressure is 1.2 ~ 1.5MPa, and the time is 3 ~ 5 minutes, and pressure measurement pressure is 0.8 ~ 1.0MPa; Temperature between described constant temperature and humidity controls at 20 ~ 25 DEG C, and relative humidity controls 70 ~ 80%.
Adhesive described in step 9) is white glue with vinyl, in use as found white glue with vinyl too thickness, can add appropriate water dilution; Described hot-forming pressure is 1.0 ~ 1.2MPa, and temperature is 80 DEG C, and the time is 3 ~ 5 minutes.
Remarkable advantage of the present invention is:
1) object of impregnating by pressure of the present invention impels the copper ion protecting look to enter bamboo wood inside to replace magnesium ion, thus reach the object of the verdant color in permanent protection surf green surface.
2) the present invention transforms traditional bamboo chip adjustable cast iron planes machine, and the top cutter group by traditional bamboo chip adjustable cast iron planes machine is removed, and original metal pineapple roller nylon roller is substituted for bamboo chip transmission, is not destroyed in process to protect surf green surface.
3) plywood made from green bamboo hot-forming after assembly is placed between constant temperature and humidity and preserves by the present invention, and object prevents plywood made from green bamboo from when outdoor temperature humidity changes greatly, craze and transfiguration occurring.
4) back side of plywood made from green bamboo is fixed on the prepackage substrate surface of vertical veneer slicer by the present invention's PUR, its objective is the thickness and fixing firmness that increase plywood made from green bamboo, is beneficial to the planing operation of plywood made from green bamboo.
5) the present invention carries out water spray process to plywood made from green bamboo surface before planing starts, and its objective is the plastic deformation ability increasing plywood made from green bamboo, prevents plywood made from green bamboo from ftractureing in process, ensure the integrality of the blue or green slicing veneer of mao bamboon two.When planing, first removing the head green grass or young crops on plywood made from green bamboo surface by less planing operation amount, and being planished as far as possible in plywood made from green bamboo surface, for two blue or green veneers of complete planing full wafer are ready.
6) two blue or green slicing veneers are made drum or tabular by the present invention, can be convenient to the preservation of the blue or green slicing veneer of gained mao bamboon two, transport and use.
7) the invention provides a kind of processing method of decorating with the blue or green slicing veneer of mao bamboon two, the method utilizes aboundresources, cheap mao bamboon is raw material, through special process process, produce the blue or green slicing veneer product of the mao bamboon two with good decorative effect, its preparation method is simple, products obtained therefrom can the naturally verdant form of simulation bamboo to greatest extent, it is processed into bamboo furniture further, the limitation of existing bamboo furniture redgreen can be overcome, be applicable to hotel, office, the various occasion such as family, and have elegant in appearance, long-lived feature, the application of bamboo wood can be widened, the scientific and technological content of General Promotion Bamboo processing enterprise and added value of product, realize the sustainable development of bamboo timber resource and bamboo wood industry, also help and optimize the structure of production, create more jobs number, increase farmers' income, therefore there is vast potential for future development.
Detailed description of the invention
More being convenient to make content of the present invention understand, below in conjunction with detailed description of the invention, technical solutions according to the invention are described further, but the present invention being not limited only to this.
Embodiment 1
Decorate the processing method with the blue or green slicing veneer of mao bamboon two, comprise the steps:
It is verdant attractive in appearance that step 1) fells outward appearance, and without worm channel, rotten, aberration, injure the defects such as bending outward, diameter, in the fresh mao bamboon of 8cm, being put down with slighing cutter branch of pruning, being cut into the bamboo section of 1 meter long on request;
Step 2) with hand plane by after in bamboo section, the ring of evagination neatly digs, feeding is cutd open bamboo machine and is cutd open into the wide bamboo chip of 1.2cm, it is split on wafer separator the wide bamboo chip of 0.6cm again after removing bamboo chip internal segment, in planing process should as far as possible by the planing of evagination ring to bamboo surf green section transitions flat smooth, note not staying the pit defect of bossed ring or planing;
Copper naphthenate and copper sulphate are the keeping color agent of 0.1% by weight the formulated mass concentration that adds water after 1:1 mixes by step 3), pour into after being stirred in impregnating autoclave, by step 2) bamboo chip that processes puts into impregnating autoclave, weighting material makes bamboo chip be immersed in completely in keeping color agent, then the opening of impregnating autoclave is closed, opening air compressor machine, in impregnating autoclave, be forced into pressure in tank be 0.2MPa, makes bamboo chip protect look process under an increased pressure 10 hours;
It is dry that the bamboo chip protected after look is sent into lumber kiln by step 4), and after dry, the moisture content of bamboo chip is 6%;
Step 5) is transformed traditional bamboo chip adjustable cast iron planes machine, and the top cutter group by traditional bamboo chip adjustable cast iron planes machine is removed, and substitutes original metal pineapple roller by nylon roller; Then dried bamboo chip is sent into improved bamboo chip adjustable cast iron planes machine, other three surfaces of scraping except bamboo strip, after scraping, the width of gained bamboo cane is 0.5cm;
Step 6) by the marshalling on the table of the bamboo cane after adjustable cast iron planes, and makes bamboo strip place upward, and side gluing carries out assembly;
The fine finishining bamboo cane completing assembly is sent into after being hot pressed into plywood made from green bamboo in the hot press of side pressure by step 7), in 20 DEG C, between the constant temperature and humidity of relative humidity 70% in deposit; The temperature of described hot pressing is 105 DEG C, and pressure is 1.2MPa, and the time is 5 minutes, and pressure measurement pressure is 0.8MPa;
Step 8) takes out plywood made from green bamboo, with PUR, the back side of plywood made from green bamboo is fixed on the prepackage substrate surface of vertical veneer slicer, after plywood made from green bamboo surface sprinkling makes surface wettability, first by less planing operation amount, plywood made from green bamboo surface head green grass or young crops is removed, then planing operation goes out two blue or green slicing veneers;
Step 9) is after plane out the two blue or green slicing veneer back sides evenly brush one deck white glue with vinyl, and itself and polypropylene is molded without imitative cloth compound thermal, makes drum or tabular; Described hot-forming pressure is 1.0MPa, and temperature is 80 DEG C, and the time is 5 minutes.
Embodiment 2
Decorate the processing method with the blue or green slicing veneer of mao bamboon two, comprise the steps:
It is verdant attractive in appearance that step 1) fells outward appearance, and without worm channel, rotten, aberration, injure the defects such as bending outward, diameter, in the fresh mao bamboon of 10cm, being put down with slighing cutter branch of pruning, being cut into the bamboo section of 2 meters long on request;
Step 2) with hand plane by after in bamboo section, the ring of evagination neatly digs, feeding is cutd open bamboo machine and is cutd open into the wide bamboo chip of 1.2cm, it is split on wafer separator the wide bamboo chip of 0.6cm again after removing bamboo chip internal segment, in planing process should as far as possible by the planing of evagination ring to bamboo surf green section transitions flat smooth, note not staying the pit defect of bossed ring or planing;
Copper naphthenate and copper sulphate are the keeping color agent of 0.5% by weight the formulated mass concentration that adds water after 1:1 mixes by step 3), pour into after being stirred in impregnating autoclave, by step 2) bamboo chip that processes puts into impregnating autoclave, weighting material makes bamboo chip be immersed in completely in keeping color agent, then the opening of impregnating autoclave is closed, opening air compressor machine, in impregnating autoclave, be forced into pressure in tank be 0.8MPa, makes bamboo chip protect look process under an increased pressure 5 hours;
It is dry that the bamboo chip protected after look is sent into lumber kiln by step 4), and after dry, the moisture content of bamboo chip is 5%;
Step 5) is transformed traditional bamboo chip adjustable cast iron planes machine, and the top cutter group by traditional bamboo chip adjustable cast iron planes machine is removed, and substitutes original metal pineapple roller by nylon roller; Then dried bamboo chip is sent into improved bamboo chip adjustable cast iron planes machine, other three surfaces of scraping except bamboo strip, after scraping, the width of gained bamboo cane is 0.5cm;
Step 6) by the marshalling on the table of the bamboo cane after adjustable cast iron planes, and makes bamboo strip place upward, and side gluing carries out assembly;
The fine finishining bamboo cane completing assembly is sent into after being hot pressed into plywood made from green bamboo in the hot press of side pressure by step 7), in 22 DEG C, between the constant temperature and humidity of relative humidity 75% in deposit; The temperature of described hot pressing is 110 DEG C, and pressure is 1.3MPa, and the time is 4 minutes, and pressure measurement pressure is 0.9MPa;
Step 8) takes out plywood made from green bamboo, with PUR, the back side of plywood made from green bamboo is fixed on the prepackage substrate surface of vertical veneer slicer, after plywood made from green bamboo surface sprinkling makes surface wettability, first by less planing operation amount, plywood made from green bamboo surface head green grass or young crops is removed, then planing operation goes out two blue or green slicing veneers;
Step 9) is after plane out the two blue or green slicing veneer back sides evenly brush one deck white glue with vinyl, and itself and polypropylene is molded without imitative cloth compound thermal, makes drum or tabular; Described hot-forming pressure is 1.1MPa, and temperature is 80 DEG C, and the time is 4 minutes.
Embodiment 3
Decorate the processing method with the blue or green slicing veneer of mao bamboon two, comprise the steps:
It is verdant attractive in appearance that step 1) fells outward appearance, and without worm channel, rotten, aberration, injure the defects such as bending outward, diameter, in the fresh mao bamboon of 12cm, being put down with slighing cutter branch of pruning, being cut into the bamboo section of 3 meters long on request;
Step 2) with hand plane by after in bamboo section, the ring of evagination neatly digs, feeding is cutd open bamboo machine and is cutd open into the wide bamboo chip of 1.2cm, it is split on wafer separator the wide bamboo chip of 0.6cm again after removing bamboo chip internal segment, in planing process should as far as possible by the planing of evagination ring to bamboo surf green section transitions flat smooth, note not staying the pit defect of bossed ring or planing;
Copper naphthenate and copper sulphate are the keeping color agent of 1.0% by weight the formulated mass concentration that adds water after 1:1 mixes by step 3), pour into after being stirred in impregnating autoclave, by step 2) bamboo chip that processes puts into impregnating autoclave, weighting material makes bamboo chip be immersed in completely in keeping color agent, then the opening of impregnating autoclave is closed, opening air compressor machine, in impregnating autoclave, be forced into pressure in tank be 1MPa, makes bamboo chip protect look process under an increased pressure 1 hour;
It is dry that the bamboo chip protected after look is sent into lumber kiln by step 4), and after dry, the moisture content of bamboo chip is 3%;
Step 5) is transformed traditional bamboo chip adjustable cast iron planes machine, and the top cutter group by traditional bamboo chip adjustable cast iron planes machine is removed, and substitutes original metal pineapple roller by nylon roller; Then dried bamboo chip is sent into improved bamboo chip adjustable cast iron planes machine, other three surfaces of scraping except bamboo strip, after scraping, the width of gained bamboo cane is 0.5cm;
Step 6) by the marshalling on the table of the bamboo cane after adjustable cast iron planes, and makes bamboo strip place upward, and side gluing carries out assembly;
The fine finishining bamboo cane completing assembly is sent into after being hot pressed into plywood made from green bamboo in the hot press of side pressure by step 7), in 25 DEG C, between the constant temperature and humidity of relative humidity 80% in deposit; The temperature of described hot pressing is 120 DEG C, and pressure is 1.5MPa, and the time is 3 minutes, and pressure measurement pressure is 1.0MPa;
Step 8) takes out plywood made from green bamboo, with PUR, the back side of plywood made from green bamboo is fixed on the prepackage substrate surface of vertical veneer slicer, after plywood made from green bamboo surface sprinkling makes surface wettability, first by less planing operation amount, plywood made from green bamboo surface head green grass or young crops is removed, then planing operation goes out two blue or green slicing veneers;
Step 9) is after plane out the two blue or green slicing veneer back sides evenly brush one deck white glue with vinyl, and itself and polypropylene is molded without imitative cloth compound thermal, makes drum or tabular; Described hot-forming pressure is 1.2MPa, and temperature is 80 DEG C, and the time is 3 minutes.
The present invention utilizes aboundresources, cheap mao bamboon is raw material, through special process process, produce the blue or green slicing veneer product of the mao bamboon two with good decorative effect, its preparation method is simple, products obtained therefrom can the naturally verdant form of simulation bamboo to greatest extent, it is processed into bamboo furniture further, the limitation of existing bamboo furniture redgreen can be overcome, be applicable to hotel, office, the various occasion such as family, and have elegant in appearance, long-lived feature, traditional application of bamboo wood can be widened, the scientific and technological content of General Promotion Bamboo processing enterprise and added value of product, realize the sustainable development of bamboo timber resource and bamboo wood industry, also help and optimize the structure of production, create more jobs number, increase farmers' income, therefore, there is vast potential for future development.
The foregoing is only preferred embodiment of the present invention, all equalizations done according to the present patent application the scope of the claims change and modify, and all should belong to covering scope of the present invention.
Claims (8)
1. decorate the processing method with the blue or green slicing veneer of mao bamboon two, it is characterized in that: comprise the steps:
Step 1) fells the fresh mao bamboon of diameter at 8 ~ 12cm, is cut into the bamboo section of 1 ~ 3 meter long after flat branch of pruning on request;
Step 2) ring of evagination in bamboo section neatly dug rear feeding and cut open bamboo machine and cut open into the wide bamboo chip of 1.2cm, it is split on wafer separator the wide bamboo chip of 0.6cm again after removing bamboo chip internal segment;
Step 3) is by step 2) to be immersed in mass concentration be completely in the keeping color agent of 0.1 ~ 1.0% for the bamboo chip that processes, then pressurization makes bamboo chip under 0.2 ~ 1.0MPa pressure, protect look process 1 ~ 10 hour;
Bamboo chip after guarantor's look is dried to moisture content below 6% by step 4);
Dried bamboo chip is sent into improved bamboo chip adjustable cast iron planes machine by step 5), other three surfaces of scraping except bamboo strip;
Step 6) by the bamboo cane marshalling after adjustable cast iron planes, and makes bamboo strip place upward, and side gluing carries out assembly;
The fine finishining bamboo cane completing assembly is sent into after being hot pressed into plywood made from green bamboo in the hot press of side pressure by step 7), deposits between constant temperature and humidity;
Step 8) takes out plywood made from green bamboo, is fixed on the prepackage substrate surface of vertical veneer slicer with PUR by the back side of plywood made from green bamboo, first removed by plywood made from green bamboo surface head green grass or young crops, then planing operation goes out two blue or green slicing veneers after plywood made from green bamboo surface sprinkling makes surface wettability;
Step 9) is after plane out the two blue or green slicing veneer back sides evenly brush one deck adhesive, and itself and polypropylene is molded without imitative cloth compound thermal, makes drum or tabular.
2. the decoration processing method of mao bamboon two blue or green slicing veneer according to claim 1, is characterized in that: fresh mao bamboon selected by step 1) answers outward appearance verdant attractive in appearance, without worm channel, rotten, aberration, outward injure bending.
3. the decoration processing method of mao bamboon two blue or green slicing veneer according to claim 1, is characterized in that: keeping color agent described in step 3) be by copper naphthenate and copper sulphate by weight 1:1 add water formulated after mixing.
4. decorate the processing method with the blue or green slicing veneer of mao bamboon two according to claim 1, it is characterized in that: improved bamboo chip adjustable cast iron planes machine described in step 5) is removed the top cutter group of traditional bamboo chip adjustable cast iron planes machine, and substitute original metal pineapple roller by nylon roller.
5. decorate the processing method with the blue or green slicing veneer of mao bamboon two according to claim 1, it is characterized in that: the temperature of hot pressing described in step 7) is 105 ~ 120 DEG C, and pressure is 1.2 ~ 1.5MPa, and the time is 3 ~ 5 minutes, and pressure measurement pressure is 0.8 ~ 1.0MPa.
6. decorate the processing method with the blue or green slicing veneer of mao bamboon two according to claim 1, it is characterized in that: the temperature described in step 7) between constant temperature and humidity controls at 20 ~ 25 DEG C, and relative humidity controls 70 ~ 80%.
7. decorate the processing method with the blue or green slicing veneer of mao bamboon two according to claim 1, it is characterized in that: adhesive described in step 9) is white glue with vinyl.
8. decorate the processing method with the blue or green slicing veneer of mao bamboon two according to claim 1, it is characterized in that: pressure hot-forming described in step 9) is 1.0 ~ 1.2MPa, temperature is 80 DEG C, and the time is 3 ~ 5 minutes.