CN102862438A - Preparation method of bamboo skin surface ironed pattern and character - Google Patents
Preparation method of bamboo skin surface ironed pattern and character Download PDFInfo
- Publication number
- CN102862438A CN102862438A CN2011101932122A CN201110193212A CN102862438A CN 102862438 A CN102862438 A CN 102862438A CN 2011101932122 A CN2011101932122 A CN 2011101932122A CN 201110193212 A CN201110193212 A CN 201110193212A CN 102862438 A CN102862438 A CN 102862438A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- pattern
- preparation
- scalding
- literal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of bamboo skin surface ironed pattern and character, comprising a bamboo skin which is manufactured by sticking a composite non-woven fabric on the lower surface of a bamboo single sheet by glue, wherein the thickness of the bamboo single sheet is 0.05-3 mm, and the length and the width can be selected according to requirements. The preparation method is characterized by comprising the following steps of: polishing the upper surface of the bamboo skin to be smooth; then remaining yellow, brown and black carbonized tracks on the surface of the bamboo skin by combining requirements of a creation theme; or compounding a flexible substrate layer on the lower surface of the bamboo skin and polishing the upper surface of the bamboo skin to be smooth; and remaining the yellow, brown and black carbonized tracks on the surface of the bamboo skin by combining the requirements of the creation theme. The preparation method has the beneficial effects that the represented effect has greater artistic appeals; damages to an original forest and an ecological environment can be reduced; a new space of an iron art is created; a new field of an ironing preparation method is explored; and the content of a bamboo culture, an ecological culture and a traditional culture can be improved and enriched.
Description
Technical field
What the present invention relates to is to iron the preparation method of scalding pattern and literal at bamboo epidermis face.
Background technology
Carrying out painting and calligraphy creation with flatiron on wooden plate, is that artists use the method that new carrier carries out artistic display.Because wooden plate belongs to fragile material, so have certain thickness wooden plate in order to prevent the works fracture, usually to use, generally need more than 3 millimeters.Cause carrier itself relatively heavier, transport and move very inconvenient; And consumed a large amount of high-quality timber, virgin forest and ecological environment are damaged.In addition, the embodiment of the surperficial natural style of wooden plate manifests not.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, provide and to embody better natural style, have more artistic appeal, reduce virgin forest and environmental destruction, and have that softness is good, easy fracture not, thin thickness, lightweight, stretch volume bamboo epidermis face freely and iron the preparation method of scalding pattern and literal.
Bamboo epidermis face of the present invention irons the first technical scheme of the preparation method of scalding pattern and literal, be included in the bamboo skin that the lower surface viscose glue compound nonwoven cloth of bamboo monolithic is made, wherein the thickness of bamboo monolithic is 0.05 millimeter～3 millimeters, its length and width are selected as required, it is characterized in that carrying out according to the following step:
(1) polishing is processed: bamboo skin upper surface is polished smooth;
(2) iron boiling hot pattern: solder horn is controlled in the required temperature range, if Electric soldering pen, the output voltage of Electric soldering pen pressure regulator can be debugged suitable temperature, iron in the process of scalding pattern and literal in conjunction with the needs of creating theme at bamboo skin upper surface, the weight of control Electric soldering pen, the variation of emergency, employing is colluded, is drawn, point, dye, the usefulness method of the Chinese painting such as chapped, wiping, stay Huang, brown, black carbonization vestige at bamboo epidermis face.
Described bamboo monolithic can be that bamboo wood is put into peeler, and rotary-cut obtains, and also can be that bamboo wood is put into slicer, and slicing obtains, and can also be the bamboo section that diameter is cut into Len req greater than 8 centimetres former bamboo, then puts into peeler, and rotary-cut obtains.
Bamboo epidermis face of the present invention irons the second technical scheme of the preparation method of scalding pattern and literal, be included in the bamboo skin that the lower surface viscose glue compound nonwoven cloth of bamboo monolithic is made, wherein the thickness of bamboo monolithic is 0.05 millimeter～3 millimeters, its length and width are selected as required, it is characterized in that carrying out according to the following step:
(1) Compound Machining: at the lower surface composite and flexible base layer of bamboo skin, the contact surface of bamboo skin and flexible substrate layer has adhesive;
(2) polishing is processed: bamboo skin upper surface is polished smooth;
(3) iron boiling hot pattern: solder horn is controlled in the required temperature range, if Electric soldering pen, the output voltage of Electric soldering pen pressure regulator can be debugged suitable temperature, iron in the process of scalding pattern and literal in conjunction with the needs of creating theme at bamboo epidermis face, the weight of control Electric soldering pen, the variation of emergency, employing is colluded, is drawn, point, dye, the usefulness method of the Chinese painting such as chapped, wiping, stay Huang, brown, black carbonization vestige at bamboo epidermis face.
Described bamboo monolithic can be that bamboo wood is put into peeler, and rotary-cut obtains, and also can be that bamboo wood is put into slicer, and slicing obtains, and can also be the bamboo section that diameter is cut into Len req greater than 8 centimetres former bamboo, then puts into peeler, and rotary-cut obtains.
Described flexible substrate layer is any material in nonwoven, silk fabric, cotton, acrylic fabric, woven dacron, chemical fabric, bast fibre spinning cloth, wool spinning thing, the blended material.
The beneficial effect that bamboo epidermis face of the present invention irons the preparation method of scalding pattern and literal is:
[1] passes through the bamboo skin that rotary-cut or slicing go out, under the irradiation of sunlight or light, its fibre bundle can reflect the radiance of multiple color, can embody better the breath of peculiar texture and the nature of bamboo, bamboo epidermis face irons the effect that the preparation method of scalding pattern and literal embodies and has more artistic appeal.
[2] the bamboo power of regeneration is very strong, and well-thought-out plan in 50 days just can be cut down use in 2 years, Hsinchu meeting self-sow, and ecological functions and the natural landscape of bamboo grove still keep, and ecological functions and the view of forest can descend greatly after the trees felling, serious is irrecoverable.Bamboo wood is internationally recognized and the environment-friendly materials actively promoted the use of.Use the bamboo skin as the carrier of painting creation, can reduce virgin forest and environmental destruction, its preparation method has been created the brand-new space of ironing the art of scalding.
[3] bamboo skin itself is the higher environment-friendly materials of a kind of scientific and technological content, and the bamboo leatherware has, and softness is good, easy fracture not, thin thickness, lightweight, stretch volume characteristics freely, ironing the preparation method of scalding pattern and literal at bamboo epidermis face irons boiling hot product and is convenient to very much various mountings and displaying, collection, more be conducive to transport and move, overcome plank and ironed the drawback of scalding product, opened up and ironed the frontier of scalding the preparation method.
[4] bamboo epidermis face irons the preparation method of scalding pattern and literal, embodied the perfect combination of bamboo culture, ecological culture, traditional culture, science and technology, product has more charm and vitality, more promotes and enriched the intension of bamboo culture, ecological culture, traditional culture.
Specific implementation method
The first embodiment
Bamboo epidermis face of the present invention irons the first embodiment of the preparation method of scalding pattern and literal, is included in the bamboo skin that the lower surface viscose glue compound nonwoven cloth of bamboo monolithic is made, and its special character is to carry out according to the following step:
(1) polishing is processed: be that 1.5 millimeters, length and width are that the bamboo skin upper surface of required size polishes smooth with thickness;
(2) iron boiling hot pattern: the output voltage of Electric soldering pen pressure regulator is debugged suitable temperature, iron in the process of scalding pattern and literal in conjunction with the needs of creating theme at bamboo skin upper surface, the weight of control Electric soldering pen, the variation of emergency, employing is colluded, is drawn, point, dye, the usefulness method of the Chinese painting such as chapped, wiping, stay Huang, brown, black carbonization vestige at bamboo epidermis face.
Described bamboo monolithic is that bamboo wood is put into slicer, and slicing obtains.
The second embodiment
Bamboo epidermis face of the present invention irons the second embodiment of the preparation method of scalding pattern and literal,, be included in the bamboo skin that the lower surface viscose glue compound nonwoven cloth of bamboo monolithic is made, its special character is to carry out according to the following step:
(1) polishing is processed: be that 1 millimeter, length and width are that the bamboo skin upper surface of required size polishes smooth with thickness;
(2) iron boiling hot pattern: the output voltage of Electric soldering pen pressure regulator is debugged suitable temperature, iron in the process of scalding pattern and literal in conjunction with the needs of creating theme at bamboo skin upper surface, the weight of control Electric soldering pen, the variation of emergency, employing is colluded, is drawn, point, dye, the usefulness method of the Chinese painting such as chapped, wiping, stay Huang, brown, black carbonization vestige at bamboo epidermis face.
Described bamboo monolithic is that bamboo wood is put into peeler, and rotary-cut obtains.
The 3rd embodiment
Bamboo epidermis face of the present invention irons the preparation method's of scalding pattern and literal the 3rd embodiment,, be included in the bamboo skin that the lower surface viscose glue compound nonwoven cloth of bamboo monolithic is made, its special character is to carry out according to the following step:
(1) Compound Machining: be that 0.6 millimeter, length and width are the lower surface composite and flexible base layer of the bamboo skin of required size at thickness, the contact surface of bamboo skin and flexible substrate layer has adhesive;
(2) polishing is processed: bamboo skin upper surface is polished smooth;
(2) iron boiling hot pattern: the output voltage of Electric soldering pen pressure regulator is debugged suitable temperature, iron in the process of scalding pattern and literal in conjunction with the needs of creating theme at bamboo skin upper surface, the weight of control Electric soldering pen, the variation of emergency, employing is colluded, is drawn, point, dye, the usefulness method of the Chinese painting such as chapped, wiping, stay Huang, brown, black carbonization vestige at bamboo epidermis face.
Described bamboo monolithic is that bamboo wood is put into peeler, and rotary-cut obtains.
The 4th embodiment
Bamboo epidermis face of the present invention irons the preparation method's of scalding pattern and literal the 4th embodiment,, be included in the bamboo skin that the lower surface viscose glue compound nonwoven cloth of bamboo monolithic is made, its special character is to carry out according to the following step:
(1) Compound Machining: be that 0.15 millimeter, length and width are the lower surface composite and flexible base layer of the bamboo skin of required size at thickness, the contact surface of bamboo skin and flexible substrate layer has adhesive;
(2) polishing is processed: bamboo skin upper surface is polished smooth;
(2) iron boiling hot pattern: the output voltage of Electric soldering pen pressure regulator is debugged suitable temperature, iron in the process of scalding pattern and literal in conjunction with the needs of creating theme at bamboo skin upper surface, the weight of control Electric soldering pen, the variation of emergency, employing is colluded, is drawn, point, dye, the usefulness method of the Chinese painting such as chapped, wiping, stay Huang, brown, black carbonization vestige at bamboo epidermis face.
Described bamboo monolithic is the bamboo section that diameter is cut into Len req greater than 8 centimetres former bamboo, then puts into peeler, and rotary-cut obtains.
Claims (6)
1. bamboo epidermis face irons the preparation method of scalding pattern and literal, be included in the bamboo skin that the lower surface viscose glue compound nonwoven cloth of bamboo monolithic is made, wherein the thickness of bamboo monolithic is 0.05 millimeter～3 millimeters, and its length and width are selected as required, it is characterized in that carrying out according to the following step:
(1) polishing is processed: bamboo skin upper surface is polished smooth;
(2) iron boiling hot pattern: solder horn is controlled in the required temperature range, if Electric soldering pen, the output voltage of Electric soldering pen pressure regulator can be debugged suitable temperature, iron in the process of scalding pattern and literal in conjunction with the needs of creating theme at bamboo skin upper surface, the weight of control Electric soldering pen, the variation of emergency, employing is colluded, is drawn, point, dye, the usefulness method of the Chinese painting such as chapped, wiping, stay Huang, brown, black carbonization vestige at bamboo epidermis face.
2. bamboo epidermis face irons the preparation method of scalding pattern and literal, be included in the bamboo skin that the lower surface viscose glue compound nonwoven cloth of bamboo monolithic is made, wherein the thickness of bamboo monolithic is 0.05 millimeter～3 millimeters, and its length and width are selected as required, it is characterized in that carrying out according to the following step:
(1) Compound Machining: at the lower surface composite and flexible base layer of bamboo skin, the contact surface of bamboo skin and flexible substrate layer has adhesive;
(2) polishing is processed: bamboo skin upper surface is polished smooth;
(3) iron boiling hot pattern: solder horn is controlled in the required temperature range, if Electric soldering pen, the output voltage of Electric soldering pen pressure regulator can be debugged suitable temperature, iron in the process of scalding pattern and literal in conjunction with the needs of creating theme at bamboo epidermis face, the weight of control Electric soldering pen, the variation of emergency, employing is colluded, is drawn, point, dye, the usefulness method of the Chinese painting such as chapped, wiping, stay Huang, brown, black carbonization vestige at bamboo epidermis face.
3. bamboo epidermis face according to claim 1 irons the preparation method of scalding pattern and literal, and it is characterized in that: described bamboo monolithic is that bamboo wood is put into peeler, and rotary-cut obtains.
4. bamboo epidermis face according to claim 1 irons the preparation method of scalding pattern and literal, and it is characterized in that: described bamboo monolithic is that bamboo wood is put into slicer, and slicing obtains.
5. bamboo epidermis face according to claim 1 irons the preparation method of scalding pattern and literal, and it is characterized in that: described bamboo monolithic is the bamboo section that diameter is cut into Len req greater than 8 centimetres former bamboo, then puts into peeler, and rotary-cut obtains.
6. bamboo epidermis face according to claim 2 irons the preparation method of scalding pattern and literal, and it is characterized in that: described flexible substrate layer is any material in nonwoven, silk fabric, cotton, acrylic fabric, woven dacron, chemical fabric, bast fibre spinning cloth, wool spinning thing, the blended material.