CN105057926A - 一种用于热作模具修复堆焊的专用药芯焊丝 - Google Patents
一种用于热作模具修复堆焊的专用药芯焊丝 Download PDFInfo
- Publication number
- CN105057926A CN105057926A CN201510608369.5A CN201510608369A CN105057926A CN 105057926 A CN105057926 A CN 105057926A CN 201510608369 A CN201510608369 A CN 201510608369A CN 105057926 A CN105057926 A CN 105057926A
- Authority
- CN
- China
- Prior art keywords
- powder
- flux
- welding
- cored wire
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供了一种用于热作模具修复堆焊的专用药芯焊丝,包括焊丝管壁和被包于其内的药粉;所述药粉包含脱氧合金剂和造渣剂。通过向铁基合金粉末中加入纳米氮化铬粉末,在堆焊金属中形成细小的氮化物间隙相,使堆焊金属具有良好的韧性和抗裂性能;同时,在合金粉末中加入氧化钇,净化堆焊金属、球化夹杂物、促使形成氮化物强化相,提高堆焊金属的抗疲劳性能。应用药芯焊丝配合富氩气体保护的熔化极气体保护焊技术对热作模具进行修复,得到的堆焊金属具有优异的高温抗氧化性能、耐磨性、洁净度以及良好抗疲劳性能。
Description
技术领域
本发明属于焊接材料领域,尤其涉及一种用于热作模具修复堆焊的专用药芯焊丝。
背景技术
近年来,随着我国冶金工业及制造业的迅猛发展,模具特别是热作模具,如热轧工作辊、热锻模、热挤压模、热冲裁模等的用量越来越大,现已成为工业生产中大量应用的消耗件之一。模具在使用过程中由于磨损及热疲劳等原因会产生剥落、擦伤、磨损等而失效。如何提高它的使用寿命一直是国内外关注的研究热点。模具的寿命主要取决于模具材料、结构设计、热处理工艺、加工等几个方面。我国模具使用寿命只有国外的1/2-1/3,存在精度低、加工周期长的问题。鉴于模具的失效大都由表面开始,从节省能源和资源、充分发挥材料性能潜力并获得特殊性能和最大技术经济效益出发,提高和改进模具工作面材料的性能是延长模具使用寿命的关键。生产中常采用堆焊的方法在模具坯料上制备合金层,获得双金属模具,既降低了成本,又提高了模具的性能;堆焊也是修复模具延长其寿命的重要技术手段。堆焊需要与各种模具用钢配套的焊接材料。
堆焊常用的焊接材料有焊条和焊丝。焊条采用气渣联合保护,冶金质量较好,可以通过药皮和焊芯过渡合金元素,焊缝杂质含量少、洁净度较高,焊缝具有较高的抗疲劳性能。同时焊条使用灵活,也比较适合模具修复的短焊缝和不规则焊缝工况。因此,焊条常用于小型模具的堆焊修复,人们为此研发了多种热作模具堆焊焊条,如公布号为CN102240872A的专利“热锻模具堆焊修复及再制造用特种焊条”其药皮化学成分的重量百分比(wt%)为钛白粉1-3,大理石25-40,萤石10-15,石英3-5,白土子2-4,高碳铬铁8-12,高碳锰铁2-4,硅铁2-4,钛铁6-9,钼铁9-11,铈氧化物4-8,金属镍5-8,石墨1-2;焊芯为H08A。该焊条采用Cr-Ni-Mo合金系,焊条药皮中高碳铬铁的最大含量为12%,熔敷金属的Cr含量远低于11%,难以保证堆焊金属在800℃及800℃以下具有足够的抗氧化能力,用于热作模具堆焊时高温抗氧化能力较差;该专利焊条加入的碳化物形成元素主要是Cr,Cr的碳化物是间隙化合物,间隙化合物的熔点和硬度不如间隙相的高,加热时也比较容易分解,氮化物和某些碳化物(如Ti、V、Nb的碳化物)形成间隙相,间隙相具有高硬度、高熔点、尺寸细小等优点,但该焊条没有采用氮化物强化;另外,该焊条起细化晶粒作用的合金元素只有Mo。授权公告号CN2507605Y“模具堆焊焊条”实用新型专利提出了一种管状焊条用于模具堆焊,该焊条以优质无缝钢管作导电载体,管外涂有药皮,管内填充粒状合金药芯,末端焊接设有夹持端。该专利没有涉及药芯和药皮的具体配方。焊条虽具有上述优点,但焊条不适于自动焊,堆焊效率较低,在大型热作模具的堆焊中使用极少。焊丝可用于自动焊,焊接效率高、焊接质量稳定,因此,焊丝是大型模具堆焊常用的焊接材料。焊丝分为实心焊丝和药芯焊丝,模具堆焊金属合金元素含量较高,合金元素含量高的实心焊丝制造困难,所以模具堆焊主要用药芯焊丝,尤以金属和铁合金粉末为药粉主要组成的金属粉芯焊丝应用最广,金属粉芯焊丝合金成分调整容易、制造简便,焊缝基本无熔渣、多层堆焊无需清渣,焊接生产效率高,也不会产生夹渣缺陷。近年来,人们对研发模具堆焊用金属粉芯焊丝比较重视,如授权公告号CN1093450C的发明专利“时效马氏体钢钨极氩弧焊金属粉芯焊丝及其制造方法”公开了一种用于模具堆焊的钨极氩弧焊用金属粉芯焊丝,金属粉芯中各粉料的重量配比为:39-78%Ni,0-26%Co,0-18%Mo,0.2-6%Ti,0.7-1.68%Al,0.2-1.455%Nb,0-0.72%Re,0-0.15%Te,0-0.25%Se,0.02-0.04%B,0.01-0.02%Zr,0.01-0.1%Ca,药芯占焊丝的重量百分比为30-52%。金属粉芯焊丝几乎没有熔渣,焊缝成形不如熔渣型药芯焊丝,且全位置焊接的适应性较差,对于大型热作模具堆焊时变位困难的难以保证堆焊质量。授权公告号为CN103008924B发明专利“一种用于锻造模具堆焊的药芯焊丝及应用”公开了一种用于锻造模具的堆焊药芯焊丝,焊丝采用碳钢钢带包裹药芯粉末,药芯焊丝填充率为30%~37%,药芯粉末包括以下质量百分含量的物质:氟化钙4%~7%,纯碱0.5%~3%,石英0.5%~4%,金红石2%~6%,高碳铬铁13.6%~27.2%,纯铬粉13.9%~19.2%,镍粉2.2%~5.7%,电解锰1.8%~4.3%,钼铁粉6.3%~13.2%,硅铁粉2.1%~5.0%,钒铁粉0.6%~1.9%;余量为还原铁粉。申请号为201410748560.5发明专利“一种热锻模具用气体保护堆焊药芯焊丝”公开的堆焊药芯焊丝采用Cr-Ni-Mo-W-V-Co合金系,采用CO2气体保护焊,加入Co提高了耐氧化性、红硬性、耐磨性能,但成本显著提高。
熔敷金属高温抗氧化性能优异、耐磨性好、洁净度高、具有良好抗疲劳性能的堆焊药芯焊丝是模具制造与修复再制造急需的焊接材料,特别是堆焊时变位困难的大型热作模具更是急需全位置焊接性能优异的药芯焊丝。目前我国该类药芯焊丝的性能与国外还存在较大差距。研发热作模具堆焊用药芯焊丝对于提高热作模具寿命具有重要意义。
发明内容
针对现有技术的不足,本发明通过合金粉末配方的优化设计提供一种马氏体基体的模具堆焊药芯焊丝,通过向铁基合金粉末中加入纳米氮化铬粉末和氧化钇粉末,使堆焊金属能够同时满足热作模具高温抗氧化性、高耐磨性、高洁净度、抗疲劳性能等技术要求。
现有的堆焊金属为铁基的药芯焊丝虽然在硬度、致密性、结合强度等方面与镍基的药芯焊丝大体相当,但铁基堆焊金属的韧性低于镍基的,难以满足高韧性的要求。富氩气体保护的熔化极气体保护焊等电弧焊的熔池存在时间短,采用微米级粉末其冶金反应不充分,难以形成足够多的氮化物、碳化物硬质相。因此,本发明中通过加入纳米氮化铬粉末来改善其韧性和抗裂性能,使其能够达到热作模具高韧性和抗裂性能的标准要求。同时,纳米级粉末活性大,冶金反应剧烈,弥补电弧焊熔池存在时间短、冶金反应不充分的弊端,使其适于富氩气体保护的熔化极气体保护焊、埋弧焊等电弧焊方法。
其中,所述的“热作模具”主要是指锤锻模具、热顶锻模具、热挤压模具、热冲裁模具、精锻模具或压铸模具等。
具体技术方案如下:
一种用于热作模具修复堆焊的专用药芯焊丝,包括焊丝管壁和被包于其内的药粉;所述药粉包含脱氧合金剂和造渣剂,所述造渣剂占药粉总质量的8-10%,所述脱氧合金剂配方以质量份计如下:电解锰4-8,45#硅铁2-6,钛铁1-4,金属铬20-35,高碳铬铁20-30,石墨0-5,钒铁2-6,钼铁12-18,钨粉2-4,镍粉4-8,纳米氮化铬粉1-2,氧化钇粉2-6;造渣剂的配方以质量份计如下:金红石5-8,钾长石2-3,氟硅酸钠2-3,萤石粉1-3。
含有纳米氮化铬粉的堆焊金属具有优异的高温硬度、耐磨性能,以及良好的韧性和抗裂性能,因此,纳米氮化铬粉优选作为用于形成热作模具的堆焊合金粉末的基础原料使用。
其中,当纳米氮化铬粉的含量低于1质量份时,高温硬度、耐磨性能,韧性和抗裂性能不良。另一方面,如果纳米氮化铬粉的含量高于2质量份,堆焊金属易产生气孔缺陷,成本亦升高。本发明已确认了下述结果:如果纳米氮化铬粉的含量不低于1质量份且不超过2质量份时,可获得期待的高温硬度、耐磨性能,韧性和抗裂性能。
氧化钇稀土作为除金属和铁合金、纳米氮化铬、造渣剂以及不可避免的杂质以外的余分而包含的金属氧化物,其发挥净化堆焊金属、球化夹杂物、促使形成氮化物间隙相,提高堆焊金属的抗疲劳性能的作用。就其含量而言,尽管不能一概而论,但当氧化钇的含量低于2质量份时,可能会导致氧化钇净化和抗疲劳性能效果减弱。
另一方面,氧化钇的含量高于6质量份时,可能会导致高温硬度和耐磨性能下降,因此,本申请中将氧化钇的加入量限定在6质量份以下,因此不会产生上述问题。
优选地,所述脱氧合金剂配方以质量份计如下:电解锰5-8,45#硅铁3-6,钛铁2-4,金属铬25-35,高碳铬铁24-30,石墨2-5,钒铁3-6,钼铁14-18,钨粉2.5-4,镍粉5-8,纳米氮化铬粉1.2-2,氧化钇粉3-6;造渣剂的配方以质量份计如下:金红石6-8,钾长石2.4-3,氟硅酸钠2.4-3,萤石粉1.5-3。
优选地,所述脱氧合金剂配方以质量份计如下:电解锰5-7,45#硅铁3-5,钛铁2-3,金属铬25-30,高碳铬铁24-28,石墨2-4,钒铁3-5,钼铁14-16,钨粉2.5-3.5,镍粉5-7,纳米氮化铬粉1.2-1.6,氧化钇粉3-5;造渣剂的配方以质量份计如下:金红石6-7,钾长石2.4-2.8,氟硅酸钠2.4-2.8,萤石粉1.5-2.5。
所述电解锰的成分以质量比计Mn含量不小于99.5%;45#硅铁的成分以质量比计是40.0%~47.0%Si,0.1%C,余为Fe和不影响性能的杂质;钛铁的成分以质量比计是23%~35%Ti,8.5%Al,5%Si,2.5%Mn,余为Fe和不影响性能的杂质;金属铬的成分以质量比计Cr含量不小于98%;高碳铬铁的成分以质量比计Cr不小于60%,C为6%~10%,Si不大于3%,S不超过0.04%,P不超过0.04%,余为Fe和不影响性能的杂质;石墨的成分以质量比计是94%~99%C;钒铁的成分以质量比计是50%V,0.2%C,2%Si,0.8%Al,余为Fe和不影响性能的杂质;钼铁的成分以质量比计是50%Mo,3%Si,余为Fe和不影响性能的杂质;钨粉的成分以质量比计W含量不小于98%;金属镍粉的成分以质量比计Ni含量不小于98%;氧化钇粉末的成分以质量百分比计Y2O3含量不小于99%;钾长石的成分以质量百分比计是62-72%SiO2,17-24%Al2O3,K2O+Na2O不小于12%,K2O不小于8%,S不超过0.04%,P不超过0.04%。金红石的成分以质量百分比计TiO2含量不小于92%;氟硅酸钠的成分以质量百分比计Na2SiF4含量不小于95%;萤石粉的成分以质量百分比计CaF2含量不小于95%。
本发明中,纳米氮化铬粉末的加入,可以在堆焊金属中形成细小的氮化物间隙相,同时利用纳米氮化铬粉末细化晶粒(纳米氮化铬粉末的粒度小于100纳米),提高堆焊金属的高温硬度、耐磨性能,并使其具有良好的韧性、抗裂性能和抗疲劳性能,纳米级氮化铬粉末活性大,冶金反应剧烈,可以弥补电弧堆焊熔池存在时间短、冶金反应不充分的弊端,适于富氩气体保护的熔化极气体保护焊、埋弧焊等电弧堆焊工艺;另一方面,为了满足堆焊金属高洁净度、抗疲劳性能的要求,通过在合金粉末中加入氧化钇稀土,净化堆焊金属、球化夹杂物、促使形成氮化物强化相,提高堆焊金属的抗疲劳性能。通过合理的合金系设计,使堆焊金属获得马氏体基体组织加少量残余奥氏体组织,并以氮化物、碳化物作为强化相;通过冶金处理和原材料优选,降低堆焊金属S、P等杂质含量,并改善工艺性能。
就本发明的铁基合金粉末而言,其至少包含以下合金元素:C、N、Si、Mn、Cr、Mo、V、Ti、Ni、W。当铁基合金粉末中含有上述合金元素时,制备的堆焊金属具有一定的高温硬度和耐腐蚀性,能够保证氮化铬和氧化钇增强效果的最大化。
专用药芯焊丝的药粉也可以使用配合有除上述以外的其它金属粉或合金粉的原料粉末而成。此时,要以不破坏本发明的特征为前提。
本发明中专用药芯焊丝的药粉为氮化铬、钒铁、硅铁、钛铁等粉末混合制成,为了降低焊接材料成本,降低焊接飞溅、提高电弧稳定性、改善焊缝成型,优选的加入一定量的造渣剂,
其中,金红石、钾长石、氟硅酸钠、萤石粉作为造渣剂,起到造渣、稳定电弧,降低飞溅的作用,使堆焊金属表面质量得到进一步提升的作用。使用时,要使金红石、钾长石、氟硅酸钠、萤石粉的含量在所述范围内。当金红石、钾长石、氟硅酸钠、萤石粉的总含量低于10质量份时,其造渣、稳定电弧、降低飞溅、改善堆焊金属表面成型的作用不明显。另一方面,如果金红石、钾长石、氟硅酸钠、萤石粉的总含量高于17质量份时,稳弧、降低飞溅的效果也不再进一步改善,且相对减少了合金元素的加入量。已确认了下述结果:使金红石、钾长石、氟硅酸钠、萤石粉含量分别在10质量份以上且17质量份以下的范围时,可获得良好的稳弧、降低飞溅、改善堆焊金属成型的效果。
就本发明的堆焊合金粉末而言,优选所述电解锰、45#硅铁、钛铁、金属铬,高碳铬铁、石墨、钒铁、钼铁、钨粉、镍粉、氧化钇粉、金红石、钾长石、氟硅酸钠以及萤石粉的粒度均为75微米~180微米。(即粒度为-80目~+200目)。
优选的,当本发明的合金粉末用于处理热作模具钢时(碳质量分数一般小于0.5%,常加入的合金元素有:Cr、Mn、W、Mo、V、Si、Ni、Nb、Al等),一般来说,由于熔覆层中添加了Cr,Ni,Mo等元素,因此熔覆层与基材之间会形成原电池,从而发生电化学腐蚀,但是由于热作模具本身和熔覆粉末中都添加了Cr,Ni,Mo等元素而使得电化学反应难以快速持续进行。首先,Cr在合金中会溶于Ni中从而形成Ni-Cr固溶体,并起到显著的钝化作用;其次,在腐蚀过程中,Cr部分取代锈层α-FeOOH中的Fe,形成了羟基氧化物α-(Fe1-xCrx)OOH。由于这种锈层微观组织较为致密且相对稳定,能将基体材料与腐蚀介质很好的隔离,同时其极高的阻抗又能很好的降低了电化学反应的速度。而Mo能在钢材中细化晶粒,固溶强化,形成固化层,这种固化层与基体结合牢固,形成钝化作用,因而具有很好的保护性能。同时由于激光熔覆过程中激光束与粉末的相互作用时间短,因此在急速冷却过程中具有较大的冷却度,而粉末中的合金元素会形成多种化合物,进一步增加非自发形核的数量,大大提高形核率,最终使得熔覆层的组织细小致密。细密的组织不仅减少了单位晶界上的杂质含量,而且减少了由于快速冷却而形成的成分偏析,从而降低了因原电池效应而加速腐蚀的影响。所以,无论是从腐蚀失重量而言,还是根据更具科学性的腐蚀失重速率分析,都说明热作模具包含Cr,Ni,Mo三种元素时,熔覆层的试样具有更好的耐腐蚀性,且并没有由于电化学腐蚀及原电池效应而加快基材的腐蚀。证明了本发明的粉末具有和基材一致的耐腐蚀性能,很好的满足了热作模具修复再制造的设计要求。
药芯焊丝的截面形状越复杂、越对称,电弧越稳定,药芯的冶金反应和保护作用越充分。但是随着焊丝直径的减小,这种差别逐渐缩小。就本发明的药芯焊丝而言,当焊丝直径在2.4毫米~4.0毫米之间时,药芯焊丝截面形状采用“O”型时,电弧稳定性最高。
上述的热作模具堆焊用金属粉芯焊丝中:所述药芯焊丝的管壁优选SPCC或H08A低碳钢钢带制备。
优选的实施方式是:所述药芯焊丝的管壁选壁厚为0.3~0.5mm,宽度为14~16mm的SPCC钢带制备;其化学成分以质量百分比计优选:C不大于0.12%、Si不大于0.05%、Mn不大于0.5%、S不大于0.035%、P不大于0.035%、余为Fe和不影响性能的杂质。
上述的热作模具堆焊用金属粉芯焊丝的填充率为30%~55%(填充率为药粉质量与药粉、钢带质量之和的比值)。
上述药粉中各组分的作用如下:
电解锰的作用是脱氧和合金化,金属锰杂质含量少,利于堆焊金属的净化。
45#硅铁的作用是脱氧和合金化,与电解锰联合加入药皮,硅锰联合脱氧的效果好。
钛铁的作用是脱氧,并析出碳化物TiC和氮化物TiN,细化晶粒,通过细晶和析出相两种方式强化焊缝,提高堆焊金属的硬度。
金属铬和高碳铬铁的作用是向焊缝金属过渡Cr,对焊缝金属起到固溶强化作用,同时析出碳化物强化焊缝,Cr含量达到11%以上还能提高堆焊金属的高温抗氧化性能。高碳铬铁除了过渡Cr外,还向焊缝过渡C。
石墨的作用是向焊缝过渡C,控制焊缝适当的含C量形成碳化物,保证焊缝的硬度。
钒铁的作用是合金化,形成碳化物、氮化物,细化晶粒。
钼铁的作用是合金化,细化晶粒,固溶强化,形成碳化物,提高堆焊金属的高温性能和耐磨性能。
钨粉的作用是合金化,向焊缝过渡W,提高焊缝金属的高温硬度和高温耐磨性能。
镍粉的作用是可以提高奥氏体稳定性,减缓奥氏体向马氏体的转变,增加残余奥氏体量,提高堆焊金属的塑性、韧性,而且可以降低马氏体开始转变温度Ms点,可以降低堆焊金属的残余应力。
纳米氮化铬粉的作用是向焊缝过渡N,与氮化物形成元素Ti、V、Cr等形成氮化物,细化晶粒,提高焊缝金属的高温硬度和组织稳定性;向焊缝金属过渡Cr。纳米粉末活性大,冶金反应充分。
氧化钇的作用是降低焊缝夹杂物含量,使夹杂物球化,净化焊缝金属,提高焊缝金属的抗疲劳性能;降低熔滴的表面张力,促使熔滴过渡,减少飞溅。
金红石的作用是造渣、稳弧,调节熔渣的物理性能,改善焊缝成型。
钾长石的作用是稳定电弧,降低飞溅,改善焊条工艺性能,造渣。
氟硅酸钠的作用是稳定电弧,降低飞溅,降低熔渣粘度,改善工艺性能,造渣。
萤石的作用是造渣、调节熔渣的熔点和粘度,增加熔渣的流动性。
本发明热作模具堆焊用药芯焊丝的制备方法包括以下步骤:
(1)配粉按药粉配方的配比称量药粉,先将比重较小的石墨、金红石、钾长石、氟硅酸钠、萤石粉按配方比例称量后混合,用现有的混粉机混粉8-10分钟,获得造渣剂混合粉末;然后将电解锰、45#硅铁、钛铁、金属铬、高碳铬铁、钒铁、钼铁、钨粉、镍粉、纳米氮化铬粉、氧化钇粉等脱氧合金剂按配方比例称量后加入到造渣剂混合粉中,再继续混粉8-10分钟,获得药粉。
其中:所述药粉包含脱氧合金剂和造渣剂,药粉脱氧合金剂配方以质量份计如下:电解锰4-8,45#硅铁2-6,钛铁1-4,金属铬20-35,高碳铬铁20-30,石墨0-5,钒铁2-6,钼铁12-18,钨粉2-4,镍粉4-8,纳米氮化铬粉1-2,氧化钇粉2-6;造渣剂的配方以质量份计如下:金红石5-8,钾长石2-3,氟硅酸钠2-3,萤石粉1-3。造渣剂为药粉质量的8-10%。纳米氮化铬粉的粒度为99%以上的小于100纳米,其他粉末的粒度为75微米~180微米(即粒度为-80目~+200目);
(2)将14~16毫米宽、0.3~0.5毫米厚低碳钢钢带用超声波清洗设备清洗后,用现有的药芯焊丝生产设备,将上述钢带轧制成U形,再向U形糟中加入步骤(1)制成的药粉,填充率(药粉质量与药芯焊丝质量的比值)为30~55%;
(3)将U形槽合口,使药粉包裹其中,合口部位采用搭接连接方式(搭接部分的宽度为1-2mm,由现有药芯焊丝生产设备的成型辊保证):通过拉丝摸,逐道拉拔、减径,最后使其直径达到2.4mm~4.0mm。
(4)将步骤(3)所得的药芯焊丝层绕成盘,即得热作模具堆焊用药芯焊丝成品。
其中:上述步骤(2)所述低碳钢钢带优选SPCC钢带。
就本发明的药芯焊丝而言,当MAG焊气体的气体流量小于18L/min时,保护气体的挺度不足,焊缝容易产生气孔等缺陷;气体流量大于23L/min时,不仅浪费气体,而且氧化性增强,焊缝表面上会形成一层暗灰色的氧化皮,使焊缝质量下降,同时有可能产生紊流降低保护效果。因此,本发明中优选的气体流量为18L/min-23L/min。
电弧电压及焊接电流是MAG焊的主要工艺参数,电弧电压是短路过渡时的关键参数,电弧电压与焊接电流相匹配,可以获得飞溅小,焊缝成形良好的稳定焊接过程。本发明中优选的焊接电流300A-450A;电压28V-42V。
由于短路过渡均采用细焊丝,所以焊丝伸出长度上所产生的电阻热对焊接效果影响很大。伸出长度增加,焊丝上的电阻热增加,焊丝熔化加快,生产率提高。但就本发明而言,伸出长度大于28mm时,焊丝容易发生过热而成段熔断,飞溅严重,焊接过程不稳定。同时伸出长度增大后,喷嘴与焊件间的距离亦增大,导致气体保护效果变差。但伸出长度小于14mm时,喷嘴与电弧间的距离过短,飞溅金属容易堵塞喷嘴。因此,本发明中优选的焊丝伸出长度为14mm-28mm。
上述热作模具堆焊用药芯焊丝采用富氩气体保护MAG焊,焊接电流300A-450A;电压28V-42V;气体流量18L/min-23L/min;焊丝伸出长度14mm-28mm。焊丝的焊接工艺性能好,电弧稳定、飞溅小、抗裂性好。堆焊金属的硬度为HRC40-55。
本发明的药芯焊丝的应用不限于气体保护焊,也可用于埋弧焊、电渣焊等。
本发明所具有的显著效果是:
(1)本专利药芯焊丝具有良好的工艺性能,适于自动焊,焊接生产效率高。通过在焊缝表面形成一层厚度不超过0.3mm、分布均匀的薄层熔渣,改善了焊缝成型,也适于全位置焊接。可用于堆焊时变位困难的大型热作模具的制造与修复。
(2)熔敷金属的成分可以通过改变药芯焊丝药粉的成分调整,可以制造出系列产品用于不同的热作模具钢,应用范围广。
(3)本专利药芯焊丝优化了熔敷金属含铬量,使堆焊金属具有良好的高温抗氧化性能,显著提高了热作模具的使用寿命。
(4)本专利药芯焊丝通过在药皮中加入纳米氮化铬粉和氮化物形成元素,通过反应原位合成氮化物,氮化物作为间隙相具有尺寸细小、高温稳定等优点,显著提高了堆焊金属的高温硬度和高温稳定性。
(5)本专利通过钢带和药粉原材料的优选(如选用纯金属,少用铁合金)和加入稀土,降低了堆焊金属夹杂物含量,使夹杂物球化,细化晶粒,提高了堆焊金属的韧性、塑性和抗疲劳性能。
具体实施方式
实施例1:
(1)配粉按药粉配方的配比称量药粉,先将比重较小的金红石、钾长石、氟硅酸钠、萤石粉按配方比例称量后混合,用现有的混粉机混粉8分钟,获得造渣剂混合粉末;然后将电解锰、45#硅铁、钛铁、金属铬,高碳铬铁、钒铁、钼铁、钨粉、镍粉、纳米氮化铬粉、氧化钇粉等脱氧合金剂按配方比例称量后加入到造渣剂混合粉中,再继续混粉8分钟,获得药粉。
其中:所述药粉包含脱氧合金剂和造渣剂,药粉脱氧合金剂配方以质量份计如下:电解锰4,45#硅铁3,钛铁2,金属铬20,高碳铬铁20,钒铁2,钼铁12,钨粉2,镍粉4,纳米氮化铬粉1,氧化钇粉2;造渣剂的配方以质量份计如下:金红石8,钾长石2,氟硅酸钠2,萤石粉2。造渣剂为药粉质量的10%。纳米氮化铬粉的粒度为99%以上的小于100纳米,其他粉末的粒度为75微米~180微米(即粒度为-80目~+200目);
(2)将14mm宽、0.3mm厚SPCC钢带用超声波清洗设备清洗后,用现有的药芯焊丝生产设备,将上述钢带轧制成U形,再向U形糟中加入步骤(1)制成的药粉,填充率(药粉质量与药芯焊丝质量的比值)为35%;
(3)将U形槽合口,使药粉包裹其中,合口部位采用搭接连接方式;通过拉丝摸,逐道拉拔、减径,最后使其直径达到2.4mm。
(4)将步骤(3)所得的药芯焊丝层绕成盘,即得热作模具堆焊用药芯焊丝成品。
上述热作模具堆焊用药芯焊丝采用富氩气体Ar+1%CO2保护的熔化极气体保护焊,焊接电流300A;电压28V;气体流量18L/min;焊丝伸出长度14mm。焊丝的焊接工艺性能好,电弧稳定、飞溅小、抗裂性好。堆焊金属的硬度为HRC42。
实施例2:
(1)配粉按药粉配方的配比称量药粉,先将比重较小的石墨、金红石、钾长石、氟硅酸钠、萤石粉按配方比例称量后混合,用现有的混粉机混粉10分钟,获得非合金混合粉;然后将电解锰、45#硅铁、钛铁、金属铬,高碳铬铁、钒铁、钼铁、钨粉、镍粉、纳米氮化铬粉、氧化钇粉等脱氧合金剂按配方比例称量后加入到非合金混合粉中,再继续混粉8分钟,获得药粉。
其中:所述药粉包含脱氧合金剂和造渣剂,药粉脱氧合金剂配方以质量份计如下:电解锰8,45#硅铁6,钛铁4,金属铬35,高碳铬铁30,石墨3,钒铁6,钼铁18,钨粉4,镍粉5,纳米氮化铬粉2,氧化钇粉6;造渣剂的配方以质量份计如下:金红石5,钾长石1,氟硅酸钠3,萤石粉1。造渣剂为药粉质量的8%。纳米氮化铬粉的粒度为99%以上的小于100纳米,其他粉末的粒度为75微米~180微米(即粒度为-80目~+200目);
(2)将16mm宽、0.3mm厚SPCC钢带用超声波清洗设备清洗后,用现有的药芯焊丝生产设备,将上述钢带轧制成U形,再向U形糟中加入步骤(1)制成的药粉,填充率(药粉质量与药芯焊丝质量的比值)为55%;
(3)将U形槽合口,使药粉包裹其中,合口部位采用搭接连接方式;通过拉丝摸,逐道拉拔、减径,最后使其直径达到4.0mm。
(4)将步骤(3)所得的药芯焊丝层绕成盘,即得热作模具堆焊用药芯焊丝成品。
上述热作模具堆焊用药芯焊丝采用Ar+1.5%CO2富氩气体保护焊,焊接电流450A;电压42V;气体流速23L/min;焊丝伸出长度28mm。焊丝的焊接工艺性能好,电弧稳定、飞溅小、抗裂性好。堆焊金属的硬度为HRC52。
实施例3:
(1)配粉按药粉配方的配比称量药粉,先将比重较小的石墨、金红石、钾长石、氟硅酸钠、萤石粉按配方比例称量后混合,用现有的混粉机混粉9分钟,获得非合金混合粉;然后将电解锰、45#硅铁、钛铁、金属铬,高碳铬铁、钒铁、钼铁、钨粉、镍粉、纳米氮化铬粉、氧化钇粉等脱氧合金剂按配方比例称量后加入到非合金混合粉中,再继续混粉9分钟,获得药粉。
其中:所述药粉包含脱氧合金剂和造渣剂,药粉脱氧合金剂配方以质量份计如下:电解锰6,45#硅铁4,钛铁3,金属铬30,高碳铬铁25,石墨3,钒铁4,钼铁15,钨粉3,镍粉6,纳米氮化铬粉1,氧化钇粉4;造渣剂的配方以质量份计如下:金红石7,钾长石2,氟硅酸钠3,萤石粉2。造渣剂为药粉质量的9%。纳米氮化铬粉的粒度为99%以上的小于100纳米,其他粉末的粒度为75微米~180微米(即粒度为-80目~+200目);
(2)将16mm宽、0.5mm厚SPCC钢带用超声波清洗设备清洗后,用现有的药芯焊丝生产设备,将上述钢带轧制成U形,再向U形糟中加入步骤(1)制成的药粉,填充率(药粉质量与药芯焊丝质量的比值)为40%;
(3)将U形槽合口,使药粉包裹其中,合口部位采用搭接连接方式;通过拉丝摸,逐道拉拔、减径,最后使其直径达到3.2mm。
(4)将步骤(3)所得的药芯焊丝层绕成盘,即得热作模具堆焊用药芯焊丝成品。
上述热作模具堆焊用药芯焊丝采用Ar+1%CO2富氩气体保护焊,焊接电流390A;电压38V;气体流速20L/min;焊丝伸出长度20mm。焊丝的焊接工艺性能好,电弧稳定、飞溅小、抗裂性好。堆焊金属的硬度为HRC40。
实施例4:
(1)配粉按药粉配方的配比称量药粉,先将比重较小的石墨、金红石、钾长石、氟硅酸钠、萤石粉按配方比例称量后混合,用现有的混粉机混粉8分钟,获得非合金混合粉;然后将电解锰、45#硅铁、钛铁、金属铬,高碳铬铁、钒铁、钼铁、钨粉、镍粉、纳米氮化铬粉、氧化钇粉等脱氧合金剂按配方比例称量后加入到非合金混合粉中,再继续混粉8分钟,获得药粉。
其中:所述药粉包含脱氧合金剂和造渣剂,药粉脱氧合金剂配方以质量份计如下:电解锰4,45#硅铁6,钛铁4,金属铬35,高碳铬铁30,石墨5,钒铁6,钼铁12,钨粉4,镍粉8,纳米氮化铬粉2,氧化钇粉6;造渣剂的配方以质量份计如下:金红石6,钾长石3,氟硅酸钠2,萤石粉1。造渣剂为药粉质量的8%。纳米氮化铬粉的粒度为99%以上的小于100纳米,其他粉末的粒度为75微米~180微米(即粒度为-80目~+200目);
(2)将16mm宽、0.3mm厚SPCC钢带用超声波清洗设备清洗后,用现有的药芯焊丝生产设备,将上述钢带轧制成U形,再向U形糟中加入步骤(1)制成的药粉,填充率(药粉质量与药芯焊丝质量的比值)为45%;
(3)将U形槽合口,使药粉包裹其中,合口部位采用搭接连接方式;通过拉丝摸,逐道拉拔、减径,最后使其直径达到3.2mm。
(4)将步骤(3)所得的药芯焊丝层绕成盘,即得热作模具堆焊用药芯焊丝成品。
上述热作模具堆焊用药芯焊丝采用富氩气体Ar+1.5%CO2保护的熔化极气体保护焊,焊接电流390A;电压38V;气体流量20L/min;焊丝伸出长度20mm。焊丝的焊接工艺性能好,电弧稳定、飞溅小、抗裂性好。堆焊金属的硬度为HRC48。
对比例1
本对比例与实施例1的不同之处在于,原料配方中不含氧化钇,对堆焊金属的热疲劳性进行测试,试样尺寸为50×20×1.5(mm),在20mm一边的中心垂直厚度方向,开60°V型缺口,进行700℃-20℃的循环加热、冷却,用出现0.5mm裂纹的循环次数反映疲劳性能。不含氧化钇粉末的对比例1的循环次数为21次,含氧化钇2份(质量)的实施例1的循环次数为43次。通过与实施例1的比对,表明本发明氧化钇能有效提升堆焊金属的抗疲劳性能。
对比例2
本对比例与实施例1的不同之处在于,原料配方中不加入纳米氮化铬粉,对韧性和抗裂性能的进行测试,不加纳米氮化铬粉的对比例2,U型缺口冲击韧性的测试值为1.06J/cm2,在厚度为80mm的5CrNiMo模具钢表面堆焊,预热250℃才能不出现裂纹;实施例1的U型缺口冲击韧性的测试值为1.21J/cm2,在厚度为80mm的5CrNiMo模具钢表面堆焊,预热50℃即可不出现裂纹。表明本发明药芯中的纳米氮化铬粉能有效地提高堆焊金属的韧性和抗裂性能。
对比例3
本对比例与实施例1的不同之处在于,原料配方中采用粒度为75微米~180微米(即粒度为-80目~+200目)的氮化铬粉,实测500℃的硬度为HRC36,硬度的最大值与最小值相差HRC6;实施例1的500℃硬度为HRC41,硬度的最大值与最小值相差HRC4。纳米氮化铬使堆焊金属高温下保持较高硬度,且堆焊金属的硬度较均匀。微米级的氮化铬由于颗粒较大,活性较小,在现有的加入量下由于焊接熔池冷却速度快,导致冶金反应不充分,无法有效提高堆焊金属的高温硬度和组织稳定性。
上述虽然对本发明的具体实施方式进行了描述,但并非对本发明保护范围的限制,所属领域技术人员应该明白,在本发明的技术方案的基础上,本领域技术人员不需要付出创造性劳动即可做出的各种修改或变形仍在本发明的保护范围以内。
Claims (10)
1.一种用于热作模具修复堆焊的专用药芯焊丝,其特征在于,包括焊丝管壁和被包于其内的药粉;所述药粉包含脱氧合金剂和造渣剂,所述造渣剂占药粉总质量的8-10%,所述脱氧合金剂配方以质量份计如下:电解锰4-8,45#硅铁2-6,钛铁1-4,金属铬20-35,高碳铬铁20-30,石墨0-5,钒铁2-6,钼铁12-18,钨粉2-4,镍粉4-8,纳米氮化铬粉1-2,氧化钇粉2-6;造渣剂的配方以质量份计如下:金红石5-8,钾长石2-3,氟硅酸钠2-3,萤石粉1-3。
2.如权利要求1所述的药芯焊丝,其特征在于,所述脱氧合金剂配方以质量份计如下:电解锰5-8,45#硅铁3-6,钛铁2-4,金属铬25-35,高碳铬铁24-30,石墨2-5,钒铁3-6,钼铁14-18,钨粉2.5-4,镍粉5-8,纳米氮化铬粉1.2-2,氧化钇粉3-6;造渣剂的配方以质量份计如下:金红石6-8,钾长石2.4-3,氟硅酸钠2.4-3,萤石粉1.5-3。
3.如权利要求1或2所述的药芯焊丝,其特征在于,所述脱氧合金剂配方以质量份计如下:电解锰5-7,45#硅铁3-5,钛铁2-3,金属铬25-30,高碳铬铁24-28,石墨2-4,钒铁3-5,钼铁14-16,钨粉2.5-3.5,镍粉5-7,纳米氮化铬粉1.2-1.6,氧化钇粉3-5;造渣剂的配方以质量份计如下:金红石6-7,钾长石2.4-2.8,氟硅酸钠2.4-2.8,萤石粉1.5-2.5。
4.如权利要求1或2所述的药芯焊丝,其特征在于,所述电解锰的成分以质量比计Mn含量不小于99.5%;45#硅铁的成分以质量比计是40.0%~47.0%Si,0.1%C,余为Fe和不影响性能的杂质;钛铁的成分以质量比计是23%~35%Ti,8.5%Al,5%Si,2.5%Mn,余为Fe和不影响性能的杂质;金属铬的成分以质量比计Cr含量不小于98%;高碳铬铁的成分以质量比计Cr不小于60%,C为6%~10%,Si不大于3%,S不超过0.04%,P不超过0.04%,余为Fe和不影响性能的杂质;钒铁的成分以质量比计是50%V,0.2%C,2%Si,0.8%Al,余为Fe和不影响性能的杂质;钼铁的成分以质量比计是50%Mo,3%Si,余为Fe和不影响性能的杂质;钨粉的成分以质量比计W含量不小于98%;金属镍粉的成分以质量比计Ni含量不小于98%;氧化钇粉末的成分以质量百分比计Y2O3含量不小于99%;钾长石的成分以质量百分比计是62-72%SiO2,17-24%Al2O3,K2O+Na2O不小于12%,K2O不小于8%,S不超过0.04%,P不超过0.04%;金红石的成分以质量百分比计TiO2含量不小于92%;氟硅酸钠的成分以质量百分比计Na2SiF4含量不小于95%;萤石粉的成分以质量百分比计CaF2含量不小于95%。
5.如权利要求1或2所述的药芯焊丝,其特征在于,所述纳米氮化铬粉末的粒度小于100纳米;所述电解锰、45#硅铁、钛铁、金属铬、高碳铬铁、钒铁、钼铁、钨粉、镍粉、氧化钇粉、金红石、钾长石、氟硅酸钠以及萤石粉的粒度均为75微米~180微米。
6.如权利要求1所述的药芯焊丝,其特征在于,所述焊丝管壁采用SPCC或H08A低碳钢钢带制备。
7.如权利要求1所述的药芯焊丝,其特征在于,所述焊丝管壁采用壁厚为0.3~0.5mm,宽度为14~16mm的SPCC钢带制备;其化学成分以质量百分比计优选:C不大于0.12%、Si不大于0.05%、Mn不大于0.5%、S不大于0.035%、P不大于0.035%、余为Fe和不影响性能的杂质。
8.如权利要求1所述的药芯焊丝,其特征在于,所述药芯焊丝的填充率为30%~55%。
9.权利要求1-8任一所述的药芯焊丝的富氩气体保护的熔化极气体保护焊接方法,其特征在于,工艺参数如下:焊接电流300A-450A;电压28V-42V;气体流量18L/min-23L/min;焊丝伸出导电嘴的长度14mm-28mm。
10.权利要求1-8任一所述的药芯焊丝在处理热作模具钢中的应用,其特征在于,所述热作模具钢中含有Cr,Ni,Mo。