CN105033410A - 一种钢结构混合气体保护焊焊接工艺 - Google Patents
一种钢结构混合气体保护焊焊接工艺 Download PDFInfo
- Publication number
- CN105033410A CN105033410A CN201510399407.0A CN201510399407A CN105033410A CN 105033410 A CN105033410 A CN 105033410A CN 201510399407 A CN201510399407 A CN 201510399407A CN 105033410 A CN105033410 A CN 105033410A
- Authority
- CN
- China
- Prior art keywords
- welding
- mixed gas
- steel
- gas arc
- arc welding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钢结构混合气体保护焊焊接工艺,包括以下步骤:根据钢结构的形状和焊接位置开坡口,清除坡口周围的杂物,并用浓度为0.5mol/L的硫酸擦拭焊接面,水洗后用丙酮擦拭,自然晾干;将钢结构待焊接部位进行对接,坡口间隙0-2mm,进行固定,防止发生移动;采用气体保护焊进行焊接,选择相应的工艺参数,选用低氢型焊条,使用前在300-350℃温度下烘干时间1-1.5h,烘干后缓冷放置于100-120℃的保温箱中待用;焊接时采用脉冲电流进行焊接,采取多层多道连续施焊,一次焊接完成,并控制层间温度在150-200℃,焊接完成后继续通保护气体3-4分钟。本发明实施方便,焊接效率高,焊接缺陷发生率低。
Description
发明领域
本发明涉及一种焊接工艺,具体是一种钢结构混合气体保护焊焊接工艺。
背景技术
目前中国已成为全球最大的钢材生产和消费国,钢结构在我国的应用越来越广泛,如厂房、桥梁、住宅、仓库、体育馆、展览馆、超市等建筑都在广泛运用钢结构。钢结构延展性好、塑性、韧性好,具有优良的抗震和承受荷载能力,大大提高了钢结构建筑的安全可靠性。钢结构建筑自重轻,基础造价低,建造周期短,在劳动力价格逐渐上涨的今日具有很强的竞争优势。另外,钢结构的工业化程度高,生产制造周期较短,精度控制好,加之能够满足超高度和超跨度的要求,提高空间利用率,钢结构在建筑行业获得了长足发展。
目前钢结构的焊接方法主要是手工电弧焊,虽然能够实现对具体固定钢结构件的焊接,但是作业范围有限,难以实现钢结构件焊接的高效快捷,在焊接结束没有后处理的情况下,焊接产生的气孔、飞溅等无法有效清理,焊缝质量无法得到保障,进而对钢结构的性能产生影响。
发明内容
为解决上述问题,本发明提供了一种钢结构混合气体保护焊焊接工艺。
本发明所采取的技术方案为:
一种钢结构混合气体保护焊焊接工艺,其特征在于,包括以下步骤:
(1)根据钢结构的形状和焊接位置开坡口,清除坡口周围的杂物,并用浓度为0.5mol/L的硫酸擦拭焊接面,水洗后用丙酮擦拭,自然晾干;
(2)将钢结构待焊接部位进行对接,坡口间隙0-2mm,使用固定装置对其进行固定,防止发生移动;
(3)采用混合气体保护焊进行焊接,根据焊接操作规范选择相应的工艺参数,选用低氢型焊条,使用前在300-350℃温度下烘干时间1-1.5h,烘干后缓冷放置于100-120℃的保温箱中待用;
(4)焊接时采用脉冲电流进行焊接,采取多层多道连续施焊,一次焊接完成,并控制层间温度在150-200℃,焊接完成后继续通保护气体3-4分钟。
进一步地,步骤(3)所述的混合保护气体是CO2和Ar,所述钢为碳钢时的保护气体的比例为80%的Ar和20%的CO2;所述钢为不锈钢时的保护气体的比例为97.5%的Ar和2.5%的CO2。
进一步地,所述焊缝坡口形式为I字型、V字型、X字型、Y字型、U字型、双面U字型或者K字型。
本发明的有益效果:
本发明实施方便,焊接效率高,混合气体保护焊是常用的焊接方法,设备及耗材易于采购实现,焊接工人易于掌握实施,可以采用自动焊工艺,焊接效率高,焊接缺陷发生率低。
具体实施方式
本发明的一种钢结构混合气体保护焊焊接工艺,其特征在于,包括以下步骤:
(1)根据钢结构的形状和焊接位置开坡口,清除坡口周围的杂物,并用浓度为0.5mol/L的硫酸擦拭焊接面,水洗后用丙酮擦拭,自然晾干;
(2)将钢结构待焊接部位进行对接,坡口间隙0-2mm,使用固定装置对其进行固定,防止发生移动;
(3)采用混合气体保护焊进行焊接,根据焊接操作规范选择相应的工艺参数,选用低氢型焊条,使用前在300-350℃温度下烘干时间1-1.5h,烘干后缓冷放置于100-120℃的保温箱中待用;
(4)焊接时采用脉冲电流进行焊接,采取多层多道连续施焊,一次焊接完成,并控制层间温度在150-200℃,焊接完成后继续通保护气体3-4分钟。
进一步地,步骤(3)所述的混合气体是CO2和Ar,所述钢为碳钢时的保护气体的比例为80%的Ar和20%的CO2;所述钢为不锈钢时的保护气体的比例为97.5%的Ar和2.5%的CO2。
进一步地,所述焊缝坡口形式为I字型、V字型、X字型、Y字型、U字型、双面U字型或者K字型。
Claims (3)
1.一种钢结构混合气体保护焊焊接工艺,其特征在于,包括以下步骤:
(1)根据钢结构的形状和焊接位置开坡口,清除坡口周围的杂物,并用浓度为0.5mol/L的硫酸擦拭焊接面,水洗后用丙酮擦拭,自然晾干;
(2)将钢结构待焊接部位进行对接,坡口间隙0-2mm,使用固定装置对其进行固定,防止发生移动;
(3)采用混合气体保护焊进行焊接,根据焊接操作规范选择相应的工艺参数,选用低氢型焊条,使用前在300-350℃温度下烘干时间1-1.5h,烘干后缓冷放置于100-120℃的保温箱中待用;
(4)焊接时采用脉冲电流进行焊接,采取多层多道连续施焊,一次焊接完成,并控制层间温度在150-200℃,焊接完成后继续通保护气体3-4分钟。
2.根据权利要求1所述的一种钢结构混合气体保护焊焊接工艺,其特征在于:步骤(3)所述的保护气体是CO2和Ar,所述钢为碳钢时的保护气体的比例为80%的Ar和20%的CO2;所述钢为不锈钢时的保护气体的比例为97.5%的Ar和2.5%的CO2。
3.根据权利要求1所述的一种钢结构混合气体保护焊焊接工艺,其特征在于:所述焊缝坡口形式为I字型、V字型、X字型、Y字型、U字型、双面U字型或者K字型。