CN105016779A - Crystalline glaze ceramic glaze - Google Patents
Crystalline glaze ceramic glaze Download PDFInfo
- Publication number
- CN105016779A CN105016779A CN201410110356.0A CN201410110356A CN105016779A CN 105016779 A CN105016779 A CN 105016779A CN 201410110356 A CN201410110356 A CN 201410110356A CN 105016779 A CN105016779 A CN 105016779A
- Authority
- CN
- China
- Prior art keywords
- glaze
- ceramic
- crystalline
- crystalline glaze
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a crystalline glaze ceramic glaze, which is prepared from the following substances by weight: 4-25% of potassium feldspar, 2-15% of quartz, 2-15% of talc, 3-20% of soil, 25-40% of high boron powder, 8-22% of manganese oxide, and 6-20% of iron oxide. With the crystalline glaze ceramic glaze of the present invention, the disadvantage that the crystal formed on the existing crystalline glaze ceramic is fine and is not obvious is solved, the large flake crystal can be formed on the ceramic surface, the crystal shape is obvious, the viewing requirement of people is met, and the viewing effect of the crystalline glaze ceramic is improved.
Description
Technical field
The present invention relates to a kind of crystalline glaze ceramic glaze.
Background technology
Crystalline glaze pottery has unique artistic charm because beautiful decorative pattern crystallization is separated out on surface, very popular with appreciation.And the crystalloid that the surface of existing crystalline glaze pottery is formed is more tiny, not obviously, what can not meet people views and admires demand.
Summary of the invention
The present invention, for overcoming the deficiencies in the prior art, provides a kind of crystalline glaze ceramic glaze, and it can form the crystallization of large sheet at ceramic surface, makes crystal form more obvious, improves sight.
crystalline glaze ceramic glaze of the present invention, it is formulated by following substances in percentage by weight:
Potassium felspar sand 4-25 %
Quartz 2-15%
Talcum 2-15%
Soil 3-20%
High boron powder 25-40%
Manganese oxide 8-22 %
Ferric oxide 6-20%.
As preferred version of the present invention, wherein
Potassium felspar sand 14 %
Quartz 7 %
Talcum 7 %
Soil 10 %
High boron powder 32 %
Manganese oxide 16 %
Ferric oxide 14 %.
Crystalline glaze ceramic glaze of the present invention, solve tiny, the unconspicuous shortcoming of crystalloid that existing crystalline glaze pottery is formed in its surface, it can form the crystallization of large sheet at ceramic surface, make crystal form more obvious, what meet people views and admires demand, improves the sight of crystalline glaze pottery.
embodiment:
embodiment one
The crystalline glaze ceramic glaze of the present embodiment is formulated by following substances in percentage by weight:
Potassium felspar sand 14 %
Quartz 7 %
Talcum 7 %
Soil 10 %
High boron powder 32 %
Manganese oxide 16 %
Ferric oxide 14 %.
During making, be mixed in proportion by above-mentioned substance, the 40%-50% that adds water in mixture stirs, and ball milling is after 24 hours, then ball milling 10 hours fast, after taking-up, filter out throw out this product.During use,
Ceramic body is directly soaked glaze, then burns till to kiln, burn till 10 hours, within first 2 hours, temperature is heated from 0 DEG C
Burn to 800 DEG C, then with 3.5 hours from 800 DEG C of burnings of heating to 1100 DEG C, then carry out the reductive firing of 2 hours, temperature is to 1250 DEG C, then the oxidation carrying out 2.5 hours is burnt till, and temperature, to 1330 DEG C, being burnt till and holding concurrently insulation again after 3 hours, opening kiln and be cooled to normal temperature gradually.
embodiment two
The ceramic glaze of the present embodiment is formulated by following substances in percentage by weight:
Potassium felspar sand 25 %
Quartz 13 %
Talcum 15 %
Soil 3 %
High boron powder 30 %
Manganese oxide 8 %
Ferric oxide 6 %.
Making method and using method are with embodiment one.
embodiment three
The ceramic glaze of the present embodiment is formulated by following substances in percentage by weight:
Potassium felspar sand 4 %
Quartz 2 %
Talcum 2 %
Soil 10 %
High boron powder 40 %
Manganese oxide 22 %.
Ferric oxide 20 %.
Making method and using method are with embodiment one.
embodiment four
The ceramic glaze of the present embodiment is formulated by following substances in percentage by weight:
Potassium felspar sand 10 %
Quartz 15%
Talcum 12 %
Soil 20 %
High boron powder 25%
Manganese oxide 10 %
Ferric oxide 8 %.
Making method and using method are with embodiment one.
Claims (2)
1. a crystalline glaze ceramic glaze, is characterized in that by following substances in percentage by weight formulated:
Potassium felspar sand 4-25 %
Quartz 2-15%
Talcum 2-15%
Soil 3-20%
High boron powder 25-40 %
Manganese oxide 8-22 %
Ferric oxide 6-20%.
2. a kind of crystalline glaze ceramic glaze as claimed in claim 1, is characterized in that by following substances in percentage by weight formulated:
Potassium felspar sand 14 %
Quartz 7 %
Talcum 7 %
Soil 10 %
High boron powder 32 %
Manganese oxide 16 %
Ferric oxide 14 %.