CN105002777A - Antistatic antibacterial release paper and preparation method therefor - Google Patents
Antistatic antibacterial release paper and preparation method therefor Download PDFInfo
- Publication number
- CN105002777A CN105002777A CN201510417676.5A CN201510417676A CN105002777A CN 105002777 A CN105002777 A CN 105002777A CN 201510417676 A CN201510417676 A CN 201510417676A CN 105002777 A CN105002777 A CN 105002777A
- Authority
- CN
- China
- Prior art keywords
- layer
- antistatic
- release liners
- preparation
- release
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a preparation method for antistatic antibacterial release paper. The method is characterized bu comprising the following steps: coating a surface on one side of raw release paper with a laminated layer by using a laminating machine; coating a surface on the other side with an adhesive layer; coating a surface of the adhesive layer with a film layer; after the film layer is coated with an antistatic layer, performing corona-pretreatment and super-calendering; coating a surface of the antistatic layer with a release agent to obtain a release layer; coating a surface of the release layer with an antibacterial agent to obtain an antibacterial layer; drying the antibacterial layer at 20-25 DEG C to obtain antistatic antibacterial release paper. The preparation method provided by the invention is simple and feasible. By using palladium calcium carbonate as a catalyst, higher production efficiency is achieved without toxic side effects. Compared to a noble metal catalyst, the palladium calcium carbonate is more advantageous. By adding a non-toxic organic antibacterial agent to the surface of the release paper, the release paper can have an antibacterial capability and is applicable to the fields of food, pharmacy and chemical engineering. The antistatic antibacterial release paper prepared by the invention has not only a high strength capability, a high stretch capability, a high antibacterial capability but also a high antistatic capability.
Description
Technical field
The present invention relates to the preparation method of release liners, be specifically related to a kind of antistatic antibiotic release liners and preparation method thereof.
Background technology
Release liners is also known as barrier paper, separate paper, silicone oil paper.Be that one prevents prepreg adhesion, the not contaminated separate paper of prepreg can be protected again.Current release liners lacks electrostatic function after adding mould release, and part release liners needs to possess antibacterial ability, and current release liners or degree of drawing high are not, or toughness is inadequate, or do not possess antibacterial ability, combination property meets the needs produced now not in a word.
Summary of the invention
Goal of the invention: for the deficiencies in the prior art, the object of this invention is to provide a kind of preparation method of antistatic antibiotic release liners.A kind of antistatic antibiotic release liners prepared by the present invention possess high strength, high stretch capability, 100% antibacterial ability and possess very strong antistatic effect.
Technical scheme: in order to solve the problem, technical scheme of the present invention is to provide a kind of preparation method of antistatic antibiotic release liners, comprise the following steps: by side surface film machine film one deck leaching membrane layer of release liners body paper, then at opposite side surface coating one deck adhesive layer, at adhesive layer side coating thin film layer, corona pre-treatment and supercalendering is carried out after thin-film surface is coated with one deck antistatic layer, then mould release is coated on electrostatic layer surface and obtains release layer, then antibiotic layer is obtained in the coated antibacterial agent of release layer surface, antibiotic layer is dried at 20 ~ 25 DEG C and obtains antistatic antibiotic release liners.
Wherein, the thickness of above-mentioned release liners is 50 ~ 80g/m
2, smoothness is greater than 78 seconds, and machine direction tensile strength is more than or equal to 60N/15mm, and cross direction tensile strength is more than or equal to 43N/15mm.
Wherein, above-mentioned antistatic layer is made up of acrylic acid epoxy resin, quartz sand, and the composition mass ratio of described acrylic acid epoxy resin and quartz sand is: 3 ~ 10:1.
Wherein, above-mentioned antiseptic is organic antibacterial agent, and described organic antibacterial agent is vanillic aldehyde or ethyl vanillin aldehyde compound.
Wherein, above-mentioned supercalendered step is: release liners corona pre-treatment crossed is after excess temperature is that 190-225 DEG C of heating is built bridge, temperature is 320-350 DEG C of heating and melting, then the pressure adding 8Mpa-15Mpa is extruded.
Wherein, above-mentioned mould release comprises food-grade silicone oil, the palladium calcium carbonate of 1 ~ 2 weight portion, the palm oil of 5 ~ 15 weight portions of 2 ~ 5 weight portions.
Wherein, the coating weight of above-mentioned mould release is 0.4 ~ 0.5g/m
2.
Wherein, the coating weight of above-mentioned antibiotic layer is 0.05 ~ 0.25g/m
2.
The antistatic antibiotic release liners that above-mentioned preparation method prepares.
Beneficial effect: preparation method's simple possible of the present invention, by adopting palladium calcium carbonate to make catalyst, production efficiency is higher, and does not have toxic and side effect, compares noble metal catalyst more favourable.By with the addition of nontoxic organic antibacterial agent on release liners surface, such release liners can also possess antibacterial ability, can be applicable to the fields such as food and medicine chemical industry.Antistatic antibiotic release liners prepared by the present invention not only possesses high strength, high stretch capability, high antibacterial ability and possesses very strong antistatic effect.
Detailed description of the invention
Below in conjunction with detailed description of the invention, set forth the present invention further.
Embodiment 1:
A kind of preparation method of antistatic antibiotic release liners, comprise the following steps: by side surface film machine film one deck leaching membrane layer of release liners body paper, then at opposite side surface coating one deck adhesive layer, at adhesive layer side coating thin film layer, corona pre-treatment and supercalendering is carried out after thin-film surface is coated with one deck antistatic layer, then mould release is coated on electrostatic layer surface and obtains release layer, then obtain antibiotic layer in the coated antibacterial agent of release layer surface, antibiotic layer is dried at 20 DEG C and obtains antistatic antibiotic release liners.The thickness of release liners is 50g/m
2, smoothness is greater than 78 seconds, and machine direction tensile strength is more than or equal to 60N/15mm, and cross direction tensile strength is more than or equal to 43N/15mm.Antistatic layer is made up of acrylic acid epoxy resin, quartz sand, and the composition mass ratio of described acrylic acid epoxy resin and quartz sand is: 3:1.Antiseptic is organic antibacterial agent, and described organic antibacterial agent is vanillic aldehyde.Supercalendered step is: release liners corona pre-treatment crossed is after excess temperature is that 190 DEG C of heating are built bridge, temperature are 320 DEG C of heating and meltings, then the pressure adding 8Mpa is extruded.Mould release comprises food-grade silicone oil, the palladium calcium carbonate of 1 weight portion, the palm oil of 5 weight portions of 2 weight portions.The coating weight of mould release is 0.4g/m
2.The coating weight of antibiotic layer is 0.05g/m
2.
Embodiment 2
A kind of preparation method of antistatic antibiotic release liners, comprise the following steps: by side surface film machine film one deck leaching membrane layer of release liners body paper, then at opposite side surface coating one deck adhesive layer, at adhesive layer side coating thin film layer, corona pre-treatment and supercalendering is carried out after thin-film surface is coated with one deck antistatic layer, then mould release is coated on electrostatic layer surface and obtains release layer, then obtain antibiotic layer in the coated antibacterial agent of release layer surface, antibiotic layer is dried at 25 DEG C and obtains antistatic antibiotic release liners.The thickness of release liners is 80g/m
2, smoothness is greater than 78 seconds, and machine direction tensile strength is more than or equal to 60N/15mm, and cross direction tensile strength is more than or equal to 43N/15mm.Antistatic layer is made up of acrylic acid epoxy resin, quartz sand, and the composition mass ratio of described acrylic acid epoxy resin and quartz sand is: 10:1.Antiseptic is organic antibacterial agent, and described organic antibacterial agent is ethyl vanillin aldehyde compound.Supercalendered step is: release liners corona pre-treatment crossed is after excess temperature is that 225 DEG C of heating are built bridge, temperature are 350 DEG C of heating and meltings, then the pressure adding 15Mpa is extruded.Mould release comprises food-grade silicone oil, the palladium calcium carbonate of 2 weight portions, the palm oil of 15 weight portions of 5 weight portions.The coating weight of mould release is 0.5g/m
2.The coating weight of antibiotic layer is 0.25g/m
2.
Embodiment 3
A kind of preparation method of antistatic antibiotic release liners, comprise the following steps: by side surface film machine film one deck leaching membrane layer of release liners body paper, then at opposite side surface coating one deck adhesive layer, at adhesive layer side coating thin film layer, corona pre-treatment and supercalendering is carried out after thin-film surface is coated with one deck antistatic layer, then mould release is coated on electrostatic layer surface and obtains release layer, then obtain antibiotic layer in the coated antibacterial agent of release layer surface, antibiotic layer is dried at 23 DEG C and obtains antistatic antibiotic release liners.The thickness of release liners is 65g/m
2, smoothness is greater than 78 seconds, and machine direction tensile strength is more than or equal to 60N/15mm, and cross direction tensile strength is more than or equal to 43N/15mm.Antistatic layer is made up of acrylic acid epoxy resin, quartz sand, and the composition mass ratio of described acrylic acid epoxy resin and quartz sand is: 8:1.Antiseptic is organic antibacterial agent, and described organic antibacterial agent is vanillic aldehyde.Supercalendered step is: release liners corona pre-treatment crossed is after excess temperature is that 200 DEG C of heating are built bridge, temperature are 330 DEG C of heating and meltings, then the pressure adding 12Mpa is extruded.Mould release comprises food-grade silicone oil, the palladium calcium carbonate of 1 weight portion, the palm oil of 10 weight portions of 3 weight portions.The coating weight of mould release is 0.45g/m
2.The coating weight of antibiotic layer is 0.15g/m
2.
The detected parameters of the antistatic antibiotic release liners that embodiment 1 ~ 3 prepares:
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (9)
1. the preparation method of an antistatic antibiotic release liners, it is characterized in that, comprise the following steps: by side surface film machine film one deck leaching membrane layer of release liners body paper, then at opposite side surface coating one deck adhesive layer, at adhesive layer side coating thin film layer, corona pre-treatment and supercalendering is carried out after thin-film surface is coated with one deck antistatic layer, then mould release is coated on electrostatic layer surface and obtains release layer, then obtain antibiotic layer in the coated antibacterial agent of release layer surface, antibiotic layer is dried at 20 ~ 25 DEG C and obtains antistatic antibiotic release liners.
2. the preparation method of a kind of antistatic antibiotic release liners according to claim 1, is characterized in that, the thickness of described release liners is 50 ~ 80g/m
2, smoothness is greater than 78 seconds, and machine direction tensile strength is more than or equal to 60N/15mm, and cross direction tensile strength is more than or equal to 43N/15mm.
3. the preparation method of a kind of antistatic antibiotic release liners according to claim 1, it is characterized in that, described antistatic layer is made up of acrylic acid epoxy resin, quartz sand, and the composition mass ratio of described acrylic acid epoxy resin and quartz sand is: 3 ~ 10:1.
4. the preparation method of a kind of antistatic antibiotic release liners according to claim 1, is characterized in that, described antiseptic is organic antibacterial agent, and described organic antibacterial agent is vanillic aldehyde or ethyl vanillin aldehyde compound.
5. the preparation method of a kind of antistatic antibiotic release liners according to claim 1, it is characterized in that, described supercalendered step is: release liners corona pre-treatment crossed is after excess temperature is that 190-225 DEG C of heating is built bridge, temperature is 320-350 DEG C of heating and melting, then the pressure adding 8Mpa-15Mpa is extruded.
6. the preparation method of a kind of antistatic antibiotic release liners according to claim 1, is characterized in that, described mould release comprises food-grade silicone oil, the palladium calcium carbonate of 1 ~ 2 weight portion, the palm oil of 5 ~ 15 weight portions of 2 ~ 5 weight portions.
7. the preparation method of a kind of antistatic antibiotic release liners according to claim 1, is characterized in that, the coating weight of described mould release is 0.4 ~ 0.5g/m
2.
8. the preparation method of a kind of antistatic antibiotic release liners according to claim 1, is characterized in that, the coating weight of described antibiotic layer is 0.05 ~ 0.25g/m
2.
9. the antistatic antibiotic release liners that the preparation method described in any one of claim 1 ~ 7 prepares.