CN104974647A - 一种高性能水性uv面漆及其制备方法 - Google Patents
一种高性能水性uv面漆及其制备方法 Download PDFInfo
- Publication number
- CN104974647A CN104974647A CN201410142838.4A CN201410142838A CN104974647A CN 104974647 A CN104974647 A CN 104974647A CN 201410142838 A CN201410142838 A CN 201410142838A CN 104974647 A CN104974647 A CN 104974647A
- Authority
- CN
- China
- Prior art keywords
- aqueous
- finishing coat
- polyurethane dispersion
- preparation
- performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及水性面漆技术领域,具体的说是一种高性能水性UV面漆及其制备方法,按质量比的配方脂肪族的聚氨酯丙烯酸共聚体乳液为5-35%,聚氨酯分散体为58-88%,高弹性聚氨酯分散体为1-15%,聚硅氧烷混合物为0.2-0.5%,聚硅氧烷混合物为0.1-0.3%,表面有机处理的沉淀法二氧化硅0-3%,该发明配方采用脂肪族的聚氨酯丙烯酸共聚体乳液、聚氨酯分散体和高弹性聚氨酯分散体三种水性树脂搭配,与现有同行业产品相比较漆膜具有透明度高、干燥快、易打磨的特点,极低的TVOC具有极佳的环境友好性,是国家目前大力倡导节能,环保产品的代表性产品。
Description
技术领域
本发明涉及水性面漆技术领域,具体的说是一种高性能水性UV面漆及其制备方法。
背景技术
水性UV面漆产品是理想的固化产品,具有优秀的平面喷涂效果。涂饰面美观、丝滑细腻、填充性能好、操作安全简单、无污染;对环境无不利影响该产品主要用于木地板方面,具有填充性好,透明度强,硬度高,性价比好,易砂光,环保性能优异等特点。现有的水性UV面漆,透明度低、干燥慢、不易打磨的特点,对特殊基材,如聚氨酯发泡素材、高油脂的木材、塑胶等,存在基材难附着的问题,漆膜的硬度不高,容易引起下陷,漆膜柔韧性不好,不能很好的顺应基材的伸缩,容易导致开裂及多次重涂后漆膜易开裂,还存在ABS、PC、PS等塑胶素材易被溶剂咬底的问题。
因此,为克服上述技术的不足而设计出一款漆膜具有透明度高、干燥快、易打磨,可以解决特殊基材难附着的问题,成膜物的交联密度高,从而显著提升漆膜的硬度及防下陷性能,漆膜耐热、耐水、耐化学品性能优异的一种高性能水性UV面漆及其制备方法,正是发明人所要解决的问题。
发明内容
针对现有技术的不足,本发明的目的是提供一种高性能水性UV面漆及其制备方法,其漆膜具有透明度高、干燥快、易打磨,可以解决特殊基材难附着的问题,成膜物的交联密度高,从而显著提升漆膜的硬度及防下陷性能,漆膜耐热、耐水、耐化学品性能优异,有非常好的实用价值。
本发明解决其技术问题所采用的技术方案是:一种高性能水性UV面漆,其特征在于按质量比的配方为:
第一部分组份:
第二部分组份:
α-羟基酮 0.4-0.8%
苯甲酰甲酸酯 0.1-0.4%
丙二醇甲醚醋酸酯 0.3-0.6%
第三部分组份:
上述一种高性能水性UV面漆的制备方法包含以下步骤:
步骤一:以上述第一部分六项组份加入后以转速800RPM搅拌混合10分钟;
步骤二:将第二部分三项组份先预混,然后再在转速1000-1200RPM搅拌下缓慢加入,分散20分钟;
步骤三:将第三部分五项组份在转速800-1000RPM搅拌下加入,分散20分钟。
本发明的有益效果是:
1、该发明配方采用脂肪族的聚氨酯丙烯酸共聚体乳液、聚氨酯分散体和高弹性聚氨酯分散体三种水性树脂搭配,与现有同行业产品相比较漆膜具有透明度高、干燥快、易打磨的特点。
2、对特殊基材,如聚氨酯发泡素材、高油脂的木材、塑胶等,有良好的附着力及广泛的适应性,解决了上述基材难附着的问题。
3、成膜物的交联密度高,从而显著提升漆膜的硬度及防下陷性能,漆膜耐热、耐水、耐化学品性能优异。
4、搭配适量的高弹性聚氨酯分散体,确保漆膜柔韧性好,能很好的顺应基材的伸缩,防止开裂及多次重涂后漆膜易开裂的问题。
5、由于是水性化产品,解决了ABS、PC、PS等塑胶素材易被溶剂咬底的问题。
6、极低的TVOC具有极佳的环境友好性,是国家目前大力倡导节能,环保产品的代表性产品。
具体实施方式
下面结合具体实施例,进一步阐述本发明,应理解,这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解,在阅读了本发明讲授的内容之后,本领域技术人员可以对本发明作各种改动或修改,这些等价形式同样落在申请所附权利要求书所限定的范围。
一种高性能水性UV面漆,具体的质量比的配方及制备方法为:
步骤一,以上述第一部分六项组份加入后以转速800RPM搅拌混合10分钟;
α-羟基酮 0.4-0.8%
苯甲酰甲酸酯 0.1-0.4%
丙二醇甲醚醋酸酯 0.3-0.6%
步骤二、将第二部分三项组份先预混,然后再在转速1000-1200RPM搅拌下缓慢加入,分散20分钟;
步骤三、将第三部分五项组份在转速800-1000RPM搅拌下加入,分散20分钟。
本发明用于木器制品、家具、地板和塑胶件制品行业,因其收缩率低,润湿性好,对特殊基材,如聚氨酯发泡素材、高油脂的木材、塑胶等,有良好的附着力及广泛的适应性,解决了上述基材难附着、费人力、生产周期长,气味重、污染严重、对客户和生产工人健康安全影响较大等问题,还解决了涂料易燃、易爆的问题;
本发明经检测技术性能参数为:
固含量40±2%
硬度:HB-H
附着力:1级
固化时间:<50秒
耗能量:200-500mj/平方厘米
粘度:40-50秒(25℃,涂4杯)。
该发明配方采用脂肪族的聚氨酯丙烯酸共聚体乳液、聚氨酯分散体和高弹性聚氨酯分散体三种水性树脂搭配,与现有同行业产品相比较漆膜具有透明度高、干燥快、易打磨的特点。对特殊基材,如聚氨酯发泡素材、高油脂的木材、塑胶等,有良好的附着力及广泛的适应性,解决了上述基材难附着的问题。成膜物的交联密度高,从而显著提升漆膜的硬度及防下陷性能,漆膜耐热、耐水、耐化学品性能优异。搭配适量的高弹性聚氨酯分散体,确保漆膜柔韧性好,能很好的顺应基材的伸缩,防止开裂及多次重涂后漆膜易开裂的问题。由于是水性化产品,解决了ABS、PC、PS等塑胶素材易被溶剂咬底的问题。极低的TVOC具有极佳的环境友好性,是国家目前大力倡导节能,环保产品的代表性产品。
Claims (2)
1.一种高性能水性UV面漆,其特征在于按质量比的配方为:
第一部分组份:
第二部分组份:
α-羟基酮 0.4-0.8%
苯甲酰甲酸酯 0.1-0.4%
丙二醇甲醚醋酸酯 0.3-0.6%
第三部分组份:
2.根据权利要求1所述的一种高性能水性UV面漆的制备方法,其特征在于方法包含以下步骤:
步骤一:以上述第一部分六项组份加入后以转速800RPM搅拌混合10分钟;
步骤二:将第二部分三项组份先预混,然后再在转速1000-1200RPM搅拌下缓慢加入,分散20分钟;
步骤三:将第三部分五项组份在转速800-1000RPM搅拌下加入,分散20分钟。