CN104945011A - 一种混合轻集料 - Google Patents

一种混合轻集料 Download PDF

Info

Publication number
CN104945011A
CN104945011A CN201510354184.6A CN201510354184A CN104945011A CN 104945011 A CN104945011 A CN 104945011A CN 201510354184 A CN201510354184 A CN 201510354184A CN 104945011 A CN104945011 A CN 104945011A
Authority
CN
China
Prior art keywords
weight
lightweight aggregate
weight part
mixed lightweight
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510354184.6A
Other languages
English (en)
Inventor
陆卫平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI SHDBM NEW MATERIALS CO Ltd
Original Assignee
SHANGHAI SHDBM NEW MATERIALS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI SHDBM NEW MATERIALS CO Ltd filed Critical SHANGHAI SHDBM NEW MATERIALS CO Ltd
Priority to CN201510354184.6A priority Critical patent/CN104945011A/zh
Publication of CN104945011A publication Critical patent/CN104945011A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种混合轻集料，其主要包括以下组分：水泥20-25重量份，粉煤灰18-23重量份，细石屑4-6重量份，玻化微珠0.6-0.8重量份，中泡沫颗粒0.6-0.8重量份，粗泡沫颗粒0.6-0.8重量份，滑石粉0.2-0.3重量份，植物纤维2-3重量份。本发明的混合轻集料具备三快(即快凝、快硬、快强)和二延伸(即早期含水性能的延伸和后期抗折性能的延伸)的优点，与现有的双快水泥相比，具有更多的优点，因此适用性更广；并且，本发明的混合轻集料的强度和初凝时间比市场上的单向混合料的强度和初凝时间均分别提高了30％；其中，本发明的混合轻集料的初凝时间在10-15分钟范围内，强度在10-30MP之间。

Description

一种混合轻集料
技术领域
本发明涉及一种建筑工程材料技术领域，特别涉及一种混合轻集料。
背景技术
双快(快凝快硬)水泥的主要特点是凝结硬化快、小时强度高，即所谓“小时水泥”。主要用于紧急抢修工程、地下工程、隧道工程、锚喷支护工程、截水堵漏以及公路面抢修等工程。但其性能优势仅包括快凝、快硬两个主要方面，在很多情况下仍不能满足实际情况的多种需要，因此需要开发其升级和替代产品。
发明内容
本发明的目的是提供一种混合轻集料，以解决现有技术中的双快水泥不能满足实际多种情况需要的缺陷。
本发明的技术方案如下：
一种混合轻集料，主要包括以下组分：
水泥20-25重量份，粉煤灰18-23重量份，细石屑4-6重量份，玻化微珠0.6-0.8重量份，细泡沫颗粒0.6-0.8重量份，粗泡沫颗粒0.6-0.8重量份，滑石粉0.2-0.3重量份，植物纤维2-3重量份。
优选地，所述玻化微珠的粒径为1-2mm。
优选地，所述细泡沫颗粒的粒径为2-4mm。
优选地，所述粗泡沫颗粒的粒径为4-6mm。
优选地，所述细泡沫颗粒和粗泡沫颗粒的材质为可发性聚苯乙烯，也可以为其它具有相同或类似效果的泡沫材料。
与现有技术相比，本发明的有益效果如下：
第一，本发明的混合轻集料具备三快(即快凝、快硬、快强)和二延伸(即早期含水性能的延伸和后期抗折性能的延伸)的优点，与现有的双快水泥相比，具有更多的优点，因此适用性更广；
第二，本发明的混合轻集料的强度和初凝时间比市场上的单向混合料的强度和初凝时间均分别提高了30％；其中，本发明的混合轻集料的初凝时间在10-15分钟范围内，强度在10-30MP之间。
当然，实施本发明的任一产品并不一定需要同时达到以上所述的所有优点。
具体实施方式
本发明提供一种混合轻集料，其主要包括以下组分：
水泥20-25重量份，粉煤灰18-23重量份，细石屑4-6重量份，玻化微珠0.6-0.8重量份，细泡沫颗粒0.6-0.8重量份，粗泡沫颗粒0.6-0.8重量份，滑石粉0.2-0.3重量份，植物纤维2-3重量份。
本发明的混合轻集料主要是利用工业废料再加上轻质料和传统胶凝水泥料混合而成的新型环保的混合轻集的新胶凝材料。本发明的混合轻集料在使用时，根据实际工况添加一定比例的水及增强剂等添加剂混合搅拌成糊状，压入定型模具内即可。
在本文中，由「一数值至另一数值」表示的范围，是一种避免在说明书中一一列举该范围中的所有数值的概要性表示方式。因此，某一特定数值范围的记载，涵盖该数值范围内的任意数值以及由该数值范围内的任意数值界定出的较小数值范围，如同在说明书中明文写出该任意数值和该较小数值范围一样。
下面结合具体实施例，进一步阐述本发明。应该理解，这些实施例仅用于说明本发明，而不用于限定本发明的保护范围。在实际应用中技术人员根据本发明做出的改进和调整，仍属于本发明的保护范围。
实施例1
本实施例提供一种混合轻集料，其主要包括以下组分：
水泥20-25重量份，粉煤灰18-23重量份，细石屑4-6重量份，玻化微珠0.6-0.8重量份，细泡沫颗粒0.6-0.8重量份，粗泡沫颗粒0.6-0.8重量份，滑石粉0.2-0.3重量份，植物纤维2-3重量份。
其中，上述混合轻集料每平方米用量如下：水泥20-25公斤，粉煤灰18-23公斤，细石屑4-6公斤，玻化微珠0.6-0.8公斤，细泡沫颗粒0.6-0.8公斤，粗泡沫颗粒0.6-0.8公斤，滑石粉0.2-0.3公斤，植物纤维2-3公斤。
其中，玻化微珠的粒径优选为1-2mm，细泡沫颗粒的粒径优选为2-4mm，粗泡沫颗粒的粒径优选为4-6mm。细泡沫颗粒和粗泡沫颗粒的材质为可发性聚苯乙烯。
使用时，在本实施例的混合轻集料添加一定比例的水及增强剂等添加剂混合搅拌成糊状，压入定型模具内即可。
本发明的混合轻集料的初凝时间在10-15分钟范围内，强度在10-30MP之间，比市场上的单向混合料的强度和初凝时间均分别提高了30％。
本发明的混合轻集料具备三快，即快凝、快硬、快强(强指强度)和二延伸(即早期含水性能的延伸和后期抗折性能的延伸)的优点，相比现有的双快水泥具有更多的优点，因此适用性更广。
在本发明及上述实施例的教导下，本领域技术人员很容易预见到，本发明所列举或例举的各原料或其等同替换物、各加工方法或其等同替换物都能实现本发明，以及各原料和加工方法的参数上下限取值、区间值都能实现本发明，在此不一一列举实施例。

Claims (5)

1.一种混合轻集料，其特征在于，主要包括以下组分：
水泥20-25重量份，粉煤灰18-23重量份，细石屑4-6重量份，玻化微珠0.6-0.8重量份，细泡沫颗粒0.6-0.8重量份，粗泡沫颗粒0.6-0.8重量份，滑石粉0.2-0.3重量份，植物纤维2-3重量份。
2.如权利要求1所述的混合轻集料，其特征在于，所述玻化微珠的粒径为1-2mm。
3.如权利要求1所述的混合轻集料，其特征在于，所述细泡沫颗粒的粒径为2-4mm。
4.如权利要求1所述的混合轻集料，其特征在于，所述粗泡沫颗粒的粒径为4-6mm。
5.如权利要求1或3或4所述的混合轻集料，其特征在于，所述细泡沫颗粒和粗泡沫颗粒的材质为可发性聚苯乙烯。
CN201510354184.6A 2015-06-23 2015-06-23 一种混合轻集料 Pending CN104945011A (zh)