CN104944971A - 镁橄榄石耐火砖 - Google Patents
镁橄榄石耐火砖 Download PDFInfo
- Publication number
- CN104944971A CN104944971A CN201510273444.7A CN201510273444A CN104944971A CN 104944971 A CN104944971 A CN 104944971A CN 201510273444 A CN201510273444 A CN 201510273444A CN 104944971 A CN104944971 A CN 104944971A
- Authority
- CN
- China
- Prior art keywords
- parts
- refractory brick
- forsterite refractory
- forsterite
- high temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种镁橄榄石耐火砖，涉及耐火材料制造技术领域，由下列重量份的原料制成：橄榄石砂70份～80份、碳酸镁15份～25份、氧化镁15份～20份、纸浆10份～15份；通过配料、混炼、制坯、干燥、烧成镁橄榄石耐火砖。与现有技术相比，本发明镁橄榄石耐火砖荷重软化温度高，在高温下不会产生收缩，热稳定性能好，用作锻造加热炉和水泥窑的内衬材料，高温下不会产生收缩而出现裂纹损坏，延长锻造加热炉和水泥窑的内衬使用寿命。
Description
技术领域
本发明涉及耐火材料制造技术领域，尤其是一种用于锻造加热炉和水泥窑的内衬的镁橄榄石耐火砖。
背景技术
耐火砖简称火砖，用耐火黏土或其他耐火原料烧制成的耐火材料。目前常用的耐火砖多是用软质粘土和硬质粘土熟料，按一定的粒度和配比要求进行配料，经成型、干燥后，在1300℃～1400℃的高温下烧成。由于该耐火砖的荷重软化温度低，热稳定性能差，并且在高温下产生收缩，导热率高；该耐火砖用作锻造加热炉和水泥窑的内衬材料，容易在高温下产生收缩而出现裂纹损坏，造成内衬的使用寿命短。
发明内容
本发明所要解决的技术问题是提供一种镁橄榄石耐火砖，以解决现有耐火砖热稳定性能差，用作锻造加热炉和水泥窑的内衬材料，容易在高温下产生收缩而出现裂纹损坏，使用寿命短的问题。
为了解决上述问题，本发明采用的技术方案是：这种镁橄榄石耐火砖，由下列重量份的原料制成：橄榄石砂70份～80份、碳酸镁15份～25份、氧化镁15份～20份、纸浆10份～15份。
上述镁橄榄石耐火砖技术方案中，更具体的技术方案还可以是：所述氧化镁为轻烧镁砂。
所述橄榄石，主要成分是铁或镁的硅酸盐，同时含有锰、镍、钴等元素，晶体呈现粒状，是一种岛状结构硅酸盐矿物，可作为耐火材料。
所述碳酸镁，为无定形粉末，无毒、无味气中稳定，可作绝热、耐高温的防火保温材料，以及食品、药品、化妆品、橡胶、墨水等的添加剂。
所述氧化镁，为白色或淡黄色粉末，无臭、无味、无毒，具有碱性氧化物的通性，属于胶凝材料，而且有高度耐火绝缘性能，经1000℃以上高温灼烧可转变为晶体。
所述纸浆，是以植物纤维为原料，经不同加工方法制得的纤维状物质，纸浆中构成纤维的主要成分为纤维素，另外还有不同程度的半纤维素、木素、树脂、色素、果胶和灰分等物质。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：
本发明采用橄榄石砂和碳酸镁为主要原料，氧化镁和纸浆作为结合剂，制成的镁橄榄石耐火砖荷重软化温度高，并且在高温下不会产生收缩，导热率低，热稳定性能好，用作锻造加热炉和水泥窑的内衬材料，高温下不会产生收缩而出现裂纹损坏，延长锻造加热炉和水泥窑的内衬使用寿命。
具体实施方式
下面结合具体实施例对本发明作进一步详述：
实施例1
一种镁橄榄石耐火砖，由下列重量份的原料制成：橄榄石砂700公斤、碳酸镁150公斤、氧化镁150公斤、纸浆100公斤；本实施例的氧化镁为轻烧镁砂。
按上述各原料的重量份称取原料，将橄榄石砂和碳酸镁放入湿碾机中进行碾压，然后加入橄榄石砂和碳酸镁总重量的1.5%的水，再进行碾压，加入轻烧镁砂和纸浆进行混炼，采用压砖机压制成砖坯，砖坯干燥后放入烧成窑在高温下焙烧，冷却至室温即得本镁橄榄石耐火砖。
实施例2
一种镁橄榄石耐火砖，由下列重量份的原料制成：橄榄石砂800公斤、碳酸镁250公斤、氧化镁200公斤、纸浆150公斤；本实施例的氧化镁为轻烧镁砂。
按上述各原料的重量份称取原料，将橄榄石砂和碳酸镁放入湿碾机中进行碾压，然后加入橄榄石砂和碳酸镁总重量的2%的水，再进行碾压，加入轻烧镁砂和纸浆进行混炼，采用压砖机压制成砖坯，砖坯干燥后放入烧成窑在高温下焙烧，冷却至室温即得本镁橄榄石耐火砖。
Claims (2)
1.一种镁橄榄石耐火砖，其特征在于由下列重量份的原料制成：橄榄石砂70份～80份、碳酸镁15份～25份、氧化镁15份～20份、纸浆10份～15份。
2.根据权利要求1所述的镁橄榄石耐火砖，其特征在于：所述氧化镁为轻烧镁砂。