CN104944901A - Transport box for slightly corrosive chemical raw materials - Google Patents
Transport box for slightly corrosive chemical raw materials Download PDFInfo
- Publication number
- CN104944901A CN104944901A CN201510293454.7A CN201510293454A CN104944901A CN 104944901 A CN104944901 A CN 104944901A CN 201510293454 A CN201510293454 A CN 201510293454A CN 104944901 A CN104944901 A CN 104944901A
- Authority
- CN
- China
- Prior art keywords
- minutes
- transport box
- takes out
- leaves standstill
- standstill
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Relating to the technical field of chemical raw material processing equipment casting, the invention provides a transport box for slightly corrosive chemical raw materials. The transport box is characterized by comprising the following components by weight percentage: 66-93 of Fe3O4, 22-35 of molybdenum, 15.5-24.5 of a sodium carbonate solution, 4.5-9.5 of zinc stearate, 25-39 of quartz sand, 5.5-12.5 of aminopropyl triethoxysilane, and 2.5-6.5 of potassium sodium tartrate. The transport box provided by the invention has the advantages of reasonable method, clear proportion, and good corrosion resistance.
Description
Technical field:
The present invention relates to chemical feedstocks processing units casting technology field, be specifically related to a kind of carrying case with the chemical feedstocks of slight erosion.
Background technology:
Definition: chemical feedstocks, refers to the raw material for the production of all kinds of preparation, is the effective ingredient in preparation, by chemosynthesis, plant extract or various prepared by biotechnology be used as powder, crystallization, medicinal extract etc.Raw material only has processing, just can become available.
No matter and be processing before or processing after material, many is all have corrodibility, oxidisability etc. chemical attribute, the equipment of such transporting material needs many chemoresistances, and due to many transporting materials be all plastics or metal, often haulage time can cause equipment damage, damage due to the chemical attribute of chemical feedstocks for a long time, and maintenance that cannot be good, so just easily causes unnecessary loss and trouble.
Summary of the invention:
Technical problem to be solved by this invention is that overcoming existing technological deficiency provides a kind of carrying case with the chemical feedstocks of slight erosion that a kind of method is reasonable, proportioning is clear, corrosion resistance nature is good.
Technical problem to be solved by this invention adopts following technical scheme to realize:
There is a carrying case for the chemical feedstocks of slight erosion, it is characterized in that: each component proportion is as follows in weight fraction,
A kind of preparation method with the carrying case of the chemical feedstocks of slight erosion comprises,
I makes mould and running channel as required, and by Fe
3o
4liquid is fused into respectively with molybdenum method for making conveniently;
II by the liquid concussion mixing in I 20 minutes, and added Zinic stearas when being mixed into the 8th minute, stirred while adding;
Material is directly put into baking box by heat by III upon mixing, and heat 45 minutes, temperature is 333-521 DEG C, adds quartz sand when being heated to 31 minutes;
Material after above-mentioned heating takes out by IV, pours into and is placed with in the running channel of model, leaves standstill 5 minutes, in the process left standstill, add aminopropyl triethoxysilane;
V by leave standstill after material put into the condensation carried out under the low temperature of-7 DEG C 33 minutes in condensation room, in 17 minutes, put into Seignette salt;
Condensed material takes out by VI, and leaves standstill 2 minutes, then puts into sodium carbonate solution and soaks 22 minutes;
Material after immersion takes out by VII, leaves standstill 3 minutes, then puts into polissoir polishing.
Beneficial effect of the present invention is: by Physical Processing and the chemical reaction of different chemical productss, and make product more better than the corrosion resistance nature of the product of common material, and product is more firm, the life-span is longer.The inventive method is reasonable, proportioning is clear, corrosion resistance nature is good.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.
There is a carrying case for the chemical feedstocks of slight erosion, it is characterized in that: each component proportion is as follows in weight fraction,
A kind of preparation method with the carrying case of the chemical feedstocks of slight erosion comprises,
I makes mould and running channel as required, and by Fe
3o
4liquid is fused into respectively with molybdenum method for making conveniently;
II by the liquid concussion mixing in I 20 minutes, and added Zinic stearas when being mixed into the 8th minute, stirred while adding;
Material is directly put into baking box by heat by III upon mixing, and heat 45 minutes, temperature is 333-521 DEG C, adds quartz sand when being heated to 31 minutes;
Material after above-mentioned heating takes out by IV, pours into and is placed with in the running channel of model, leaves standstill 5 minutes, in the process left standstill, add aminopropyl triethoxysilane;
V by leave standstill after material put into the condensation carried out under the low temperature of-7 DEG C 33 minutes in condensation room, in 17 minutes, put into Seignette salt;
Condensed material takes out by VI, and leaves standstill 2 minutes, then puts into sodium carbonate solution and soaks 22 minutes;
Material after immersion takes out by VII, leaves standstill 3 minutes, then puts into polissoir polishing.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (1)
1. there is a carrying case for the chemical feedstocks of slight erosion, it is characterized in that: each component proportion is as follows in weight fraction,
A kind of preparation method with the carrying case of the chemical feedstocks of slight erosion comprises,
I makes mould and running channel as required, and by Fe
3o
4liquid is fused into respectively with molybdenum method for making conveniently;
II by the liquid concussion mixing in I 20 minutes, and added Zinic stearas when being mixed into the 8th minute, stirred while adding;
Material is directly put into baking box by heat by III upon mixing, and heat 45 minutes, temperature is 333-521 DEG C, adds quartz sand when being heated to 31 minutes;
Material after above-mentioned heating takes out by IV, pours into and is placed with in the running channel of model, leaves standstill 5 minutes, in the process left standstill, add aminopropyl triethoxysilane;
V by leave standstill after material put into the condensation carried out under the low temperature of-7 DEG C 33 minutes in condensation room, in 17 minutes, put into Seignette salt;
Condensed material takes out by VI, and leaves standstill 2 minutes, then puts into sodium carbonate solution and soaks 22 minutes;
Material after immersion takes out by VII, leaves standstill 3 minutes, then puts into polissoir polishing.