CN104928665B - 用于裸钢锈层稳定的含铬处理液 - Google Patents

用于裸钢锈层稳定的含铬处理液 Download PDF

Info

Publication number
CN104928665B
CN104928665B CN201510250594.6A CN201510250594A CN104928665B CN 104928665 B CN104928665 B CN 104928665B CN 201510250594 A CN201510250594 A CN 201510250594A CN 104928665 B CN104928665 B CN 104928665B
Authority
CN
China
Prior art keywords
treatment fluid
rusty scale
naked
steel
stable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510250594.6A
Other languages
English (en)
Other versions
CN104928665A (zh
Inventor
黄先球
程鹏
郎丰军
庞涛
马颖
何锐
刘建容
王辉
李安平
周桂峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Iron and Steel Co Ltd
Original Assignee
Wuhan Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Iron and Steel Co Ltd filed Critical Wuhan Iron and Steel Co Ltd
Priority to CN201510250594.6A priority Critical patent/CN104928665B/zh
Publication of CN104928665A publication Critical patent/CN104928665A/zh
Application granted granted Critical
Publication of CN104928665B publication Critical patent/CN104928665B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明的目的在于提供一种用于裸钢锈层稳定的含铬处理液，该含铬处理液中各组分的重量百分比为：重铬酸钠为0.5～5％、NaHSO3为0.1～3％、FeSO4为0.1～2％、FeCl3为0.1～2％、醋酸为0.1～1％、三乙醇胺为0.1～0.5％、其余为水。该含铬处理液具有优良的防锈液流挂性能，喷淋在除掉氧化铁皮的耐候钢裸样表面后，促进稳定锈层的形成，锈层具有优良的防腐蚀性能，适合裸钢的涂覆。

Description

用于裸钢锈层稳定的含铬处理液
技术领域
本发明属于金属防护技术领域，具体是指一种用于裸钢锈层稳定的含铬处理液。
背景技术
金属腐蚀是金属在环境腐蚀介质作用下的一种失效过程，是一种完全自发进行的不可避免自然现象，是冶金生产的逆过程。大气腐蚀是造成产品、设备、装置、结构件等早期失效与破坏的重要原因。每年因大气腐蚀造成的经济损失极为惊人。在大气自然环境下，裸钢形成稳定保护锈层是一个逐步过程，需要相当长的时间，至少3年以上，有的裸钢表面形成致密稳定锈层的时间超过10年以上。在形成稳定锈层的过程中，常常出现早期锈液流挂与飞散污染周围环境的现象。而锈层稳定表面处理就是对裸钢表面进行化学处理，直接生成稳定致密的锈层，形成自我保护。涂覆锈层稳定表面处理剂后，既可避免裸钢使用初期黄色锈液流挂的现象，防止污染，又能在其表面迅速形成稳定的保护性锈层，使裸钢的腐蚀速度趋于稳定。
发明内容
本发明的目的在于提供一种用于裸钢锈层稳定的含铬处理液，能有效解决裸钢锈层稳定化及锈液流挂问题。
为实现上述目的，本发明所设计的用于裸钢锈层稳定的含铬处理液，其特特殊之处在于，该含铬处理液中各组分的重量百分比为：重铬酸钠为0.5～5％、NaHSO3为0.1～3％、FeSO4为0.1～2％、FeCl3为0.1～2％、醋酸为0.1～1％、三乙醇胺为0.1～0.5％、其余为水。
进一步优选地，该含铬处理液中各组分的重量百分比为：重铬酸钠为2.1～2.9％、NaHSO3为1.1～2.2％、FeSO4为0.8～1.4％、FeCl3为0.7～1.5％、醋酸为0.3～0.8％、三乙醇胺为0.2～0.3％、其余为水。
再进一步地，该含铬处理液中各组分的重量百分比为：重铬酸钠为2.6％、NaHSO3为1.4％、FeSO4为1.0％、FeCl3为0.9％、醋酸为0.5％、三乙醇胺为0.3％、水93.3％。
本发明的用于裸钢锈层稳定的含铬处理液作用机理为：
含铬处理液中，重铬酸钠的加入促进锈层中α-FeOOH的生成，Cr可部分置换α-FeOOH生成稳定的α-(Fe1-xCrx)OOH，锈层完整、致密，附着性强，提高了锈层的防护性能，阻止腐蚀介质进一步腐蚀钢板内部。NaHSO3、FeSO4、FeCl3作为腐蚀性化学物质。Cl-是浸蚀性离子，加速钢的腐蚀。Fe3+是高价离子，能与钢基发生快速氧化还原反应，生成Fe2+离子。NaHSO3与FeSO4可使钢基发生均匀腐蚀，得到均匀锈层。硫酸根离子可促进α-FeOOH的生成。醋酸涂覆时可使钢基发生腐蚀程度较轻的均匀腐蚀，有利得到均匀锈层，还可除掉钢基表面的浮锈。三乙醇胺作为添加剂，能在金属表面形成非常薄的覆盖层，隔绝了金属与O2接触，有效地防止金属发生大气腐蚀。
利用本发明的用于裸钢锈层稳定的含铬处理液不含亚硝酸盐、无强烈刺激性气味；具有优良的防锈液流挂性能，喷淋在除掉氧化铁皮的耐候钢裸样表面后，促进稳定锈层的形成，锈层具有优良的防腐蚀性能，适合裸钢的涂覆。
具体实施方式
下面结合具体实施实例对本发明的用于裸钢锈层稳定的含铬处理液作进一步的详细说明。
实施例1
一种用于裸钢锈层稳定的含铬处理液，其各组分按重量百分比为，重铬酸钠占0.5％，NaHSO3占3％，FeSO4占1％，FeCl3占2％，醋酸占0.1％，三乙醇胺占0.5％，水占92.9％。
实施例2
一种用于裸钢锈层稳定的含铬处理液，其各组分按重量百分比为，重铬酸钠占5％，NaHSO3占0.1％，FeSO4占0.1％，FeCl3占0.1％，醋酸占1％，三乙醇胺占0.1％，水占93.6％。
实施例3
一种用于裸钢锈层稳定的含铬处理液，其各组分按重量百分比为，重铬酸钠占3％，NaHSO3占0.5％，FeSO4占2％，FeCl3占0.5％，醋酸占0.8％，三乙醇胺占0.4％，水占92.8％。
实施例4
一种用于裸钢锈层稳定的含铬处理液，其各组分按重量百分比为，重铬酸钠占4％，NaHSO3占1％，FeSO4占0.5％，FeCl3占1％，醋酸占0.5％，三乙醇胺占0.2％，水占92.8％。
实施例5
一种用于裸钢锈层稳定的含铬处理液，其各组分按重量百分比为，重铬酸钠占1.5％，NaHSO3占2％，FeSO4占1.5％，FeCl3占1.5％，醋酸占0.3％，三乙醇胺占0.3％，水占92.9％。
实施例6
一种用于裸钢锈层稳定的含铬处理液，其各组分按重量百分比为，重铬酸钠为2.6％、NaHSO3为1.4％、FeSO4为1.0％、FeCl3为0.9％、醋酸为0.5％、三乙醇胺为0.3％、水93.3％。
使用时，将原料按各实施例所述比例均匀混合配制成含铬处理液。将含铬处理液喷淋在耐候钢裸样表面上，自然干燥后，重复喷淋。
对比试验：采用同一批除掉氧化铁皮的耐候钢裸样，在蒸馏水环境下加速10天(每隔3小时喷淋一次蒸馏水)进行测试实验。其中对比例钢样未喷淋含铬处理液。涂覆本实施例含铬处理液的耐候钢裸样在加速腐蚀期间，腐蚀速率是未经表面处理的耐候候钢裸样的25～35％，防腐效果明显。同时，采用未经表面处理的耐候钢裸样表面锈层颜色不均匀且锈液流挂，腐蚀速率随时间增加而增大；涂覆本发明含铬处理液的耐候钢裸样表面锈层颜色均匀，锈液不流挂，腐蚀速率变化不大。

Claims (2)

1.一种用于裸钢锈层稳定的含铬处理液，其特征在于：该含铬处理液中各组分的重量百分比为：重铬酸钠为2.1～2.9％、NaHSO3为1.1～2.2％、FeSO4为0.8～1.4％、FeCl3为0.7～1.5％、醋酸为0.3～0.8％、三乙醇胺为0.2～0.3％、其余为水。
2.根据权利要求1所述的用于裸钢锈层稳定的含铬处理液，其特征在于：该含铬处理液中各组分的重量百分比为：重铬酸钠为2.6％、NaHSO3为1.4％、FeSO4为1.0％、FeCl3为0.9％、醋酸为0.5％、三乙醇胺为0.3％、水93.3％。
CN201510250594.6A 2015-05-15 2015-05-15 用于裸钢锈层稳定的含铬处理液 Expired - Fee Related CN104928665B (zh)