CN104927216B - 一种橡塑共混高阻燃绝热保温材料 - Google Patents
一种橡塑共混高阻燃绝热保温材料 Download PDFInfo
- Publication number
- CN104927216B CN104927216B CN201510064677.6A CN201510064677A CN104927216B CN 104927216 B CN104927216 B CN 104927216B CN 201510064677 A CN201510064677 A CN 201510064677A CN 104927216 B CN104927216 B CN 104927216B
- Authority
- CN
- China
- Prior art keywords
- foaming
- agent
- parts
- rubber
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
PVC | 30 | 30 | 30 | 30 | 30 |
CM | 70 | 70 | 70 | 70 | 70 |
Mg(OH)2 | 0 | 40 | 30 | 20 | 20 |
Al(OH)3 | 100 | 100 | 110 | 100 | 120 |
DOP | 10 | 20 | 20 | 20 | 20 |
CPO | 25 | 35 | 35 | 35 | 35 |
硫化剂 | 1.6 | 1.6 | 1.6 | 1.6 | 1.6 |
发泡剂 | 24 | 24 | 24 | 24 | 24 |
活性剂 | 2 | 2 | 2 | 2 | 2 |
防老剂 | 2 | 2 | 2 | 2 | 2 |
硼酸锌 | 0 | 0 | 0 | 40 | 20 |
Sb2O3 | 0 | 0 | 3 | 0 | 4 |
DBDPE | 0 | 0 | 9 | 0 | 12 |
氧指数 | 32 | 34 | 43 | 38 | 48 |
实施例6 | 实施例7 | 实施例8 | 实施例9 | 实施例10 | |
PVC | 30 | 30 | 30 | 30 | 30 |
EVM | 70 | 70 | 70 | 70 | 70 |
Mg(OH)2 | 140 | 160 | 140 | 120 | 140 |
Al(OH)3 | 20 | 0 | 0 | 20 | 20 |
DOP | 20 | 20 | 20 | 20 | 20 |
CPO | 35 | 35 | 35 | 35 | 40 |
硫化剂 | 2 | 2 | 2 | 2 | 2 |
发泡剂 | 24 | 24 | 24 | 24 | 24 |
活性剂 | 3 | 3 | 3 | 3 | 3 |
防老剂 | 2 | 2 | 2 | 2 | 2 |
硼酸锌 | 0 | 0 | 30 | 30 | 20 |
Sb2O3 | 0 | 0 | 3 | 0 | 4 |
DBDPE | 0 | 0 | 9 | 0 | 12 |
氧指数 | 46 | 52 | 56 | 48 | 62 |
Claims (1)