CN104894879A - Preparation method of silk canvas - Google Patents
Preparation method of silk canvas Download PDFInfo
- Publication number
- CN104894879A CN104894879A CN201510265219.9A CN201510265219A CN104894879A CN 104894879 A CN104894879 A CN 104894879A CN 201510265219 A CN201510265219 A CN 201510265219A CN 104894879 A CN104894879 A CN 104894879A
- Authority
- CN
- China
- Prior art keywords
- silk
- preparation
- painting canvas
- weight portion
- weight portions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparation method of a silk canvas. The method is characterized by comprising the following steps: S01, coating the lower surface of silk with a drying layer, wherein the drying layer comprises a main material and auxiliary materials, the main material comprises 80-130 parts by weight of cellulose and the auxiliary materials comprises a binder, a wetting agent, a surfactant, an antioxidant, a lubricant and a preservative; uniformly mixing the main material and the auxiliary materials to obtain a mixture, and coating the lower surface of the silk with the mixture,; S02, after the drying layer is dry, adhering a chemical dye adsorbing layer to the lower surface of the drying layer; and S03, adhering a lining layer for supporting to the lower surface of the chemical dye adsorbing layer. According to the preparation method of the silk canvas, prepared by adopting the method disclosed by the invention, the silk canvas is high in grade, good in glossiness, easy to store, capable of adsorbing harmful gas in chemical dye and short in preparation cycle.
Description
Technical field
The present invention relates to a kind of preparation method of silk painting canvas, belong to material for calligraphy and painting technical field.
Background technology
Current material for calligraphy and painting great majority adopt rice paper, and rice paper exists cracky, and easy yellowing is gone bad, and is difficult to the problems such as preservation.Also some painting canvas have been there are at present, but exist matt, moisten black effect undesirable, the problem such as of low grade, therefore the invention provides a kind of preparation method of silk painting canvas, the silk painting canvas that a kind of class is high, glossiness good to prepare, the easy pernicious gas preserved in collection, adsorbable chemical dyestuff, manufacturing cycle are short.
Summary of the invention
Technical problem to be solved by this invention is, provides that a kind of class is high, glossiness good, easily preserves pernicious gas in collection, adsorbable chemical dyestuff and the preparation method of the short silk painting canvas of manufacturing cycle.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A preparation method for silk painting canvas, is characterized in that: comprise the following steps:
S01, at the lower surface coating drying layer of silk; Described drying layer comprises major ingredient and auxiliary material; Described major ingredient comprises the microcrystalline cellulose of 80 ~ 130 weight portions; Described auxiliary material comprises adhesive, wetting agent, surfactant, antioxidant, lubricant and preservative agent; The lower surface of described silk is coated on after described major ingredient and auxiliary material being mixed;
S02, after described drying layer drying, adheres to chemical dyestuff adsorption layer at the lower surface of described drying layer;
S03, adheres to the lining as supporting at the lower surface of described chemical dyestuff adsorption layer.
Described silk is made up of mulberry silk or tussah silk.
Described adhesive comprises the dextrin of 10 ~ 20 weight portions or the polyvinylpyrrolidone of 5 ~ 10 weight portions.
Described lubricant comprises the dolomol of 3 ~ 5 weight portions.
Described antioxidant is natural inhibitor.
Described natural inhibitor comprises the Tea Polyphenols of 3 ~ 7 weight portions and/or the OPC of 3 ~ 7 weight portions.
Described preservative agent comprises one or more in the calcium propionate of the benzoic acid of 0.01 ~ 0.03 weight portion, the Sodium Benzoate of 0.02 ~ 0.03 weight portion, the sorbic acid of 0.005 ~ 0.01 weight portion, the potassium sorbate of 0.01 ~ 0.015 weight portion and 0.01 ~ 0.03 weight portion.
Described surfactant comprises the dodecyl sodium sulfate of 0.3 ~ 0.5 weight portion.
Described wetting agent is 80% ethanol.
Described lining is made up of paper mulberry bark; Described chemical dyestuff adsorption layer is active carbon filter screen.
The preparation method of a kind of silk painting canvas provided by the invention, the setting of silk fabrics, good, the easy preservation of glossiness is collected, class is high; The pernicious gas arranged in adsorbable chemical dyestuff of chemical dyestuff adsorption layer; Short and the moisture in Absorbable rod dyestuff of drying layer manufacturing cycle, makes painting and calligraphy pieces rapid draing; The setting that lining is made up of paper mulberry bark, can make full use of paper mulberry bark resource, turn waste into wealth, and more makes cost of the present invention reduce, raw material sources natural health; The setting of the microcrystalline cellulose of 80 ~ 130 weight portions, have compared with low polymerization degree and larger specific area characteristic, make drying layer thinner, the thickness of silk painting canvas is moderate; The setting of natural inhibitor, makes present component natural health, and makes silk also possess certain antioxidant, substantially prolongs storage life and the glossiness of silk painting and calligraphy pieces; Wetting agent is the setting of 80% ethanol, major ingredient and auxiliary material are uniformly dispersed and dry after in flakes, the ethanol of 80% is volatile and major ingredient auxiliary material flakiness is good, substantially reduces the manufacturing cycle of silk painting canvas; The setting of the dolomol of 3 ~ 5 weight portions, makes drying layer thinner and moisture in Absorbable rod dyestuff equally.The preparation method of a kind of silk painting canvas provided by the invention, silk painting canvas class is high, glossiness good, easily preserve collection, pernicious gas in adsorbable chemical dyestuff and manufacturing cycle is short.
Detailed description of the invention
Below the present invention is further described.
embodiment 1:
A preparation method for silk painting canvas, is characterized in that: comprise the following steps:
S01, at the lower surface coating drying layer of silk; Described drying layer comprises major ingredient and auxiliary material; Described major ingredient comprises the microcrystalline cellulose of 80 weight portions; Described auxiliary material comprises adhesive, wetting agent, surfactant, antioxidant, lubricant and preservative agent; The lower surface of described silk is coated on after described major ingredient and auxiliary material being mixed;
S02, after described drying layer drying, adheres to chemical dyestuff adsorption layer at the lower surface of described drying layer;
S03, adheres to the lining as supporting at the lower surface of described chemical dyestuff adsorption layer.
Described silk is made up of mulberry silk or tussah silk.
Described adhesive comprises the dextrin of 10 weight portions or the polyvinylpyrrolidone of 5 weight portions.
Described lubricant comprises the dolomol of 3 weight portions.
Described antioxidant is natural inhibitor.
Described natural inhibitor comprises the Tea Polyphenols of 3 weight portions and/or the OPC of 3 weight portions.
Described preservative agent comprises one or more in the calcium propionate of the benzoic acid of 0.01 weight portion, the Sodium Benzoate of 0.02 weight portion, the sorbic acid of 0.005 weight portion, the potassium sorbate of 0.01 weight portion and 0.01 weight portion.
Described surfactant comprises the dodecyl sodium sulfate of 0.3 weight portion.
Described wetting agent is 80% ethanol.
Described lining is made up of paper mulberry bark; Described chemical dyestuff adsorption layer is active carbon filter screen.
embodiment 2:
A preparation method for silk painting canvas, is characterized in that: comprise the following steps:
S01, at the lower surface coating drying layer of silk; Described drying layer comprises major ingredient and auxiliary material; Described major ingredient comprises the microcrystalline cellulose of 130 weight portions; Described auxiliary material comprises adhesive, wetting agent, surfactant, antioxidant, lubricant and preservative agent; The lower surface of described silk is coated on after described major ingredient and auxiliary material being mixed;
S02, after described drying layer drying, adheres to chemical dyestuff adsorption layer at the lower surface of described drying layer;
S03, adheres to the lining as supporting at the lower surface of described chemical dyestuff adsorption layer.
Described silk is made up of mulberry silk or tussah silk.
Described adhesive comprises the dextrin of 20 weight portions or the polyvinylpyrrolidone of 10 weight portions.
Described lubricant comprises the dolomol of 5 weight portions.
Described antioxidant is natural inhibitor.
Described natural inhibitor comprises the Tea Polyphenols of 7 weight portions and/or the OPC of 7 weight portions.
Described preservative agent comprises one or more in the calcium propionate of the benzoic acid of 0.03 weight portion, the Sodium Benzoate of 0.03 weight portion, the sorbic acid of 0.01 weight portion, the potassium sorbate of 0.015 weight portion and 0.03 weight portion.
Described surfactant comprises the dodecyl sodium sulfate of 0.5 weight portion.
Described wetting agent is 80% ethanol.
Described lining is made up of paper mulberry bark; Described chemical dyestuff adsorption layer is active carbon filter screen.
The above is only the preferred embodiment of the present invention; be noted that for those skilled in the art; under the premise without departing from the principles of the invention, can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (10)
1. a preparation method for silk painting canvas, is characterized in that: comprise the following steps:
S01, at the lower surface coating drying layer of silk; Described drying layer comprises major ingredient and auxiliary material; Described major ingredient comprises the microcrystalline cellulose of 80 ~ 130 weight portions; Described auxiliary material comprises adhesive, wetting agent, surfactant, antioxidant, lubricant and preservative agent; The lower surface of described silk is coated on after described major ingredient and auxiliary material being mixed;
S02, after described drying layer drying, adheres to chemical dyestuff adsorption layer at the lower surface of described drying layer;
S03, adheres to the lining as supporting at the lower surface of described chemical dyestuff adsorption layer.
2. the preparation method of a kind of silk painting canvas according to claim 1, is characterized in that: described silk is made up of mulberry silk or tussah silk.
3. the preparation method of a kind of silk painting canvas according to claim 1, is characterized in that: described adhesive comprises the dextrin of 10 ~ 20 weight portions or the polyvinylpyrrolidone of 5 ~ 10 weight portions.
4. the preparation method of a kind of silk painting canvas according to claim 1, is characterized in that: described lubricant comprises the dolomol of 3 ~ 5 weight portions.
5. the preparation method of a kind of silk painting canvas according to claim 1, is characterized in that: described antioxidant is natural inhibitor.
6. the preparation method of a kind of silk painting canvas according to claim 5, is characterized in that: described natural inhibitor comprises the Tea Polyphenols of 3 ~ 7 weight portions and/or the OPC of 3 ~ 7 weight portions.
7. the preparation method of a kind of silk painting canvas according to claim 1, is characterized in that: described preservative agent comprises one or more in the calcium propionate of the benzoic acid of 0.01 ~ 0.03 weight portion, the Sodium Benzoate of 0.02 ~ 0.03 weight portion, the sorbic acid of 0.005 ~ 0.01 weight portion, the potassium sorbate of 0.01 ~ 0.015 weight portion and 0.01 ~ 0.03 weight portion.
8. the preparation method of a kind of silk painting canvas according to claim 1, is characterized in that: described surfactant comprises the dodecyl sodium sulfate of 0.3 ~ 0.5 weight portion.
9. the preparation method of a kind of silk painting canvas according to claim 1, is characterized in that: described wetting agent is 80% ethanol.
10. the preparation method of a kind of silk painting canvas according to claim 1, is characterized in that: described lining is made up of paper mulberry bark; Described chemical dyestuff adsorption layer is active carbon filter screen.